5 Werkstofftechnik
Filtern
Dokumenttyp
- Vortrag (33) (entfernen)
Referierte Publikation
- nein (33)
Schlagworte
- Corrosion (10)
- CCUS (6)
- CO2 (4)
- Droplet corrosion (4)
- Martensitic steel (4)
- Supercritical/dense phase CO2 (4)
- CCS (3)
- CCU (3)
- Carbon steels (3)
- Full Notch Creep Test (3)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (33) (entfernen)
Eingeladener Vortrag
- nein (33)
Slow crack growth (SCG) under the influence of external fluid media, usually termed environmental stress cracking (ESC), is still one of the most frequent origins of severe damage and failure of polymeric materials. For polyethylene (PE) this is relevant for mass products, like bottles for consumer products, but also for high-performance materials for pipes or industrial packaging, including containers for chemicals and other dangerous goods. Especially for high-density polyethylene (PE-HD) the susceptibility to SGC and ESC is depending on the complex interplay between molecular weight and architecture and the resulting semicrystalline morphology, especially the formation of tie-molecules.
A reliable assessment of the resistance against this damage phenomenon is essential for demanding as well as safety-critical applications and has to take into account suitable testing methodologies and conditions in combination with environmental media reflecting the properties representative for typical fillings and relevant components causing ESC. In this context a better understanding of different influencing factors, such as sorption, swelling or surface activity is necessary together with a detailed characterization of different stages of crack propagation and underlying mechanisms. Therefor well-established testing methods, such as the Full Notch Creep Test (FNCT), were complemented by detailed fracture surface analysis using e.g. LSM and SEM in combination with a time-dependent optical monitoring of the progressing crack growth.
For the crack growth also the ratio of fibrillated craze zone to crack opening is important for the deeper understanding of crack propagation and related material parameters which can be additionally addressed by X-ray computed tomography.
To reveal the corrosion resistance of casing steel/mortar interface in CO2 injection condition, sandwich samples were prepared and exposed up to 20 weeks in aquifer fluid under 10 MPa and 60 °C.
Cross section analysis revealed the crevice corrosion as main mechanism instead of pitting corrosion despite very high concentration of Cl in NGB.
EDS element line scan analysis of the 20-week-exposed metal/mortar coupon showed Chloride distribution, which still not reached the metal/mortar interface, explaining no pitting was observed.
It was confirmed that FeCO3 cannot protect the steel surface in CO2 saturated NGB.
To verify the protective possibility of passivation happened on casing steel/mortar interface, simulated pore solution was synthesized and used to passivate the steel for 42 days. OCP and EIS confirmed the formation of passive layer.
The 42 day passivated layer was broken during the first minute of exposure in CO2 saturated NGB.
However, due to high concentration of Ca2+, a new carbonate CaCO3 dense layer was formed, increased the corrosion resistance of steel surface.
Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited. (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv) Corrosion rates increase with increasing water content. (0.2 – 20 mm/a) Condensation of acids and therefore droplet formation is always possible, even at low water contents. A low SO2 content within the CO2-stream might be more important than a low water content. Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications. Low alloyed steels showed better corrosion behavior (predictable uniform corrosion). For direct contact with saline aquifer fluids only high alloyed steels shall be used.
Das langsame Risswachstum (slow crack growth, SCG) sowie der umgebungsbedingte Spannungsriss (environmental stress cracking, ESC) sind relevante Schädigungsmechanismen für teilkristalline Werkstoffe auf Basis von Polyethylen hoher Dichte (PE-HD).
Der Vortrag gibt einerseits einen Überblick über die grundlegenden Struktur-Eigenschafts-Beziehungen in diesem Kontext, andererseits werden auch verschiedene praxisorientierte Prüfverfahren vorgestellt. Letztere wurden in gemeinsamen Forschungsprojekten von BAM und LBF mit dem Schwerpunkt Gefahrgutbehälter bzw. Pflanzenschutzmittel vergleichend untersucht und durch weitergehende Analytik ergänzt.
Polyethylen hoher Dichte (PE-HD) ist ein weit verbreitetes Material für Transportbehälter, die oft für eine längere Nutzungsdauer vorgesehen sind. Insbesondere in diesem Fall können mikroskopische Schäden im Material auch weit unterhalb der Streckgrenze auftreten, die durch eine Spannungskonzentration verursacht werden, deren Ursprung in intrinsischen Materialfehlern oder äußeren Kratzern liegt. Mit fortschreitender Schädigung bilden sich Rissstrukturen, die von verstreckten Fibrillen aufgespannt werden, bis es zum Versagen dieser Fibrillen kommt und sich der Riss ausbreitet. Dieser Schadensmechanismus des langsamen Risswachstums kann durch eine Vielzahl von Umgebungsmedien beschleunigt werden und wird dann als "environmental stress cracking" (ESC) bezeichnet. Eine international normierte Methode zur Validierung der Spannungsrissbeständigkeit von PE-HD Materialien ist der „Full Notch Creep Test“ (FNCT).
Anhand von Bruchflächenauswertungen mittels Rasterelektronenmikroskopie und Laser-Scanning-Mikroskopie, werden die typischen Schädigungsstrukturen des ESC sichtbar. Die fibrillierten Strukturen des ESC auf der Bruchfläche von PE-HD ergeben sich besonders bei oberflächenaktiven wässrigen Umgebungsmedien. In Lösungsmittel-Umgebungsmedien, im Zusammenspiel mit PE-HD, kommt es aufgrund der plastifizierenden Wirkung zur Herabsetzung der Streckspannung und Bruchflächen aus dem FNCT veranschaulichen keine signifikanten Anzeichen des Schädigungsmechanismus ESC.
Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited. (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv).
Corrosion rates increase with increasing water content.
(0.2 – 20 mm/a).
Condensation of acids and therefore droplet formation is always possible, even at low water contents.
A low SO2 content within the CO2-stream might be more important than a low water content.
Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications.
Low alloyed steels showed better corrosion behavior. (predictable uniform corrosion)
For direct contact with saline aquifer fluids only high alloyed steels shall be used.
Currently, the Full Notch Creep Test (FNCT) [1] method is used by material suppliers and end users in industry for the approval of container and pipe materials based on high-density polyethylene (PE-HD). The resistance to environmental stress cracking (ESC) of the material is evaluated using the time to failure of the specimen in an aqueous solution of a detergent [2, 3]. Usually specimens made of sheets with isotropic material properties, manufactured by hot pressing, are employed in order to obtain intrinsic properties of the material in terms of ESC failure. In contrast, the processes used in manufacturing to form containers and pipes, such as extrusion blow molding or extrusion, impose anisotropic properties to the material. These are mostly due to a microstructural orientation (polymer chains or crystallites) [4]. Furthermore, the different cooling conditions significantly affect the size distribution of crystallites as well as the overall morphology. It is therefore essential to understand the influence of process-induced material characteristics on failure due to ESC.
A large number of studies on material properties as a function of microstructural preferential orientation have already been conducted [5-7]. However, effects on ESC as the major failure mechanism of containers and pipes are still rather unexplored [8, 9]. The most important factor is whether primarily intramolecular high-strength covalent bonds or the substantially weaker intermolecular van der Waals forces are predominantly loaded.
In addition to the widely established classification by time to failure, the strain or crack opening displacement (COD) provides valuable information about the evolution and progression of damage as a function of time [10, 11]. Optical strain measurement using digital image correlation allows the differences in COD for isotropic and different angles of orientation of anisotropic specimens to be discussed. Also, a post-fracture surface analysis provides clarification on the craze-crack mechanism of the ESC. These different ESC-related properties of extruded and hot-pressed specimens have been investigated at different environmental medium temperatures and different initial stresses to provide a broad characterization of the fracture behavior of PE-HD.
Polyethylen hoher Dichte (PE-HD) wird als Werkstoff für Rohre und Behälter für den Transport und zur Lagerung von Gefahrgütern verwendet. Für die Beurteilung und technische Freigabe dieser Materialien ist insbesondere das Verständnis des Schädigungsmechanismus des langsamen, umgebungsbedingten Spannungsrisses (engl.: „environmental stress cracking“, ESC) essentiell. ESC tritt bei relativ geringen auf einen Werkstoff einwirkenden mechanischen Spannungen auf. An lokalen Fehlstellen (z.B. Defekte, Inhomogenitäten, Kerben) beginnend wächst ein Riss langsam durch das Material und führt nach gewisser Zeit zu einem charakteristischen, pseudo-spröden Bruch. Dabei wird das Risswachstum durch äußere Medieneinwirkung zusätzlich entscheidend beeinflusst. Dieses langsame Risswachstum wird als Hauptursache für das plötzliche und unerwartete Versagen von Polymerwerkstoffen angesehen.
Eine etablierte Prüfmethode zur Bewertung des Materialverhaltens gegenüber dieses Schädigungsmechanismus ist der Full-Notch Creep Test (FNCT), der für PE-HD Behältermaterialien üblicherweise unter Verwendung von wässrigen Netzmittellösungen (Arkopal N 100) durchgeführt wird. Die aus dem FNCT erhaltene Standzeit dient dabei als Bewertungskriterium für verschiedene PE-HD-Werkstoffe. In einer Studie wurden neben einer typischen Arkopal-N-100-Netzmittellösung praktisch relevante, organische Flüssigkeiten wie Biodiesel und Diesel als Testmedien verwendet, um deren Einfluss auf das ESC-Verhalten von PE-HD-Behältermaterialien zu charakterisieren. Neben der klassischen Standzeit-Auswertung erfolgte eine erweiterte Bruchflächenanalyse mittels Licht- (LM), Laserscanning- (LSM) und Rasterelektronenmikroskopie (REM). Insbesondere die LSM erlaubt eine schnelle und einfache Unterscheidung pseudo-spröder und duktiler Bruchbilder, die zur Beurteilung der Repräsentativität des FNCT für das dem Spannungsriss zugrundeliegenden langsamen Risswachstum von Bedeutung ist.
Study of Polyaniline/Silicon Dioxide based Coating on Carbon Steel in Artificial Geothermal Brine
(2021)
By using the available resources in Indonesia, such as silicon dioxide and marine coating base, the PANI/SiO2 modified alkyd coating was able to protect carbon steel in a deaerated artificial geothermal water. The screening of coatings shows that the modification by adding individual pigment was not sufficient to protect carbon steel even during a short-term exposure, indicated by the discoloration after only seven days of exposure. Electrochemical tests indicated that there was no significant change in the Ecorr between the coated and uncoated carbon steel at room temperature. At 150 °C, the coated carbon steel has a lower potential than that of carbon steel, indicating that the coating is protecting carbon steel cathodically or slowing down the corrosion reaction. Finally, a long-term exposure test confirmed that the PANI/SiO2 modified coating successfully protects the carbon steel in the Sibayak artificial geothermal water up to 150 °C for 6 months.
Al2O3 coatings are often used as protective layers on steels against electrochemical and high-temperature corrosion because they are chemically inert and stable at elevated temperatures. This study presents preliminary work on the possibilities of using Al2O3 sol-gel coatings for corrosion protection of martensitic stainless steels in geothermal environments. Al2O3 sol-gel coatings were applied on UNS S42000, which is known to be susceptible to uniform and localized corrosion. The coated steel specimens were then tested in two types of artificial geothermal water, which simulate the geothermal fluids found in Sibayak (SBY), Indonesia, and North German Basin (NGB), Germany, respectively. SBY has pH 4 and 1.5 g/L of chloride ions, whereas NGB has a pH of 6 and 166 g/L of chloride ions. All experiments were carried out in autoclaves at 150 °C and 1 MPa under the deaerated condition. Evaluations were performed by investigating the surface profiles of both uncoated and coated steels before and after the corrosion test using a Laser Scanning Microscope (LSM) and Scanning Electron Microscope (SEM). Finally, Electrochemical Impedance Spectroscopy (EIS) was performed to compare the corrosion resistance of Al2O3 coated steels in SBY and NGB solutions. It was observed from the corrosion test that Al2O3 coatings are more suitable for use in the geothermal water with a higher pH.