5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2018 (24) (entfernen)
Dokumenttyp
- Vortrag (12)
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (5)
- Buchkapitel (1)
- Posterpräsentation (1)
Schlagworte
- CCUS (6)
- Carbon steels (5)
- Martensitic steel (5)
- Superaustenite steel (5)
- Supercritical/dense phase CO2 (5)
- Concrete (4)
- Droplet corrosion (4)
- Fatigue (3)
- PE-HD (3)
- Continnum damage model (2)
- Damage (2)
- Environmental stress cracking (ESC) (2)
- Impurities (2)
- Injection (2)
- Simulation of concrete (2)
- UV-irradiation (2)
- Under cyclic loading (2)
- Accelerated integration scheme (1)
- Accelerated temporal integration (1)
- Additive manufacturing (1)
- Biodiesel (1)
- Brittle / ductile fracture behavior (1)
- CCUS, supercritical/dense phase CO2, carbon steels, martensitic steel, superaustenite steel, droplet corrosion (1)
- Calcination (1)
- Calcium Cobaltite (1)
- Carbon steels (1)
- Cement (1)
- Coating (1)
- Corrosion (1)
- Crack propagation analysis (1)
- Cycle jump (1)
- Diesel (1)
- Fatigue damage (1)
- Flow Coefficient (1)
- Fourier series (1)
- Full Notch Creep Test (FNCT) (1)
- Full notch creep test (FNCT) (1)
- GMR sensors (1)
- Geopolymers (1)
- Geothermal (1)
- Gradient-enhanced fatigue model (1)
- Imaging techniques (1)
- Initial attachment (1)
- Laser curing (1)
- Laser scanning microscopy (LSM) (1)
- Limestone Filler (1)
- Long-term storage (1)
- Low carbon steel (1)
- Magnetic stray field (1)
- Martensitic steel (1)
- Microstructure (1)
- Neutron diffraction (1)
- Particle Size Distribution (1)
- Polyaniline (1)
- Polymerwissenschaften (1)
- Reaction-sintering (1)
- Reference Material (1)
- Residual stress (1)
- Rheology (1)
- Scanning acoustic microscopy (SAM) (1)
- SiO2 (1)
- Slow crack growth (SCG) (1)
- Solid-State-Synthesis (1)
- Superaustenite steel (1)
- Supercritical/dense phase CO 2 (1)
- TIG-welding (1)
- Thermoelectrics (1)
- Volume Fraction (1)
- X-ray computed tomography (CT) (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (24) (entfernen)
Eingeladener Vortrag
- nein (12)
As the well-known damage mechanisms slow crack growth (SCG) and environmental stress cracking (ESC) are the major causes for possible failure of polyolefin-based materials, especially for PE-HD, they are highly relevant and need to be considered thoroughly. Furthermore, due to slight but perceptible differences in damaging effect, a differentiation between SCG and ESC is expedient. SCG appears in “inert” or “neutral” media without a decisive influence of the surrounding medium whereas ESC occurs in “active” media, which influence the failure behavior and time to failure crucially.
To characterize the inherent resistance of the material against those damage mechanisms, the well-established Full-Notch Creep Test (FNCT) is used. In this study, the FNCT – usually applied according to ISO 16770 [3] using a few universal model liquid media and mainly for pipe materials – is extended by investigations with appropriate parameters of selected relevant PE-HD container materials also in real media, such as the topical fuels diesel and biodiesel. The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Especially, mechanical stress and temperature were varied systematically during FNCT and time to failure values, time-dependent elongation data as well as detailed fracture surface analysis by laser scanning microscopy (LSM) were combined for the first time (Fig. 1). Particularly, the fracture surface analysis provides a sound basis to characterize failure behavior, mainly regarding the balance between brittle crack propagation and ductile deformation. Therefore, fracture surface analysis is an essential tool for a decent assessment of SCG and ESC by FNCT measurements.
In order to observe the effect of the aggregate phases between 2 mm and 16 mm without overlap with rheological effects induced by the cement hy-dration and without interactions with a threshold fine sand particle size that affects both, paste and aggregates, rheological experiments were conducted on a limestone filler based paste mixed with aggregates up to 16 mm. Vari-ous aggregate fractions were blended and mixed with the replacement paste in different volumetric ratios.
The dry aggregates’ flow coefficients were determined and compared to yield stress and plastic viscosity values at different aggregate volume fractions. The results indicated that the flow coefficient is not a suitable parameter to predict the performance of the aggregates in the paste. It was shown that the yield stress of pastes is largely determined by the blend of different aggregate fractions, while the plastic viscosity to large extend depends upon the coars-est aggregate fraction.
Based on the results, ideal aggregate composition ranges for minimised yield stress are presented. For the plastic viscosity no such grading curves to achieve minimum values could be found, but high viscosity curves are identified.
Calcium cobaltite is one of the most promising oxide p-type thermoelectric materials. The solid-state reaction (or calcination, respectively), which is well known for large-scale powder synthesis of functional materials, can also be used for the synthesis of thermoelectric oxides. There are various calcination routines in literature for Ca3Co4O9 powder synthesis, but no systematic study has been done on the influence of calcination procedure on thermoelectric properties. Therefore, the influence of calcination conditions on the Seebeck coefficient and the electrical conductivity was studied by modifying calcination temperature, dwell time, particle size of raw materials and number of calcination cycles. This study shows that elevated temperatures, longer dwell times, or repeated calcinations during powder synthesis do not improve but deteriorate the thermoelectric properties of calcium cobaltite. Diffusion during calcination leads to idiomorphic grain growth, which lowers the driving force for sintering of the calcined powder. A lower driving force for sintering reduces the densification. The electrical conductivity increases linearly with densification. The calcination procedure barely influences the Seebeck coefficient. The calcination procedure has no influence on the phase formation of the sintered specimens.
A key limitation of the most constitutive models that reproduce a Degradation of quasi-brittle materials is that they generally do not address issues related to fatigue. One reason is the huge computational costs to resolve each load cycle on the structural level. The goal of this paper is the development of a temporal Integration scheme, which significantly increases the computational efficiency of the finite element method in comparison to conventional temporal integrations.
The essential constituent of the fatigue model is an implicit gradient-enhanced formulation of the damage rate. The evolution of the field variables is computed as amultiscale Fourier series in time.On a microchronological scale attributed to single cycles, the initial boundary value problem is approximated by linear BVPs with respect to the Fourier coefficients. Using the adaptive cycle jump concept, the obtained damage rates are transferred to a coarsermacrochronological scale associated with the duration of material deterioration. The performance of the developedmethod is hence improved due to an efficient numerical treatment of the microchronological problem in combination with the cycle jump technique on the macrochronological scale. Validation examples demonstrate the convergence of the obtained solutions to the reference simulations while significantly reducing the computational costs.