5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2019 (16) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (8)
- Vortrag (6)
- Sonstiges (1)
- Posterpräsentation (1)
Schlagworte
- Additive Manufacturing (4)
- Low Cycle Fatigue (4)
- Ti-6Al-4V (4)
- Additive Fertigung (2)
- Additive manufacturing (2)
- CT (2)
- Computed Tomography (2)
- Ductile iron (2)
- Fatigue (2)
- High Temperature Testing (2)
- LCF (2)
- Microstructure (2)
- Mikrostruktur (2)
- Niobium alloying (2)
- Tensile Properties (2)
- Ti64 (2)
- TiAl5V4 (2)
- Titan (2)
- Titanium (2)
- Zugeigenschaften (2)
- 3D printing (1)
- AISI 304L (1)
- Abrasion (1)
- Carbidic austempered ductile iron (1)
- Characterisation (1)
- Contact fatigue (1)
- Corrosion pits (1)
- Crack arrest (1)
- Crack propagation (1)
- Crystal Plasticity Modelling (1)
- DED-L (1)
- Defects (1)
- Deuterium (1)
- Druckgasspeicher (1)
- Energiespeicherung (1)
- Environment (1)
- Erneuerbare Energien (1)
- Explosionsschutz (1)
- Fatigue crack propagation stages (1)
- Gasdetektion (1)
- Gassensorik (1)
- Glasspeicher (1)
- Hydrogen (1)
- Impact damage (1)
- In-situ Process Monitoring (1)
- Inclusion cluster (1)
- Inclusion size (1)
- LMD (1)
- Laser beam melting (1)
- Martensite (1)
- Micro-shrinkages (1)
- Microstructure characterisation (1)
- Mini-UAV (1)
- Mis-match (1)
- Multiple cracks (1)
- NDT (1)
- Non-destructive Materials (1)
- Non-destructive testing (1)
- Non-metallic inclusions (1)
- Parabolic flight (1)
- Pores (1)
- Power-to-Gas (1)
- Process development (1)
- Process monitoring (1)
- Residual stress (1)
- Risikoanalyse (1)
- Safety (1)
- Scratches (1)
- Slip-rolling (1)
- Standardisation (1)
- Statistics (1)
- Tensile testing (1)
- ToF-SIMS (1)
- Tribologie (1)
- Wasserstoff (1)
- Wasserstofferzeugung (1)
- Windenergie (1)
- arbidic austempered ductile iron (1)
- µ-gravity (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (16) (entfernen)
Eingeladener Vortrag
- nein (6)
Die BAM ist nahezu über die gesamte Wertschöpfungskette hinweg wissenschaftlich tätig. Von der sicheren und effizienten Wasserstofferzeugung (POWER-to-GAS), über die (Zwischen-)Speicherung von Wasserstoff in Druckgasspeichern bis hin zum Transport bspw. mittels Trailerfahrzeug zum Endverbraucher.
Komplettiert werden die Aktivitäten der BAM durch die sicherheitstechnische Beurteilung von wasserstoffhaltigen Gasgemischen, die Verträglichkeitsbewertung von Werkstoffen bis hin zur Detektion von Wasserstoffkonzentrationen über geeignete Sensorik, auch mittels ferngesteuerter Messdrohnen (sog. UAV-Drohnen).
Zudem untersucht die BAM proaktiv Schadensrisiken und Unfallszenarien für die Sicherheitsbetrachtung, um mögliche Schwachstellen aufzeigen und potenzielle Gefährdungen erkennen zu können.
The damaging impact of hydrogen on the austenitic stainless steel AISI 304 L was analysed.
To this aim, samples were charged electrochemically with the hydrogen isotope deuterium (2H, D) and examined with time-of-flight secondary ion mass spectrometry (ToF-SIMS) and electron backscatter diffraction (EBSD). The fusion of the obtained chemical and structural information revealed local enrichment of deuterium in austenite, transformation into martensite, crack formation and severe roughening of the specimen surface. The results indicated that martensite was not only formed during charging but also during Desorption and ToF-SIMS examinations. Furthermore, cross-sections of deuterium-charged samples revealed that in preferred deformation bands a g/ε/a 0 evolution is taking place.
By means of microscopic analyses and carrier gas hot extraction (CGHE), it was found that the use of NaAsO2 as recombination poison decreased the uptake of hydrogen significantly and resulted in severe precipitation on the specimen surfaces. This is in contrast to the popular presumption that NaAsO2 enhances the uptake of hydrogen (and
deuterium) during electrochemical charging by hampering its recombination from Atoms to molecules.
Defects as a root cause of fatigue failure of metallic components. II: Non-metallic inclusions
(2019)
This second part of the review on defects as root cause of fatigue failure comprises the origin, the nature and the effects of non-metallic inclusions. Topics addressed are the different kinds of inclusions formed during the manufacturing process, various types of mis-match causing local stresses and, as a consequence, fatigue crack initiation, and effects of characteristics such as size, morphology, localization, spatial distribution and orientation of the defects on the fatigue behavior. Methods for inclusion counting and sizing are discussed along with statistical aspects necessary to be considered when evaluating structural components.
This third part of the review on defects as root cause of fatigue failure addresses cavities (pores, micro-shrinkages, unmelted regions), defective microstructures and microcracks as material defects and defects due to local damage during manufacturing, service and maintenance such as dents, scratches and localized corrosion. In addition, damage due to contact fatigue and the effect of surface roughness are discussed in the context of fatigue failure. Also addressed is the competition between different kinds of defects in controlling the initiation and early growth of fatigue cracks.
According to the definition of the ASM handbook [1,3], a defect is "an imperfection. that can be shown to cause failure by a quantitative analysis and that would not have occurred in the absence of the imperfection". The topic of the present three-part review is a discussion of defects which can cause failure in cyclically loaded structures. The features discussed comprise material defects such as non-metallic inclusions, pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches which have their origin in manufacturing, and defects such as surface damage due to scratches, impact events or contact fatigue as well as corrosion pits which arise in service. In this first part, the discussion is prefaced by an introduction to basic aspects which are essential for a deeper understanding of the characteristics and mechanisms how the defects influence fatigue crack initiation and propagation. These include the life cycle of a fatigue crack from initiation up to fracture, crack arrest, multiple crack initiation and coalescence, and the material and geometrical properties affecting these.