Lamellar eutectics are known to evidence plastic shear in otherwise brittle intermetallics, if the lamella spacing is small enough. Here we pursue this idea of confined plasticity in intermetallics further and demonstrate room-temperature shear-deformation in a two-phase CuAl 2 -CuAl intermetallic nano- composite. The presence of a phase with a 3-fold symmetry is also revealed after deformation. Simula- tion of transmission electron microscopy images shows this to be monoclinic CuAl. These observations are made in the deformation zone underneath locations of nanoindents, of which the force-displacement curves exhibit an unusual response of continuously increasing pop-in sizes with load.
The onset of plasticity in a single crystal C60 fullerite was investigated by nanoindentation on the (111) crystallographic plane. The transition from elastic to plastic deformation in a contact was observed as pop-in events on loading curves. The respective resolved shear stresses were computed for the octahedral slip systems ⟨011¯¯¯⟩{111}, supposing that their activation resulted in the onset of plasticity. A finite element analysis was applied, which reproduced the elastic loading until the first pop-in, using a realistic geometry of the Berkovich indenter blunt tip. The obtained estimate of the C60 theoretical shear strength was about 1/11 of the shear modulus on {111} planes.