5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2019 (22) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (22) (entfernen)
Sprache
- Englisch (22)
Schlagworte
- Corrosion (7)
- Carbon steel (3)
- Condensate (2)
- Corrosion Fatigue (2)
- High Alloyed Steel (2)
- Impurities (2)
- Oxidation (2)
- Pitting (2)
- 3D printing (1)
- AISI 304L (1)
- Additive Manufacturing (1)
- Additive manufacturing (1)
- Aquifer (1)
- Biogeochemical cycling (1)
- Biomineralisation (1)
- CCS (1)
- CCUS (1)
- CO2 (1)
- Carbon capture (1)
- Carbon capture, utilization and storage technology (1)
- Carbon storage (1)
- Characterisation (1)
- Contact angle (1)
- Contact fatigue (1)
- Corrosion pits (1)
- Crack arrest (1)
- Defects (1)
- Deuterium (1)
- EBSD (1)
- Early oxidation (1)
- Early sulfidation (1)
- Electrochemical characterisation (1)
- Electrochemical deposition (1)
- Electrochemical impedance spectroscopy (1)
- Electron energy (1)
- Electron microscopy (1)
- Endurance Limit (1)
- Energy distribution (1)
- Environment (1)
- Fabrication (1)
- Fatigue (1)
- Fatigue crack propagation stages (1)
- Ferritic steels (1)
- Friction Stir Welding (1)
- Geothermal (1)
- Gold (1)
- Heat treatment (1)
- High temperature corrosion (1)
- High-temperature oxidation (1)
- Hydrogen (1)
- Impact damage (1)
- In-situ Process Monitoring (1)
- Inclusion cluster (1)
- Inclusion size (1)
- Inconel 625 (1)
- Infrared nano AFM (1)
- Intermodulation AFM (1)
- Internal oxidation (1)
- Interphase (1)
- Iron meteorite (1)
- Kikuchi pattern (1)
- Laser beam melting (1)
- Magmatic and hydrothermal processes (1)
- Martensite (1)
- Micro-shrinkages (1)
- Mis-match (1)
- Multiple cracks (1)
- Nanocomposites (1)
- Nitride (1)
- Non-destructive Materials (1)
- Non-metallic inclusions (1)
- Orientation relationship (1)
- Oxidation protection (1)
- Parabolic flight (1)
- Pitting corrosion (1)
- Plastic deformation (1)
- Platinum-group-metals (1)
- Polyaniline (1)
- Pores (1)
- Process development (1)
- Roughness (1)
- STEM (1)
- Safety (1)
- Scratches (1)
- Simulation (1)
- Sol-gel coating (1)
- Standardisation (1)
- Statistics (1)
- Steel (1)
- Sulfidation (1)
- Surface (1)
- ToF-SIMS (1)
- Tungsten-Rhenium (1)
- Utilization, and storage (CCUS) technology (1)
- Wetting (1)
- X-ray absorption spectroscopy (1)
- µ-gravity (1)
Organisationseinheit der BAM
- 5.1 Mikrostruktur Design und Degradation (22) (entfernen)
To study the effects of condensed acid liquid, hereafter referred to as condensate, on the CO2 transport pipeline steels, gas mixtures containing a varying concentration of H2O, O2, NO2, and SO2, were proposed and resulted in the condensate containing H2SO4 and HNO3 with the pH ranging from 0.5 to 2.5. By exposing the pipeline steel to the synthetic condensate with different concentration of acidic components, the corrosion kinetic is significantly changed. Reaction kinetic was studied using electrochemical methods coupled with water analysis and compared with surface analysis (scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffractometry (XRD)) of corroded coupons. The results showed that, although the condensation of NO2 in the form of HNO3 causes faster general corrosion rate, it is the condensation of SO2 in the form of H2SO4 or the combination of SO2 and NO2 that may cause much more severe problems in the form of localized and pitting corrosions. The resulting corrosion forms were depended on the chemical nature of acids and their concentration at the same investigated pH. The effects of changing CO2 flow rate and renewing condensate on pitting corrosion were further studied.
Real-time observation of high- temperature gas corrosion in dry and wet SO2-containing atmosphere
(2019)
Sulfur and water have a fundamental impact on the corrosion rate and potential failure of materials. It is therefore necessary to understand the mechanisms, rates, and potential means of transport, as well as the reactions of these elements with an alloy. This paper investigates the effect of water vapor in the initial stages of SO2 corrosion of an Fe-9Cr-0.5Mn model alloy at 650°C in situ under laboratory conditions using energy-dispersive x-ray diffraction analysis. Two separate experiments were run, one with a 99.5% Ar + 0.5% SO2 atmosphere and one with a 69.5% Ar + 0.5% SO2 + 30% H2O atmosphere. With a wet atmosphere, the alloy formed a scale with decreasing oxygen content towards the scale–alloy interface. Sulfides were identified above and below a (Fe, Cr)3O4 layer in the inner corrosion zone. In contrast to this, the overall scale growth was slower in a dry SO2 atmosphere.