5 Werkstofftechnik
Filtern
Dokumenttyp
- Vortrag (431)
Sprache
- Englisch (332)
- Deutsch (96)
- Mehrsprachig (3)
Referierte Publikation
- nein (431) (entfernen)
Schlagworte
- Additive Manufacturing (38)
- Additive manufacturing (24)
- Microstructure (21)
- Corrosion (20)
- Glass (18)
- Ontology (17)
- Fatigue (13)
- Ceramics (12)
- LCF (11)
- 316L (10)
- Additive Fertigung (10)
- Creep (10)
- Ontologie (10)
- Transmission electron microscopy (10)
- Crack growth (9)
- Fraktographie (9)
- Sintering (9)
- Ceramic (8)
- Thermoelectrics (8)
- Diffraction (7)
- Fractography (7)
- Machine Learning (7)
- Particle size (7)
- Powder (7)
- Ti-6Al-4V (7)
- CCUS (6)
- DCB (6)
- Digitalisierung (6)
- EBSD (6)
- Glas (6)
- High entropy alloys (6)
- Low Cycle Fatigue (6)
- Mikrostruktur (6)
- Scanning electron microscopy (6)
- Zugversuch (6)
- 3D printing (5)
- AGIL (5)
- Aluminium (5)
- Anisotropy (5)
- Crystal plasticity (5)
- Crystallization (5)
- Glass fiber reinforced polymers (5)
- In situ (5)
- Microgravity (5)
- Oxidation (5)
- Slurry (5)
- VSSA (5)
- Water speciation (5)
- AISI 316L (4)
- Alloy 2618A (4)
- CALPHAD (4)
- CCS (4)
- CO2 (4)
- Coarsening (4)
- Creep behavior (4)
- Degradation (4)
- Droplet corrosion (4)
- EN AW-2618A (4)
- FAIR (4)
- FAIR data management (4)
- Fatigue crack growth (4)
- Fe-Al alloys (4)
- Foaming (4)
- High-temperature corrosion (4)
- In-space manufacturing (4)
- Intermetallics (4)
- Iron aluminides (4)
- Kriechen (4)
- Laser powder bed fusion (4)
- Layerwise slurry deposition (4)
- Martensitic steel (4)
- Mechanical properties (4)
- Nano (4)
- Nano powder (4)
- Neutron diffraction (4)
- Nickel-base superalloys (4)
- Non-destructive testing (4)
- Normung (4)
- Plattform MaterialDigital (4)
- Polymer matrix composites (4)
- Residual Stress (4)
- Semantic Web Technologies (4)
- Sulfidation (4)
- Supercritical/dense phase CO2 (4)
- TMF (4)
- Thermomechanical fatigue (4)
- Vickers (4)
- Wissensrepräsentation (4)
- Alkali ions (3)
- Alumina (3)
- Aluminium Alloy (3)
- Aluminium alloy (3)
- Betriebsfestigkeit (3)
- CCU (3)
- Carbon steels (3)
- Ceramic spring (3)
- Computed Tomography (3)
- Dielectric strength (3)
- Fracture surface (3)
- Full Notch Creep Test (3)
- Gassensorik (3)
- Geothermal (3)
- H2Safety@BAM (3)
- Heat treatment (3)
- High temperature corrosion (3)
- Keramik (3)
- Knowledge graph and ontologies (3)
- Lebensdauer (3)
- Mechanical behavior (3)
- Mechanical testing (3)
- Mikroplastik (3)
- Ni-Resist (3)
- PMD (3)
- Residual stress (3)
- S-phase (3)
- SEM (3)
- Scarf repairs (3)
- Semantic Interoperability (3)
- Silicate Glasses (3)
- Soda-lime silicate glass (3)
- Superaustenite steel (3)
- Tensile Test (3)
- Texture (3)
- Transmission electron microscopy (TEM) (3)
- Wasser (3)
- Water content (3)
- Welding (3)
- Wind turbine blades (3)
- X-ray diffraction (3)
- Zerstörungsfreie Prüfung (3)
- μ-gravity (3)
- Advanced ceramics (2)
- Alkali zinc borate glasses (2)
- Alterung (2)
- Analytische Zentrifuge (2)
- Bildanalyse (2)
- CLS (2)
- CO2 quality (2)
- CT (2)
- Calciumcobaltit (2)
- Calciummanganat (2)
- Carbon capture (2)
- Carbon capture storage (2)
- Carbon dioxide (2)
- Carbon steel (2)
- Characterization (2)
- Chemically complex alloy (2)
- Composite (2)
- Composites (2)
- Concrete (2)
- Copper (2)
- Crack tip opening displacement (2)
- Creep data (2)
- Dark-field transmission electron microscopy (2)
- Data Fusion (2)
- Data Interoperability (2)
- Data mapping (2)
- Datenbank (2)
- Dielectric breakdown (2)
- Diesel (2)
- Diffraction Elastic Constants (2)
- Diffusion (2)
- Digital image correlation (2)
- Digitaler Zwilling (2)
- Digitalization (2)
- Digitization (2)
- Digtial Representation (2)
- Diopside (2)
- Dislocation (2)
- EDXRD (2)
- Electron microscopy (2)
- Electron-beam-induced modification (2)
- Electronic Lab Notebook (2)
- Environmental Stress Cracking (2)
- Environmental stress cracking (2)
- Faser-Kunststoff-Verbunde (2)
- Faserkunststoffverbunde (2)
- Faseroptische Sensorik (2)
- Ferritic-martensitic steels (2)
- Fracture Toughness (2)
- Full-Notch Creep Test (FNCT) (2)
- Geführte Ultraschallwellen (2)
- Gitterkonstanten (2)
- Glass-ceramics (2)
- Hard machining (2)
- High Cycle Fatigue (2)
- High Entropy Alloy (2)
- High Temperature Corrosion (2)
- High temperature (2)
- High temperature mechanical properties (2)
- High-entropy alloy (2)
- High-entropy alloys (2)
- Hochentropie-Legierung (2)
- Hochtemperatur (2)
- Impurities (2)
- In-situ (2)
- Interoperability (2)
- Joined nickel-based alloys (2)
- L-PBF (2)
- Laser (2)
- Laser Powder Bed Fusion (2)
- Laser Powder Bed fusion (2)
- Laser beam melting (2)
- Layerwise (2)
- Leckdetektion (2)
- Lunar regolith simulant (2)
- ML (2)
- Material Digital (2)
- Material digital (2)
- Metrologie zur Wasserstoffspeicherung (2)
- Microplastics (2)
- Microstrucrue Design (2)
- Microstructural analysis (2)
- Microstructure Design (2)
- Mixed gas atmosphere (2)
- Modeling (2)
- Multilayer (2)
- Multilayer technology (2)
- Multilayertechnik (2)
- NDT (2)
- Nano particle (2)
- Nano screening (2)
- Nano-powder (2)
- Nanomaterial (2)
- Nanoparticles (2)
- Nanopulver (2)
- Notches (2)
- OECD TG 124 (2)
- Ontologien (2)
- Ontology development (2)
- Orientation (2)
- Oriented surface crystallization (2)
- Oxidation behavior (2)
- Oxide Glasses (2)
- Oxidglas (2)
- PBF-LB/M/316L (2)
- PE-HD (2)
- PMD Core Ontology (2)
- PMDco (2)
- Partikelgrößenverteilung (2)
- Phase-field simulation (2)
- Phasenidentifikation (2)
- Pipeline (2)
- Plattform Material Digital (2)
- Polyethylen (2)
- Polyethylen hoher Dichte (2)
- Polymer Matrix Composites (2)
- Process monitoring (2)
- Push-out Test (2)
- REM (2)
- Reaction sintering (2)
- Residual Stresses (2)
- Ressidual stress (2)
- Rotor blade (2)
- Sandwich (2)
- Scale-bridging (2)
- Schadensanalyse (2)
- Schädigung (2)
- Selective Laser Melting (2)
- Semantic Representation (2)
- Semantic Web (2)
- Semantisches Web (2)
- SensRef (2)
- Silicon Carbide (2)
- Silver diffusion (2)
- Silver-glass-metallization-paste (2)
- Simulation (2)
- Sinter additive (2)
- Sintering additives (2)
- Sintern (2)
- Spannungsriss (2)
- Spectroscopy (2)
- Spray drying (2)
- Spring constant (2)
- Standard (2)
- Standardisierung (2)
- Standardization (2)
- Structural Health Monitoring (SHM) (2)
- Superlegierung (2)
- Surface energy (2)
- TED-GC-MS (2)
- TEM (2)
- Tensile Test Ontology (2)
- Tensile data (2)
- Tensile test (2)
- Thermo-Mechanical Fatigue (2)
- Thermoelectric (2)
- Ti64 (2)
- TiAl5V4 (2)
- Titan (2)
- Topographie (2)
- Topography (2)
- UV-irradiation (2)
- Ultrasound (2)
- Virtual experiments (2)
- Viscoplasticity (2)
- Viscosity (2)
- Wall thickness (2)
- Wind turbine blade shells (2)
- Windenergie (2)
- XANES (2)
- XRD (2)
- Zero-g (2)
- Zugeigenschaften (2)
- robotische Glasschmelzanlage (2)
- µ-gravity (2)
- 3D (1)
- 3D Druck (1)
- 3D REM (1)
- 3D Reconstruction (1)
- 3D glass structure model (1)
- 3D materialography (1)
- 3D-printing (1)
- 9-12% Cr ferritic-martensitic steels (1)
- 9–12%Cr steel (1)
- AFM based test methods (1)
- AM (1)
- Accelerated integration scheme (1)
- Acids (1)
- Active thermography (1)
- Additiv gefertigter Stahl (1)
- Adiabatic shear bands (1)
- Advanced manufacturing (1)
- Aerospace (1)
- Age hardening (1)
- Ageing (1)
- Agglomerates (1)
- Aggressive gases (1)
- Aging (1)
- Air-coupled ultrasonic testing (1)
- Airborne ultrasonic testing (1)
- Al-Li alloys (1)
- Alkali zinc borate glass (1)
- Aluminum (1)
- Aluminum alloys (1)
- Analyse (1)
- Analysis (1)
- Analytik (1)
- Annealing (1)
- Atmospheric plasma spraying (1)
- Aussonderugnsrate (1)
- Austenitic cast iron (1)
- Austenitic steel 316L (1)
- Automatable digital approach (1)
- Automation (1)
- BET (1)
- Biaxial strength (1)
- Binder jetting (1)
- Bioactive (1)
- Bioactive Glass (1)
- Bioceramics (1)
- Biodiesel (1)
- Blähen (1)
- Bond energy (1)
- Breakdown strength (1)
- Brinell hardness (1)
- Bruchflächen (1)
- Bruchflächenanalyse (1)
- Bruchflächenauswertung (1)
- Bundesoberbehörden (1)
- CFK (1)
- CO2-corrosion (1)
- Calcination (1)
- Calcium cobaltite (1)
- Calcium manganate (1)
- Calcium sulfates (1)
- Calibration (1)
- Cantor alloy (1)
- Capture (1)
- Carbon (1)
- Carbon steels (1)
- Carbon Capture (1)
- Carbon Capture, Utilization and Storage (CCUS) (1)
- Carbon Fiber Reinforced Plastics (1)
- Carbon Fibers (1)
- Casting (1)
- Centrifugal casting (1)
- Ceramic multilayer (1)
- Ceramic springs (1)
- Certification Standard 22 (1)
- Certified Referencematerial (1)
- Cetrifugal Liquid Sedimentation CLS (1)
- Chemically complex alloys (1)
- Chemo-mechanical coupling (1)
- Chromatography (1)
- Chromia (1)
- Chromium oxide (1)
- Co-firing (1)
- Co-segregation (1)
- Coatings (1)
- Complex borides (1)
- Complex loading (1)
- Component assessment (1)
- Composite testing (1)
- Compositionally complex alloys (1)
- Computed tomography (1)
- Condensation (1)
- Contamination (1)
- Continnum damage model (1)
- Cooling simulations (1)
- Cow stress (1)
- Cr2O3 (1)
- Crack (1)
- Crack Propagation (1)
- Crack evolution (1)
- Crack propagation (1)
- Creep anisotropy (1)
- Creep behaviour (1)
- Creep-Fatigue (1)
- Creep-fatigue (1)
- Crevice corrosion (1)
- Cross linking (1)
- Crystal Defects (1)
- Crystal Orientation (1)
- Crystal Plasticity Modelling (1)
- Cubical Iron Oxide (1)
- Cure process (1)
- Cycle jump (1)
- Cyclic R-Curve (1)
- Cyclic oxidation (1)
- Cyclic softening (1)
- DIN (1)
- DLS (1)
- Damage (1)
- Damage Behavior (1)
- Damage Tolerance (1)
- Damage behavior (1)
- Damage mechanisms (1)
- Dark-field transmission electron microscopy (DFTEM) (1)
- Data Exchange (1)
- Data Management (1)
- Data Structures (1)
- Data linking (1)
- Data management (1)
- Data pipeline concept (1)
- Data space (1)
- Data storage (1)
- Data structure (1)
- Datenökosystem (1)
- Deep learning (1)
- Defects (1)
- Defects phase diagram (1)
- Defects thermodynamics (1)
- Deformation behavior (1)
- Dehnungsfehler (1)
- Density (1)
- Density-based Thermodynamics (1)
- Density-based model (1)
- Density-based phase-field modelling (1)
- Dental (1)
- Destabilization (1)
- Die casting (1)
- Dielectric breakdown strength (1)
- Dielectric characterization (1)
- Diffraction Enhanced Imaging (1)
- Diffraction contrast (1)
- Diffusion coefficient (1)
- Digital representation (1)
- Digital workflow (1)
- Dislocation substructure (1)
- Dislocations (1)
- Disordered assemblies (1)
- Dispersion process (1)
- Dissimilar metal weld (1)
- Dissolved water (1)
- Distribution function (1)
- Driving physical mechanism (1)
- Dual-energy (1)
- Durchschlagfestigkeit (1)
- Dynamic mechanical analysis (1)
- Dynamic mechanical analysis (DMA) (1)
- Dynamisch Mechanische Analyse (1)
- EAC-1A (1)
- EASA (1)
- EDX (1)
- EN AW 2618A (1)
- Early oxidation (1)
- Eigenspannung (1)
- Elastic constants (1)
- Electric field distribution (1)
- Electric field strength (1)
- Electrical insulation (1)
- Electron Backscatter Diffraction (1)
- Electron Microscopy (1)
- Electron backscatter diffraction (1)
- Electron backscattered diffraction (EBSD) (1)
- Elektronisches Laborbuch (ELN) (1)
- Energy harvesting (1)
- Entwicklung (1)
- Environmental Stress Cracking (ESC) (1)
- Ermüdung (1)
- Ermüdungsriss (1)
- Erneuerbare Energien (1)
- Etching (1)
- Extensometer (1)
- FAIR Data Management (1)
- FAIR data (1)
- FCH JU (1)
- FIB (1)
- Fabrication method (1)
- Fahrrad (1)
- Failure test (1)
- Faser (1)
- Faseroptik (1)
- Faserverstärkte Kunstoffe (1)
- Fatigue Crack Growth (1)
- Fatigue Life Evaluation (1)
- Fatigue damage (1)
- Fatigue fracture (1)
- Fatigue of sandwich shell structures (1)
- Fatigue of sandwich structures (1)
- Fatigue performance (1)
- FeCr- alloys (1)
- Federkonstante (1)
- Feldspar (1)
- Fem (1)
- Ferritic Alloys (1)
- Ferroelectret (1)
- Ferroelektret (1)
- Fertigungstechnologie (1)
- Festigkeit (1)
- Fiber (1)
- Fiber reinforced polymer (1)
- Fiber reinforced polymers (1)
- Fine Powder (1)
- Finite element analysis (1)
- Finite elmenet simulation (1)
- Flowability (1)
- Fluorescence spectroscopy (1)
- Focused Ion Beam (1)
- Foliengießen (1)
- Force-distance diagram (1)
- Formerkennung (1)
- Fracture Mechanics (1)
- Fracture Surface Analysis (1)
- Fracture behavior (1)
- Fracture surface analysis (1)
- Fracture toughness (1)
- Freeze Drying (1)
- GC-MS (1)
- GD-OES (1)
- Gas storage (1)
- Gasabgabe (1)
- Gasgehalt (1)
- Gasturbinen (1)
- Gefüge (1)
- General Aviation (1)
- Geopolymers (1)
- Gitterfehlpassung (1)
- Glasmatrixkomposit (1)
- Glass Fibres (1)
- Glass composition (1)
- Glass fibre reinforced plastics (1)
- Glass melting (1)
- Glass powder (1)
- Glass screening device (1)
- Gold nanoparticle synthesis (1)
- Gold nanoparticles (1)
- Gradient-enhanced damage (1)
- Grain boundaries (1)
- Grain boundary engineering (1)
- Granules (1)
- Granulometrie (1)
- Graphic design (1)
- Grünfolieneigenschaften (1)
- HDPE Soprption (1)
- HEA (1)
- HIP (1)
- Hardness (1)
- Hartbearbeitung (1)
- Heat Treatment (1)
- Heat Treatments (1)
- Heißgasextraktion (1)
- Heißgaskorrosion (1)
- High Entropy Alloys (1)
- High Temperature Testing (1)
- High entropy alloy (1)
- High entropy superalloys (1)
- High-Temperature Corrosion (1)
- High-density polyethylene (1)
- Hochentropielegierungen (1)
- Hochspannungsprüfung (1)
- Hochtemperaturbrennstoffzelle (1)
- Hochtemperaturermüdung (1)
- Horizon 2020 (1)
- Hot Press (1)
- Hot isostatic pressing (1)
- Hot pressing (1)
- Hydrogen (1)
- Hydrogen permeation (1)
- Hydrogen sensor (1)
- Hydrogen sensors (1)
- Hyper-arid (1)
- IN 718 (1)
- IN738LC (1)
- IR (1)
- ISRU (1)
- Implant failures (1)
- Implants (1)
- In situ tensile test (1)
- In-Situ Testing (1)
- Inconel 686 coating (1)
- Inconel 718 (1)
- Infrastructure (1)
- Initial attachment (1)
- Injection (1)
- Interface (1)
- Interface Strength (1)
- Interfacial Spinodal (1)
- Internal friction (1)
- Inverse ostwald ripening (1)
- Investment casting (1)
- Iron oxide nanoparticles (1)
- Kalzinierung (1)
- Kavitation (1)
- Kennwertermittlung (1)
- Keramikfeder (1)
- Keramische Folien (1)
- Klebung (1)
- Kleinprobenprüfung (1)
- Knowledge Graphs (1)
- Knowledge Representation (1)
- Knowledge graph (1)
- Kontrastierung (1)
- Korrosion (1)
- Kriechversuche (1)
- Kristallisation (1)
- Kunststoffe (1)
- Kupfer (1)
- Kurzzeitfestigkeit (1)
- L-PBF 316L (1)
- LSD-print (1)
- LTCC (1)
- Laminography (1)
- Laser Poeder Bed Fusion (1)
- Laser Scanning Microscopy (LSM) (1)
- Laser cladding (1)
- Laser curing (1)
- Laser induced slipcasting (1)
- Laserbearbeitung (1)
- Laserscanningmikroskopie (LSM) (1)
- Lattice misfit (1)
- Layer depostion (1)
- Layer system (1)
- Layerwise Slurry Deposition (1)
- Legierung mit komplexer Zusammensetzung (1)
- Li-ion battery (1)
- Life cycle (1)
- Lightweight materials (1)
- Lightweighting (1)
- Lithium Ion Batteries (1)
- Localized plasmons (1)
- Long-term storage (1)
- Low cycle fatigue (1)
- Low-Cycle-Fatigue (1)
- Low-cycle-fatigue behaviour (1)
- Luftultraschall (1)
- Lunar habitat (1)
- Lösungsmittel (1)
- MEA (1)
- Manganese oxide (1)
- Manufacturing (1)
- Martensitic steel (1)
- Mat-o-lab (1)
- Material Life Cycle (1)
- Material defects (1)
- MaterialDigital (1)
- Materialcharakterisierung (1)
- Materialentwicklung (1)
- Materialmodell (1)
- Materials Data Space (1)
- Materials Modelling (1)
- Materials Science (1)
- Materials and Processes Data Reusability (1)
- Materials science (1)
- Materials testing (1)
- Materialwissenschaft (1)
- Matrix (1)
- Mechanical and thermal testing (1)
- Mechanische Eigenschaften (1)
- Mechanisches Verhalten (1)
- Mechanistic Modelling (1)
- Medium Entropy Alloys (1)
- Medium entopy alloy (1)
- Medium-entropy alloy (1)
- Melt pool boundary (1)
- Metadata schema (1)
- Metallic components (1)
- Metallic silver precipitates (1)
- Metallography (1)
- Metrologie (1)
- Micro-shrinkages (1)
- Microbiologically influenced corrosion (1)
- Microhardness (1)
- Micromechanical model (1)
- Microstructural characterization (1)
- Microstructural evolution (1)
- Microstructural orientation (1)
- Microstructure Characterization (1)
- Microstructure Evolution (1)
- Microstructure characterisation (1)
- Microstructure design (1)
- Microstructure evolution (1)
- Microstructure modification (1)
- Microstructure-property-correlation (1)
- Mid-Level Ontology for MSE (1)
- Mikro-Computertomographie (1)
- Mikrogravitation (1)
- Mikrostrukturentwicklung (1)
- Mindedestberstdruck (1)
- Mixed Ca-K-Na phosphates (1)
- Mn3O4 (1)
- Modell (1)
- Monte-Carlo Simulation (1)
- Mortar (1)
- Mortel (1)
- Multi-principal element alloys (1)
- Multiaxial stress state (1)
- NTE (1)
- Na and K rhenanites (1)
- Nano material (1)
- Nano-assemblies (1)
- Nanoparticle synthesis (1)
- Nanopartikel (1)
- Nanoplattform (1)
- Negative charged microparticle (1)
- Neutron Diffraction (1)
- New standards (1)
- Nickel-base superalloy (1)
- Non-desired foaming (1)
- Nondestructive testing (1)
- Nucleation (1)
- Nucleation mode (1)
- OECD TG (1)
- Oberflächenaktive wässrige Medien (1)
- Online quality control (1)
- Ontologies (1)
- Ooxidation (1)
- Optic (1)
- Overaging (1)
- Oxide glass (1)
- P92 (1)
- P92 steels (1)
- PA6.6 (1)
- PPA (1)
- Parametric modeling (1)
- Particle size determination (1)
- Partikelgröße (1)
- Patent (1)
- Paving (1)
- Phase Diagrams (1)
- Phase Separation (1)
- Phase analysis (1)
- Phase diagram (1)
- Phase field simulation (1)
- Phase separation (1)
- Phase transformation (1)
- Phase transformations (1)
- Phase-Field Simulation (1)
- Phase-Field Simulations (1)
- Phase-field Simulation (1)
- Photon counting detector (1)
- Physically based material model (1)
- Physics-informed Neural Network (1)
- Pipeline network (1)
- Planetary surface (1)
- Platform Material Digital (1)
- Platform Material Digital (PMD) (1)
- Platform MaterialDigital (1)
- Platform MaterialDigital (PMD) (1)
- Plattform Material Digital (PMD) (1)
- Pole figures (1)
- Polyaniline (1)
- Polyethylene, PE-HD (1)
- Polymer (1)
- Polymer Matrix Composite (1)
- Polymerwissenschaften (1)
- Porcelain (1)
- Pores (1)
- Powder deposition (1)
- Power plant (1)
- Precipitates (1)
- Precipitation (1)
- Precipitation Analysis (1)
- Precipitation hardening (1)
- Preparation (1)
- Pressure assisted sintering (1)
- Pressure-assisted sintering (1)
- Probengrößeneffekt (1)
- Protective coating (1)
- Präparation (1)
- Pull-out (1)
- Pycnometry (1)
- Quantitative Precipitation Analysis (1)
- Quantitative image analysis (1)
- Rafting (1)
- Recommendations (1)
- Recycling (1)
- Reference data (1)
- Reference material (1)
- Referenzdaten (1)
- Refractory chemically complex alloy (1)
- Refractory chemically complex alloys (1)
- Regelwerke (1)
- Relaxation (1)
- Relaxation metallic glasses (1)
- Relaxationsphänomene (1)
- Repair of sandwich shell structures (1)
- Reproducibility (1)
- Research Data Management (1)
- Residual stress analysis (1)
- Residual stresses (1)
- Resistance (1)
- Restberstfestigkeit (1)
- Review (1)
- Rissentwicklung (1)
- Rissheilung (1)
- Risswachstum (1)
- Roboter (1)
- Robotic melting (1)
- Robotische Schmelzanlage (1)
- Rotorblattschalen (1)
- Roughness (1)
- Röntgen-Refraktion (1)
- Röntgenbeugung (1)
- Röntgenrefraktion (1)
- S355 steel sheet (1)
- SHM (1)
- SIMS (1)
- SLM (1)
- Safety assessment (1)
- Sailplane Development Panel (1)
- Salzschmelzen (1)
- Sample preparation (1)
- Sandwich structures (1)
- Scanning Electron Microscopy (SEM) (1)
- Scanning electron microscope (1)
- Scanning transmission electron microscopy (STEM) (1)
- Scarf joint repair (1)
- Schadensprävention (1)
- Schwerelosigkeit (1)
- Schwingbrüche (1)
- Schwingstreifen (1)
- Screen printing (1)
- Selective laser melting (1)
- Semantic Data (1)
- Semantic Interioerability (1)
- Semantic structuring (1)
- Semantic web (1)
- Semiconductor materials (1)
- Sensor (1)
- SiO2 (1)
- Sibayak (1)
- Silber (1)
- Silicatglas (1)
- Silver cluster (1)
- Silver metallization paste (1)
- Silver precipitates (1)
- Silver-glass metallization paste (1)
- Simulation of concrete (1)
- Single-Crystal (1)
- Single-crystals (1)
- Sintering atmosphere (1)
- Sintertemperatur (1)
- Sinterung (1)
- Size distribution (1)
- Slow Crack Growth (SCG) (1)
- Slow crack growth (1)
- Small-Angle X-ray Scattering (1)
- Soda-lime-silica glass (1)
- Sol-gel coating (1)
- Solar sintering (1)
- Solid solution strengthening (1)
- Space exploration (1)
- Spannungs-Dehnungs-Verhalten (1)
- Spark plasma sintering (1)
- Specific surface (1)
- Spezifische Oberfläche (1)
- Spinodal Decomposition (1)
- Split Hopkinson bar (1)
- Spring constant (1)
- Stainless steel (1)
- Stanzen (1)
- Steel (1)
- Storage (1)
- Strain rate dependence (1)
- Structure (1)
- Structured heating (1)
- Struktur (1)
- Subsurface defects (1)
- Sulfiding (1)
- Superalloy (1)
- Superalloy single crystals (1)
- Superalloys (1)
- Superaustenite steel (1)
- Supercritical/dense phase CO 2 (1)
- Superlegierungen (1)
- Surface (1)
- Surface Energy (1)
- Surface Nucleation (1)
- Surface crystallization (1)
- Surface nucleation (1)
- Symbolik (1)
- Symmetric dwell periods (1)
- Synchrotron CT (1)
- Synchrotron radiation (1)
- Synchrotronstrahlung (1)
- Syngle Crystal alloy (1)
- Synthetic air (1)
- Systematische Schadensanalysen, Prozeduren (1)
- TAHYA (1)
- TED (1)
- TMF experiments (1)
- Temperature (1)
- Temperature driven process (1)
- Temperaturschwankungen (1)
- Tempered Martensite Ferritic Steels (1)
- Tempered martensite ferritic steel (1)
- Tempered martensite ferritic steels (1)
- Tensile Properties (1)
- Tensile stress relaxation (1)
- Tensile testing (1)
- Texturation (1)
- Thermal degradation (1)
- Thermal stress (1)
- Thermische Analyse (1)
- Thermo mechanical fatigue (1)
- Thermo-mechanical fatigue (1)
- Thermo-mechanical-loading (1)
- Thermo-optical measurement (1)
- Thermoanalytical Methods (1)
- Thermoelectric generator (1)
- Thermoelectric oxide (1)
- Thermoelektrika (1)
- Thermoelektrischer Generator (1)
- Thermographie (1)
- Thermogravimetric analysis (1)
- Thermogravimetry (1)
- Thermomechanics (1)
- Thermomechanik (1)
- Thermomechanische Eigenschaften (1)
- Thermoset polymers (1)
- Thesaurus (1)
- Titanium (1)
- Tomography (1)
- Tools (1)
- Transmissionselektronenmikroskopie (1)
- Transparent ceramics (1)
- Two Photon Polymerization (1)
- Ultraschall (1)
- Umgebungsbedingter Spannungsriss (1)
- Under cyclic loading (1)
- Utilization (1)
- Utilization, and storage (CCUS) technology (1)
- VCSEL (1)
- Vacuum hot extraction (1)
- Vernetzung (1)
- Versetzungsstrukturen (1)
- Vickers hardness (1)
- Virtueller Materialdatenraum (1)
- Viscose sintering (1)
- Viskoplastisch (1)
- Wandler (1)
- Waste water (1)
- Water-based (1)
- Weibull Distribution (1)
- Weibull distribution (1)
- Welding processing influences (1)
- Werkstoffdaten (1)
- Werkstoffprüfung (1)
- Whole-chain CCS scenario (1)
- Wind energy (1)
- Wind turbine (1)
- Wind turbine blade shell structures (1)
- Withstand voltage tests (1)
- Workshop (1)
- Wärmespeicher (1)
- X-Ray Diffraction (1)
- X-ray imaging (1)
- X-ray laminography (1)
- X-ray refraction (1)
- XRM (1)
- Zugversuchsontologie (1)
- Zyklische Belastung (1)
- Zyklische R-Kurve (1)
- alumina (1)
- arbon capture (1)
- carbon steel (1)
- ceramic (1)
- ceramics (1)
- condensate (1)
- corrosion (1)
- dental (1)
- dispersion (1)
- electrochemical characterization (1)
- impurities (1)
- microstructure analysis (1)
- multi scale testing (1)
- particle size determination (1)
- pitting corrosion (1)
- sample preparation (1)
- selective laser melting (1)
- thermomechanische Beanspruchung (1)
- utilization, and storage (CCUS) technology (1)
- volume resistivity (1)
- zertifizierte Referenzmaterialien (1)
- Öffentliche Sicherheit (1)
- Überblick (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (431)
- 5.2 Metallische Hochtemperaturwerkstoffe (115)
- 5.1 Mikrostruktur Design und Degradation (112)
- 5.4 Multimateriale Fertigungsprozesse (101)
- 5.3 Polymere Verbundwerkstoffe (52)
- 5.6 Glas (51)
- 8 Zerstörungsfreie Prüfung (46)
- 5.5 Materialmodellierung (45)
- 9 Komponentensicherheit (44)
- 8.5 Röntgenbildgebung (35)
Eingeladener Vortrag
- nein (431) (entfernen)
Many microstructural features exhibit non-trivial geometries, which can only be derived to a limited extent from two-dimensional images. E.g., graphite arrangements in lamellar gray cast iron have complex geometries, and the same is true for additively manufactured materials and three-dimensional conductive path structures. Some can be visualized using tomographic methods, but some cannot be due to weak contrast and/or lack of resolution when analyzing macroscopic objects. Classic metallography can help but must be expanded to the third dimension. The method of reconstructing three-dimensional structures from serial metallographic sections surely is not new. However, the effort required to manually assemble many individual sections into image stacks is very high and stands in the way of frequent application. For this reason, an automated, robot-supported 3D metallography system is being developed at BAM, which carries out the steps of repeated preparation and image acquisition on polished specimen.
Preparation includes grinding, polishing and optionally etching of the polished surface. Image acquisition comprises autofocused light microscopic imaging at several magnification levels. The image stacks obtained are then pre-processed, segmented, and converted into 3D models, which in the result appear like microtomographic models, but with high resolution at large volume. Contrasting by classical chemical etching reveals structures that cannot be resolved using tomographic methods. The integration of further imaging and measuring methods into this system is underway. Some examples will be discussed in the presentation.
Determination of Distribution Function used in MCS on Safety Analysis of Hydrogen Pressure Vessel
(2019)
The test data of static burst strength and load cycle strength of composite pressure vessels are often described by GAUSSian normal or WEIBULL distribution function to perform safety analyses. The goodness of assumed distribution function plays a significant role in the inferential statistics to predict the population properties by using limited test data. Often, GAUSSian and WEIBULL probability nets are empirical methods used to validate the distribution function; Anderson-Darling and KolmogorovSmirnov tests are the mostly favorable approaches for Goodness of Fit. However, the different approaches used to determine the parameters of distribution function lead mostly to different conclusions for safety assessments. In this study, six different methods are investigated to show the variations on the rates for accepting the composite pressure vessels according to GTR No. 13 life test procedure. The six methods are: a) NormLog based method, b) Least squares regression, c) Weighted least squares regression, d) A linear approach based on good linear unbiased estimators, e) Maximum likelihood estimation and f) The method of moments estimation. In addition, various approaches of ranking function are considered. In the study, Monte Carlo simulations are conducted to generate basic populations based on the distribution functions which are determined using different methods. Then the samples are extracted randomly from a population and evaluated to obtain acceptance rate. Here, the “populations” and “samples” are corresponding to the burst strength or load cycle strength of the pressure vessels made from composite material and a plastic liner (type 4) for the storage of hydrogen. To the end, the results are discussed, and the best reliable methods are proposed.
The presence of large quantities of plastic waste and its fragmentation in various environmental compartments are an important subject of current research. In the environment, (photo ) oxidation processes and mechanical abrasion lead to the formation of microplastics. However, until now, there are no established quality assurance concepts for the analysis of microplastic (<5 mm) in environmental compartments, including sampling, processing and analysis.
The aim of the present work is the development of suitable examination methods and protocols (sampling, sample preparation and detection) to qualify and quantify microplastic in urbane water management systems. At first a fractional filtration system for sampling and the analytical tool, the so-called TED-GC-MS (thermal desorption gas chromatography mass spectrometry) were developed. The TED-GC-MS method is a two-step analytical procedure which consists of a thermal extraction where the sample is annealed and characteristic decomposition products of the polymers are collected on a solid phase. Afterwards these products are analysed using GC-MS. The developed fractional filtration for sampling and the TED-GC-MS for detection were used for quantitative analysis to screen the waste water influent and effluent of a Berlin waste water treatment plant for the most relevant polymers, polyethylene (PE), polypropylene (PP), polystyrene (PS), polyethylene terephthalate (PET) and polyamide (PA).
The results of the study revealed that the polymeres PE, PS and PP were detected in the effluent, and PE and PS were find in the raw waste water of the sewage treatment plant in Ruhleben, Berlin. Differences in polymer types and amounts were detected at different sampling dates and within different sieve fractions. Much higher amounts of polymers were observed in the raw waste water. The peak areas of the decomposition products, used for quantification of the polymers, were adjusted using so-called response factors since the TED-GC-MS method is more sensitive for PP and PS than for PE. It has been shown that PE is the most dominant polymer in the samples. Comparing the masses of polymers in the effluent and in the raw sewage, a removal of 99 % of the polymers in the water treatment plant can be assumed. These results are consistent with the literature where removal rates between 98-99 % were described.
Destructive and non-destructive 3D-characterization of inner metal structures in ceramic packages
(2023)
Ceramic multilayer packages provide successful solutions for manifold
applications in telecommunication, microsystem, and sensor technology. In such packages, three-dimensional circuitry is generated by combination of structured and metallized ceramic layers by means of tape casting and multilayer technology. During development and for quality assurance in manufacturing, characterization of integrity, deformation, and positioning of the inner metal features is necessary.
Visualization with high resolution and material contrast is needed.
Robot-assisted 3D-materialography is a useful technique to characterize such multimaterial structures. In that, many sections of the specimen are polished and imaged automatically. A three-dimensional representation of the structure is created by digital combination of the image stack. A quasi non-destructive approach is to perform X-ray computer tomography (CT) with different beam energies. The energies are chosen to achieve a good imaging of either the metal features, or the ceramic matrix of the structure. The combination of the respective tomograms results in a high contrast representation of the entire structure. Both methods were tested to characterize Ag and Ag/Pd conductors in a ceramic multilayer package. The results were compared in terms of information content, effort, and applicability of the methods.
Ceramic springs offer versatile possibilities for load bearing or sensor applications in challenging environments. Although it may appear unexpected, a wide range of spring constants can be implemented by material selection and especially by the design of the spring. Based on a rectangular cross-section of the windings, it is possible to design a spring geometry that generates the desired spring constant simply by choosing appropriate diameter, height, widths, and number of windings. In a recent research project the calculation of helical compression springs made of rectangular steel (German standard DIN 2090) was applied for the design of ceramic springs. A manufacturing technology has been worked out to fabricate such springs from hollow cylinders of several highly dense technical ceramics by milling. Ceramic springs with precise rectangular section, without edge damage, and mean surface roughness smaller than 0.2 µm were produced after parameter optimization. Tolerances of less than 10 µm were achieved regarding spring diameter, height, and width of cross section. It is shown that the calculations outlined in the standard are valid for a variety of ceramic materials as well. Demonstrator springs with a wide range of spring constants have been fabricated, including zirconia springs with 0.02 N/mm, alumina springs with 1 N/mm and Si3N4 springs with 5 N/mm. A reproducibility study of six zirconia springs with a constant of 0.3 N/mm showed a relative difference in spring constants of less than +/- 1 %. This combination of a valid calculation approach for spring geometry and a reliable manufacturing technology allows for purposeful development and fabrication of ceramic springs with precise mechanical properties and superior chemical stability.
Systematic microstructure design requires reliable thermodynamic descriptions and phase diagrams of each and all microstructure elements. While such descriptions are well established for most bulk phases, thermodynamic assessment of crystal defects is greatly challenged by their individualistic aspects. In this talk, we present a density-based thermodynamic concept to describe defects based on available bulk thermodynamic data. Here dealing with grain boundaries (GBs), we apply this concept to compute GB (phase) diagram. Applications to segregation engineering of GBs in bulk and nanocrystalline alloys will be presented. We further develop this model to include the effect of elastic interactions due to atom size mismatch and obtain the corresponding GB (phase) diagram for the ternary Al-Cu-Li system.
Grain boundary (GB) chemical and structural variations can significantly influence materials performance. The former is generally ascribed to the structural gradient between the grain and GB. While GB segregation may be accompanied by chemical and structural variations, clear insights about the GB’s thermodynamic phase behaviour upon coupling between its chemistry and structure is lacking. Using the CALPHAD integrated density-based phase field model, we study the co-evolution of GB’s structure and segregation in Fe-Mn alloys. We found that the GB segregation transition is amplified if its structure can respond to chemical variation. Additionally, the coupling between GB structural and segregation evolution was found to enable co-existence of the spinodally formed low- and high-Mn phases within the GB. In the light of atomistic simulations, we expand on investigating the correlation between the parameters that characterise the GB density map with GB properties.
Regarding feedstocks for the additive manufacturing (AM) of ceramics, two features are most critical in classical powder based AM processes: a high particle packing density (typically >50% TD) must be achieved with very fine particles (typically submicron) in order to ensure sufficient sintering activity. Three innovative approaches will be introduced to overcome this problem:
1. Layer wise slurry deposition: The use of water based ceramic slurries as feedstock for the additive manufacture of ceramics has many advantages which are not fully exploit yet. In the layerwise slurry deposition (LSD) process a slurry with no or low organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle on the previously deposited and dried material to form thin layers with a high packing density (55-60%). The LSD therefore shares aspects both of tape casting and slip casting. The LSD differentiates from the classical powder-based AM layer deposition, which typically achieves with a flowable coarse grained powder a low packing density (35-50%) only, consequently hindering the ability of sintering ceramic parts to full density. The LSD is coupled with the principles of selective laser sintering (SLS) or binder jetting, to generate novel processes which take advantage of the possibility of achieving a highly dense powder-bed.
2. Laser induced slip casting: Contrary to the LSD process, which requires drying of each individual layer, the direct interaction of ceramic slurries with intense laser radiation, for the laser induced slip casting (LIS), is a promising approach for the additive manufacture of voluminous parts.
3. Gas flow assisted powder deposition: By the application of a vacuum pump a gas flow is realized throughout the powder bed. This gas flow stabilizes the powder bed and results into an enhanced flowability and packing density of the powder during layer deposition.
The presentation will provide a detailed discussion of potentialities and issues connected to the mentioned technologies and will describe the most recent developments in their application to technical ceramics.
Many of the most successful and precise additive manufacturing (AM) technologies are based on the deposition layer-by-layer of a flowable powder. Since the first pioneering work at the end of the 1980th many developments have been introduced, greatly extending the use of different materials, improving the physical properties of the components built and enhancing the accuracy of the process. Still very important issues remain nowadays, hampering a completely autonomous production of parts and even restricting the freedom of design by means of these technologies. One of the major issues is the low density and stability of the parts during the building process, which implies the need of support structures: The powder bed surrounding the part has an essential role, since it should support the structure during building, until it’s ready for removal. Moreover, the microstructure of the powder bed is a template for the microstructure of the part produced. In this context, the use of submicron ceramic powders is still a challenge. Three approaches for the stabilization and densification of powder beds will be presented: The Layerwise Slurry Deposition process LSD, the gas flow assisted powder deposition and the Laser Induced Slipcasting (LIS) of ceramic powder compacts.
In our current view, reference datasets in the MSE domain represent specific material properties, e.g., structural, mechanical, … characteristics. A reference dataset must fulfill high-quality standards, not only in precision of measurement but also in a comprehensive documentation of material, processing, and testing history (metadata). This Infrastructure Use Case (IUC) aims to develop a framework for generating reference material datasets using creep data of a single crystal Ni-based superalloy as a best practice example. In a community-driven process, we aim to encourage the discussion and establish a framework for the creation and distribution of reference material datasets. In this poster presentation, we highlight our current vision and activities and intend to stimulate the discussion about the topic reference datasets and future collaborations and work.
At high temperatures and in harsh environments ceramic springs are often superior to metallic springs and allow for innovative solutions. A recently proposed application involves ceramic springs with metallized surfaces as capacitive force sensor. A strictly linear stress-strain characteristic of the spring is a precondition for such a sensor.
Helical ceramic springs with rectangular cross-section have been produced from sintered hollow cylinders. Alumina, ATZ, Y-TZP, and Ce-TZP springs with identical dimensions were characterized and compared regarding deformation behavior.
Spring deformation was investigated under various load scenarios.
Dynamic compression was performed with deformation speeds from 0.3 to 30 mm/min. Spring constants of alumina springs are strain rate independent. By contrast, Y-TZP spring constant increases by approximately 3 % within the experimental framework.
A high-precision test facility was developed to characterize spring displacement in nm range under static tensile load over long periods of time. Spring elongation with asymptotic course was observed for zirconia containing materials at room temperature. This effect is particularly strong in the case of Y-TZP. Up to 0.3 % time-dependent elongation was measured after 24 h under constant load. Deformation is completely reversible after unloading. Alumina springs do not show any time-dependent deformation under identical test conditions.
Contrary to alumina springs, a non-linear stress-strain behavior of TZP springs at room temperature was proved in both test series. It is supposed, that pseudo-elasticity caused by stress-induced phase transformation from tetragonal to monoclinic is responsible for this special behavior of TZP springs.
The Topic of the presentationis a discussion on defects which can cause failure in cyclically loaded metallic components. Although also touching Features such as material defects such as pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches (which are not considered in the design process) which origin in manufacturing, and others the presentation concentrates on non-metallic inclusions. It is prefaced by an introduction to the life cycle of a fatigue crack from initiation up to fracture. Special emphasis is put on the fact that only cracks which are not arrested during one of their distinct Propagation stages can grow to a critical size.
Damage tolerance counts as one of the most widespread approach to fatigue assessment and surely as one of the most promising in understanding the process-structure-property-performance relationships in additively manufactured metallic materials. Manufacturing defects, surface roughness, microstructural features, short and long crack fatigue propagation, residual stresses and applied loads can be taken into consideration in a fracture mechanics-based fatigue assessment. Many aspects are crucial to the reliable component life prediction. Among those a prominent role is played by an accurate measurement and modelling of the short crack fatigue behavior, and reliable statistical characterization of defects and residual stresses.
This work aims at addressing the issues related to both experimental testing, fatigue and fatigue crack propagation, and fracture mechanics-based modelling of fatigue lives. Examples will be provided on an additively manufactured AISI 316 L.
Currently, the Full Notch Creep Test (FNCT) [1] method is used by material suppliers and end users in industry for the approval of container and pipe materials based on high-density polyethylene (PE-HD). The resistance to environmental stress cracking (ESC) of the material is evaluated using the time to failure of the specimen in an aqueous solution of a detergent [2, 3]. Usually specimens made of sheets with isotropic material properties, manufactured by hot pressing, are employed in order to obtain intrinsic properties of the material in terms of ESC failure. In contrast, the processes used in manufacturing to form containers and pipes, such as extrusion blow molding or extrusion, impose anisotropic properties to the material. These are mostly due to a microstructural orientation (polymer chains or crystallites) [4]. Furthermore, the different cooling conditions significantly affect the size distribution of crystallites as well as the overall morphology. It is therefore essential to understand the influence of process-induced material characteristics on failure due to ESC.
A large number of studies on material properties as a function of microstructural preferential orientation have already been conducted [5-7]. However, effects on ESC as the major failure mechanism of containers and pipes are still rather unexplored [8, 9]. The most important factor is whether primarily intramolecular high-strength covalent bonds or the substantially weaker intermolecular van der Waals forces are predominantly loaded.
In addition to the widely established classification by time to failure, the strain or crack opening displacement (COD) provides valuable information about the evolution and progression of damage as a function of time [10, 11]. Optical strain measurement using digital image correlation allows the differences in COD for isotropic and different angles of orientation of anisotropic specimens to be discussed. Also, a post-fracture surface analysis provides clarification on the craze-crack mechanism of the ESC. These different ESC-related properties of extruded and hot-pressed specimens have been investigated at different environmental medium temperatures and different initial stresses to provide a broad characterization of the fracture behavior of PE-HD.
Wind turbine rotor blades, made of fiber reinforced polymers (FRP), often fail before their projected 20-year lifespan, largely due to defects that originate during manufacturing and are propagated by operational fatigue and environmental conditions. The cost-intensive replacement outcomes lead to a high loss of earnings, and are one of the inhibitors of wind turbine production [1]. A potential repair alternative is to locally patch these areas of the blades with adhesively bonded structural repairs. However, the effects of such repair methods of the outer shell region on the structural integrity of the rotor blades are still largely unknown, and are thus investigated in this project.
The shell components of rotor blades are made of FRP composite material sandwiching a lightweight core, often a rigid foam or Balsa wood. The repair methods involve replacing the lost load path with a new material that is joined to the parent structure [2]. Repairs in this project focus on the scarf method, which allow for a smoother load distribution across the joint, aiming to study the damage mechanism of glass FRP scarf repairs for wind turbine blade shell applications. Namely, the source and path of the damage initiation and propagation, role of the interface between parent and patch material, and the role of the fiber orientation mismatch at this interface are examined. Biaxial ±45° and 0/90° FRP specimens are produced with the vacuum-assisted resin infusion (VARI) process using E-glass non-crimp fabric. The patch layers are then joined using VARI with a scarf ratio of 1:50, using glass FRP fabric with half the areal weight of the parent side to allow for better drapability. The methods and practices in specimen production are based on common industry practice in rotor blade shell manufacturing and repairs.
The specimens are tested under uniaxial tensile load, during which they are periodically monitored for damage onset. A comparison of the ±45° and 0/90° specimens allows for an understanding of the role of a highly mismatching fiber orientation in the transition zone between parent and patch material on the failure mechanism of the scarf joint. Although failure in both orientations begins as delamination at the joint edge, the difference in the mechanisms at play in the two different specimen types leads ultimately to different fracture paths. Namely, in the inter fiber failure mechanism of the ±45° specimens, the higher interlaminar strength compared to the intralaminar strength of the laminate leads to intralaminar failure of the ±45° scarf joint specimens. Alternatively, the competition in the 0/90° specimens lies between the interlaminar strength and fiber failure strength, and here we experience failure primarily across the scarf joint length. The scarf joint in the 0/90° specimens disrupts the continuity of the load-carrying 0° layers, directing the failure path to remain primarily along the scarf joint. Experimental results are compared to finite element analyses of scarf patch repairs on glass FRP sandwich specimens with the same respective layup orientations, where the damage initiation regions are identified and correlated to fiber orientation, serving as a bridge to future work which will experimentally examine the scarf repair patches on sandwich shell specimens.
The current trend towards cyclic, “flexible” operation of fossil-fueled power plants constitutes a major issue regarding lifetime and operational safety of the respective installations and their components, as was outlined in our complementary contribution (Part 1). The present contribution reports on the investigation of the microstructure evolution in cyclically loaded ferritic-martensitic steels and its representation in a physically-based micromechanical model.
For this purpose, specimens of P92 steel grade from the mechanical test programme outlined in our companion contribution (Part 1) were analyzed by scanning electron microscopy (SEM), including backscattered diffraction (EBSD) mapping, and transmission electron microscopy (TEM). A novel method was implemented to improve angular resolution of EBSD scans. Additionally, a correlative microscopy approach was developed and used to correlate EBSD and TEM measurements on the same locations of thick regions of electron transparent specimens. By applying these techniques, a detailed quantitative microstructure description of the as-received material condition, namely in terms of subgrain morphology and dislocation density/distributions, was established. Comparisons of as-received and cyclically loaded conditions from tests interrupted at different stages of lifetime indicate a rapid redistribution of in-grain dislocations with a strong interaction between mobile dislocations and low angle grain boundaries (LABs).
The proposed micromechanical model is formulated in a viscoplastic self-consistent (VPSC) scheme, which is a mean-field approach that allows us to include the crystal details at the level of slip systems while avoiding the considerable computational costs of full-field approaches (such as the classical crystal plasticity finite element analysis). Being physically-based, the model uses dislocation densities and includes the interaction between dislocations, e.g. annihilation of mobile dislocations, and evolution of microstructure, e.g. the grain coarsening. Particularly, the constitutive laws for dislocation evolution and interaction between dislocations and low angle boundaries are calibrated based on two-dimensional discrete dislocation dynamic (2D DDD) simulations, which are performed at a micro-/meso-scale. The results of the beforementioned EBSD experiments are considered as a direct input, involving e.g. the amount of geometrically necessary dislocations, average misorientations and grain characteristics.
9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in fossil fueled power plants due to their excellent creep and oxidation resistance, but changes in electricity markets during the last two decades have considerably changed the typical working conditions of these facilities. The growing share of renewable energy sources in power generation forces most of these plants into flexible operation with frequent load shifts or shutdowns. These cyclic operation profiles constitute a major lifetime issue, raising the question which fundamental processes govern the reaction of ferritic-martensitic steels to cyclic load and temperature variations.
The present contribution reports on current findings obtained in a multidisciplinary project funded by German Ministry of Education and Research (BMBF) which combines cyclic mechanical and cyclic oxidation testing of different 9-12% Cr grades with detailed microstructural analyses and related micromechanical modeling.
In the present first part of our contribution, an overview will be given on the results obtained in the mechanical testing programme of the project. Mechanical analyses were carried out on P91 and (mainly) P92 steel grades, particularly looking at softening phenomena and lifetimes obtained in isothermal cyclic loading (low cycle fatigue, LCF), non-isothermal cyclic loading (thermo-mechanical fatigue, TMF), and service-like combinations of creep and fatigue periods. For this purpose, cylindrical specimens were extracted from thick-walled steam pipes, orthogonal to the pipe axis, and subjected to strain controlled cyclic loading (± 0.2 to ±0.5 % mechanical strain) to different degrees of softening at temperatures up to 620 °C.
The test results will be presented and discussed with a focus on the impact of hold periods (i.e. combined creep-fatigue conditions) on mechanical softening, lifetime and crack formation. Details on the microstructural evolution and their representation in a micromechanical model will be given in a second, complementary contribution to this conference.
Cyclic mechanical performance and microstructure evolution of P92 under LCF and TMF conditions
(2019)
9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in fossil fueled power plants due to their excellent creep and oxidation resistance, but changes in electricity markets during the last two decades have considerably changed the typical working conditions of these facilities. The growing contribution of renewable energy sources in power generation forces most of these plants into flexible operation with frequent load shifts or shutdowns. These cyclic operation profiles constitute a major lifetime issue, raising the question which fundamental processes govern the reaction of ferritic-martensitic steels to cyclic load and temperature variations.
The present contribution reports on current findings obtained in a multidisciplinary project funded by German Ministry of Education and Research (BMBF) which combines cyclic mechanical and cyclic oxidation testing of different 9-12% Cr grades with detailed microstructural analyses and related micromechanical modeling.
In this contribution, an overview will be given on the results obtained in the mechanical testing programme of the project. Mechanical analyses were carried out on P91 and (mainly) P92 steel grades, particularly looking at softening phenomena and lifetimes obtained in isothermal cyclic loading (low cycle fatigue, LCF), non-isothermal cyclic loading (thermo-mechanical fatigue, TMF), and service-like combinations of fatigue and creep/relaxation periods. For this purpose, cylindrical specimens were extracted from thick-walled steam pipes, orthogonal to the pipe axis, and subjected to strain controlled cyclic loading (± 0.2 to ±0.5 % mechanical strain). Temperature intervals of TMF tests were chosen as either 300-620°C or 500-620°C, resembling so-called warm or hot start conditions of a power plant.
The test results will be presented and discussed with a focus on the impact of hold periods during testing (combined creep/relaxation-fatigue conditions) on mechanical softening, lifetime and formation of cracks. The findings will be complemented by results on the modification of the hierarchical ferritic-martensitic microstructure under different loading scenarios.