5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2022 (5) (entfernen)
Dokumenttyp
- Vortrag (4)
- Zeitschriftenartikel (1)
Schlagworte
- Ceramics (2)
- Keramik (2)
- Alumina (1)
- Biaxial strength (1)
- Dielectric breakdown strength (1)
- Electric field distribution (1)
- Federkonstante (1)
- Festigkeit (1)
- Hartbearbeitung (1)
- Implants (1)
- Liquid phase sintering (1)
- Pressure assisted sintering (1)
- Sintering additive (1)
- Überblick (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
This study combines three different approaches to lower the sintering temperature of Sm-doped CaMnO3 to save energy in production and facilitate co-firing with other low-firing oxides or metallization. The surface energy of the powder was increased by fine milling, sintering kinetics were enhanced by additives, and uniaxial pressure during sintering was applied. The shrinkage, density, microstructure, and thermoelectric properties were evaluated. Compared to micro-sized powder, the use of finely ground powder allows us to lower the sintering temperature by 150 K without reduction of the power factor. By screening the effect of various common additives on linear shrinkage of CaMnO3 after sintering at 1100 ○C for 2 h, CuO is identified as the most effective additive. Densification at sintering temperatures below 1000 ○C can be significantly increased by pressure-assisted sintering. The power factor at room temperature of CaMnO3 nano-powder sintered at 1250 ○C was 445 μW/(m K2). Sintering at 1100 ○C reduced the power factor to 130 μW/(m K2) for CaMnO3 nano-powder, while addition of 4 wt.% CuO to the same powder led to ∼290 μW/(m K2). The combination of fine milling, CuO addition, and pressureassisted sintering at 950 ○C resulted in a power factor of ∼130 μW/(m K2). These results show that nano-sized powder and CuO addition are successful and recommendable strategies to produce CaMnO3 with competitive properties at significantly reduced temperatures and dwell times.
Aufgrund ihres spezifischen Eigenschaftsprofils sind keramische Federn attraktiv für Spezialanwendungen in Maschinenanlagen, Metrologie und Sensortechnik. Durch Hartbearbeitung keramischer Hohlzylinder können Spiralfedern mit rechteckigem Windungsquerschnitt präzise gefertigt werden. Dabei kann durch gezielte Auslegung der Federgeometrie die Federkonstante über mehrere Größenordnungen variiert werden. Der Vortrag gibt einen Überblick über den Herstellungsprozess, verschiedene Eigenschaften keramischer Federn und Anwendungsbeispiele.
Roughening of zirconia dental implants is a common clinical practice to improve ingrowth behavior. It depends on the manufacturer of the implant at which stage of the manufacturing process and by which method the surface is roughened. Systematic studies on this topic are rarely found in the literature. Therefore, the influence of surface treatment on the strength of a dental zirconia was investigated as part of a research project on the development of ceramic implants. The material under test was a commercial zirconia consisting of a Y-TZP matrix and Ce-TZP inclusions in the sintered state. This material is characterized by a slightly higher fracture toughness and slightly reduced strength compared to typical 3Y-TZP. Sets of samples were sandblasted in the white-fired or sintered condition. The ball-on-three-ball-strength of these samples was measured and compared to the strength of as-fired samples and polished samples. The complete study was performed two times for validation of the results. It is found that the average strength of TZP ceramics differs by almost 500 MPa depending on the surface treatment. Conventionally sintered specimens with as-fired surface exhibit a strength of 880 MPa. Sandblasting in the white fired state reduces the strength to 690 MPa. Both polishing and sandblasting in the sintered condition result in an increase in strength to about 1180 MPa. Comparative microstructural investigations, roughness measurements and X-ray phase analyses were carried out to determine the causes of these huge differences in strength. These findings may challenge the practice of white body surface treatment and give reason for further investigations on other commercial dental TZP materials.
Der Vortrag gibt einen Überblick über die Materialklasse Keramik, insbesondere Technische Keramik. Nach einem kurzen Überblick über typische Anwendungen und Werkstoffe wird die keramische Prozesskette erläutert. Am Beispiel von Festigkeit wird der für Keramik typische, enge Zusammenhang zwischen Technologie, Mikrostruktur und Eigenschaften herausgearbeitet. Daraus werden Anforderungen für eine erfolgreiche Digitalisierung abgeleitet.
Dielectric breakdown of insulators is a combined electrical, thermal, and mechanical failure. The exact breakdown mechanism in ceramics and the formulation of useful models are still subject of investigation. Recent studies highlighted that several experimental aspects of dielectric breakdown strength testing affect the test results, and thus impede the recognition of fundamental principles.
Excess field strength near the electrode can lead to premature breakdown in the insulating liquid. This would cause superficial damage to the test specimen and thus falsify the measurement results.
The field strength distribution is influenced by the ratio of permittivity of the sample and the surrounding insulating liquid. Premature breakdown depends on the breakdown strength of the liquid and the actual test voltage. The test voltage again depends on the specimen thickness.
To systematically investigate these relations, a numerical simulation study (FEM) of the electric field distribution in a typical testing rig with cylindrical electrodes was performed. The permittivity of the sample and the insulating liquid was parameterized, as well as the sample thickness. The electric field distribution was calculated for increasing test voltage. Field strength maxima are compared to experimental breakdown strength of typical insulating liquids and experimental breakdown locations on alumina. Strategies are discussed to adjust the insulation liquid and the sample thickness to reduce the influence of the testing setup on the dielectric breakdown strength results.