5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2018 (15) (entfernen)
Dokumenttyp
- Vortrag (15) (entfernen)
Sprache
- Englisch (15) (entfernen)
Referierte Publikation
- nein (15)
Schlagworte
- Alloy 2618A (4)
- Coarsening (4)
- Aluminium (3)
- Creep (3)
- Degradation (3)
- Fatigue (3)
- S-phase (3)
- Dark-field transmission electron microscopy (2)
- Ferritic-martensitic steels (2)
- Transmission electron microscopy (2)
Organisationseinheit der BAM
- 5.2 Metallische Hochtemperaturwerkstoffe (15) (entfernen)
Eingeladener Vortrag
- nein (15)
The employment of renewable energy resources, which are naturally intermittent, for electricity generation has altered the working conditions of conventional power plants from continuous (baseload) to cyclic or flexible operation. For a long time, 9-12% Cr ferritic-martensitic stainless steels have been widely used in power plants due to their favorable characteristics such as high creep strength at high temperatures and oxidation and corrosion resistance. The components of power plants are subjected to long term cyclic loadings including fatigue and creep-fatigue at high temperatures. As ferritic-martensitic steels are known to exhibit cyclic softening when subjected to such loading scenarios, it is crucial to study the material response in such conditions. Since it is impossible to test the material behavior exactly as the operation conditions of power plants, due to technical difficulties and cost issues, it is necessary to develop physically-based material models that can predict the material behavior in more realistic situations.
In recent years, many material models have been proposed to describe the behavior of 9-12% Cr ferritic-martensitic stainless steels, which follow phenomenological or physically-based approaches. Phenomenological models provide a stress-strain relation based on empirical observations although they usually lack physical background. To alleviate this drawback and to allow for more flexibility and wider ranges of strain-rate and temperature, physically-based models are suggested. In this approach, microstructural evolution, dislocation movement and/or kinetics of plastic deformation processes are included. The physically-based models allow for a better extrapolation from the experiment results to other operation conditions and their material constants can be interpreted physically. Compared to the former approach, the material behavior can be described more accurately and flexibly and the number of material constants is less in general. In the presented work, the existing micromechanical models developed for P92 steel are compared and extended to allow for new dislocation-based strengthening/cyclic mechanisms. Their performance is assessed in the light of mechanical test data from creep-fatigue and thermo-mechanical fatigue experiments and detailed characterizations of the microstructure evolution in the fatigued material.
A constitutive model for the mechanical behaviour of single crystal Ni-base superalloys under high temperature conditions has been developed in the framework of a Cooretec project in cooperation with Siemens AG, MTU Aero Engines AG and University Bayreuth. In addition to the conventional material properties e.g. elastic constants, the model requires the parameters of the initial microstructure as an input. Thus, the γ’-precipitate size and the channel width of the γ-matrix were obtained from SEM micrographs. The model uses the slip system theory and describes the movement, multiplication and annihilation of dislocations in the channels. Furthermore, the cutting of precipitates is another mechanism contributing to the plastic flow. The evolution of the morphology due to rafting and its effects on the deformation have been implemented according to. The kinematic hardening is introduced as a stress tensor to realistically represent the strain hardening of arbitrary oriented single crystals.
The mechanical behaviour of single crystal specimens has been experimentally investigated in tension tests at different strain rates and in creep tests under various loads. The constitutive model has been calibrated based on the experimental data for temperatures of 950°C and 850°C and the [001] and [111] crystallographic orientations.
Finally, a micromechanical model was created to simulate the creep response of additive manufactured polycrystalline structures. An EBSD image is taken to obtain the grain geometry and their respective orientation. The grain boundaries are discretised using cohesive elements, whereas the single crystal model was applied to each grain in the representative volume. The polycrystal model is generated using Dream3D, NetGen and other software previously developed at the BAM.
The creep behavior of single-crystals of the nickel-base superalloy CMSX-4 was investigated at 1288°C, which is the temperature of the hot isostatic pressing (HIP) treatment applied to this superalloy in the industry. It was found that at this super-solvus temperature, where no Gamma’-strengthening occurs, the superalloy is very soft and rapidly deforms under stresses between 4 and 16 MPa. The creep resistance was found to be very anisotropic, e.g. the creep rate of [001] crystals was about 11 times higher than that of a [111] crystal. The specimens of different orientations also showed a very different necking behavior. The reduction of the cross-section area psi of [001] crystals reached nearly 100%, while for a [111] crystal psi=62%. The EBSD analysis of deformed specimens showed that despite such a large local strain the [001] crystals didn’t not recrystallize, while a less deformed [111] crystal totally recrystallized within the necking zone. From the shape of deformed specimens and TEM investigations it was concluded that the main strain contribution resulted from <011> {111} octahedral slip.
Virtual-lab-based determination of a macroscopic yield function for additively manufactured parts
(2018)
This work presents a method for the yield function determination of additively manufactured parts of S316L steel. A crystal plasticity model is calibrated with test results and used afterwards to perform so-called virtual experiments, that account for the specific process-related microstructure including crystallographic and morphological textures. These simulations are undertaken on a representative volume element (RVE), that is generated from EBSD/CT-Scans on in-house additively manufactured specimen, considering grain structure and crystal orientations. The results of the virtual experiments are used to determine an anisotropic Barlat yield function, that can be used in a macroscopical continuum-sense afterwards. This scale-bridging approach enables the calculation of large-scale parts, that would be numerically too expensive to be simulated by a crystal plasticity model.
9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep and oxidation resistance. The growing share of renewable energy sources in power generation forces many of these plants into more flexible operation with frequent load shifts or shutdowns. These cyclic operation profiles constitute a major lifetime issue.
The present contribution reports on current findings obtained in a multidisciplinary project which combines cyclic mechanical and cyclic oxidation testing with detailed microstructural analyses. Mechanical analyses are carried out on P92 and P91 steel grades to give an overview of softening phenomena and lifetimes obtained in isothermal cyclic loading (low cycle fatigue, LCF), non-isothermal cyclic loading (thermo-mechanical fatigue, TMF), and service-like combinations of creep and fatigue periods (creep-fatigue interaction).
Oxidation testing focuses on the grades P92 and VM12 with the intention of clarifying the impact of frequent passes through intermediate temperature levels on the kinetics of steam-side oxidation and the characteristics of the evolving oxide scales. An attempt is made to evaluate their composition, strength, integrity and adhesion after up to 250 temperature cycles. Flat coupons as well as curved tube sections are tested to assess the mutual influence of geometry on oxide scale integrity.
Complementary microstructural investigations by scanning and transmission electron microscopy plus EBSD are used for phase identification and substrate/oxide interface characterisation. The evolutions of grain size and dislocation density under different test conditions are quantified.
9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep and oxidation resistance. The growing share of renewable energy sources in power generation forces many of these plants into more flexible operation with frequent load shifts or shutdowns. These cyclic operation profiles constitute a major lifetime issue. The present contribution reports on current findings obtained in a multidisciplinary project which combines cyclic mechanical and cyclic oxidation testing of different 9-12% Cr grades with detailed microstructural analyses.
Mechanical analyses are carried out on P92 and P91 steel grades to give an overview of softening phenomena and lifetimes obtained in isothermal cyclic loading (low cycle fatigue, LCF), non-isothermal cyclic loading (thermo-mechanical fatigue, TMF), and service-like combinations of creep and fatigue periods.
Complementary microstructural investigations by scanning and transmission electron microscopy plus EBSD are used for phase identification, substrate/oxide interface characterization and quantification of the microstructure evolution under cyclic conditions.