5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (32)
- Beitrag zu einem Tagungsband (18)
- Forschungsdatensatz (17)
- Vortrag (16)
- Buchkapitel (5)
- Forschungsbericht (4)
- Monografie (1)
- Posterpräsentation (1)
Schlagworte
- Creep (11)
- Ontology (11)
- Aging (9)
- Microstructure (7)
- Additive manufacturing (6)
- Aluminium (6)
- Aluminium alloy (6)
- EN AW-2618A (5)
- FAIR data (5)
- Shear modulus (5)
Organisationseinheit der BAM
- 5 Werkstofftechnik (94)
- 5.2 Metallische Hochtemperaturwerkstoffe (93)
- 5.5 Materialmodellierung (14)
- 9 Komponentensicherheit (13)
- 8 Zerstörungsfreie Prüfung (11)
- 5.1 Mikrostruktur Design und Degradation (10)
- 8.5 Röntgenbildgebung (7)
- 9.6 Additive Fertigung metallischer Komponenten (7)
- 9.4 Integrität von Schweißverbindungen (5)
- 8.0 Abteilungsleitung und andere (3)
Eingeladener Vortrag
- nein (16)
The integration of additive manufacturing with traditional processes, termed hybrid additive manufacturing, has expanded its application domain, particularly in the repair of gas turbine blade tips. However, process-related defects in additively manufactured materials, interface formation, and material property mismatches in dual-material structures can significantly impact the fatigue performance of components. This investigation examines the low cycle fatigue and fatigue crack growth behaviors in dual-material specimens of nickel-based alloys, specifically the additively manufactured STAL15 and the cast alloy 247DS, at elevated temperatures. Low cycle fatigue experiments were conducted at temperatures of 950 °C and 1000 °C under a range of strain levels (0.3%–0.8%) and fatigue crack growth tests were conducted at 950 °C with stress ratios of 0.1 and −1. Fractographic and microscopic analyses were performed to comprehend fatigue crack initiation and crack growth mechanisms in the dual-material structure. The results consistently indicated crack initiation and fatigue fracture in the additively manufactured STAL15 material. Notably, fatigue crack growth retardation was observed near the interface when the crack extended from the additively manufactured STAL15 material to the perpendicularly positioned interface. This study highlights the importance of considering yield strength mismatch, as well as the potential effects of residual stresses and grain structure differences, in the interpretation of fatigue crack growth behavior at the interface.
High Temperature Fatigue Crack Growth in Nickel-Based Alloys Refurbished by Additive Manufacturing
(2024)
Hybrid additive manufacturing plays a crucial role in the restoration of gas turbine blades, where, e.g., the damaged blade tip is reconstructed by the additive manufacturing process on the existing blade made of a parent nickel-based alloy. However, inherent process-related defects in additively manufactured material, along with the interface created between the additively manufactured and the cast base material, impact the fatigue crack growth behavior in bi-material components. This study investigates the fatigue crack growth behavior in bi-material specimens of nickel-based alloys, specifically, additively manufactured STAL15 and cast alloy 247DS. The tests were conducted at 950 °C with stress ratios of 0.1 and −1. Metallographic and fractographic investigations were carried out to understand crack growth mechanisms. The results revealed significant retardation in crack growth at the interface. This study highlights the potential contributions of residual stresses and microstructural differences to the observed crack growth retardation phenomenon, along with the conclusion from an earlier study on the effect of yield strength mismatch on crack growth behavior at a perpendicular interface in bi-material specimens.
Fatigue test ontology (FTO)
(2024)
Fatigue Test Ontology (FTO) has developed for representing the fatigue testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 12106 standard.
Versions info:
V2 developed using PROVO+PMDco top-level ontologies.
V3 developed using BFO+IOF top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/lcf-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Fatigue-Test-Ontology-FTO-
MatPortal: https://matportal.org/ontologies/FTO
IndustryPortal: https://industryportal.enit.fr/ontologies/FTO
Tensile Stress Relaxation Test Ontology (TSRTO) has developed for representing the tensile stress relaxation testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 10319-1 standard.
Versions info:
V1 developed using BFO+CCO top-level ontologies.
V3 developed using PROV+PMDco top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/relaxation-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Tensile-Stress-Relaxation-Test-Ontology-TSRTO
MatPortal: https://matportal.org/ontologies/TSRTO
IndustryPortal: https://industryportal.enit.fr/ontologies/TSRTO
Tensile test ontology (TTO)
(2024)
Tensile Test Ontology (TTO) has developed for representing the Tensile testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6892-1 standard.
Versions info:
V2 developed using BFO+CCO top-level ontologies.
V3 developed using PROVO+PMDco top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/tensile-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Tensile-Test-Ontology-TTO-
MatPortal: https://matportal.org/ontologies/TTO
IndustryPortal: https://industryportal.enit.fr/ontologies/TTO
Vickers test ontology (VTO)
(2024)
Vickers Test Ontology (VTO) has developed for representing the Vickers testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6507-1 standard.
Versions info:
V2 developed using BFO+CCO top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/vickers-hardness-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Vickers-Test-Ontology-VTO-
MatPortal: https://matportal.org/ontologies/VTO
IndustryPortal: https://industryportal.enit.fr/ontologies/VTO
Brinell test ontology (BTO)
(2024)
Brinell Test Ontology (BTO) has developed for representing the Brinell testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6506-1 standard.
Versions info:
V2 developed using BFO+CCO top-level ontologies.
V3 developed using EMMO+CHAMEO top-level ontologies.
V4 developed using PROVO+PMDco top-level ontologies.
V5 developed using BFO+IOF top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/brinell-hardness-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Brinell-Test-Ontology-BTO-
MatPortal: https://matportal.org/ontologies/BTO
IndustryPortal: https://industryportal.enit.fr/ontologies/BTO
This data article presents a set of primary, analyzed, and digitalized mechanical testing datasets for nine copper alloys. The mechanical testing methods including the Brinell and Vickers hardness, tensile, stress relaxation, and low-cycle fatigue (LCF) testing were performed according to the DIN/ISO standards. The obtained primary testing data (84 files) mainly contain the raw measured data along with the testing metadata of the processes, materials, and testing machines. Five secondary datasets were also provided for each testing method by collecting the main meta- and measurement data from the primary data and the outputs of data analyses. These datasets give materials scientists beneficial data for comparative material selection analyses by clarifying the wide range of mechanical properties of copper alloys, including Brinell and Vickers hardness, yield and tensile strengths, elongation, reduction of area, relaxed and residual stresses, and LCF fatigue life. Furthermore, both the primary and secondary datasets were digitalized by the approach introduced in the research article entitled “Toward a digital materials mechanical testing lab” [1]. The resulting open-linked data are the machine-processable semantic descriptions of data and their generation processes and can be easily queried by semantic searches to enable advanced data-driven materials research.
Addressing a strategy for publishing open and digital research data, this article presents the approach for streamlining and automating the process of storage and conversion of research data to those of semantically queryable data on the web. As the use case for demonstrating and evaluating the digitalization process, the primary datasets from low‐cycle‐fatigue testing of several copper alloys are prepared. The fatigue test ontology (FTO) and ckan.kupferdigital data management system are developed as two main prerequisites of the data digitalization process. FTO has been modeled according to the content of the fatigue testing standard and by reusing the basic formal ontology, industrial ontology foundry core ontology, and material science and engineering ontology. The ckan.kupferdigital data management system is also constructed in such a way that enables the users to prepare the protocols for mapping the datasets into the knowledge graph and automatically convert all the primary datasets to those machine‐readable data which are represented by the web ontology language. The retrievability of the converted digital data is also evaluated by querying the example competency questions, confirming that ckan.kupferdigital enables publishing open data that can be highly reused in the semantic web.
The strength of age-hardenable aluminum alloys is based on the controlled formation of nm-sized precipitates, which represent obstacles to dislocation movement. Transmission electron microscopy (TEM) is generally used to identify precipitate types and orientations and to determine their size. This geometric quantification (e.g., length, diameter) is often performed by manual image analysis, which is very time consuming and sometimes poses reproducibility problems. The present work aims at the digital representation of this characterization method by proposing an automatable digital approach. Based on DF-TEM images of different precipitation states of alloy EN AW-2618A, a modularizable digital workflow is described for the quantitative analysis of precipitate dimensions. The integration of this workflow into a data pipeline concept is also presented. The semantic structuring of data allows data to be shared and reused for other applications and purposes, which enables interoperability.