5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (58) (entfernen)
Sprache
- Englisch (52)
- Deutsch (5)
- Französisch (1)
Referierte Publikation
- nein (58) (entfernen)
Schlagworte
- Corrosion (8)
- Additive manufacturing (6)
- Additive Manufacturing (4)
- CCS (4)
- Steel (4)
- Corrosion Fatigue (3)
- High alloyed steel (3)
- Alkali zinc borate glasses (2)
- Aquifer (2)
- Binder Jetting (2)
- Carbon storage (2)
- Corrosion fatigue (2)
- Crystallization (2)
- Damage (2)
- Glass (2)
- Heat treatment (2)
- High Alloyed Steel (2)
- Layerwise Slurry Deposition (2)
- Lead borate glasses (2)
- Nanoparticles (2)
- Pitting (2)
- Solubility (2)
- Viscosity (2)
- 150 Years (1)
- 2PP (1)
- 3D Druck (1)
- 3D-printing (1)
- ATZ (1)
- Acid-leaching (1)
- Additive Fertigung (1)
- Adolf Martens (1)
- Advanced wastewater treatment (1)
- Agglomerates (1)
- Aging (1)
- Al2O3 (1)
- Alkali-activated materials (1)
- Alpha-tricalcium phosphate (1)
- Alterung (1)
- Alumina toughened zirconia (1)
- Aluminiumlegierung (1)
- Aluminosilicate glasses (1)
- Aluminum alloy (1)
- Amorphous silica (1)
- Annealing (1)
- Anticorrosion (1)
- Bio-ceramic engineering (1)
- Bioactive glass (1)
- Blended learning (1)
- Bond energy (1)
- Brown-rot fungi (1)
- CALPHAD (1)
- Cabon capture and storage (1)
- Carbidic austempered ductile iron (1)
- Carbon capture and storage (1)
- Ccs (1)
- Ceramic (1)
- Ceramic nano particles (1)
- Ceramics (1)
- Ceramics 3D printing (1)
- Chemically complex alloy (1)
- Co2-Storage (1)
- Coating (1)
- Composite (1)
- Coniophora puteana (1)
- Corrosion mechanism (1)
- Coûts de la corrosion (1)
- CrMnFeCoNi (1)
- Crack propagation (1)
- Creep (1)
- Critical energy release rate (1)
- Crystal lattice (1)
- Cubical shape (1)
- Cytocompatibility (1)
- Defect detection (1)
- Density-based Model (1)
- Dentine (1)
- Diffusion (1)
- Diffusivity (1)
- Dispersion process (1)
- Diversity (1)
- Ductile iron (1)
- EBSD (1)
- Electrochemical deposition (1)
- Electron diffraction (1)
- Electron microscopy (1)
- Enamel (1)
- Endurance Limit (1)
- Energiedisersive Röntgenspektroskopie (1)
- Environmentally assisted cracking (1)
- Fatigue (1)
- Fluoride nanoparticles (1)
- Fluorolytic sol−gel (1)
- Fourier transform infrared spectroscopy (1)
- Fracture mechanics (1)
- Fracture surface energy (1)
- Fragility (1)
- Gas flow assisted powder deposition (1)
- General Chemistry (1)
- Geometrical factors (1)
- Glass fiber reinforced polymer (1)
- Glass liner (1)
- Glass powder (1)
- Grain boundary engineering (1)
- High Cycle Fatigue (1)
- High entropy alloy (1)
- Hochleistungskeramik (1)
- Hot isostatic pressing (HIP) (1)
- Hybrid Manufacturing (1)
- Hydrogen permeation (1)
- Hydrogen storage tank (1)
- IR spectroscopy (1)
- Inconel 625 (1)
- Indentation hardness (1)
- Infrarotspektroskopie (1)
- Interface (1)
- Interfacial shear strength (1)
- Inverted classroom (1)
- Ionic porosity (1)
- Iron oxide (1)
- Kikuchi diffraction (1)
- Laser ablation in liquid (1)
- Laser-induced slip casting (1)
- Lattice misfit (1)
- Lattices (1)
- Lebensdauervorhersage (1)
- Lecture films (1)
- Lifetime prediction (1)
- Lithography-based technologies (1)
- Martensitic steel (1)
- Mass transport (1)
- Materials Chemistry (1)
- Mechanical Engineering (1)
- Mechanics of Materials (1)
- Metals and Alloys (1)
- Microsegregation (1)
- Microstructure (1)
- Microstructure Design (1)
- Mikrostruktur (1)
- Molecular Dynamics (1)
- Molecular dynamics (1)
- Nano CRM (1)
- Nano-ceramic-additive-manufacturing photoresin (1)
- Nano-powder (1)
- NanoCAM (1)
- Networking (1)
- Niobium alloying (1)
- Nucleation tendency (1)
- Nydrogen melting (1)
- Particle morphology (1)
- Pattern matching (1)
- Permeability (1)
- Phase-field (1)
- Physical properties (1)
- Phytolith (1)
- Polyaniline (1)
- Polymer matrix composites (1)
- Polymer-ceramic mixtures (1)
- Porosity (1)
- Portfolio (1)
- Powder bed density (1)
- Powder-based processes (1)
- Powdered activated carbon (1)
- Process (1)
- Protection (1)
- Pull-out composite materials (1)
- Pulveraktivkohle (1)
- Quality assurance (1)
- Raman spectroscopy (1)
- Reference nanoparticles (1)
- Resistance stress (1)
- Rhodonia placenta (1)
- Roughness (1)
- SAXS (1)
- SEM wood characterization (1)
- Scaffold (1)
- Schlickerdeposition (1)
- SchwarzP cells (1)
- Schädigung (1)
- Segregation Engineering (1)
- Sewage treatment plant (1)
- Shear thinning (1)
- Silikatkeramik (1)
- Single crystal superalloys (1)
- Sinter retardation (1)
- Sintering (1)
- Size (1)
- Sliding simulation (1)
- Slip-rolling (1)
- Slurry (1)
- Soda lime silicate glass (1)
- Space (1)
- Steels (1)
- Stratégies deprévention (1)
- Surface (1)
- Surface roughness (1)
- Surface-induced Melting (1)
- Technical Ceramics (1)
- Temperature (1)
- Thermo-mechanics (1)
- Thermoanalysis (1)
- Thermogravimetrie (1)
- Thermogravimetry (1)
- Thin tribofilm (1)
- Titanium oxide (1)
- Tooth wear (1)
- Transmission electron microscopy (1)
- Transmissionselektronenmikroskopie (1)
- Two-photon adsorption (1)
- Two-photon polymerization (1)
- Vacancies (1)
- Viscous sintering (1)
- Water in glass (1)
- Wood protection (1)
- X-ray diffraction (1)
- Young’s Modulus (1)
- bioactive (1)
- biomaterials (1)
- bone (1)
- corrosion (1)
- high entropy alloys (1)
- hydrogen storage (1)
- oxidation (1)
- scanning electron microscopy (1)
- sulfidation (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (58)
- 5.1 Mikrostruktur Design und Degradation (20)
- 5.4 Multimateriale Fertigungsprozesse (16)
- 5.6 Glas (10)
- 6 Materialchemie (9)
- 5.2 Metallische Hochtemperaturwerkstoffe (5)
- 5.3 Polymere Verbundwerkstoffe (5)
- 7 Bauwerkssicherheit (5)
- 5.5 Materialmodellierung (4)
- 6.3 Strukturanalytik (4)
During capture and storage technology (CCS) as well as in geothermal energy production Steels need to withstand the corrosive environment such as: heat, pressure, salinity of the aquifer and CO2-partial pressure. 1.4542 shows unusual corrosion phenomena, but is still sufficiently resistant in corrosive environments. To better understand its behaviour differently heat treated coupons of 1.4542 and for comparison X20Cr13 and X46Cr13 were kept in the artificial brine of the Northern German Basin at T=60 °C. Ambient pressure as well as p=100 bar for 700 h - 8000 h in water saturated supercritical CO2 and CO2-saturated synthetic aquifer Environment was applied. Fatigue tests were performed via push-pull tests with a series of 30 specimens from 150 MPa to 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). FeCO3 and FeOOH are corrosion products also after dynamic corrosion tests. Martensitic microstructure offers good corrosion resistance in geothermal environment. The S-N-curve showing no typical fatigue strength and very steep slopes of possible fatigue strength for finite life. Possible influencing artefacts, such as Al-inclusions could not be correlated to early rupture despite specimens containing inclusions at the fracture surface and cross section reached lower number of cycles. Applied potential proofed to enhance fatigue life tremendously.
Corrosion fatigue specimen with different surfaces (technical surfaces after machining and polished surfaces) of high alloyed martensitic stainless steel X46Cr13 (1.4043) and duplex stai nless steel X2CrNiMoN22 3 2 (1.4462) were compared at load amplitudes from 175 MPa to 325 MPa in the geothermal brine of the N orthern German Basin at 98 °C. Surface corrosion layers and pits reveal carbonate corrosion products on the surface such as FeCO 3 and FeOOH as the main precipitation phases with no dependence on the original surface roughness . At high stress amplitudes above 275 MPa technical surfaces (P50% at σa 300 MPa=5 × 10 5 ) resulted in more cycles to failure than polished (P50% at σa 300 MPa=1.5 × 10 5 ). The greater slope coefficient for technical surfaces k = 19.006 compared to polished surfaces k =8.78 demonstrate s earlier failure at given stress amplitude σa .
Spherical mesoporous bioactive glasses in the silicon dioxide (SiO2)-phosphorus pentoxide (P2O5)–calcium oxide (CaO) system with a high specific surface area of up to 300m2/g and a medium pore radius of 4 nm were synthesized by using a simple one-pot surfactant-assisted sol–gel synthesis method followed by calcination at 500–700°C. The authors were able to control the particle properties by varying synthesis parameters to achieve microscale powders with spherical morphology and a particle size of around 5–10 mm by employing one structure-directing agent. Due to a high Calcium oxide content of 33·6mol% and a phosphorus pentoxide content of 4·0mol%, the powder showed very good bioactivity up to 7 d of immersion in simulated Body fluid. The resulting microspheres are promising materials for a variety of life science applications, as further processing – for example, granulation – is unnecessary. Microspheres can be applied as materials for powder-based additive manufacturing or in stable suspensions for drug release, in bone cements or fillers.
Our research focused on Inconel 625 weld overlays on 16Mo3 steel boiler pipes. The Investigation focused on the characterization of changes in the microstructure and chemical composition after annealing. The annealing was performed for ten hours at temperatures from 600 to 1000°C. Changes in the microstructure were observed with a scanning and transmission electron microscope (SEM and TEM). The investigation was supplemented by hardness measurements.
Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles.
Electrochemical deposition of polyaniline on carbon steel for corrosion study in geothermal solution
(2019)
Polyaniline has been widely developed for many applications, e.g. sensor, supercapacitor components, electrochromic devices, and anticorrosion pigments. Although the addition of polyaniline pigment in organic coatings has been an alternative for corrosion protection in industrial applications, the protection mechanism is still not fully understood. Herein in this study, as a part of the development of polyaniline/silicon dioxide coating for geothermal application, polyaniline has been deposited electrochemically on carbon steel surface in oxalic acid medium and tested in geothermal solution to understand the contribution of polyaniline to the corrosion protection of a polyaniline-based composite in the geothermal system. To observe the surface/interface reaction between the electrolyte and electrode surface during the electrochemical polymerization, electrochemical impedance spectroscopy (EIS) was applied after each cycle. For corrosion study in the geothermal application, an artificial geothermal solution was used with the composition of 1,500 mg/l Cl⁻, 20 mg/l SO₄²⁻, 15 mg/l HCO₃⁻, 200 mg/l Ca²⁺, 250 mg/l K⁺, and 600 mg/l Na⁺, and pH 4 to simulate a geothermal brine found in Sibayak, Indonesia. An electrochemical measurement was performed by monitoring the open circuit potential over seven days, with the interruption by EIS every 22 hours. The experiments were performed at room temperature and 150 °C (1 MPa) in an oxygen-free environment. Impedance spectra showed a reduction of the total impedance value of approximately 10 times for specimens measured at 150 °C compared to the specimens measured at room temperature, suggesting a less stable layer at high temperature.
Carbon Capture and Storage (CCS) is well acknowledged to mitigate climate change. Therefore, pipe Steels suitable for CCS technology require resistance against the corrosive environment of a potential CCS-site, e.g. heat, pressure, salinity of the aquifer, CO2-partial pressure. Samples of different mild and high alloyed stainless injection-pipe Steels partially heat treated: 42CrMo4, X20Cr13, X46Cr13, X35CrMo4 as well as X5CrNiCuNb16-4 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CO2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. Main corrosion products analysed on pits are FeCO3 and FeOOH. The carbon content does not show significant influence on the pitting behaviour. Generally, higher chromium Content results in better corrosion resistance. Although X35CrMo17-1 and X5CrNiCuNb16-4 show low surface corrosion rates, their resistance against local corrosion in CCS environment is not significantly better compared to the much less costly Steels X20Cr13 and X46Cr13.
With the introduction of a mass transport mechanism the entire problem is subjected to a time frame that dictates the time-dependent action of soluted species on mechanical properties. A numerical framework within the phase-field approach is presented with an embrittlement-based coupling mechanism. The underlying functionals are expressed in terms of the displacement, mass concentration and crack phase-field. Within the phase-field approach the modelling of sharp crack discontinuities is replaced by a diffusive crack model facilitating crack initiation and complex crack topologies without the requirement of a predefined crack path. The isotropic hardening of the elasto-plastic deformation model and the local fracture criterion are affected by the species concentration. This allows for embrittlement and leads to an accelerated crack propagation. An extended mass transport equation for hydrogen embrittlement, accounting for mechanical stresses and deformations, is implemented. For stabilisation purposes a staggered scheme is applied to solve the system of partial differential equations by a multi-field finite-element method. A thermodynamically consistent coupling relation that accommodates the required mechanisms is presented.
Effects of various geometrical and physical factors, as well as the method of data reduction (analysis of
experimental forceedisplacement curves) on the values of local interfacial strength parameters (local IFSS, td, and critical energy release rate, Gic) determined by means of a single fiber pull-out test are discussed. Experimental results of our pull-out tests on several fiberepolymer matrix systems showed that td and Gic weakly depended on geometrical factors. However, the pull-out test appeared to be sensitive to the conditions of specimen formation and testing, such as changing the nature of the contacting surfaces (fiber sizing) and the fiber pull-out rate. Of several methods of td and Gic Determination from a forceedisplacement curve, the most reliable and reproducible one is the approach based on the values of the maximum force recorded in a pull-out test and the interfacial frictional force immediately after fiber debonding.
Materials subjected to high-temperature service conditions will change their microstructure with time. Associated with this aging process is a change of mechanical properties as well as a change of damage mechanisms. Within the scope of the FVV project Aging and Lifetime, Fraunhofer IWM in Freiburg and BAM in Berlin (both Germany) experimentally characterized the widespread high-temperature aluminum alloy EN AW-2618A in different overaging states. Based on the experimental findings, models for numerical lifetime assessment with the finite-element method were implemented.
Werkstoffe im Hochtemperatureinsatz verändern mit der Zeit ihre Mikrostruktur. Mit diesem Alterungsprozess einher geht eine Veränderung der mechanischen Eigenschaften ebenso wie eine Veränderung des Schädigungsverhaltens. Im Rahmen des FVV Vorhabens „Alterung und Lebensdauer“ haben das Fraunhofer IWM in Freiburg und die BAM in Berlin die weit verbreitete warmfeste Aluminiumlegierung EN AW-2618A in verschiedenen Alterungszuständen experimentell charakterisiert und darauf aufbauend Modelle für die Lebensdauerbewertung mit der Finite-Elemente- Methode implementiert.
A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD(two instruments operated in different geometries) and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation.
Tooth wear induced by abrasive particles is a key process affecting dental function and life expectancy in mammals. Abrasive particles may be plant endogenous opal phytoliths, exogene wind-blown quartz dust or rain borne mineral particles ingested by mammals. Nano-indentation hardness of abrasive particles and dental tissues is a significant yet not fully established parameter of this tribological system. We provide consistent nano-indentation hardness data for some of the major antagonists in the dental tribosystem (tooth enamel, tooth dentine and opaline phytoliths from silica controlled cultivation). All indentation data were gathered from native tissues under stable and controlled conditions and thus maximize comparability to natural systems. Here we show that native (hydrated) wild boar enamel exceeds any hardness measures known for dry herbivore tooth enamel by at least 3 GPa. The native tooth enamel is not necessarily softer then environmental quartz grit, although there is little overlap. The native hardness of the tooth enamel exceeds that of any silica phytolith hardness recently published. Further, we find that native reed phytoliths equal native suine dentine in hardness, but does not exceed native suine enamel. We also find that native suine enamel is significantly harder than dry enamel and dry phytoliths are harder than native phytoliths. Our data challenge the claim that the culprit of tooth wear may be the food we chew, but suggest instead that wear may relates more to exogenous than endogenous abrasives.
Advanced wastewater treatment with powdered activated carbon (PAC) leads to a spread of PAC into different purification stages of wastewater treatment plants (WWTP) due to recirculation and filter back-wash. Currently, no methods for quantification of PAC in activated sludge are available. In this study, PAC containing activated sludge from four WWTP were examined by two-step thermogravimetric analysis (TGA) with heating up to 600°C in N2 and subsequently in synthetic air. Direct quantification of PAC according to temperature specific weight losses was possible for one WWTP. Quantification by combining specific mass losses was found to be an alternative direct method, with a detection limit of 1.2% PAC in dry sample mass.
Additionally, evolved gas analysis (EGA) by infrared-spectroscopy (FTIR) during TGA revealed interaction mechanisms between PAC and activated sludge. Aliphatic compounds from activated sludge were identified as major substances influenced by PAC. In derivative thermogravimetry (DTG), a typical double peak at approximately 300°C was found to be related to carbonylic species with increased evolution of acetic acid in aged activated sludge. TGA and EGA are promising tools to understand, control and optimise the application of PAC in advanced wastewater treatment.
The sliding behavior of an amorphous silica sample between two rigid surfaces is in the focus of the present paper. Molecular Dynamics using a classical Tersoff’s potential and a recently developed ReaxFF potential was applied for simulating sliding within a thin film corresponding to a tribofilm formed from silica nanoparticles. The simulations were performed at different temperatures corresponding to moderate and severe tribological stressing conditions. Simulations with both potentials revealed the need of considering different temperatures in order to obtain a sound interpretation of experimental findings. The results show the striking differences between the two potentials not only in terms of magnitude of the resistance stress (about one order of magnitude) but also in terms of friction mechanisms. The expected smooth sliding regime under high temperature conditions was predicted by both simulations, although with Tersoff’s potential smooth sliding was obtained only at the highest temperature. On the other hand, at room temperature Tersoff-style calculations demonstrate stick-slip behavior, which corresponds qualitatively with our experimental findings. Nevertheless, comparison with a macroscopic coefficient of friction is not possible because simulated resistance stresses do not depend on the applied normal pressure.
Wood treated with nano metal fluorides is found to resist fungal decay. Sol−gel synthesis was used to synthesize MgF2 and CaF2 nanoparticles. Electron microscopy images confirmed the localization of MgF2 and CaF2 nanoparticles in wood. Efficacy of nano metal fluoride-treated wood was tested against brown-rot fungi Coniophora puteana and Rhodonia placenta. Untreated wood specimens had higher
mass losses (∼30%) compared to treated specimens, which had average mass loss of 2% against C. puteana and 14% against R. placenta, respectively. Nano metal fluorides provide a viable alternative to current wood preservatives.
An improved diffusion model is proposed for pore annihilation during HIP of single-crystal nickel-base superalloys. The model assumes the pore dissolution by emission of vacancies and their sink to the low angle boundaries. Calculation, considering distribution of the pore sizes, predicts the kinetics of pore annihilation similar to the experimental one.