5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2018 (188) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (70)
- Vortrag (68)
- Beitrag zu einem Tagungsband (23)
- Posterpräsentation (23)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (1)
- Sonstiges (1)
Sprache
- Englisch (188) (entfernen)
Schlagworte
- Additive manufacturing (12)
- Additive Manufacturing (10)
- Coarsening (8)
- Creep (8)
- Degradation (8)
- Residual stress (8)
- Fatigue (7)
- Glass (7)
- Alloy 2618A (6)
- Aluminium (6)
- CCUS (6)
- Corrosion (6)
- Crack growth (6)
- High temperature corrosion (6)
- Carbon steels (5)
- Martensitic steel (5)
- Neutron diffraction (5)
- S-phase (5)
- Superaustenite steel (5)
- Supercritical/dense phase CO2 (5)
- Vickers (5)
- Water speciation (5)
- CCS (4)
- Concrete (4)
- DCB (4)
- Damage (4)
- Droplet corrosion (4)
- EBSD (4)
- Hydrogen (4)
- Microplastics (4)
- Microstructure (4)
- Nanoparticles (4)
- Selective laser melting (4)
- Soda-lime silicate glass (4)
- Transmission electron microscopy (4)
- 3D-Printing (3)
- Calcination (3)
- Ceramic (3)
- Coating (3)
- Dark-field transmission electron microscopy (3)
- Ferritic-martensitic steels (3)
- IN718 (3)
- Inconel 686 (3)
- Laser ablation in liquid (3)
- PE-HD (3)
- Powder (3)
- Residual Stresses (3)
- Rotor blade (3)
- SLM (3)
- Selective Laser Melting (3)
- Sintering (3)
- Titanium oxide (3)
- ToF-SIMS (3)
- Wind turbine blades (3)
- 3D printing (2)
- AISI 304L (2)
- Adiabatic calorimeter (2)
- Aging (2)
- Air-coupled ultrasonic testing (2)
- Airborne ultrasonic testing (2)
- Alumina (2)
- Analysis (2)
- Anisotropy (2)
- Austenitic stainless steel (2)
- Bacteria (2)
- Carbon capture (2)
- Carbon dioxide (2)
- Composite (2)
- Composites (2)
- Continnum damage model (2)
- Crystal plasticity (2)
- Crystallization (2)
- Dark-field transmission electron microscopy (DFTEM) (2)
- Destabilization (2)
- Deuterium (2)
- Diffraction contrast (2)
- Diffusion (2)
- Diffusion coefficient (2)
- Dislocation (2)
- Electron microscopy (2)
- Environmental stress cracking (ESC) (2)
- Fatigue of sandwich shell structures (2)
- Ferroelectret (2)
- Foaming (2)
- Glass composition (2)
- High-temperature corrosion (2)
- Impurities (2)
- Injection (2)
- Long-term behavior (2)
- Metal seal (2)
- Microstructure evolution (2)
- Multilayer (2)
- Non-destructive testing (2)
- Particle morphology (2)
- Phase change material (2)
- Plastic deformation (2)
- Polymer (2)
- Porcelain (2)
- Precipitation (2)
- Pressure-assisted sintering (2)
- Reaction-sintering (2)
- Relaxation (2)
- Residual stresses (2)
- Ressidual stress (2)
- Safety assessment (2)
- Salt eutectics (2)
- Scale-bridging (2)
- Scanning transmission electron microscopy (STEM) (2)
- Simulation of concrete (2)
- Spray drying (2)
- Steel (2)
- Sulfidation (2)
- TED-GC-MS (2)
- TEM (2)
- Temperature (2)
- Thermal energy storage (2)
- Thermoelectric oxide (2)
- Thermoelectrics (2)
- Thermogravimetry (2)
- Thermomechanics (2)
- UV-irradiation (2)
- Under cyclic loading (2)
- VSSA (2)
- Virtual experiments (2)
- Viscoplasticity (2)
- Wind turbine (2)
- X-ray laminography (2)
- XANES (2)
- 316L (1)
- 3D glass structure model (1)
- 3D-finite element modeling (1)
- 3D-printing (1)
- 9-12% Cr ferritic-martensitic steels (1)
- Accelerated integration scheme (1)
- Accelerated temporal integration (1)
- Active thermography (1)
- Advanced wastewater treatment (1)
- Ageing (1)
- Aggressive environement (1)
- Aggressive environment (1)
- Aggressive gases (1)
- Al-Cu-Li-alloy (1)
- Al-Li alloys (1)
- Alloy 2818A (1)
- Alloys (1)
- Alumina coatings (1)
- Aluminium alloys (1)
- Aluminum (1)
- Aluminum alloy (1)
- Aluminum alloys (1)
- Amorphization (1)
- Amorphous silica (1)
- Annealing (1)
- Aquifer (1)
- Artefact (1)
- Atomic packing factor (1)
- Austenitic steel (1)
- BTEX (1)
- Biaxial strength (1)
- Bimodal distribution (1)
- Binder jetting (1)
- Bio Ceramic (1)
- Bio Ceramics (1)
- Bioactive glass (1)
- Biodiesel (1)
- Biogeochemistry (1)
- Bioresorbable (1)
- Bitter technique (1)
- Bone regeneration (1)
- Borosilicate glass (1)
- Bravais lattice (1)
- Brittle / ductile fracture behavior (1)
- Brown-rot fungi (1)
- CCUS, supercritical/dense phase CO2, carbon steels, martensitic steel, superaustenite steel, droplet corrosion (1)
- CO2 corrosion (1)
- Calcium Cobaltite (1)
- Calcium cobaltite (1)
- Carbon steels (1)
- Carbon fibre-reinforced-plastics (1)
- Carbon steel (1)
- Carbon storage (1)
- Ccs (1)
- Cement (1)
- Ceramic springs (1)
- Ceramics (1)
- Chemometrics (1)
- Chromatography (1)
- Co2-Storage (1)
- Cobald based alloy (1)
- Complex loading (1)
- Composite structures (1)
- Coniophora puteana (1)
- Coordinate measurement machine (1)
- Corrosion Fatigue (1)
- CrN/NbN (1)
- Crack Propagation (1)
- Crack healing (1)
- Crack propagation (1)
- Crack propagation analysis (1)
- Creep mechanisms (1)
- Creep, Creep Rupture, and Stress Rupture (1)
- Creep-fatigue (1)
- Critical energy release rate (1)
- Crystal Orientation (1)
- Crystallographic texture (1)
- Cupriavidus metallidurans (1)
- Cycle jump (1)
- Cyclic loading (1)
- Cyclic oxidation (1)
- Cyclic softening (1)
- Damage evolution (1)
- Deformation (1)
- Dentine (1)
- Dielectric strength (1)
- Diesel (1)
- Diffraction (1)
- Digital image correlation (1)
- Dissolved water (1)
- Distributed fibre optic sensors (1)
- Dynamic recrystallization (1)
- EDXRD (1)
- EFTEM (1)
- Early stages (1)
- Efficiency (1)
- Electric conductivity (1)
- Electrical resistance (1)
- Electron back-scattered diffraction (1)
- Enamel (1)
- End of life (1)
- Environmentally assisted cracking (1)
- Epoxy resin (1)
- Expanding cavity model (1)
- FCH JU (1)
- FIB Tomography (1)
- Failure rate (1)
- Fatigue crack propagation (1)
- Fatigue damage (1)
- Fatigue fracture (1)
- Fatigue of sandwich structures (1)
- Femtosecond laser (1)
- Fiber-matrix interface (1)
- Filters (1)
- Finland (1)
- Flow Coefficient (1)
- Fluoride nanoparticles (1)
- Fluorolytic sol−gel (1)
- Fourier series (1)
- Fourier transform infrared spectroscopy (1)
- Fracture mechanics (1)
- Friction (1)
- Friction stir processing (1)
- Full Notch Creep Test (FNCT) (1)
- Full notch creep test (FNCT) (1)
- Fungi (1)
- GMR (1)
- GMR sensors (1)
- Gasabgabe (1)
- Gasgehalt (1)
- Geometrical factors (1)
- Geopolymers (1)
- Geothermal (1)
- Glas (1)
- Glass capillaries (1)
- Glass crystallization stress (1)
- Glass fiber reinforced polymers (1)
- Glass transition (1)
- Glass-ceramics definition (1)
- Gold (1)
- Grade S960QL steel (1)
- Gradient-enhanced fatigue model (1)
- Grain Boundary Corrosion (1)
- Grain boundaries (1)
- Granules (1)
- Graphite (1)
- Heat treatment (1)
- High - temperature corrosion (1)
- High Cycle Fatigue (1)
- High Temperature Corrosion (1)
- High interstitial austenitic steel (1)
- High temperature (1)
- Hipims (1)
- Horizon 2020 (1)
- Hot Press (1)
- Hot isostatic pressing (HIP) (1)
- Hydrogen permeability (1)
- Hydrogen permeation (1)
- Hydrogen storage (1)
- Imaging techniques (1)
- Impact wear (1)
- Implant failures (1)
- In situ (1)
- In situ diffraction (1)
- In-situ (1)
- In-situ SEM micro shear deformation (1)
- In718 (1)
- Inconel 625 (1)
- Inconel 686 coating (1)
- Indentation (1)
- Indentation hardness (1)
- Initial attachment (1)
- Interdiffusion (1)
- Interface (1)
- Interfacial shear strength (1)
- Internal Sulfidation (1)
- Internal friction (1)
- Inverse ostwald ripening (1)
- Kikuchi pattern (1)
- Laboratory X-ray diffraction (1)
- Laser (1)
- Laser Cladding (1)
- Laser cladding (1)
- Laser curing (1)
- Laser scanning microscopy (LSM) (1)
- Lattice parameters (1)
- Lifetime prediction (1)
- Light curing (1)
- Lightweight materials (1)
- Limestone Filler (1)
- Log-normal distribution (1)
- Long-term calculation (1)
- Long-term storage (1)
- Low Cycle Fatigue (LCF) (1)
- Low carbon steel (1)
- Low cycle fatigue (1)
- Magnetic domain distribution (1)
- Magnetic stray field (1)
- Magnetic stray fields (1)
- Magnetomechanical effect (1)
- Manufacturing (1)
- Mars (1)
- Martensite (1)
- Martensitic steel (1)
- Martensitic transformation (1)
- Mass transport (1)
- Master curve (1)
- Material characterization (1)
- Material defects (1)
- Material modeling (1)
- Material oxidation (1)
- Mechanical and thermal testing (1)
- Metal Magnetic Memory (1)
- Metal magnetic memory (1)
- Metallic components (1)
- Metformin (1)
- Micro-shrinkages (1)
- Micromechanical model (1)
- Microsegregation (1)
- Microstructur (1)
- Microstructural evolution (1)
- Microstructure and texture (1)
- Microwave technology (1)
- Mikroplastik (1)
- Misorientation (1)
- Mobility (1)
- Modeling (1)
- Molecular dynamics (1)
- Multiaxial deformation (1)
- Multilayer technology (1)
- NGS (1)
- Nano-powder characterization (1)
- Nano-scratch test (1)
- Nanomaterial screening (1)
- Nanoparticle structure (1)
- Nanoscale multilayers (1)
- Natural silver wires (1)
- Near Infrared Spectroscopy (1)
- NiTi (1)
- Nickel based coatings (1)
- Nickel-base superalloy (1)
- Nickel-base superalloys (1)
- Notch (1)
- Number density (1)
- Optical backscatter reflectometry (1)
- Optical centrifugation (1)
- Optical fibre (1)
- Orientation (1)
- Orientation refinement (1)
- Oxidation (1)
- Oxide coatings (1)
- Oxide scale (1)
- Oxyfuel (1)
- P92 steels (1)
- PLS-DA (1)
- PV modules (1)
- Particle Size Distribution (1)
- Passive components and circuits (1)
- Permeability (1)
- Phase field simulation (1)
- Phase-field (1)
- Photocatalysis (1)
- Photocleavable organosilanes (1)
- Photopolymer composites (1)
- Phototrophs (1)
- Photovoltaic modules (1)
- Phytolith (1)
- Pipeline (1)
- Polyaniline (1)
- Polymer matrix composites (1)
- Polymeric Materials (1)
- Polypropylene (1)
- Polystyrene (1)
- Porosity (1)
- Powdered activated carbon (1)
- Power factor (1)
- Preceramic polymer (1)
- Production scatter (1)
- Pull-out composite materials (1)
- Rafting (1)
- Raman spectroscopy (1)
- Real-time qPCR (1)
- Reference Material (1)
- Relaxation tests (1)
- Relaxationsphänomene (1)
- Resistance stress (1)
- Rheology (1)
- Rhodonia placenta (1)
- Risswachstum (1)
- Roughness (1)
- S-Phase (1)
- SEM (1)
- SEM wood characterization (1)
- SIMS (1)
- Sand blasting (1)
- Sandwich (1)
- Scanning acoustic microscopy (SAM) (1)
- Scanning electron microscopy (1)
- Segregation (1)
- Self-Assembly (1)
- Sewage treatment plant (1)
- Shape memory alloys (1)
- Shear load (1)
- Shear testing (1)
- SiO2 (1)
- Silicate Glasses (1)
- Silicatglas (1)
- Silicon Carbide (1)
- Single crystal superalloys (1)
- Single fiber pull-out test (1)
- Single-crystals (1)
- Sinter additive (1)
- Sliding simulation (1)
- Slow crack growth (SCG) (1)
- Slurry optimization (1)
- Soil (1)
- Soil sample (1)
- Solar panels (1)
- Solid-State-Synthesis (1)
- Solid-state-synthesis (1)
- Sorption (1)
- Steam oxidation resistance (1)
- Steel P92 (1)
- Stereoscopy (1)
- Strain difference (1)
- Stress-strain-behavior (1)
- Structural health monitoring (SHM) (1)
- Structural steel (1)
- Structured heating (1)
- Subsurface defects (1)
- Sulphidation (1)
- Superalloy single crystals (1)
- Superaustenite steel (1)
- Superconducting magnet (1)
- Supercritical/dense phase CO 2 (1)
- Support configurations (1)
- Support vector machines (1)
- Surface Nucleation (1)
- Surface modification (1)
- Surface nucleation (1)
- Swept wavelength interferometry (SWI) (1)
- Synchrotron X-ray diffraction (1)
- T1 precipitate (1)
- TAHYA (1)
- TED (1)
- TIG-welding (1)
- Texturation (1)
- Thermal degradation (1)
- Thermal expansion (1)
- Thermo-mechanical fatigue (1)
- Thermo-mechanical loading (1)
- Thermoanalysis (1)
- Thermoanalytical Methods (1)
- Thermoelectric generator (1)
- Thermoelectric oxides (1)
- Thermomechanical Fatigue (TMF) (1)
- Thickening (1)
- Thin tribofilm (1)
- Titanium (1)
- Tooth wear (1)
- Topography (1)
- Transducers (1)
- Transmittance (1)
- Tricalcium Phosphate (1)
- Ultrasound (1)
- VCSEL (1)
- Vacancies (1)
- Very high cycle fatigue (1)
- Vickers indentation (1)
- Visualization (1)
- Volume Fraction (1)
- Volume fraction (1)
- Wasser (1)
- Waste water (1)
- Water (1)
- Water droplet erosion resistance (1)
- Withstand voltage tests (1)
- Wood protection (1)
- X-ray computed tomography (CT) (1)
- X-ray refractography (1)
- XRD (1)
- Young`s modulus (1)
- laser cladding (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (188)
- 5.1 Mikrostruktur Design und Degradation (60)
- 5.2 Metallische Hochtemperaturwerkstoffe (40)
- 5.3 Polymere Verbundwerkstoffe (29)
- 5.4 Multimateriale Fertigungsprozesse (28)
- 5.6 Glas (28)
- 7 Bauwerkssicherheit (23)
- 8 Zerstörungsfreie Prüfung (21)
- 9 Komponentensicherheit (21)
- 5.5 Materialmodellierung (20)
Eingeladener Vortrag
- nein (68)
Degradation of AISI 630 exposed to CO2-saturated saline aquifer at ambient pressure and 100 bar
(2018)
In general high alloyed steels are suitable as pipe steels for carbon capture and storage technology (CCS), because they provide sufficient resistance against the corrosive environment of CO2-saturated saline aquifer which serves as potential CCS-site in Germany. High alloyed martensitic steel AISI 630 has been proven to be sufficient resistant in corrosive environments, e.g. regarding heat, pressure, salinity of the aquifer, CO2-partial pressure), but reveals a distinct corrosion pattern in CCS environment. Therefore coupons of AISI 630 heat treated using usual protocols were kept at T=60 °C and ambient pressure as well as p=100 bar up to 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. AISI 630 precipitates a discontinuous ellipsoidal corrosion layer after being exposed for more than 4000 hours. Best corrosion resistance in the CO2-saturated synthetic aquifer environment phase is achieved via normalizing prior to exposure. In water saturated supercritical CO2 tempering at medium temperatures after hardening gives lowest corrosion rates. Corrosion fatigue via push-pull tests with a series of 30 specimens was evaluated at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). The endurance limit of AISI 630 is reduced by more than 50% when exposed to CCS environment (maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa).
In CCS environment (carbon capture and storage) pipes are loaded statically and/or cyclically and at the same time exposed constantly to the highly corrosive hot thermal water. Experimental procedures such as ambient pressure immersions tests, in-situ corrosion fatigue experiments using a flexibly designed corrosion chamber at ambient pressure and a specially designed corrosion chamber at high pressure. Experimental set-ups for push/pull and rotation bending load are introduced. The corrosion behavior and lifetime reduction of high alloyed steels (X46Cr13, 1.4043), (X5CrNiCuNb16-4, 1.4542) and (X2CrNiMoN22-5-3, 1.4462) is demonstrated (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2 ).
The commercial usage of latent thermal energy storages primarily depends on the development of a suitable phase change material (PCM). For industrial high temperature applications above 400 °C multicomponent chloride eutectics are promising and therefore discussed seriously. The profound thermodynamic investigation of such eutectics requires a much greater amount of specimen material than conventional calorimeter can handle. Therefore, a special adiabatic calorimeter was developed and designed. With a specimen mass of > 100 g the typical thermodynamic measurements with a commercial calorimeter can be extended by cycle stability measurements, which are often decisive for practical application of PCM. Furthermore, by implementing corrosion specimens inside the calorimeter high temperature corrosion experiments according to ISO 21608 can be performed inside the calorimeter. Adiabatic measuring conditions can be provided by using two separate heating systems. Therefore, the outer “protective system” follows the temperature curve of the inner “measuring system” minimizing the temperature difference between the heating systems and simultaneously preventing heat losses from the measuring systems.
A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated.
The application of implants e.g. for osteosynthesis or substitution of worn out joints is common practice since decades. Successes in surgery and orthopedics are highly dependent on the use of artificial parts for implanting into the human body. Over the years the number of surgical procedures and the number of different implants were growing rapidly. Implants, however, are exposed to complex mechanical, corrosive and tribological loads along with restriction in geometric dimension. While being essentially successful, the sheer number of cases leads to a rising number of implant failures. Such failures are painful for the affected patients and are very costly.
The failure cases presented in this paper occurred from 1981 to 2016. The predominant failure mechanism of all kinds of implants is fatigue fracture. Fatigue cracks are initiated due to a whole bunch of reasons: Material defects and fabrication defects are rare events. The main factors are cyclic overload due to improper fitting with delayed bone healing, corrosion and unauthorized modification of the implant during surgery
A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated.
The described investigation of carbon-fibre-reinforced plastics (CFRP) documents that damage evolution can be observed by means of X-ray refractography. Comparative investigations with synchrotron technique on CFRP and grey-scale analysis on glass fibre-reinforced-plastics (GFRP) confirm these results. Moreover it was found that the fracture mechanical properties of the matrix system influence damage nucleation and propagation in the laminate during static and fatigue loads. Single-step fatigue tests were carried out on Laminates with RIM135 and LY556 matrix systems made from non-crimped fabric (NCF) or twill weave in different fibre orientations. The damage to the LY556 laminates was characterized by laminate cracks growing rapidly over the whole specimen width, whereas the damage on the RIM135 laminates was characterized by an earlier onset of micro-cracking followed by laminate cracks. The specimens were fatigued up to 108 (very high cycle fatigue (VHCF) regime) load cycles. S-N-curves of damage initiation were drawn and boundaries were identified for endurance within the VHCF regime. A phenomenology based model focusing on matrix stress was applied to reproduce the first inter-fibre failure (IFF) under static and fatigue loads.
The work presents the microstructure, chemical composition and mechanical properties of Inconel 686 coatings after high - temperature corrosion in environment of aggressive gases and ashes. To produce the Ni - based coatings the QS Nd:YAG laser cladding process was carried out. As the substrate used 13CrMo4-5 boilers plate steel. Ni - base alloys characterize the excellent high-temperature corrosion resistance, good strength and ability to work in aggressive environments. Formed clad were characterized by high quality of metallurgical bonding with the substrate material and sufficiently low amount of the iron close to the clad layer surface. After corrosion experiment the oxide scale on the substrate and clad created. The scale on 13CrMo4-5 steel had 70 μm thickness while the scale of the clad had less than 10 μm. The microstructure, chemical composition of the obtained clad and scales were investigated by scanning electron microscope (SEM) and electron probe microanalyzer (EPMA) equipped with the EDS detectors.
Our research focused on Inconel 625 weld overlays on 16Mo3 steel boiler pipes. The Investigation focused on the characterization of changes in the microstructure and chemical composition after annealing. The annealing was performed for ten hours at temperatures from 600 to 1000°C. Changes in the microstructure were observed with a scanning and transmission electron microscope (SEM and TEM). The investigation was supplemented by hardness measurements.
Fiber-reinforced-polymers (FRPs) are in current research focus in the lightweight construction industry, because of their extraordinary characteristics (stiffness and strength-to-density relation). The structure of polymer matrix and the interaction with reinforcement are crucial for optimization of the mechanical and thermal properties of FRPs. Due to the macromolecular chain structure, the mechanical properties of a polymer strongly vary with temperature: Below the glass transition, the chain segments of a polymer are “frozen”. Regarding fracture, the total changed energy during fracture if only dissipates for the generation of the new surfaces. However, in the region of the glass transition, the polymer chain segments start to get “unfrozen”, and the energy is not only required for generating new surfaces, but also for irreversibly deformation. This irreversible deformation is affected by the global temperature and the local temperature near the crack tip, which is affected by the local strain rate and crack propagation velocity.
Hence, in this research project, the irreversible deformation of neat and reinforced polymers will be controlled by changing the global temperature as well as the local temperature. With using different fracture experiments, the amount of energy required for creating new surfaces and for the irreversible deformation will be separated. The fracture tests include the conventional tensile test, the macroscopic peel test and the single fiber peel – off test.
A continuum damage model for concrete is developed with a focus on fatigue under compressive stresses. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. The model is designed to represent failure under static loading as a particular case of fatigue failure after a single loading cycle. As a consequence, most of the material parameters can be deduced from statictests. Only a limit set of additional constitutive parameters is required to accurately describe the evolution under fatigue loading. Another advantage of the proposed model is the possibility to directly incorporate other multi-physics effects such as creep and shrinkage or thermal loading on the constitutive level. A multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach. This evolution equation is then solved on the long time scale using different implicit and explicit time integration schemes. Their performance and some limitations for specific loading regimes is discussed.
A continuum damage model for concrete is developed with a focus on fatigue under compressive stresses. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. The model is designed to represent failure under static loading as a particular case of fatigue failure after a single loading cycle. As a consequence, most of the material parameters can be deduced from statictests. Only a limit set of additional constitutive parameters is required to accurately describe the evolution under fatigue loading. Another advantage of the proposed model is the possibility to directly incorporate other multi-physics effects such as creep and shrinkage or thermal loading on the constitutive level. A multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach. This evolution equation is then solved on the long time scale using different implicit and explicit time integration schemes. Their performance and some limitations for specific loading regimes is discussed.
Lifetime aspects including fatigue failure of concrete structures were traditionally only of minor importance. Because of the growing interest in maxing out the capacities of concrete, its fatigue failure under compression has become an issue. A variety of interacting phenomena such as e.g. loss of prestress, degradation due to chemical reactions or creep and shrinkage influence the fatigue resistance. Failure due to cyclic loads is generally not instantaneous, but characterized by a steady damage accumulation. Therefore, a reliable numerical model to predict the performance of concrete over its lifetime is required, which accurately captures order effects and full three-dimensional stress states.
Many constitutive models for concrete are currently available, which are applicable for specific loading regimes, different time scales and different resolution scales.
However, a key limitation of those models is that they generally do not address issues related to fatigue on a structural level. Very few models can be found in the literature that reproduce deterioration of concrete under repeated loading-unloading cycles. This is due to the computational effort necessary to explicitly resolve every cycle which exceeds the currently available computational resources. The limitation can only be overcome by the application of multiscale methods in time.
The objective of the paper is the development of numerical methods for the simulation of concrete under fatigue loading using temporal multiscale methods.
First, a continuum damage model for concrete is developed with a focus on fatigue under compressive stresses [1]. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. The model is designed to represent failure under static loading as a particular case of fatigue failure after a single loading cycle. As a consequence, most of the material parameters can be deduced from static tests. Only a limit set of additional constitutive parameters is required to accurately describe the evolution under fatigue loading. Another advantage of the proposed model is the possibility to directly incorporate other multi-physics effects such as creep and shrinkage or thermal loading on the constitutive level.
Second, a multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach [2]. This evolution equation is then solved on the long time scale using different implicit and explicit time integration schemes. Their performance and some limitations for specific loading regimes is discussed.
Finally, the developed methods will be validated and compared to experimental data.
[1] Vitaliy Kindrachuk, Marc Thiele, Jörg F. Unger. Constitutive modeling of creep-fatigue interaction for normal strength concrete under compression, International Journal of Fatigue, 78:81-94, 2015
[2] Vitaliy Kindrachuk, Jörg F. Unger. A Fourier transformation-based temporal integration scheme for viscoplastic solids subjected to fatigue deterioration, International Journal of Fatigue, 100:215-228, 2017
Lifetime aspects including fatigue failure of concrete structures were traditionally only of minor importance. Because of the growing interest in maxing out the capacities of concrete, its fatigue failure under compression has become an issue. A variety of interacting phenomena such as e.g. loss of prestress, degradation due to chemical reactions or creep and shrinkage influence the fatigue resistance. Failure due to cyclic loads is generally not instantaneous, but characterized by a steady damage accumulation. Therefore, a reliable numerical model to predict the performance of concrete over its lifetime is required, which accurately captures order effects and full three-dimensional stress states.
Many constitutive models for concrete are currently available, which are applicable for specific loading regimes, different time scales and different resolution scales.
However, a key limitation of those models is that they generally do not address issues related to fatigue on a structural level. Very few models can be found in the literature that reproduce deterioration of concrete under repeated loading-unloading cycles. This is due to the computational effort necessary to explicitly resolve every cycle which exceeds the currently available computational resources. The limitation can only be overcome by the application of multiscale methods in time.
The objective of the paper is the development of numerical methods for the simulation of concrete under fatigue loading using temporal multiscale methods.
First, a continuum damage model for concrete is developed with a focus on fatigue under compressive stresses. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. The model is designed to represent failure under static loading as a particular case of fatigue failure after a single loading cycle. As a consequence, most of the material parameters can be deduced from static tests. Only a limit set of additional constitutive parameters is required to accurately describe the evolution under fatigue loading. Another advantage of the proposed model is the possibility to directly incorporate other multi-physics effects such as creep and shrinkage or thermal loading on the constitutive level.
Second, a multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach. This evolution equation is then solved on the long time scale using different implicit and explicit time integration schemes. Their performance and some limitations for specific loading regimes is discussed.
Finally, the developed methods will be validated and compared to experimental data.
For the additive manufacturing of large components typically powder-based methods are used. A powder is deposited layer by layer by means of a recoater, then, the component structure is printed into each individual layer. We introduce here the new method of local laser drying, which is a suspension-based method specially developed for the manufacturing of large voluminous ceramic parts. The structure information is directly written into the freshly deposited layer of suspension by laser drying. Initially, the technology was developed for ceramic suspensions, however, first experiments with geopolymers reveal a high potential for this class of materials. Metakaolin, fly ash and lithium aluminate-based one-part geopolymers were used in first experiments. The local annealing of the geopolymer slurry results in a drying and crosslinking reaction and, thus, in a local consolidation of the material. First parts made are introduced and their properties are discussed.
Dislocations are the carriers of plastic deformation. As such, their characterization offers important information on the properties they affect. In this contribution, a new tool is presented, which is incorporated in Amira ZIB Edition and allows for three-dimensional (3D) imaging and quantification of dislocations substructures from thick regions an electron-transparent specimen. In the tool, the dislocation segments are traced on diffraction contrast images that are obtained in the transmission electron microscope (TEM). The uncertainties related to the experimental setup and to the proposed method are discussed on the base of a tilt series.
The Ni-Cr-Mo-W alloy is characterized by the excellent high-temperature corrosion resistance, good strength and ability to work in aggressive environments. To protect the surface of the substrate 13CrMo4-5 steel against aggressive environments the Inconel 686 as clad layer was used. The corrosion process was performed in oxidizing mixture of gases like O2, COx, SOx. The second part of corrosion Experiment concerned the corrosion test of the coating in reducing atmosphere of the specified gases with ashes, which contained e.g. Na, Cl, Ca, Si, C, Fe, Al.
We describe a lattice-based crystallographic approximation for the analysis of distorted crystal structures via Electron Backscatter Diffraction (EBSD) in the scanning electron microscope. EBSD patterns are closely linked to local lattice parameter ratios via Kikuchi bands that indicate geometrical lattice plane projections. Based on the transformation properties of points and lines in the real projective plane, we can obtain continuous estimations of the local lattice distortion based on projectively transformed Kikuchi diffraction simulations for a reference structure. By quantitative image matching to a projective transformation model of the lattice distortion in the full solid angle of possible scattering directions, we enforce a crystallographically consistent approximation in the fitting procedure of distorted simulations to the experimentally observed diffraction patterns. As an application example, we map the locally varying tetragonality in martensite grains of steel.
Ferritic-martensitic Fe-Cr alloys are widely utilised as materials for high temperature applications such as super heater tubes in coal, biomass or co-fired power plants. Various corrosive gases are produced in combustion processes, but especially SO2 is known to cause catastrophic application failure. In order to understand the effect of orientation and grain size of the alloy on the initial corrosion processes we analysed metal coupons of Fe-Cr- alloys (2-13 wt. % Cr) by electron backscattered diffraction (EBSD) before and after exposure to SO2 containing atmospheres in 650°C for short time spans (2 min – 12 h). An infra red heated furnace with integrated water-cooling was used for the ageing procedures to conduct short time experiments and to keep the reaction products in a ‘frozen’ state.
EBSD characterization of oxides formed on the surface of the alloys showed a topotactic relationship between grain orientation of the alloys and the oxides. With increasing scale thickness this relation diminishes possibly due to lattice strain. There appears to be no correlation between oxide growth and absolute, initial orientation, grain size, or the quality of polishing. An initially topotactic relationship between scale and steel had been already described for the formation of magnetite in hot steam environments, indicating that the initial corrosion mechanisms are mainly depending on the presence of Oxygen, and not changed by the presence of Sulphur. However, Sulphur is incorporated into the oxide scale in the low Cr alloy, and mainly observable in the inner corrosion zone for the higher alloyed material. Furthermore, oxides formed directly on grain boundaries in higher Cr alloyed materials are enriched in Cr compared to oxides on grain faces.
Ferritic high temperature alloys are widely used as boiler tube and heat exchanger materials in coal, biomass and co-fired power plants. All technologies have in common that the applied materials are exposed to different temperatures, process pressures and reactive atmospheres that lead to a change of the material properties and a further degradation of the material. Material changes caused by aging in highly corrosive and toxic gases such as SO2 are mainly studied ex situ after the reaction is finished. The solid material is deposited in the atmosphere for a certain period of time, and material changes are then examined by various microscopic techniques such as optical microscopy (OM), electron microprobe analysis (EMPA), scanning electron microscopy (SEM and TEM) and X-ray diffraction (XRD). Nevertheless, extensive efforts were made to study material changes of high temperature alloys under oxidizing and reducing atmospheres by environmental scanning electron microscopy or in situ TEM techniques However, the possibilities of microscopic in situ techniques are very limited for the use of highly corrosive and toxic gases such as SO2. Since Sulfur induced corrosion at temperatures relevant for coal and biomass fired power plants, which is causing breakaway oxidation and sulfide precipitation at grain boundaries, is still of scientific interest, the current work focuses on the effect of SO2 in an initial stage of corrosion of ferritic alloys. For the analysis of early stages of combined oxidation and sulphidation processes of Fe-Cr model alloys the usage of a light furnace to conduct a rapid reactive annealing experiment is feasible. Previous studies presented distinct results of the influence of chromium on early high temperature corrosion by SO2 by this technique and subsequent classical metallographic analyses. However, it is still not possible to trace the corrosion mechanism in real time by conducting single aging experiments. The current work introduces two different approaches to study the initial stages of high temperature oxidation processes by applying above state of the art X-ray diffraction and spectroscopy methods. One part focuses on the real time observation of the formation of corrosion products such as oxides and sulfides by energy dispersive X-ray diffraction (EDXRD). The potential of this technique to study crystallization and growth processes of thin films in a reactive environment in real time was previously shown for different compound semiconductors. This approach was now applied to follow oxidation and sulphidation processes of ferritic model alloys in SO2 and SO2/H2O environments. The diffraction signals of the X-rays were detected during the corrosion process and the peak area and positions were analyzed as a function of time. This procedure enables monitoring external oxide growth and material loss in real time in an early stage of corrosion.
The other part of the current work presents the possibilities of X-ray absorption near edge structure spectroscopy (XANES) to characterize oxide scales and their growth mechanisms. Precise phase identification and quantification of corrosion products in a multi-phase oxide/sulfide scale is a pre-requisite to understand diffusion paths of metal ions and gas components. It is a challenging task to distinguish structurally similar reaction products such as Fe3O4 and FeCr2O4 especially in thin films with texture effects by diffraction. To illustrate for example Cr-out diffusion of an alloy throughout an inner and external oxide scale the differentiation of Fe3O4 and FeCr2O4 is indispensable. XANES uses the photoionization effect at the metal absorption edge in an aging product and accesses by this structural and chemical information. The current work uses XANES at the Fe-K and Cr-K absorption edge to identify various aging products grown as thin layers on alloys after short time aging experiments. A reaction chamber for combining high temperature oxidation experiments with surface sensitive X-ray absorption near edge structure spectroscopy will be introduced and first results of XANES on scales at high temperatures will be presented.