Common air-coupled transducers for non-destructive testing consist of a piezocomposite material and several matching layers. Better acoustical matching to air is achieved by transducers based on charged cellular polypropylene (PP). This material has about hundred times lower acoustic impedance than any piezocomposite, having about the same piezoelectric coefficient. The piezoelectric properties of cellular PP are caused by the polarization of air cells. Alternatively, a ferroelectret receiver can be understood as a capacitive microphone with internal polarization creating permanent internal voltage. The sensitivity of the receiver can be increased by applying additional bias voltage. We present an ultrasonic receiver based on cellular PP including a high-voltage module providing bias voltage up to 2 kV. The application of bias voltage increased the signal by 12 to 15 dB with only 1 dB increase of the noise.
This receiver was combined with a cellular PP transmitter in through transmission to inspect several test specimens consisting of glass-fiber-reinforced polymer face sheets and a porous closed-cell PVC core. These test specimens were inspected before and after load. Fatigue cracks in the porous PVC core and some fatigue damage in the face sheets were detected. These test specimens were originally developed to emulate a rotor blade segment of a wind power plant. Similar composite materials are used in lightweight aircrafts for the general aviation. The other inspected test specimen was a composite consisted of glass-fiber-reinforced polymer face sheets and a wooden core. The structure of the wooden core could be detected only with cellular PP transducers, while commercial air-coupled transducers lacked the necessary sensitivity. Measured on a 4-mm thick carbon-fiber-reinforced polymer plate, cellular PP transducers with additional bias voltage achieved a 32 dB higher signal-to-noise ratio than commercial air-coupled transducers.
Glass-fibre-reinforced plastics (GFRP) are commonly used for the construction of pressure vessels and tanks for example in automotive and aerospace industries. Especially for pressure vessels used for the storage of natural gas or hydrogen with operation pressures up to 700 bar, an early material fatigue detection is of great interest. Measuring the distributed strain profile of GFRP structures helps to understand and detect material fatigue. In this article, we demonstrate the great potential of swept wavelength interferometry (SWI) based distributed strain sensing for the monitoring of pressure vessels made from GFRP. A resin transfer molding (RTM) process was used to manufacture GFRP-tube specimens. Commercial optical fibres with polyimid coating were glued to the surface externally in circumferential and axial direction. A cyclic load of up to 150 bar was applied to the samples using a servo-hydraulic test bench. Comparing the loaded and unloaded test conditions, we determined up to 2 % elongation in circumferential direction. We demonstrate reliable distributed strain measurements with sub-centimetre spatial resolution. By monitoring these high-resolution strain profiles, we were able to detect local material degradation that manifested itself as localized strain changes. Crucially, the material Degradation could be detected already after 75 % of dat the fatigue life before a crack appeared that led to leakage.
Cyclic fatigue behavior of glass fiber reinforced epoxy resin at ambient and elevated temperatures
(2018)
The fatigue behavior of ±45° glass fiber reinforced epoxy resin under cyclic mechanical and constant thermal loading is investigated in this study. Tests at three different temperature levels in the range 296 K to 343 K have been performed in order to create S-N curves for each temperature level. The specimen damage is measured in-situ using optical grayscale analysis. The characteristic damage state (CDS) is evaluated for each specimen. It is shown that the point of CDS is suitable as a failure criterion to compare the resulting S-N curves. With micromechanical formulations, the temperature-dependent matrix effort is calculated for each stress-temperature level. In terms of matrix effort, the longest fatigue life is reached at high temperatures, while, in terms of stress, the lowest fatigue life is reached at the highest temperatures.
A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated.
Um den sicheren Betrieb von Windkraftanlagen zu gewährleisten, werden Rotorblätter nach der Fertigung und nach Reparatur mit verschiedenen zerstörungsfreien Verfahren auf Schaden untersucht. Bei der Fertigung von Blattschalen, die in einer Sandwich-Schalenbauweise gefertigt werden, entstehen Imperfektionen, die unter Belastung zu großen Rissen führen können. Zur Prüfung von Blattschalen wird unter anderem Ultraschallprüfung in Kontakttechnik eingesetzt. Um den Wartungsaufwand von Ultraschallanlagen zu reduzieren und um manche Kompositstrukturen vor Koppelmittel zu schützen, wird die Anwendung von Luftultraschall erforscht. Insbesondere große Fortschritte gibt es im Bereich der Entwicklung neuer Wandler.
In diesem Beitrag berichten wir über die Luftultraschallprüfung von Schalen für Rotorblätter. Es wurden typische Sandwichschalenstrukturen hergestellt und mit einem eigenentwickelten Schalenprüfstand unter simulierter Betriebsbeanspruchung belastet. Die in den Schalenprüfkörpern entstandenen Schäden wurden außerhalb des Prüfstandes mit Luftultraschall in Durchschallung untersucht. Es wurden fokussierende Wandler auf Basis von Ferroelektreten entwickelt und für diese Prüfungen eingesetzt. Mit zusätzlicher elektrischer Vorspannung konnte die Empfindlichkeit der Empfänger deutlich erhöht werden. Die nach dem Lastwechsel entstandenen Schäden in den Rotorblattschalen waren eindeutig zu detektieren.
Sandwich-Schalenstrukturen in situ charakterisiert mit Thermographie und Felddehnungsmessungen
(2018)
An der BAM wurde ein Schalenprüfstand entwickelt, mit dem typische Sandwichschalenstrukturen unter simulierter Betriebsbeanspruchung belastet werden können. Im mechanischen Ermüdungsversuch wurden in situ die Entstehung von Schäden in Schalenprüfkörpern mit Test-Imperfektionen mittels der passiven Thermographie und Felddehnungsmessungen verfolgt. Damit konnten der Zeitpunkt, der Schadensursprung und der Schadensfortschritt zerstörungsfrei bestimmt werden. Zudem wurden vergleichend Schalenprüfkörper mit Luftultraschall und der Röntgen-Laminographie untersucht. Im Rahmen eines BMWi-Forschungsvorhabens wurden die Schädigungsmechanismen evaluiert und Empfehlungen für die Praxis der Fertigung von Rotorblättern abgeleitet. In diesem Beitrag wird sich auf die Darstellung der ZfP-Verfahren und der ZfP-Ergebnisse konzentriert.
3D structural investigations are described by X-ray laminography studies of sandwich shell segments, made of a PVC foam core, covered by non-crimp fabric glass fibre composite lay-ups processed by vacuum assisted resin infusion of epoxy. The specific scope of this study is to image transversal flaws within the foam core (joints) and of single ply overlaps. Test flaws were purposely implemented in order to simulate typical failure under cyclic load. In a dedicated test rig for shell structures, the flaw evolution/propagation is monitored by thermography and optical 3D inspection of deformation. Due to the unfavourable preconditions for classical computed tomography as of large aspect ratio, the samples were investigated by coplanar translational laminography. Its limited range of observation angles of ± 45°, results in anisotropic artefacts about the normal to the sample surface, but the typical flaws are well visualized in the as-prepared state, in a state of early damage, and in the repaired state.