5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (13)
- Vortrag (12)
- Posterpräsentation (7)
- Forschungsdatensatz (3)
- Beitrag zu einem Tagungsband (2)
- Buchkapitel (1)
- Dissertation (1)
Sprache
- Englisch (36)
- Deutsch (2)
- Französisch (1)
Schlagworte
- Creep (39) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (39)
- 5.2 Metallische Hochtemperaturwerkstoffe (30)
- 5.5 Materialmodellierung (11)
- 5.1 Mikrostruktur Design und Degradation (10)
- 6 Materialchemie (3)
- 8 Zerstörungsfreie Prüfung (3)
- 8.5 Röntgenbildgebung (3)
- 9 Komponentensicherheit (3)
- 9.6 Additive Fertigung metallischer Komponenten (3)
- 3 Gefahrgutumschließungen; Energiespeicher (2)
Eingeladener Vortrag
- nein (12)
This study introduces an innovative method for efficiently determining the creep properties of high-temperature materials through high-throughput testing, employing digital image correlation [1,2]. The focus is on the AlCoCrFeNiTi alloy [3-5], synthesized by directional solidification, known for its exceptional strength and unique properties. Experimental investigations, including compression, and bending creep tests, were conducted at 750°C.
Capitalizing on the inhomogeneous stress and strain distribution within a cantilever subjected to bending, we leverage this characteristic to extract multiple creep curves from a single test. Stresses at key points were determined using existing analytical solutions [5,6]. Uniaxial tests spanning 300 to 500 MPa initial stress were complemented by bending tests designed to induce similar stress levels. A detailed comparison between bending and uniaxial creep is presented, including the results of verification studies on additional alloys.
This methodology not only expedites testing but also minimizes material usage, energy consumption, and manual labour. This research showcases a reliable and time-efficient approach to exploring the creep behavior of high-temperature materials. The technique is particularly advantageous for characterizing precious alloys with limited dimensions. Microstructural heterogeneity may exist in specimens tested under bending load, however, it can still be correlated to the mechanical properties with modern high-resolution characterization methods. Stress and resulting strain can be directly compared in a single specimen, ensuring uniform manufacturing, and heating history. This method eliminates the possible errors due to testing with different rigs, which could impair the accuracy of studies based on individual tests.
Metal additive manufacturing (Metal AM) continues to gain momentum. Many companies explore the manufacturing of innovative products, including components for safety critical applications. Despite the intensive research of recent years, a fundamental understanding of the process‑structure‑property relationships remains challenging due to, i.a., the inherently complex and highly hierarchical microstructures arising from the wide range of build process parameter variability. This contribution presents the resu lts of an experimental study on the creep behavior of an austenitic 316L stainless steel produced by laser powder bed fusion (PBF LB/M/316L) with an emphasis on understanding the effects of microstructure on creep mechanisms. Hot tensile tests and constant force creep tests at 600 °C and 650 °C, X ray computed tomography, as well as optical and electron microscopy were performed. The produced PBF LB/M/316L exhibits a low void population 0.01 %) resulting from the manufacturing parameters used and which a llowed us to understand the effects of other microstructural aspects on creep behavior, e.g., grain morphology and dislocation substructure. A hot‑rolled variant of 316L hwas also tested as a reference. The produced PBF LB/M/316L possesses shorter primary and secondary creep stages and times to rupture and smaller creep stress exponents than the hot‑rolled variant. Overall, the creep damage is more extensive in the PBF LB/M/316L and is characterized as predominantly intergranular. It is considered that the damage behavior is mainly impacted by the formation of precipitates at the grain boundaries combined with their unfavorable orientation. The dislocation substructure and local elemental segregation appear to have a decisive impact on the overall creep behavior.
In times of digital data processing and sharing, a central challenge for the Materials Science and Engineering (MSE) community is the complete digital representation of materials, including their relevant processing and microstructure details and the resulting properties. This digital representation, supported by digital infrastructures, enables entirely new qualities of collaborative work and is central to how we will conduct MSE research and develop products in the future. The main challenges are the composition, shaping, and description of the data so that it can be easily interpreted, trusted, and re-used. This presentation introduces our current effort to develop a best practice framework for generating and distributing creep reference datasets for Ni-based superalloys, which builds on previous approaches. Researchers can use such datasets to compare their own experimental or simulation results, used, for instance, to perform simulation-based alloy design and optimization or in the verification of the own testing equipment. The concept includes building an easily accessible digital infrastructure to annotate and discover the datasets and the integration of an ontology that aligns with the necessary metadata schema. With the help of an ontology, the reference dataset for creep can be semantically described, thus enabling the digital representation and reusage of shared concepts from domain experts and the community. To achieve this, it is necessary to establish a defined vocabulary with corresponding relations and annotations. The interplay between a digital infrastructure, the agreement on the necessary metadata and related metadata schema, and an underlying ontology will ensure that data and results can be easily shared, taken up, and re-used, thus fulfilling the FAIR principles (Findable, Accessible, Interoperable, Reusable). Furthermore, we aim to develop a widely accepted definition of reference data and data quality levels and to reach a self-supported community process. We intend to motivate the discussion about reference material datasets, necessary metadata, and future collaborations within the creep community.
Low-Temperature High Stress (LTHS) creep plays a crucial role in Ni-base Superalloys, particularly affecting components like blades near the root. Below 850°C, the precipitate microstructure remains stable, characterized by periodically arranged ’ cubic precipitates surrounded by the -matrix. In these conditions, macroscopic traces of cubic slip have been observed in <111> oriented tensile specimens, whereas their microscopic origin has been a topic of debate. Furthermore, in LTHS conditions, Superlattice Intrinsic, Extrinsic Stacking Faults (SISF/SESF), or micro-twins are also frequently reported in crept specimens. Usually, these mechanisms are investigated separately, so that a unified picture and a detailed understanding of these mechanisms and their activation conditions have only recently emerged in the literature, despite the intensive investigations of the last decades.
The objective of this work is to develop a dislocation-based constitutive law that includes these recent developments. In particular, the pseudo-cubic slip mechanism is considered as resulting from the lack of hardening in <111> oriented tensile specimens and is represented by a novel estimate of the back-stresses based on the spectral decomposition of a tensorial representation of the back-stress. An additional novelty is that SISF- and SESF-related slip systems are accounted for as distinct slip systems with corresponding dislocation densities. The model has been implemented as a user-defined constitutive law for commercial Finite Element codes and identified as well as validated with data from the literature obtained with <001>, <011> and <111> oriented crystals tested in tension and compression creep.
The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed.
The current lack of quantitative knowledge on processing-microstructure–property relationships is one of the major bottlenecks in today’s rapidly expanding field of additive manufacturing. This is centrally rooted in the nature of the processing, leading to complex microstructural features. Experimentally-guided modeling can offer reliable solutions for the safe application of additively manufactured materials. In this work, we combine a set of systematic experiments and modeling to address creep anisotropy and its correlation with microstructural characteristics in laser-based powder bed fusion (PBF-LB/M) additively manufactured Inconel-738LC (IN738LC). Three sample orientations (with the tensile axis parallel, perpendicular, and 45° tilted, relative to the building direction) are crept at 850 °C, accompanied by electron backscatter secondary diffraction (EBSD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) investigations. A crystal plasticity (CP) model for Ni-base superalloys, capable of modeling different types of slip systems, is developed and combined with various polycrystalline representative volume elements (RVEs) built on the experimental measurements. Besides our experiments, we verify our modeling framework on electron beam powder bed fusion (PBF-EB/M) additively manufactured Inconel-738LC. The results of our simulations show that while the crystallographic texture alone cannot explain the observed creep anisotropy, the superlattice extrinsic stacking faults (SESF) and related microtwinning slip systems play major roles as active deformation mechanisms. We confirm this using TEM investigations, revealing evidence of SESFs in crept specimens. We also show that the elongated grain morphology can result in higher creep rates, especially in the specimens with a tilted tensile axis.
Today’s industrial demands challenge the research and development sector to make advances in the design and properties of materials that can withstand harsh environments. The AlMo0.5NbTa0.5TiZr refractory high-entropy superalloy (RSA), with a remarkable morphological similarity to the γ/γ' microstructure of Ni-based superalloys and promising high-temperature compressive properties, has been considered as a candidate for structural applications. However, additional properties need to be investigated in order to assess the suitability of this alloy for high temperature applications. Therefore, this work investigates the thermodynamic and microstructural stabilities of the RSA at room temperature and between 900 and 1100 °C, and their influence on the mechanical properties. Although it is possible to improve the mechanical properties at 20 °C by tuning the cooling rate, long-term high temperature exposures lead to phase instabilities that negatively influence the creep behavior.
Using the method of directional solidification, single crystals of experimental nickel-based superalloys with negative, zero, and positive γ/γ' misfits are obtained. The γ' solvus, solidus, and liquidus temperatures of the alloys are determined, and the microstructures of the alloys after directional solidification, heat treatment, and creep tests are investigated. Creep tests are performed at temperatures of 800 and 1000°C. It is found that single crystals of the alloy with a negative γ/γ' misfit have the highest creep resistance and lifetime (the crystal lattice period of the γ' phase is smaller than that of the γ matrix).
The multi-phase approach has proven to widen the application properties of high entropy alloys. After a decade of testing different alloys in the Al-Co-Cr-Cu-Fe-Ni-Ti family the Al10Co25Cr8Fe15Ni36Ti6 was found to be a solid base for more fine-tuned microstructural optimization. Following the example of superalloys, the Al10Co25Cr8Fe15Ni36Ti6 alloy aims for a γ/γ' microstructures in order to guarantee a good microstructural stability at high temperatures. The shape and volume fraction of the γ' particles is known to influence the mechanical properties of superalloys, and they do so in the high entropy family as well [1]. Shape, misfit and creep properties of several modified versions of the Al10Co25Cr8Fe15Ni36Ti6 alloy are compared and discussed in this talk.
The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed.