5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2022 (142) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (61)
- Vortrag (54)
- Posterpräsentation (12)
- Beitrag zu einem Tagungsband (8)
- Forschungsdatensatz (4)
- Buchkapitel (2)
- Forschungsbericht (1)
Sprache
- Englisch (142) (entfernen)
Schlagworte
- Additive manufacturing (12)
- Additive Manufacturing (9)
- Transmission electron microscopy (9)
- Corrosion (8)
- Microstructure (7)
- Ceramics (6)
- Creep (6)
- Ontology (6)
- Aluminium alloy (5)
- EN AW-2618A (5)
- Glass (5)
- High entropy alloy (5)
- Nickel-base superalloys (5)
- AGIL (4)
- Alkali zinc borate glasses (4)
- FAIR (4)
- Fatigue (4)
- Fractography (4)
- Sintering (4)
- Aging (3)
- Alumina (3)
- Aluminium Alloy (3)
- CCS (3)
- CO2 quality (3)
- Crystallization (3)
- HIP (3)
- In-space manufacturing (3)
- LCF (3)
- Laser powder bed fusion (3)
- Machine Learning (3)
- Microgravity (3)
- Raman spectroscopy (3)
- SEM (3)
- Self-healing (3)
- Sulfiding (3)
- μ-gravity (3)
- 3D printing (2)
- Austenitic steel 316L (2)
- Bioactive Glass (2)
- Bond energy (2)
- Brinell hardness (2)
- CALPHAD (2)
- CO2 (2)
- Characterization (2)
- Copper (2)
- Crop protection products (2)
- Cross linking (2)
- Cure process (2)
- Data management (2)
- Data mapping (2)
- Dielectric properties (2)
- Diffraction (2)
- Dislocation (2)
- Dynamic mechanical analysis (DMA) (2)
- EDX (2)
- Electron backscatter diffraction (2)
- Electron microscopy (2)
- Environmental stress cracking (2)
- FIB (2)
- Fracture (2)
- Fracture toughness (2)
- GD-OES (2)
- Glass fiber reinforced polymers (2)
- High Cycle Fatigue (2)
- High-density polyethylene (2)
- ISRU (2)
- Infrastructure (2)
- Interfacial strength (2)
- Laser beam melting (2)
- Layerwise slurry deposition (2)
- Lead borate glasses (2)
- Lithium Ion Batteries (2)
- Lunar habitat (2)
- Lunar regolith simulant (2)
- Material digital (2)
- Mechanical behavior (2)
- Mechanical testing (2)
- Melt pool boundary (2)
- Microstructural characterization (2)
- Microstructure Design (2)
- NFDI (2)
- Nanoparticles (2)
- Neutron diffraction (2)
- Notches (2)
- Paving (2)
- Pipeline network (2)
- Plasticity (2)
- Rapid solidification (2)
- S355 steel sheet (2)
- Scarf repairs (2)
- Silver metallization paste (2)
- Solar sintering (2)
- Steel (2)
- Superalloy (2)
- Surface energy (2)
- Tensile properties (2)
- Tensile test (2)
- Texture (2)
- Thermal Spray (2)
- Thermoset polymers (2)
- Ti-6Al-4V (2)
- Topography (2)
- Viscosity (2)
- X-ray diffraction (2)
- 12%Cr steel (1)
- 150 Years (1)
- 316L (1)
- 3D (1)
- Adolf Martens (1)
- Advanced ceramics (1)
- Advanced manufacturing (1)
- Aerospace (1)
- Al-Cu binary alloy system (1)
- Al2CuMg (1)
- Alloy design (1)
- Alloy microstructure (1)
- Atmospheric Plasma Spraying (1)
- Atmospheric plasma spraying (1)
- Automated finite element analysis (1)
- Automatische Finite Element Simulation (1)
- Batch reactions (1)
- Biaxial strength (1)
- Binder Jetting (1)
- Binder jetting (1)
- Bioactivity (1)
- Biphasic calcium phosphate (1)
- Borate (1)
- Brass (1)
- CALPHAD database analysis (1)
- CCU (1)
- Calcium cobaltite (1)
- Cantor alloy (1)
- Carbide phase NbC (1)
- Carbon fibres (1)
- Carbon nanotubes (1)
- Ceramic (1)
- Certified Referencematerial (1)
- Charpy test (1)
- Chemically complex alloy (1)
- Co-firing (1)
- Compositionally complex alloys (1)
- Corrosion costs (1)
- Corrosion mechanism (1)
- Corrosion protection (1)
- Crack growth (1)
- Crack opening displacement (1)
- Crack propagation (1)
- Craze–crack mechanism (1)
- Creation-relaxation algorithm (1)
- Creep behavior (1)
- Creep data (1)
- Creep under thermal cycling (1)
- Creep-fatigue (1)
- Crystal lattice (1)
- Crystal lattice period (1)
- Crystal orientation (1)
- Crystal plasticity (1)
- Crystalline defects (1)
- Cubical Iron Oxide (1)
- Cubical shape (1)
- Cuttlefish (1)
- Cyclic steam oxidation (1)
- Damage Behavior (1)
- Data format (1)
- Data infrastructures (1)
- Data linking (1)
- Data structure (1)
- Debonding (1)
- Degradation (1)
- Dielectric Spectroscopy (1)
- Dielectric breakdown strength (1)
- Dielectric characterization (1)
- Digital representation (1)
- Digital representations (1)
- Digital workflows (1)
- Digitalization (1)
- Digitization (1)
- Dimensional mismatch of crystalline lattice periods (misfit) (1)
- Dwell-Fatigue (1)
- EAC-1A (1)
- EBSD (1)
- EN AW 2618A a (1)
- EXAFS (1)
- Elasticity (1)
- Electric field distribution (1)
- Electrical insulation (1)
- Electron Backscatter Diffraction (1)
- Electron Microscopy (1)
- Electron beam induced modification (1)
- Epoxy (1)
- Equilibrium relaxation (1)
- Explosive welding (1)
- Faceting (1)
- Fatigue crack growth (1)
- Fe-Al alloys (1)
- Fe-Mn steels (1)
- Fiber/matrix bond (1)
- Film depositition (1)
- Finite element method (1)
- Finite elmenet simulation (1)
- Fluorescence spectroscopy (1)
- Foaming (1)
- Fracture surface (1)
- Fracture surface analysis (1)
- Fracture surface energy (1)
- Fragility (1)
- Full notch creep test (1)
- Geothermal (1)
- Glass fiber-epoxy composites (1)
- Glass forming melts (1)
- Glass manufacturing (1)
- Glass melt (1)
- Gold nanoparticles (1)
- Grain boundary engineering (1)
- Grain boundary precipitates (1)
- Grain boundary structure (1)
- Grain structure (1)
- Graphic design (1)
- Hausner ratio (1)
- Heat Treatment (1)
- Heat treatment (1)
- Heat-resistant nickel alloys (1)
- High Entropy Alloy (1)
- High Voltage Insulation (1)
- High alloyed steel (1)
- High cycle fatigue (1)
- High entropy alloys (1)
- High temperature mechanical properties (1)
- High temperature nickel-based eutectic alloys (1)
- High temperatures (1)
- High-entropy alloys (1)
- High‐temperature corrosion (1)
- Hot stage microscopy (1)
- Hydrogen sensor (1)
- IR spectroscopy (1)
- Implants (1)
- Impurities (1)
- In situ thermal-annealing experiment (1)
- In-situ composites (1)
- Inconel 718 (1)
- Intermetallics (1)
- Intermittent microplasticity (1)
- Interoperability (1)
- Intrinsic stress (1)
- Invar (1)
- Iron (1)
- Iron aluminides (1)
- Iron oxide (1)
- KCl (1)
- Keywords: Poly(ether ether ketone) (1)
- Knowledge graphs (1)
- LTCC (1)
- Laser Powder Bed Fusion (1)
- Laser Powder Bed Fusion (LPBF) (1)
- Laser induced slipcasting (1)
- Laser light scattering (1)
- Laser powder-based directed energy deposition (1)
- Lattice misfit (1)
- Laves phase (1)
- Life cycle (1)
- Linear elastic fracture mechanics (1)
- Liquid phase sintering (1)
- Low-Cycle-Fatigue (1)
- Machine learning (1)
- Mat-o-lab (1)
- Material Digital (1)
- Material failure (1)
- Materials Modelling (1)
- Materials Science (1)
- Materials Testing (1)
- Materials informatics (1)
- Materials testing (1)
- Mechanical Behavior (1)
- Mechanical deformation (1)
- Medium Entropy Alloys (1)
- Meta material (1)
- Metal additive manufacturing (1)
- Metallic glasses (1)
- Microplastic stress (1)
- Microstructural changes of a Fe Si alloy (1)
- Microstructural evolution (1)
- Microstructure analysis (1)
- Microstructure evolution (1)
- Model (1)
- Molecular Dynamics (1)
- Molecular dynamics (1)
- Mortar (1)
- Multilayer technology (1)
- NFDI-MatWerk (1)
- Nano CRM (1)
- Nanoelectromechanical systems (NEMS) (1)
- Native oxide (1)
- Networking (1)
- Nickel-based superalloys (1)
- Nucleation mode (1)
- Nucleation tendency (1)
- Ontologies (1)
- Ontology development (1)
- Ordering (1)
- Oriented surface crystallization (1)
- Oxide (1)
- Oxide glass (1)
- Oxidglas (1)
- Particle size (1)
- Phase Diagrams (1)
- Phase field crystal (1)
- Phase field method (1)
- Phase stability (1)
- Phase-Field Simulations (1)
- Phase-field (1)
- Phase-field model (1)
- Physical aging (1)
- Physical properties (1)
- Pipeline (1)
- Plasma spray (1)
- Plastic deformation (1)
- Platform MaterialDigital (PMD) (1)
- Polymer-matrix composites (PMC) (1)
- Pore (1)
- Porosity (1)
- Powder (1)
- Powder processing (1)
- Precipitation (1)
- Precipitation Analysis (1)
- Precipitation hardening (1)
- Pressure assisted sintering (1)
- Preventive strategies (1)
- Process (1)
- Process monitoring (1)
- Proficiency test (1)
- Radii distribution (1)
- Recommendations (1)
- Reference Data (1)
- Reference Dataset (1)
- Reference nanoparticles (1)
- Refractory superalloys (1)
- Research Data Management (1)
- Residual Stress (1)
- Residual stress analysis (1)
- Rissausbreitung (1)
- Robotische Glasschmelzanlage (1)
- Roughness (1)
- S-phase (1)
- SAXS (1)
- SIMS (1)
- SO2 (1)
- Scaffold geometry (1)
- Scale-dependent behavior (1)
- Segregation engineering (1)
- Shear (1)
- Short range order (1)
- Silicon carbide (1)
- Silicon nanowires (1)
- Silver (1)
- Silver cluster (1)
- Silver diffusion (1)
- Single crystal (1)
- Sintering additive (1)
- Size (1)
- Slurry (1)
- Small-Angle X-ray Scattering (1)
- Smart materials (1)
- Sodium zinc borate glass (1)
- Space (1)
- Space exploration (1)
- Spark plasma sintering (1)
- Specimen geometry (1)
- Spray drying (1)
- Stainless steel (1)
- Steel alloy (1)
- Strain energy (1)
- Stress intensity factor (1)
- Stress relaxation (1)
- Structure (1)
- Superalloys (1)
- Surface treatments (1)
- Surface-induced Melting (1)
- TEM (1)
- TMF (1)
- TMF experiments (1)
- Tempered martensite-ferritic steel (1)
- Tensile data (1)
- Tensile testing (1)
- Thermobimetal (1)
- Thermoelectric generator design (1)
- Thermoelectric oxides (1)
- Thermoelectrics (1)
- Thermomechanical fatigue (1)
- Thermomechanische Ermüdung (1)
- Thermoplastic (1)
- Thesaurus (1)
- Tools (1)
- Transmission electron microscopy (TEM) (1)
- Transparency (1)
- Tribology (1)
- Two-photon-polymerization (1)
- Ultrasonic assited machining (1)
- Ultrasound (1)
- Vickers hardness (1)
- Visual ontology development (1)
- Vocabulary providers (1)
- Wetting (1)
- Whole-chain CCS scenario (1)
- X-Ray Diffraction (1)
- X-ray diffraction analysis (1)
- XRD (1)
- Young’s Modulus (1)
- Yttria stabilized zirconia (1)
- negative crystal growth (1)
- γ/γ' matrix (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (142)
- 5.1 Mikrostruktur Design und Degradation (44)
- 5.2 Metallische Hochtemperaturwerkstoffe (39)
- 5.4 Multimateriale Fertigungsprozesse (32)
- 5.5 Materialmodellierung (15)
- 5.6 Glas (14)
- 5.3 Polymere Verbundwerkstoffe (11)
- 8 Zerstörungsfreie Prüfung (10)
- 7 Bauwerkssicherheit (9)
- 9 Komponentensicherheit (9)
Paper des Monats
- ja (2)
Due to their unique physico-chemical properties, nanoparticles are well established in research and industrial applications. A reliable characterization of their size, shape, and size distribution is not only mandatory to fully understand and exploit their potential and develop reproducible syntheses, but also to manage environmental and health risks related to their exposure and for regulatory requirements. To validate and standardize methods for the accurate and reliable particle size determination nanoscale reference materials (nanoRMs) are necessary. However, there is only a very small number of nanoRMs for particle size offered by key distributors such as the National Institute of Standards and Technology (NIST) and the Joint Research Centre (JRC) and, moreover, few provide certified values. In addition, these materials are currently restricted to polymers, silica, titanium dioxide, gold and silver, which have a spherical shape except for titania nanorods. To expand this list with other relevant nanomaterials of different shapes and elemental composition, that can be used for more than one sizing technique, we are currently building up a platform of novel nanoRMs relying on iron oxide nanoparticles of different shape, size and surface chemistry. Iron oxide was chosen as a core material because of its relevance for the material and life sciences.
BAM is currently building up a platform of novel nanoRMs relying on iron oxide nanoparticles of different shape, size and surface chemistry. Iron oxide was chosen as a core material because of its relevance to the material and life sciences.
As a first candidate of this series, we present cubic iron oxide nanoparticles with a nominal edge length of 8 nm. These particles were synthesized by thermal decomposition of iron oleate in high boiling organic solvents adapting well-known literature procedures. After dilution to a concentration suitable for electron microscopy (TEM and SEM) as well as for small-angle X-ray scattering (SAXS) measurements, the candidate nanoRM was bottled and assessed for homogeneity and stability by both methods following the guidelines of ISO 17034 and ISO Guide 35.
The particle sizes obtained by both STEM-in-SEM and TEM are in excellent agreement with a minimum Feret of 8.3 nm ± 0.7 nm. The aspect ratio (AR) of the iron oxide cubes were extracted from the images as the ratio of minimum Feret to Feret resulting in an AR of 1.18 for TEM to 1.25 for SEM. Alternatively, a rectangular bounding box was fitted originating from the minimum Feret and the longest distance through the particle in perpendicular direction. This led to AR values of 1.05 for TEM and 1.12 for SEM, respectively. The results confirm the almost ideal cubic shape.
In this study, the influence of aging and mean stress on fatigue of the aluminium-alloy EN AW-2618A is investigated. Therefore axial fatigue tests are carried out on smooth specimens. The experiments show that the fatigue life decreases with increasing mean stress. Furthermore, the tests with the overaged specimens demonstrate that the number of cycles to failure is decreasing with increasing aging time.
The interest to additively manufacture Nickel-based superalloys has substantially grown within the past decade both academically and industrially. More specifically, additive manufacturing processes such as laser powder bed fusion (LPBF) offer the ability to produce dense parts within a single manufacturing step. In fact, the exceptional freedom in design associated with the layer-based nature of the processes is of particular interest for the complex shapes typically required in turbine applications. In certain cases, the overall part performance can be achieved by tailoring the microstructure and the crystallographic texture to the specific application. However, these advantages must be paid at a price: the large local temperature gradients associated with the rapid melting and solidification produce parts that inherently contain large residual stress in the as-manufactured state. In addition, the presence of pores in the final part may further affect the in-service part failure. As among Nickel-based alloys Inconel 718 exhibits excellent weldability, this alloy has been widely studied in open research in the domain of LPBF. However, significant microsegregation of the heavier alloying elements such as Niobium and Molybdenum accompanied by dislocation entanglements may preclude the application of conventional heat treatment schedules. Therefore, different post processing heat treatments are required for laser powder bed fused Inconel 718 as compared to conventional variants of the same alloy.
In this study, we investigated two different heat treatment routes for LPBF Inconel 718. In a first routine, the samples were stress relieved and subsequently subjected to hot isostatic pressing (HIP) followed by a solution heat treatment and a two-step age (referred to as FHT). In a second routine, the samples were subjected to a single-step direct age post stress relieving heat treatment (referred to DA). We investigated the consequences of such heat treatment schedules on the microstructure, texture, and mechanical behavior. We show that by applying a DA heat treatment the typical columnar microstructure possessing a crystallographic texture is retained, while an equiaxed untextured microstructure prevails in case of an FHT heat treatment. We further evaluate how these heat treatments affect the mechanical behaviour on the macroscopic and microscopic scale.
BAM! This issue of Advanced Engineering Materials celebrates 150 years of scientific and technical research at the interface between academia, industry and politics. Rooted in 1871 at the birth of the German Empire and at that time located in simple basements and barracks, the institutional development began around mechanical metallurgy of iron and steel and represents today a diverse portfolio of fore-front research that orients itself along tomorrow's societal challenges and long-term research horizons.
Detailed microstructural characterization of the AlMo0.5NbTa0.5TiZr refractory high entropy superalloy in the as-cast state is reported for first time and compared with the state annealed at 1400 oC for 24 h. The former shows a dendritic structure, with a mixture of A2/B2 phases < 20 nm in both the dendritic and interdendritic regions. A mostly amorphous phase, rich in Al and Zr, is found within the interdendritic region. The annealed state reproduced the combination of A2/B2/Al-Zr-rich phases reported previously. Calculations from two relevant ThermoCalc databases were compared with the experimental results. Equilibrium calculations were compared with results for the annealed alloy, whereas solidification paths calculated using Scheil-Gulliver model were used for comparison with the as-cast alloy. A previously hypothesized spinodal decomposition during cooling as the mechanism responsible for the patterned A2/B2 microstructure is confirmed via the CALPHAD calculations, pointing to its use as an efficient design tool for such alloys. Finally, the comparison between the experimental and computational findings allowed better understanding the solidification path and equilibrium stability of this alloy, giving a base to make better decisions on the field of new refractory superalloy design.
Additive manufacturing methods such as laser powder bed fusion (LPBF) allow geometrically complex parts to be manufactured within a single step. However, as an aftereffect of the localized heat input, the rapid cooling rates are the origin of the large residual stress (RS) retained in as-manufactured parts. With a view on the microstructure, the rapid directional cooling leads to a cellular solidification mode which is accompanied by columnar grown grains possessing crystallographic texture. The solidification conditions can be controlled by the processing parameters and the scanning strategy. Thus, the process allows one to tailor the microstructure and the texture to the specific needs. Yet, such microstructures are not only the origin of the mechanical anisotropy but also pose metrological challenges for the diffraction-based RS determination. In that context the micromechanical elastic anisotropy plays an important role: it translates the measured microscopic strain to macroscopic stress. Therefore, it is of uttermost importance to understand the influence of the hierarchical microstructures and the texture on the elastic anisotropy of LPBF manufactured materials.
This study reveals the influence of the build orientation and the texture on the micro-mechanical anisotropy of as-built Inconel 718. Through variations of the build orientation and the scanning strategy, we manufactured specimens possessing [001]/[011]-, [001]-, and [011]/[111]-type textures. The resulting microstructures lead to differences in the macroscopic mechanical properties. Even further, tensile in-situ loading experiments during neutron diffraction measurements along the different texture components revealed differences in the microstrain response of multiple crystal lattice planes. In particular, the load partitioning and the residual strain accumulation among the [011]/[111] textured specimen displayed distinct differences measured up to a macroscopic strain of 10 %. However, the behavior of the specimens possessing [001]/[011]-and [001]-type texture was only minorly affected. The consequences on the metrology of RS analysis by diffraction-based methods are discussed.
Up to now, oriented surface crystallization phenomena are discussed controversially, and related studies are restricted to few glasses. For silicate glasses we found a good correlation between the calculated surface energy of crystal faces and oriented surface nucleation. Surface energies were estimated assuming that crystal surfaces resemble minimum energy crack paths along the given crystal plane. This concept was successfully applied by Rouxel in calculating fracture surface energies of glasses. Several oriented nucleation phenomena can be herby explained assuming that high energy crystal surfaces tend to be wetted by the melt. This would minimize the total interfacial energy of the nucleus. Furthermore, we will discuss the evolution of the microstructure and its effect on the preferred crystal orientation.
The fracture surface of slow and continuous crack propagation during environmental stress cracking of a semicrystalline polyethylene exhibits isotropic roughness exponents at the local scale but resolved across the macroscopic fracture surface a clear position dependence is found. The spatially resolved roughness exponent admits values in the range between 0.1 and 0.4, demonstrating nontrivial exponents in the small length-scale regime. Instead, they vary across the fracture surface according to the stress-state distribution, which suggests that the exponents are intimately linked to the locally dominating dissipation processes during craze cracking.
Sintering, crystallization, and foaming of 44.8SiO2–2.5P2O3–36.5CaO–6.6Na2O–6.6K2O–3.0CaF2 (F3) and 54.6SiO2–1.7P2O3–22.1CaO–6.0Na2O–7.9K2O–7.7MgO (13–93) bioactive glass powders milled in isopropanol and CO2 were studied via heating microscopy, differential thermal analysis, vacuum hot extraction (VHE), Infrared spectroscopy, and time-of-flight secondary ion mass spectrometry. Full densification was reached in any case and followed by significant foaming.
VHE studies show that foaming is driven by carbon gases and carbonates were detected by Infrared spectroscopy to provide the major foaming source. Carbonates could be detected even after heating to 750◦C, which hints on a thermally very stable species or mechanical trapping. Otherwise, dark gray compact colors for milling in isopropanol indicate the presence of residual carbon as well. Its significant contribution to foaming, however, could not be proved and might be
limited by the diffusivity of oxygen needed for carbon oxidation to carbon gas.
Single-crystal components made of nickel base superalloys contain pores after casting and homogenization heat treatment. Hot isostatic pressing (HIP), which is carried above the γ' -solvus temperature of the alloy, is industrially applied to reduce porosity. A modeling of HIP based on continuously distributed dislocations is developed in a 2D setting. Glide and climb of straight-edge dislocations, as well as vacancy diffusion, are the deformation mechanisms taken into account.
Thereby, dislocation glide is controlled by dragging a cloud of large atoms, and climb is controlled by vacancy diffusion. Relying on previous investigations of the creep behavior at HIP temperatures, it is assumed that new dislocations are nucleated at low-angle boundaries (LAB) and move through subgrains until they either reach the opposite LABs or react with other dislocations and annihilate.
Vacancies are created at the pore surface and diffuse through the alloy until they are either consumed by climbing dislocations or disappear at the LABs. The field equations are solved by finite elements. It is shown that pore shrinking is mostly controlled by vacancy diffusion as the shear stresses at the LABs are too low to
nucleate a sufficient amount of dislocations.
Substitution of lead oxide in low-melting glasses, e.g., for application in silver metallization pastes, is a current research goal. This work is focused on the investigation of silver diffusion in alkali zinc borate glasses (X2O-ZnO-B2O3, X = Li, Na, K, Rb). In addition, the redox state of silver (Ag) and thus the type of diffusing silver species were studied. For this purpose, a metallic silver coating was applied on glass cubes by means of sputtering. Heat treatment of the samples was performed close to the glass transition temperatures at 470 °C for 2 h under air and nitrogen atmosphere. Coating thickness was 1.8 µm after heat treatment, measured by a white light interferometer.
Silver diffusion profiles were measured by means of secondary neutral mass spectrometry. The silver diffusion coefficients are in the range of ~10-14 cm2/s and indicate no significant differences depending on the type of alkali ions in the glass. Dissolved Ag+-ions and [Agm]n+-clusters in the glasses were differentiated using fluorescence spectroscopy.
Precipitated metallic silver particles in the sodium containing glass were observed by means of transmission electron microcopy. Their mean particle diameter was ~6 nm.
Thermally stimulated interactions between silver and glass, that is, silver dissolution as Ag+ and precipitation as Ag0 were studied in two glass series of molar target composition xAg2O–(19 − x)Na2O–28ZnO–53B2O3 with x = 0, 0.1, 0.5, 5 and (19Na2O–28ZnO–53B2O3)+yAg2O with y = 0.01, 0.05. These act as model for low-melting borate glasses being part of metallization pastes. The occurrence of metallic silver precipitates in melt-quenched glass ingots demonstrated that silver dissolved only in traces (< 0.01 mol%) in the glasses. The dissolved silver was detected by means of Raman spectroscopy and energy-dispersive X-ray spectroscopy. Increasing x in the batch could not lead to a significant increase of the silver ion fraction in the glass as possible in binary silver borate glasses. In situ observation of heated AgNO3 mixed with the base glass frit in a hot stage microscope showed that Ag0 precipitation occurs already at the solid state. At higher temperatures, small droplets of liquid silver were found to move freely within the melt, whereas coalescence caused a stepwise increase of their size.
These results contribute to the understanding of formation of silver precipitates in metallization pastes described in the literature.
In the current study, the 3D nature of the melt pool boundaries (MPBs) in a 316 L austenitic steel additively manufactured by laser-based powder bed fusion (L-PBF) is investigated. The change of the cell growth direction and its relationship to the MPBs is investigated by transmission electron microscopy. A hitherto unreported modulated substructure with a periodicity of 21 nm is further discovered within the cell cores of the cellular substructure, which results from a partial transformation of the austenite, which is induced by a Ga+ focused ion beam. While the cell cores show the modulated substructure, cell boundaries do not. The diffraction pattern of the modulated substructure is exploited to show a thickness ≥200 nm for the MPB. At MPBs, the cell walls are suppressed, leading to continuously connecting cell cores across the MPB. This continuous MPB is described either as overlapping regions of cells of different growing directions when a new melt pool solidifies or as a narrow planar growth preceding the new melt pool.
Additive manufacturing (AM) of metallic alloys has gained momentum in the past decade for industrial applications. The microstructures of AM metallic alloys are complex and hierarchical from the macroscopic to the nanometer scale. When using laser-based powder bed fusion (L-PBF) process, two main microstructural features emerge at the nanoscale: the melt pool boundaries (MPB) and the solidification cellular substructure.
Here, details of the MPB are revealed to clearly show the three-dimensional nature of MPBs with changes of cell growth of direction and their relation to their surrounding cellular substructure, as investigated by transmission electron microscopy (TEM) for L-PBF 316L austenitic stainless steel (cf. Figure 1). A hitherto unknown modulated substructure with a period of 21 nm is further discovered within cells as the result of a partial Ga+-focused ion beam-induced ferritic transformation of the austenite. Cell cores and cell boundaries differ notably regarding the modulated substructure.
Grain boundaries (GBs) are planar lattice defects that govern the properties of many types of polycrystalline materials. Hence, their structures have been investigated in great detail. However, much less is known about their chemical features, owing to the experimental difficulties to probe these features at the atomic length scale inside bulk material specimens. Atom probe tomography (APT) is a tool capable of accomplishing this task, with an ability to quantify chemical characteristics at near-atomic scale. Using APT data sets, we present here a machine-learning-based approach for the automated quantification of chemical features of GBs. We trained a convolutional neural network (CNN) using twenty thousand synthesized images of grain interiors, GBs, or triple junctions. Such a trained CNN automatically detects the locations of GBs from APT data. Those GBs are then subjected to compositional mapping and analysis, including revealing their in-plane chemical decoration patterns. We applied this approach to experimentally obtained APT data sets pertaining to three case studies, namely, Ni-P, Pt-Au, and Al-Zn-Mg-Cu alloys. In the first case, we extracted GB specific segregation features as a function of misorientation and coincidence site lattice character. Secondly, we revealed interfacial excesses and in-plane chemical features that could not have been found by standard compositional analyses. Lastly, we tracked the temporal evolution of chemical decoration from early-stage solute GB segregation in the dilute limit to interfacial phase separation, characterized by the evolution of complex composition patterns. This machine-learning-based approach provides quantitative, unbiased, and automated access to GB chemical analyses, serving as an enabling tool for new discoveries related to interface thermodynamics, kinetics, and the associated chemistry-structure-property relations.
The finite element software ProCrackPlast is developed for the automated simulation of fatigue crack growth in arbitrarily loaded three-dimensional components with large scale plastic deformations, in particular under cyclic thermomechanical (TMF) loading.
ProCrackPlast is developed by extending the software Procrack, created at TU Freiberg for linear-elastic crack growth simulations. The pre-processing, FEM analysis, and the post-processing in ProCrackPlast are done by the commercial software ABAQUS. ProCrackPlast resorts to a crack growth procedure which adaptively updates the crack in finite increments based on the fracture-mechanical parameter, cyclic crack tip opening displacement ΔCTOD . Features of this software along with two application examples of fatigue crack growth in a typical cast steel, Ni-Resist, are presented in this paper to show its capability and performance.
Predicting nonlinear physical aging of glasses from equilibrium relaxation via the material time
(2022)
The noncrystalline glassy state of matter plays a role in virtually all fields of materials science and offers complementary properties to those of the crystalline counterpart. The caveat of the glassy state is that it is out of equilibrium and therefore exhibits physical aging, i.e., material properties change over time. For half a century, the physical aging of glasses has been known to be described well by the material-time concept, although the existence of a material time has never been directly validated. We do this here by successfully predicting the aging of the molecular glass 4-vinyl-1,3-dioxolan-2-one from its linear relaxation behavior. This establishes the defining property of the material time. Via the fluctuation-dissipation theorem, our results imply that physical aging can be predicted from thermal-equilibrium fluctuation data, which is confirmed by computer simulations of a binary liquid mixture.