5 Werkstofftechnik
Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (18)
- Forschungsdatensatz (17)
- Vortrag (16)
- Zeitschriftenartikel (5)
- Buchkapitel (5)
- Forschungsbericht (4)
- Monografie (1)
- Posterpräsentation (1)
Referierte Publikation
- nein (67) (entfernen)
Schlagworte
- Ontology (10)
- Aluminium (6)
- Aluminium alloy (6)
- Creep (6)
- Aging (5)
- FAIR data (5)
- Additive manufacturing (4)
- Degradation (4)
- EN AW-2618A (4)
- LCF (4)
- Mechanical testing (4)
- Ni-Resist (4)
- Shear modulus (4)
- Young's modulus (4)
- Alloy 2618A (3)
- Data mapping (3)
- Digitalisierung (3)
- Elastic modulus (3)
- Knowledge graph (3)
- Kriechen (3)
- Lebensdauer (3)
- S-phase (3)
- Schädigung (3)
- TMF (3)
- Transmission electron microscopy (3)
- AISI 316L (2)
- Alterung (2)
- Brinell hardness (2)
- Coarsening (2)
- Copper alloys (2)
- Dark-field transmission electron microscopy (DFTEM) (2)
- Data management (2)
- Dataset (2)
- Digital representation (2)
- Fatigue (2)
- Fatigue crack growth (2)
- Low Cycle Fatigue (2)
- Microstructure (2)
- P92 (2)
- Reference data (2)
- Standardisierung (2)
- Stress relaxation (2)
- TEM (2)
- Tempered Martensite Ferritic Steels (2)
- Tensile test (2)
- Tensile testing (2)
- Vickers hardness (2)
- AM (1)
- Abgasturbolader Heißteile (1)
- Age hardening (1)
- Al-Cu-Li alloys (1)
- Al2CuMg (1)
- Alloy 2818A (1)
- Aluminiumlegierung (1)
- Aluminum (1)
- Aluminum alloy (1)
- Aluminum alloys (1)
- Anisotropy (1)
- Anwendungen (1)
- Aufbau von Festkörpern (1)
- Austenitic cast iron (1)
- Automatable digital approach (1)
- Beanspruchung (1)
- Bi-material structure (1)
- Bruch (1)
- CALPHAD (1)
- Casting (1)
- Centrifugal compressor wheel (1)
- Charpy test (1)
- Chemische Analyse (1)
- Crack (1)
- Creep data (1)
- Creep, Creep Rupture, and Stress Rupture (1)
- Creep-Fatigue (1)
- Creep-fatigue (1)
- Crystal Defects (1)
- Cyclic loading (1)
- Damage (1)
- Damage behavior (1)
- Data Fusion (1)
- Data Mapping (1)
- Data format (1)
- Data linking (1)
- Data pipeline concept (1)
- Datenfusion (1)
- Defects phase diagram (1)
- Defects thermodynamics (1)
- Density-based model (1)
- Digital material representation (1)
- Digital workflow (1)
- Digitalization (1)
- Digitization (1)
- Dual-material nickel-based alloys (1)
- Dwell-Fatigue (1)
- EBSD (1)
- EN AW 2618A (1)
- EN AW 2618A a (1)
- Eigenschaften (1)
- Ermüdung (1)
- FAIR Data (1)
- FAIR data management (1)
- FAIR data. (1)
- Fatigue crack propagation (1)
- Fatigue testing (1)
- Fe-Al alloys (1)
- Ferritic-martensitic steels (1)
- Fractography (1)
- Gefügeuntersuchung (1)
- Gefügte Nickelbasislegierungen (1)
- General Chemistry (1)
- Glas (1)
- Gleichgewicht (1)
- HCF (1)
- Hardness test (1)
- High cycle fatigue (1)
- High temperature mechanical properties (1)
- High-temperature fatigue crack growth (1)
- Hochtemperatur (1)
- Hybrid additive manufacturing (1)
- IN 718 (1)
- IN718 (1)
- Intermetallics (1)
- Intermetallische FeAl-Legierungen (1)
- Interoperability (1)
- Iron aluminides (1)
- Kennwertermittlung (1)
- Keramik (1)
- Kleinprobenprüfung (1)
- Knowledge Graph (1)
- Knowledge Representation (1)
- Korrosion (1)
- Kreislaufwirtschaft (1)
- Kristallsystem (1)
- Lebensdauervorhersage (1)
- Lifetime prediction (1)
- Long-term behavior (1)
- Low Cycle Fatigue (LCF) (1)
- Low cycle fatigue (1)
- Low-cycle fatigue. (1)
- Lötverbindung (1)
- Material degradation (1)
- Materialkreislauf (1)
- Materialprüfung (1)
- Materials Chemistry (1)
- Materialwissenschaft (1)
- Mechanical Engineering (1)
- Mechanical behavior (1)
- Mechanics of Materials (1)
- Mechanische Eigenschaften (1)
- Mechanisches Verhalten (1)
- Metadata schema (1)
- Metal seal (1)
- Metall (1)
- Metals and Alloys (1)
- Micromechanical model (1)
- Microstructure analysis (1)
- Microstructure evolution (1)
- Microstructure-property-correlation (1)
- Mikrostruktur (1)
- Mikrostrukturuntersuchung (1)
- Modeling (1)
- Nickel-base alloy (1)
- Nickel-based alloys (1)
- Nimonic 75 (1)
- Normung (1)
- Numerische Simulation (1)
- Ontologie (1)
- Ontologien (1)
- Overaging (1)
- Phase-field simulation (1)
- Polymer (1)
- Precipitates (1)
- Precipitation hardening (1)
- Probengrößeneffekt (1)
- Quantitative image analysis (1)
- Radii distribution (1)
- Reference material BCR-425 (1)
- Referenzdaten (1)
- Referenzmaterial (1)
- Referenzorganismus (1)
- Referenzverfahren (1)
- Relaxation tests (1)
- Risse (1)
- Rissform (1)
- Rissfortschritt (1)
- Rissverlauf (1)
- S-Phase (1)
- S355 steel sheet (1)
- SEN-Probe (1)
- Schadenskunde (1)
- Semantic Web (1)
- Semantic structuring (1)
- Simulation (1)
- Simulationsgestützte Gießkonzepte (1)
- Standardization (1)
- Strength (1)
- Struktur (1)
- Syngle Crystal alloy (1)
- Tempered martensite-ferritic steel (1)
- Tensile Test (1)
- Tensile data (1)
- Tensile stress relaxation testing (1)
- Thermo-Mechanical Fatigue (1)
- Thermomechanical Fatigue (TMF) (1)
- Thermomechanical fatigue (1)
- Thermophysikalische Eigenschaften (1)
- Thesaurus (1)
- Ti-6Al-4V (1)
- Tribologie (1)
- Ungleichgewicht (1)
- Verbundwerkstoff (1)
- Vickers Hardness (1)
- Werkstoffauswahl (1)
- Werkstoffdaten (1)
- Werkstoffkennwerte (1)
- Werkstoffmechanische Prüfung (1)
- Werkstoffprüfung (1)
- Wissensrepräsentation (1)
- Zerstörungsfreie Prüfung (1)
- Zugversuch (1)
- coarsening (1)
- hardness (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (67) (entfernen)
Eingeladener Vortrag
- nein (16)
The mechanical strength of wrought high-strength aluminum alloys is essentially based on precipitation hardening, possibly in combination with prior forming, e. g. by stretching. Important parameters for achieving an optimum combination of hardness, strength, ductility, toughness, and further properties such as corrosion resistance are age-hardening temperature and time.
During thermal (mechanical) treatment, nucleation and growth of precipitates takes place, leading to the desired degree of hardening. In aluminum alloys, precipitation sequences are usually passed through, i. e. a sequence of metastable precipitates is formed before the stable phase can precipitate. The optimum combination of properties is therefore based on a certain (optimum) microstructure, which can, however, change during the use of a component, since the microstructure is not stable. This happens in particular when the operating temperatures are close to the aging temperature and/or the operating times are sufficiently long. An external mechanical load may accelerate the processes. The presentation gives some examples for this.
The studied aluminium alloy is EN AW-2618A (2618A). It is very widely used for exhaust gas turbo-charger compressor wheels. Due to long operating times, high cycle fatigue (HCF) and material aging under the influence of temperatures up to 230 °C is particularly relevant for the wheels. The wheels are typically milled from round wrought blanks. From such round blanks, different testpieces are extracted and a comprehensive series of HCF tests is conducted at room temperature. The tests investigate the materials fatigue performance in the T61 state for two load-ratios, namely R = -1 and R = 0.1. Additionally, two overaged material states are tested, accounting for the aging process the material undergoes during long operating times at high temperatures. The experimental results are evaluated and compared to each other.
Furthermore, the design process of notched specimens is presented. With the notched specimens, it is aimed to quantify the notch sensitivity of the material. Relating thereto, two potential model parameters for the fatigue lifetime model are introduced. Finally, the extended research data management in this project is highlighted and its advantages for sustainable use in material science and engineering applications are shown.
Die hohen Betriebstemperaturen während des Einsatzes von Radialverdichterrädern in Abgasturboladern führen zu einer Änderung der ursprünglich eingestellten Mikrostruktur in der warmfesten Aluminiumlegierung EN AW-2618A (Überalterung). Grund dafür sind thermische Belastungen, die nahe der Aushärtetemperatur liegen und diese kurzzeitig sogar überschreiten können. Die Alterungsmechanismen wurden zusammen mit den Themen niederzyklische (LCF) und thermomechanische Ermüdung (TMF) sowie Kriechen bis max. 190 °C in vorangegangenen Forschungsvorhaben untersucht. Kaum untersucht war bisher das Verhalten der Legierung unter hochzyklischer Beanspruchung (HCF) sowie der Einfluss von Kerben und Lastkollektiven. Da zukünftig mit weiter steigenden Betriebstemperaturen für Radialverdichter zu rechnen ist, wurde in diesem Forschungsvorhaben das HCF-Verhalten bei 230 °C untersucht und somit bei einer Prüftemperatur, die deutlich oberhalb der Aushärtetemperatur liegt. Das Ziel des Projektes war der Aufbau einer geeigneten experimentellen Datenbasis, das Verständnis der relevanten mikrostrukturellen Prozesse sowie die Weiterentwicklung und Anpassung geeigneter Modelle und Bewertungsmethoden.
Das experimentelle Untersuchungsprogramm umfasste neben einer Basischarakterisierung des HCF-Verhaltens am Ausgangszustand T61 gezielte mechanische Versuche zur Isolierung der Einflussfakto-ren Mittelspannung (𝑅 = −1, 𝑅 = 0,1), Werkstoffüberalterung (T61, 10 h/230 °C, 1000 h/230 °C), Prüftemperatur (20 °C, 230 °C), Prüffrequenz (0,2 Hz, 20 Hz) sowie Kerbwirkung und variable Amplituden. Darauf aufbauend wurden die in den vorangegangenen Projekten entwickelten Modelle und Bewertungsmethoden angepasst und weiterentwickelt, um die genannten thermischen und mechanischen Belastungen in der Lebensdauerbewertung abzubilden.
The high operating temperatures of radial compressor wheels in exhaust gas turbochargers lead to a change in the original microstructure of the heat-resistant aluminum alloy EN AW-2618A (overaging). This is caused by thermal loads that are close to the age hardening temperature and can even exceed it for a short time. The aging mechanisms have been investigated together with low cycle fatigue (LCF), thermomechanical fatigue (TMF) and creep up to max. 190 °C in previous research projects. The be-havior of the alloy under high cycle fatigue (HCF) and the influence of load spectra have hardly been investigated. Since the operating temperatures of centrifugal compressors are expected to increase in the future, this research project investigated the HCF behavior at 230 °C, a test temperature significantly higher than the age hardening temperature. The objectives of the project were to establish a suitable experimental database, to understand the relevant microstructural processes, and to further develop and adapt suitable models and evaluation methods.
In addition to a basic characterization of the HCF behavior in the initial condition T61, the experimental investigation program included targeted mechanical tests to isolate the influencing factors of mean stress (𝑅=−1, 𝑅=0.1), material overaging (T61, 10 h/230 °C, 1000 h/230 °C), test temperature (20 °C, 230 °C), test frequency (0.2 Hz, 20 Hz) as well as variable amplitudes. On this basis, the models and evaluation methods developed in the previous projects were adapted and further developed to reflect thermal and mechanical loads in the lifetime assessment.
Die Eigenschaften verschiedener Werkstoffe werden behandelt und typische Werkstoffkennwerte angegeben. Es werden Arten der Beanspruchung von Bauteilen und Werkstoffen vorgestellt, die diese in technischen Anwendungen unterworfen sind. Im Betrieb von Bauteilen kann Materialschädigung und unter Umständen auch Versagen eintreten. Mögliche Mechanismen und Ursachen werden erläutert und Einblicke in die Methodik der Schadensanalyse gegeben.
The elastic properties (Young's modulus, shear modulus) of austenitic stainless steel AISI 316L were investigated between room temperature and 900 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled sheet). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty.
The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data.
The elastic properties (Young's modulus, shear modulus) of Ni-based alloy Inconel IN718 were investigated between room temperature and 800 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty.
The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data.
The elastic properties (Young's modulus, shear modulus) of titanium alloy Ti-6Al-4V were investigated between room temperature and 400 °C in an additively manufactured variant (laser-based directed energy deposition with powder as feedstock, DED-LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, microstructure, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty.
The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data.
Brinell test ontology (BTO)
(2024)
Brinell Test Ontology (BTO) has developed for representing the Brinell testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6506-1 standard.
Versions info:
V2 developed using BFO+CCO top-level ontologies.
V3 developed using EMMO+CHAMEO top-level ontologies.
V4 developed using PROVO+PMDco top-level ontologies.
V5 developed using BFO+IOF top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/brinell-hardness-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Brinell-Test-Ontology-BTO-
MatPortal: https://matportal.org/ontologies/BTO
IndustryPortal: https://industryportal.enit.fr/ontologies/BTO
The Gibbs free energy of a grain boundary is a complex thermodynamic function of temperature, pressure, and composition. These complexities add to the intrinsic crystallographic and chemical constraints imposed by the adjacent bulk phase. Recently we have proposed a density-based model for assessing grain boundary thermodynamics that enables a CALPHAD-informed description of the grain boundary. As such, the Gibbs free energy of the grain boundary is directly linked with available CALPHAD thermodynamic data. In this talk, new aspects of interfacial segregation and phase transformation are revealed by benchmarking the current model for various experimental cases, including several steels, high-entropy alloys and aluminum alloys. The effects of elastic interactions on the grain boundary segregation and the application of the model to a nanocrystalline Pt-Au alloy, with numerous grain boundaries of various characters, will be discussed.
Charakterisierung von Hochtemperaturwerkstoffen durch Zug- und Ermüdungsversuche an Kleinproben
(2019)
Die Verwendung von miniaturisierten Probengeometrien in der mechanischen Prüfung ermöglicht die Entnahme des Probenmaterials direkt aus kritischen Bereichen wie Fügeverbindungen und ermöglicht die Prüfung von kleinen Bauteilen wie additiv gefertigten Strukturen. In der vorliegenden Arbeit werden exemplarisch die Ergebnisse von vergleichenden Zug- und niederzyklischen Schwing-versuchen (LCF) an dem austenitischen Stahl AISI 316L und der Nickelbasislegierung IN718 vorgestellt. Die Prüfergebnisse der Kleinproben aus AISI 316L weisen die charakteristischen Eigenschaften des Werkstoffs auf, und die Analyse der Zug- und Ermüdungsdaten führt zu Werten, die den Literaturdaten weitgehend entsprechen. Der direkte Vergleich mit Standardprobendaten zeigt jedoch systematische Abweichungen bei Zugfestigkeit, Dehngrenze und Gleichmaßdehnung, die in diesem Beitrag diskutiert werden.
In Germany spent nuclear fuel and high level radioactive waste is stored in interim storage containers with double lid systems. Those lids are equipped with metal seals (e.g. Helicoflex®) that ensure the safe enclosure of the inventory. The used metal seals consist of three components as can be seen in the cross-sectional view in Figure 1. The innermost part is a helical spring that is surrounded by an inner jacket made of stainless steel. The outer jacket that is made of a softer material which in case of assembly in the aforementioned storage containers is silver or aluminum (i.e. Al 99.5). During application the seal is compressed and due to the restoring force of the helical spring, the outer jacket is plastically deformed and adapts to the sealing surface. Hence, leakage paths are closed and the sealing function is generated. In Germany the above-mentioned containers are licensed for up to 40 years of interim storage, which in case extended storage becomes necessary before a final repository is available will have to be extended to even longer periods. Therefore, the evaluation of the long-term behavior of the seals is necessary, taking into account storage conditions, decay heat and possible mechanical loads as well.
At Bundesanstalt für Materialforschung und –prüfung (BAM) long-term investigations are being conducted in which seals are assembled in test flanges and aged at temperatures ranging from room temperature to 150°C for accelerated aging. The aged seals are tested semi-annually (after the first 6 months in which the seals are tested more frequently) regarding the sealing performance, the remaining seal force, and the useable resilience upon decompression. Results of these investigations have been published over the past years (e.g. Grelle, Wolff, Probst, Jaunich, & Völzke, 2017; Völzke, Wolff, Probst, Nagelschmidt, & Schulz, 2014). It was found that the seal force and the useable resilience decrease with time and temperature, which is in agreement with the result of other studies (Sassoulas et al., 2006; Wataru et al., 2016) as well. Geometry change of the outer jacket has been identified as the main reason for this seal behavior. At the prevailing operating temperatures and stresses the aluminum is subjected to creep deformation leading to a thinning of the outer jacket. Since the seal groove depth remains unchanged the helical spring expands, which in turn leads to a decrease of the generated spring and seal force.
Although the main reason for the change of seal parameters over time and temperature is known, a detailed characterization of the seal behavior and a reliable prediction of the parameter development for aging times that exceed the experimental time frame have not been possible, yet.
For deeper understanding of the aging processes, an Investigation program, which is covered in this contribution, is conducted at Bundesanstalt für Materialforschung und –prüfung (BAM) that focusses on the behavior of the aluminum jacket and its influence on the long-term sealing performance. The program investigates properties of material samples as well as the behavior of the seal as a component.
Original sheet material of the same aluminum that is used for manufacturing of the seals is investigated in compression creep tests. For this, a DMA (dynamic mechanical analysis) machine is employed (here used for static tests) that allows for a measurement of the specimens deformation under forces of up to 500 N. The advantage of this method is that the original material can be tested in the same shape as used for the seals which is 0.5 mm thick sheet material. For investigation of tensile creep standard specimens are used, that were machined from surrogate material of the same composition and annealing condition.
Furthermore, aluminum seals that are cut into smaller segments are assembled in flanges and placed in heating chambers at temperatures ranging from 23°C to 150°C. After different periods of time from 3 days to 300 days the segments are taken out of the flanges and are investigated, thus giving information on different states of aging. Measurements of the development of the seal contact width and the aluminum jacket thickness are done with an optical microscope. Further investigations on the segments will include metallography and hardness measurements.
From the detailed material and component behavior including the results of the long-term seal force and useable resilience investigations a better understanding of the overall seal behavior can be gained. The aim is to contribute to the development of material models and analytical approaches for the prediction of the sealing behavior in dependence of time and temperature.
The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach.
The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach, both of which are presented in “Part 2: Microstructural Evolution during Cyclic Loading and its Representation in a Physically-based Micromechanical Model“.
The current competitive situation on electricity markets forces conventional power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach.
The dataset contains experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress.
Further information on data and data acquisition, analysis, and experimental details are given in “Experimental Data from Service-Like Creep-Fatigue Experiments on Grade P92 Steel”, submitted to Data in Brief. Additional analyses of these datasets, as well as experimental findings and discussions are presented in “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times”, submitted to International Journal of Fatigue.
Die Bereitstellung von zuverlässigen Werkstoffdaten stand für die Werkstoffprüfung seit dem 19. Jahrhundert in zentraler Stelle. Mit der zunehmender Digitalisierung unserer Gesellschaft gewinnt das Datenmanagement insbesondere im Hinblick auf die Modellierungs- und Simulationsaktivitäten an Bedeutung.
In unserem Beitrag beschreiben wir die gegenwärtigen Aktivitäten in Deutschland – insbesondere die NFDI-MatWerk und die BMBF-Initiative MaterialDigital – sowie in Europa und Übersee. Abschließend heben wir die Auswirkungen auf die technische und akademische Aus- und Weiterbildung.
Die Werkstoffklassen
(2020)
Es werden die vier Werkstoffklassen Metalle, Keramiken, Polymere und Verbundwerkstoffe sowie ihre Untergruppen vorgestellt. Die metallischen Werkstoffe umfassen die Eisen- wie die Nichteisenwerkstoffe und ihre Legierungen. Neben den Ingenieurkeramiken werden auch Glas und Glaskeramik, Naturstoffe und Erdstoffe sowie Baustoffe behandelt.
Die warmfeste austenitische Gusseisenlegierung EN-GJSA-XNiSiCr35-5-2 (häufig auch als Ni-Resist D-5S bezeichnet) wurde hinsichtlich ihres mechanischen Verhaltens bei hoher Temperatur charakterisiert. Dazu wurden (isotherme) niederzyklische (LCF-) und (nicht-isotherme) thermomechanische Ermüdungsversuche (TMF) zwischen Raumtemperatur und 900 °C durchgeführt. Diese Ergebnisse dienten (zusammen mit weiteren Versuchsdaten) der Kalibrierung werkstoffmechanischer Modelle. Bei den höchsten Prüftemperaturen wurde Schädigung in Form von Kriechen beobachtet und metallographisch dokumentiert.
Die warmfeste austenitische Gusseisenlegierung EN-GJSA-XNiSiCr35-5-2 (häufig auch als Ni-Resist D-5S bezeichnet) wurde hinsichtlich ihres mechanischen Verhal-tens bei hoher Temperatur charakterisiert. Dazu wurden (isotherme) niederzyklische (LCF-) und (nicht-isotherme) thermomechanische Ermüdungsversuche (TMF) zwischen Raumtemperatur und 900 °C durchgeführt. Diese Ergebnisse dienten (zu-sammen mit weiteren Versuchsdaten) der Kalibrierung werkstoffmechanischer Modelle. Bei den höchsten Prüftemperaturen wurde Schädigung in Form von Kriechen beobachtet und metallographisch dokumentiert.
Die warmfeste austenitische Gusseisenlegierung EN-GJSA-XNiSiCr35-5-2 (häufig auch als Ni-Resist D-5S bezeichnet) wurde hinsichtlich ihres mechanischen Verhal-tens bei hoher Temperatur charakterisiert. Dazu wurden (isotherme) niederzyklische (LCF-) und (nicht-isotherme) thermomechanische Ermüdungsversuche (TMF) zwischen Raumtemperatur und 900 °C durchgeführt. Diese Ergebnisse dienten (zu-sammen mit weiteren Versuchsdaten) der Kalibrierung werkstoffmechanischer Modelle. Bei den höchsten Prüftemperaturen wurde Schädigung in Form von Kriechen beobachtet und metallographisch dokumentiert.
The integration of additive manufacturing with traditional processes, termed hybrid additive manufacturing, has expanded its application domain, particularly in the repair of gas turbine blade tips. However, process-related defects in additively manufactured materials, interface formation, and material property mismatches in dual-material structures can significantly impact the fatigue performance of components. This investigation examines the low cycle fatigue and fatigue crack growth behaviors in dual-material specimens of nickel-based alloys, specifically the additively manufactured STAL15 and the cast alloy 247DS, at elevated temperatures. Low cycle fatigue experiments were conducted at temperatures of 950 °C and 1000 °C under a range of strain levels (0.3%–0.8%) and fatigue crack growth tests were conducted at 950 °C with stress ratios of 0.1 and −1. Fractographic and microscopic analyses were performed to comprehend fatigue crack initiation and crack growth mechanisms in the dual-material structure. The results consistently indicated crack initiation and fatigue fracture in the additively manufactured STAL15 material. Notably, fatigue crack growth retardation was observed near the interface when the crack extended from the additively manufactured STAL15 material to the perpendicularly positioned interface. This study highlights the importance of considering yield strength mismatch, as well as the potential effects of residual stresses and grain structure differences, in the interpretation of fatigue crack growth behavior at the interface.
The influence of test temperature and frequency on the fatigue life of the alloy EN AW-2618A (2618A) was characterized. The overaged condition (T61 followed by 1000 h/230 °C) was investigated in load-controlled tests with a stress ratio of R = -1 and two test frequencies (0.2 Hz, 20 Hz) at room temperature and at 230°C, respectively. An increase in the test temperature reduces fatigue life, whereby this effect is more pronounced at lower stress amplitudes. Decreasing the test frequency in tests at high temperatures further reduces the service life.
The heat-resistant cast iron EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) was investigated for its fatigue crack growth behavior at room and high temperatures. Force-controlled tests were carried out at constant temperatures (20 °C, 500 °C, 700 °C) without and with hold time and different load ratios. The crack growth behavior was also characterized under TMF loading (Tmin = 400 °C, Tmax = 700 °C) by applying IP and OP conditions and different load ratios. Three different techniques were combined to monitor crack growth: potential drop, thermography, and compliance method. The effect of the different loading conditions on the fatigue crack growth behavior will be presented and discussed.
Fatigue test ontology (FTO)
(2024)
Fatigue Test Ontology (FTO) has developed for representing the fatigue testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 12106 standard.
Versions info:
V2 developed using PROVO+PMDco top-level ontologies.
V3 developed using BFO+IOF top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/lcf-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Fatigue-Test-Ontology-FTO-
MatPortal: https://matportal.org/ontologies/FTO
IndustryPortal: https://industryportal.enit.fr/ontologies/FTO
The dataset provided in this repository comprises data obtained from a series of characterization tests performed to a sheet of typical S355 (material number: 1.0577) structural steel (designation of steel according to DIN EN 10025-2:2019). The tests include methods for the determination of mechanical properties such as, e.g., tensile test, Charpy test and sonic resonance test. This dataset is intended to be extended by the inclusion of data obtained from further test methods. Therefore, the entire dataset (concept DOI) comprises several parts (versions), each of which is addressed by a unique version DOI.
The data were generated in the frame of the digitization project Innovationplatform MaterialDigital (PMD) which, amongst other activities, aims to store data in a semantically and machine understandable way. Therefore, data structuring and data formats are focused in addition to aspects in the field of material science and engineering (MSE). Hence, this data is supposed to provide reference data as basis for experimental data inclusion, conversion and structuring (data management and processing) that leads to semantical expressivity as well as for MSE experts being generally interested in the material properties and knowledge.
Der Aufbau der Werkstoffe wird durch Merkmale wie Bindungsart, atomare Strukturen, Kristallstrukturen einschließlich ihrer Gitterbaufehler, Körner und Phasen bestimmt. Die Mikrostruktur (Gefüge) stellt den Verbund der Kristalle, Phasen und Gitterbaufehler auf mikroskopischer und nanoskopischer Skala dar. Die Grundlagen der Phasenumwandlungen werden behandelt und die Bedeutung von Diffusionsprozessen erläutert. Werkstoffe sind bedeutend für Kultur, Wirtschaft, Technik und Umwelt. Ihre Herstellung benötigt Ressourcen und Energie. Recycling ist eine Möglichkeit zur Erhöhung der Ressourcenproduktivität.
High Temperature Fatigue Crack Growth in Nickel-Based Alloys Refurbished by Additive Manufacturing
(2024)
Hybrid additive manufacturing plays a crucial role in the restoration of gas turbine blades, where, e.g., the damaged blade tip is reconstructed by the additive manufacturing process on the existing blade made of a parent nickel-based alloy. However, inherent process-related defects in additively manufactured material, along with the interface created between the additively manufactured and the cast base material, impact the fatigue crack growth behavior in bi-material components. This study investigates the fatigue crack growth behavior in bi-material specimens of nickel-based alloys, specifically, additively manufactured STAL15 and cast alloy 247DS. The tests were conducted at 950 °C with stress ratios of 0.1 and −1. Metallographic and fractographic investigations were carried out to understand crack growth mechanisms. The results revealed significant retardation in crack growth at the interface. This study highlights the potential contributions of residual stresses and microstructural differences to the observed crack growth retardation phenomenon, along with the conclusion from an earlier study on the effect of yield strength mismatch on crack growth behavior at a perpendicular interface in bi-material specimens.
Performing mechanical tests at high temperatures is a nontrivial issue: Compared to room temperature testing, additional phenomena like time-dependent Deformation processes and oxidation effects raise the complexity of the material’s response, while more sophisticated test setups and additional control parameters increase the number of potential sources of error. To a large extent, these complications can be overcome by carefully following all recommendations given in the respective high temperature testing standards, but more comprehensive background information helps to identify points of specific importance in particular test campaigns. In this chapter, an overview is given on general high temperature testing issues like the appropriate choice of experimental equipment and key aspects of temperature measurement. In subsequent sections, the major static and dynamic high temperature test methods are reviewed and their Special features, as compared to testing at room temperature, are highlighted based on example data sets. Influences of specimen size and environmental effects are shortly outlined in a concluding section. In the whole chapter, a focus is set on testing of “classical” metallic high temperature materials, but many considerations are equally valid for testing of intermetallics, composites, and high temperature ceramics.
The strength of age-hardenable aluminum alloys is based on the controlled formation of nm-sized precipitates, which represent obstacles to dislocation movement. Transmission electron microscopy (TEM) is generally used to identify precipitate types and orientations and to determine their size. This geometric quantification (e.g., length, diameter) is often performed by manual image analysis, which is very time consuming and sometimes poses reproducibility problems. The present work aims at the digital representation of this characterization method by proposing an automatable digital approach. Based on DF-TEM images of different precipitation states of alloy EN AW-2618A, a modularizable digital workflow is described for the quantitative analysis of precipitate dimensions. The integration of this workflow into a data pipeline concept is also presented. The semantic structuring of data allows data to be shared and reused for other applications and purposes, which enables interoperability.
Iron aluminides, already reported in the late 19th century, did not cease to attract the interest of scientists and engineers ever since. Besides good oxidation resistance, low density and resource availability, potentials for hightemperature strengths that compete with high-alloy steels were unlocked by low alloy contents. Still, research on alloy design continues, as alloying usually comes at the price of brittleness in low-temperature regimes. A potential candidate is the quinary Fe–Al–Mo–Ti–B system which is strengthened by solid solution and eutectic borides. It was shown to have good strength and outstanding creep resistance under compressive loading up to elevated temperatures. Although the individual effect of alloy additions is well understood in iron aluminides, little is known about the combined effects of alloying concentrations on microstructure, phase stability and mechanical properties. Therefore a systematic study of two Ti-doped near-Fe3Al alloys with varying contents of Mo (2–4 at.%) and B (0.5–1 at.%) was conducted. In total eight different alloys were fabricated by investment casting into ceramic shell molds. Alloys were characterized and compared by grain size, phase transitions, microstructure evolution as well as elemental compositions and volume fractions of phases. For mechanical characterization, macrohardness and microhardness tests as well as tensile tests at ambient and high tempera tures were conducted. Independent of alloy additions, alloys with 24–25 at.% Al exhibit superior proof strength due to a higher matrix hardness. Decreasing B content generally decreases strength by lower secondary phase fractions which contribute via particle hardening. Reducing Mo content decreases both the solute concentration in the matrix and secondary phase fractions. Surprisingly, strength is similar or even superior to alloys with higher Mo content. Strength relations are discussed with a focus on solid-solution hardening theory and other competing strengthening mechanisms.
The influence of prestraining on the aging response of an Al-Cu-Li alloy is investigated by preparation of different strain states (3 %, 4 %, 6 %) of the initial aging state. The Brinell hardness of the subsequently aged samples (up to 60 h aging time) was measured and it was found that the increasing dislocation concentration in the 3 different initial states leads to faster hardness increases and slightly higher maximum hardness.
In typical material oriented research projects numerous types and sources of data need to get connected to form the final outcome. The data-structures have to be described in a manner semantically concise enough so that all participants share the meaning and at the same time flexible enough to allow connecting findings and facts that have not been connected before.
The present contribution describes the approach that is being taken in a public funded research project with two cooperating research institutes. The aim of the data-management solution is to describe and interlink three main entity types: material entities like a test specimen that is under observation, immaterial entities like a fatigue life model and processes that generate and transform the immaterial and material entities.
The shared understanding of what is described by the data is achieved by referring to existing linked data resources. In addition a common thesaurus that is subject to ongoing discussion is used for concepts and terms that need precision beyond publicly available concept descriptions. The data associated with the entities and processes and entities is rather small and well structured. The entities and processes covered by the vocabularies are typical to laboratories performing fatigue testing and microstructure analysis. Through the interlinking of the entities and processes it becomes possible to intuitively understand the knowledge that is accumulating in the database. For example it is easy to trace the history of a creep test specimen starting from the chemical composition that has been analyzed for the heat, continuing with the heat treatment of the material, going into the creep test itself with the associated creep data and finally finding the transmission electron microscopy images that have been taken from the crept sample.
The presented approach is prototypical way to tackle the sustainable management of structured open research data. Open questions remain for example with the management of attributions, the acceptance of an increased effort in data creation and the access control to specific regions of the data. On the other hand the approach sketches what added value can be created, if the community adopts and contributes to the linked data principles.
In our current view, reference datasets in the MSE domain represent specific material properties, e.g., structural, mechanical, … characteristics. A reference dataset must fulfill high-quality standards, not only in precision of measurement but also in a comprehensive documentation of material, processing, and testing history (metadata). This Infrastructure Use Case (IUC) aims to develop a framework for generating reference material datasets using creep data of a single crystal Ni-based superalloy as a best practice example. In a community-driven process, we aim to encourage the discussion and establish a framework for the creation and distribution of reference material datasets. In this poster presentation, we highlight our current vision and activities and intend to stimulate the discussion about the topic reference datasets and future collaborations and work.
The KupferDigital project aims to develop digital methods, tools, and data space infrastructures for digitalizing the entire life cycle of copper materials. The mechanical testing process is one of the main chains of such life cycles which generates lots of important testing data about the mechanical properties of the materials and their related materials and testing metadata. To train the digitalization of the mechanical testing process, different kinds of copper alloys were provided for this project, and their mechanical properties were measured by typical methods like Brinell and Vickers hardness and tensile testing. The primary raw testing data as well as the secondary datasets of these tests are provided. The detailed materials specifications, the utilized mechanical testing methods, and provided datasets are described in the content file. The test data files of heterogeneous structures are processed by the KupferDigital digital tools to be converted to standardized machine-readable data files.
KupferDigital mechanical testing datasets: Stress relaxation and low-cycle fatigue (LCF) tests
(2024)
The KupferDigital project deals with the development of a data ecosystem for digital materials research on the basis of ontology-based digital representations of copper and copper alloys. This document provides exemplary mechanical testing datasets for training the developed KupferDigital infrastructures. Different types of cast copper alloys were provided for this research and their mechanical testing (stress relaxation and low-cycle fatigue) was performed in the accredited materials testing laboratory, while the test results were reported according to the DIN/ISO standards and attached with the maximum possible metadata about the sample history, equipment, and calibration. The attached content file consisted of the obtained primary raw testing data as well as the secondary datasets of these tests containing the detailed metadata of mechanical testing methods. Such test data files are processed by the KupferDigital digital tools to be converted to standardized machine-readable data files.
Die Mikrostruktur von ausscheidungsgehärteten Aluminiumlegierungen ist von herausragender Bedeutung für ihre Festigkeit, da nur Werkstoffe mit gezielt eingestellter Mikrostruktur für Radialverdichterräder ausreichende Festigkeiten erreichen. Diese optimierte Mikrostruktur ändert sich jedoch während des Betriebs, denn die Bauteile werden bei Temperaturen eingesetzt, die nahe der Aushärtetemperatur liegen oder sogar darüber hinausgehen und folglich ist mit Alterung der Mikrostruktur und damit einhergehender Degradation der Eigenschaften zu rechnen. Diese Effekte konnten bisher in der Lebensdauervorhersage nicht berücksichtigt werden, da ihre diesbezüglichen Auswirkungen lediglich qualitativ bekannt waren. In diesem Forschungsvorhaben wurde daher für die Legierung EN AW-2618A einerseits eine sorgfältige und umfassende Charakterisierung der Gefügeentwicklung für anwendungsrelevante Temperaturen und Zeiten bis zu 25.000 h vorgenommen und andererseits eine solide Datenbasis bezüglich der mechanischen Eigenschaften (Zugfestigkeit, Kriechwiderstand, LCF-, TMF-Verhalten) und ihren Änderungen geschaffen. Darauf aufbauend wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus EN AW-2618A zu verbessern. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer unter Rainflow-klassierten Betriebslastkollektiven wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein.
In diesem Forschungsvorhaben wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus der ausscheidungs-härtbaren Aluminiumlegierung EN AW-2618A zu verbessern. Dies umfasst insbesondere die Berücksichtigung der Werkstoffalterung, mit der beim Einsatz dieser Bauteile unter entsprechender Betriebsbeanspruchung (Temperatur, Zeit, Spannung) gerechnet werden muss. Zunächst wurde eine solide experimentelle Datenbasis für den untersuchten Werkstoff geschaffen. Dies umfasste sowohl eine mechanische als auch eine mikrostrukturelle Charakterisierung des Ausgangszustands (T61) sowie von ausgelagerten Zuständen bis zu 25.000 h bei betriebsrelevanten Temperaturen (160 °C, 180 °C, 190 °C). Bei den Untersuchungen zur Mikrostruktur wurde der Fokus auf die Entwicklung der Radien der stäbchen-förmigen aushärtenden Phase gelegt, die während der Alterung vergröbern. Der Zusammenhang zwischen Auslagerungstemperatur, -zeit und ggfs. mechanischer Belastung wurde erstmals in diesem Umfang quantifiziert und entsprechende Gesetzmäßigkeiten zur Beschreibung der Vergröberung ermittelt. Vergleichend dazu wurde der Einfluss der Alterung auf die Härte, die Festigkeit, das Kriechverhalten und die Ermüdungslebensdauer (LCF, TMF) bestimmt, so dass eine Korrelation zur Mikrostruktur vorliegt.
Die Ergebnisse der Kriechversuche wurden zur Kalibrierung eines modifizierten Sinus-hyperbolicus-Kriechmodells verwendet. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein. Lediglich ein LCF-Versuch mit einer Haltezeit von 900 s im Zug weicht deutlich vom Mittelwert ab und zeigt die Grenzen des zeitunabhängigen Schädigungsmodells auf. Versuche mit kürzeren Haltezeiten bis zu 60 s liegen im Streuband, ebenso die verschiedenen Alterungszustände. Eine Schädigungsakkumulation unter Berücksichtigung der fortschreitenden Alterung über der Lebensdauer wurde entwickelt und implementiert. Neben der Berücksichtigung der Alterung in der Verformungs- und Lebensdaueranalyse besteht auch die Möglichkeit, komplexe Belastungszyklen in einem Postprozessing zu bewerten, indem Rainflow-Klassierungen typischer komplexer Belastungszyklen vorgenommen werden.
Die Methodik und die Modelle wurden in die Finite-Elemente-Programme Abaqus und Ansys implementiert und stehen für die rechnerische Bewertung von Bauteilen zur Verfügung.
Werkstoffe im Hochtemperatureinsatz verändern mit der Zeit ihre Mikrostruktur. Mit diesem Alterungsprozess einher geht eine Veränderung der mechanischen Eigenschaften ebenso wie eine Veränderung des Schädigungsverhaltens. Im Rahmen des FVV Vorhabens „Alterung und Lebensdauer“ haben das Fraunhofer IWM in Freiburg und die BAM in Berlin die weit verbreitete warmfeste Aluminiumlegierung EN AW-2618A in verschiedenen Alterungszuständen experimentell charakterisiert und darauf aufbauend Modelle für die Lebensdauerbewertung mit der Finite-Elemente- Methode implementiert.
Materials subjected to high-temperature service conditions will change their microstructure with time. Associated with this aging process is a change of mechanical properties as well as a change of damage mechanisms. Within the scope of the FVV project Aging and Lifetime, Fraunhofer IWM in Freiburg and BAM in Berlin (both Germany) experimentally characterized the widespread high-temperature aluminum alloy EN AW-2618A in different overaging states. Based on the experimental findings, models for numerical lifetime assessment with the finite-element method were implemented.
Materialprüfung
(2019)
Die Materialprüfung dient der Analyse der Eigenschaften, der Qualität und der Sicherheit vonMaterialien undWerkstoffen. Die häufigsten Verfahren umfassen die Analyse der chemischen Zusammensetzung und der Mikrostruktur sowie die Ermittlung von Werkstoffkennwerten. Dazu zählt auch die Bestimmung des Materialverhaltens unter verschiedenen Beanspruchungen bis hin zu komplexen Beanspruchungen. Die Verwendung von Referenzmaterialien, Referenzorganismen und Referenzverfahren dient der Zuverlässigkeit und Richtigkeit von Messungen, Prüfungen und Analysen.
The increasing importance of resource availability and closed-loop material cycles are driving materials research to reduce alloying content in conventional materials or even substitute them with more sustainable alternatives. Intermetallic iron aluminide alloys (FeAl) present a potential alternative. Many alloy concepts for improved high-temperature properties or ductility have already been successfully implemented in casting technologies on a laboratory scale. However, successful testing of FeAl alloys on an industrial scale was still pending at the beginning of the project.
Therefore, the aim of the project was to develop simulation based casting concepts for industrial casting processes using the base alloy Fe-26Al-4Mo-0.5Ti-1B and to narrow down process limits by means of hot cracking tests. Findings were transferred into practice-oriented guidelines for casting of iron aluminides, which is accessible to future applicants in SMEs. The focus was placed on centrifugal casting combined with investment casting or die casting. In addition to numerous design and casting process parameters, heat treatments and alloying additions (Al, Mo, B) were varied to determine the influence of alloying elements on castability, microstructure and mechanical properties. Data from microstructure analyses (microscopic imaging, determination of grain sizes as well as phase compositions and volume fractions, fractography), mechanical tests (hardness measurements, compression tests, ambient and high-temperature tensile tests, creep tests) as well as measurements of thermophysical properties could be generated on the base alloy. Correlations of materials data with process variables allowed conclusions to be drawn on strengthening mechanisms and ductility of the alloy and how they can be controlled in terms of processing and component design. Successful casting of highly complex components with thin wall thicknesses and optimised alloy compositions points out prospects for new fields of application.
The materials mechanical testing ontology (MTO) was developed by collecting the mechanical testing vocabulary from ISO 23718 standard, as well as the standardized testing processes described for various mechanical testing of materials like tensile testing, Brinell hardness test, Vickers hardness test, stress relaxation test, and fatigue testing.
Versions info:
V2 developed using BFO+CCO top-level ontologies.
V3 developed using PROVO+PMDco top-level ontologies.
V4 developed using BFO+IOF top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/ontologies/mechanical-testing-ontology
GitHub: https://github.com/HosseinBeygiNasrabadi/Mechanical-Testing-Ontology
MatPortal: https://matportal.org/ontologies/MTO
IndustryPortal: https://industryportal.enit.fr/ontologies/MTO
Metalle
(2019)
Dieses Standardwerk bietet eine Darstellung der Struktur und Eigenschaften der Metalle und ihrer Anwendungen als Werkstoffe. Im ersten, wissenschaftlichen Teil werden der atomare und mikroskopische Aufbau, die thermodynamischen und die grundlegenden physikalischen und mechanischen Eigenschaften der Metalle beschrieben sowie die Grundlagen der thermisch aktivierten Reaktionen und der Phasenumwandlungen. Die wichtigsten experimentellen Untersuchungsmethoden werden erläutert, wobei die mikroskopischen und Beugungsverfahren einen Schwerpunkt bilden.
Im zweiten, technischen Teil werden die Werkstoffgruppen der Metalle und ihre anwendungsbezogenen Eigenschaften behandelt. Dabei wird auf die zugrunde liegenden Legierungen und die Verfahren zur gezielten Einstellung ihrer Eigenschaften eingegangen. Schwerpunkte bei der Darstellung der Werkstoffe sind die Stähle, die teilchengehärteten Legierungen, die Magnetwerkstoffe und die pulvermetallurgisch hergestellten Werkstoffe. Außerdem werden die Oberflächeneigenschaften und die Verfahren zur Oberflächenbehandlung dargestellt.
This research deals with the development of the Vickers hardness knowledge graph, mapping the example dataset in them, and exporting the data-mapped knowledge graph as a machine-readable Resource Description Framework (RDF). Modeling the knowledge graph according to the standardized test procedure and using the appropriate upper-level ontologies were taken into consideration to develop the highly standardized, incorporable, and industrial applicable models. Furthermore, the Ontopanel approach was utilized for mapping the real experimental data in the developed knowledge graphs and the resulting RDF files were successfully evaluated through the SPARQL queries.
This research deals with the development of the Vickers hardness knowledge graph, mapping the example dataset in them, and exporting the data-mapped knowledge graph as a machine-readable Resource Description Framework (RDF). Modeling the knowledge graph according to the standardized test procedure and using the appropriate upper-level ontologies were taken into consideration to develop the highly standardized, incorporable, and industrial applicable models. Furthermore, the Ontopanel approach was utilized for mapping the real experimental data in the developed knowledge graphs and the resulting RDF files were successfully evaluated through the SPARQL queries.
Es konnte anhand einer numerischen Voruntersuchung gezeigt werden, dass anhand der kombinierten Auswertung der im Versuch verwendeten Sensorik eine Einteilung der unter Ermüdung in Bohrlochproben auftretenden Rissformen in verschiedene Hauptkategorien (Eckriss, Oberflächenriss, Durchgangsriss) möglich ist.
In nickelbasierten Superlegierungen, die für Gasturbinenschaufeln verwendet werden, sind bei hohen Betriebstemperaturen und -belastungen Kriechschäden, Ermüdung, Korrosion und Oxi-dation zu beobachten. Die betroffenen Turbinenschaufeln müssen ersetzt oder repariert werden, um Effizienzverluste und ein eventuelles Bauteilversagen zu vermeiden. In letzter Zeit wurden additive Fertigungs- und Lötverfahren für die Reparatur und das Fügen von Nickelbasiswerk-stoffen entwickelt, um die Einschränkungen der traditionellen Reparaturverfahren zu überwinden. Für eine auslegungsrelevante Bewertung des Risswachstumsverhaltens in den Fügezonen, die durch diese neuen Technologien erzeugt werden, sind Rissfortschrittsuntersuchungen erfor-derlich. Entsprechende Untersuchungen an gefügten Proben werden in diesem Beitrag vorge-stellt. Die Rissfortschrittsversuche werden an gefügten SEN-Proben (Single Edge Notch) bei einem Spannungsverhältnis von 0,1 und einer Temperatur von 950 °C durchgeführt. Das Riss-wachstum wird mit der DCPD-Methode (Direct Current Potential Drop) überwacht, und die ge-messenen Potenzialsignale werden anhand der optisch vermessenen Risslänge und einer Finite-Elemente-Analyse kalibriert. Der Spannungsintensitätsfaktor (SIF) für die gefügte SEN-Geometrie wird mit Hilfe von Finite-Elemente-Analysen berechnet. Auf diese Weise können Rissfortschrittskurven aus den experimentellen Daten abgeleitet werden.
Tensile Stress Relaxation Test Ontology (TSRTO) has developed for representing the tensile stress relaxation testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 10319-1 standard.
Versions info:
V1 developed using BFO+CCO top-level ontologies.
V3 developed using PROV+PMDco top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/relaxation-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Tensile-Stress-Relaxation-Test-Ontology-TSRTO
MatPortal: https://matportal.org/ontologies/TSRTO
IndustryPortal: https://industryportal.enit.fr/ontologies/TSRTO
Tensile test ontology (TTO)
(2024)
Tensile Test Ontology (TTO) has developed for representing the Tensile testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6892-1 standard.
Versions info:
V2 developed using BFO+CCO top-level ontologies.
V3 developed using PROVO+PMDco top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/tensile-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Tensile-Test-Ontology-TTO-
MatPortal: https://matportal.org/ontologies/TTO
IndustryPortal: https://industryportal.enit.fr/ontologies/TTO
Die Steigerung der Leistung und des thermodynamischen Wirkungsgrades von Verbrennungsmotoren führt zu erhöhten Anforderungen an die Festigkeit abgasführender Komponenten wie z. Bsp. Abgasturbolader. Als Folge erhöhter thermomechanischer Wechselbeanspruchungen (TMF) im Betrieb kommt es an den mechanisch und/oder thermisch höchst beanspruchten Stellen der Bauteile zur Bildung von Rissen, wodurch die Lebensdauer der Komponenten begrenzt wird. Derzeit werden bei Turboladern heißgehende Bauteile mit detektierten Rissen zumeist prophylaktisch ersetzt, da die weitere Ausbreitung der Risse während des Betriebs nicht vorhergesagt werden kann. Um diese aufwändige und un- ökonomische Praxis zu vermeiden, wurde im vorliegenden Forschungsvorhaben eine rechnerische Bewertungsmethode auf Basis der experimentellen und numerischen Bruchmechanik erarbeitet, mit deren Hilfe bereits in der Auslegungsphase oder während des Betriebs die (restliche) Lebensdauer der abgasführenden Komponenten vorhergesagt werden kann. Damit wird erstmalig die quantitative Vorhersage der Rissentwicklung bei TMF-Beanspruchungsbedingungen unter Berücksichtigung großer zyklischer viskoplastischer Verformungen ermöglicht.
Zentrales Ergebnis des Vorhabens ist eine automatisierte Berechnungsprozedur auf der Basis spezieller Finite-Elemente-Techniken (FEM), womit sowohl der Pfad als auch die Größe eines Risses als Funktion der Anzahl der Lastwechsel in Bauteilen unter TMF-Bedingungen berechnet werden kann. Als geeigneter Beanspruchungsparameter zur Bewertung des Rissfortschritts unter TMF wurde die zyklische Rissöffnungsverschiebung ΔCTOD verwendet. Das Werkstoffverhalten des betrachteten austenitischen Gusseisens Ni-Resist D-5S wurde mit einem validierten viskoplastischen, temperaturabhängigen Materialmodell modelliert, das zur Berücksichtigung große Verzerrungen und Rotationen am Riss erweitert wurde. Für die genaue Berechnung des ΔCTOD bei TMF wurden effiziente FEM-Techniken erarbeitet. Zur Simulation der Rissausbreitung wurde ein automatischer FEM-Algorithmus mit inkrementeller adaptiver Neuvernetzung entwickelt, bei dem die Verformungen und inelastischen Zustandsvariablen jeweils vom alten auf das neue Netz übertragen werden. Dieser Algorithmus wurde im Software-Paket ProCrackPlast implementiert, das in Verbindung mit dem kommerziellen FEM-Code Abaqus zur Lösung dreidimensionaler Rissprobleme zur Verfügung steht. Ziel der umfangreichen experimentellen Arbeiten war es, an isothermen LCF und anisothermen TMF-Versuchen mit gekerbten Flachzugproben (SENT) das Risswachstum im Temperaturbereich von 20 °C bis 700 °C zu ermitteln. Mit Hilfe begleitender 2D FEM Simulationen wurden anhand dieser Datenbasis die Rissfortschrittskurven des Werkstoffs unter Anwendung des ΔCTOD-Konzepts bestimmt und in geeigneter, parametrisierter Form den Nutzern zur Verfügung gestellt. Die Versuche an SENT-Proben wurden mit der entwickelten Software ProCrackPlast als 3D Modell simuliert. Der Vergleich der 2D und 3D Simulationen ergab einen systematischen Unterschied im CTOD und CTOD, der mit Hilfe eines Übertragungsfaktors korrigiert wurde. Der Vergleich der 3D Berechnungen mit den Experimenten zeigte eine zufriedenstellende Übereinstimmung der er- reichten Risslänge mit der Zahl der Lastzyklen im gesamten Temperaturbereich, wobei die numerische Prognose meist auf der konservativen / sicheren Seite lag. Die Übertragbarkeit der Ergebnisse der 2D Parameteridentifikation auf 3D Risskonfigurationen mit Mixed-Mode Beanspruchung ist mit zusätzlichen Versagenshypothesen verbunden, die aufgrund fehlender Versuchsdaten im Vorhaben nicht endgültig geklärt werden konnten. Zur Validierung des Gesamtkonzeptes wurden LCF-Proben mit einem bauteil- typischen Oberflächenriss experimentell und numerisch untersucht. In der Simulation konnte die komplexe Form und Größe der Rissentwicklung zufriedenstellend (richtig) vorhergesagt werden. Die Leis- tungsfähigkeit der erarbeiteten rechnerische Bewertungsmethode wurde an weiteren TMF-Beispielen vorgestellt und diskutiert. Die Software ProCrackPlast und die viskoplastische Materialroutine wurden dem Anwenderkreis des Vorhabens zusammen mit einem Nutzer-Handbuch und Verifikationsbeispielen zur Verfügung gestellt.
Das Ziel des Forschungsvorhabens ist erreicht worden.
Vickers test ontology (VTO)
(2024)
Vickers Test Ontology (VTO) has developed for representing the Vickers testing process, testing equipment requirements, test pieces charactristics, and related testing parameters and their measurement procedure according to DIN EN ISO 6507-1 standard.
Versions info:
V2 developed using BFO+CCO top-level ontologies.
Repositories:
GitLab: https://gitlab.com/kupferdigital/process-graphs/vickers-hardness-test
GitHub: https://github.com/HosseinBeygiNasrabadi/Vickers-Test-Ontology-VTO-
MatPortal: https://matportal.org/ontologies/VTO
IndustryPortal: https://industryportal.enit.fr/ontologies/VTO
Die zunehmende geopolitische Bedeutung der Ressourcenverfügbarkeit sowie die Anforderungen an einen geschlossenen Materialkreislauf treiben die Materialforschung voran, um konventionelle Werkstoffe mit weniger kritischen Zusätzen zu legieren oder sogar vollständig mit nachhaltigeren Alternativen zu substituieren. Eine potenzielle Alternative stellen die intermetallischen Eisenaluminid-Legierungen (FeAl) dar. Im Labormaßstab wurden bereits viele Legierungskonzepte für verbesserte Hochtempera- tureigenschaften oder Duktilität erfolgreich gießtechnisch umgesetzt. Eine erfolgreiche Erprobung von FeAl-Legierungen im industriellen Maßstab stand zu Beginn des Projekts aber weiterhin aus. Ziel des Vorhabens war daher die Entwicklung von simulationsgestützten Gießkonzepten in industrienahe Gießprozesse anhand der Modelllegierung Fe-26Al-4Mo-0,5Ti-1B und die Eingrenzung der prozesstechnischen Verfahrensgrenzen durch Warmrissversuche. Erkenntnisse hieraus wurden in einen praxisorientierten, für zukünftige Anwender in KMUs zugänglichen Handlungskatalog für die gießgerechte Auslegung von Bauteilen aus Eisenaluminiden überführt. Fokus wurde insbesondere auf das Feinguss- und Kokillengussverfahren im Schleuderguss gesetzt. Neben zahlreicher Konstruktions- und Gießprozessparameter wurden auch Wärmebehandlungen und Legierungszusätze (Al, Mo, B) variiert, um den Einfluss von Legierungselementen auf Gießbarkeit, Mikrostruktur und mechanische Kennwerte zu be- stimmen. Eine umfangreiche Basis an Daten aus Mikrostrukturanalysen (Mikroskopische Bildgebung, Bestimmung von Korngrößen sowie Phasenzusammensetzungen und -anteilen, Fraktographie), mechanischen Tests (Härtemessungen, Druckversuch, Zugversuch, Warmzugversuch, Kriechversuch) sowie Messungen thermophysikalischer Eigenschaften konnte für die Modelllegierung erzeugt werden. Korrelationen dieser Informationen mit Prozessvariablen erlaubten Schlussfolgerungen zu Härtungsmechanismen und Duktilität in der Legierung und wie sie prozesstechnisch in Gieß- und Bauteilauslegung gesteuert werden können. Der erfolgreiche Abguss von hochkomplexen Bauteilgeometrien mit dünnen Wandstärken sowie optimierte Legierungszusammensetzungen zeigen Perspektiven auf neue Anwendungsfelder auf.
Das Ziel des Forschungsvorhabens ist erreicht worden.
Die Entwicklung digitaler Prozesse für die Materialwissenschaft und Werkstofftechnik muss naturgemäß auch die Charakterisierungsmethoden der Werkstoffprüfung abbilden, die oft durch eine hohe Komplexität gekennzeichnet sind. Als vorteilhaft erweist sich dabei der hohe Standardisierungsgrad, der sich z.B. in klaren Anforderungen an die eingesetzten Prüfmittel und festgelegten Vorgehensweisen ausdrückt. Diese können (und müssen) in entsprechenden digitalen Versuchsbeschreibungen abgebildet werden, wobei sich die klaren Datenstrukturen und Terminologien als vorteilhaft erweisen.
Das hochaktuelle Thema der Integration und Wiederverwendung von Wissen und Daten aus Herstellung, Bearbeitung und Charakterisierung von Materialien ('Digitalisierung von Materialien') wird in den Projekten Innovationsplattform MaterialDigital (PMD, materialdigital.de) und Materials-open-Lab (Mat-o-Lab, matolab.org) adressiert. In diesem Beitrag werden die Weiterentwicklungen in diesen Projekten hinsichtlich der Speicherung von Zugversuchsdaten gemäß einer normenkonformen (DIN EN ISO 6892-1:2019-11) ontologischen Repräsentation vorgestellt. Das umfasst den Weg von der Entwicklung einer Ontologie nach Norm, der Konvertierung von Daten aus Standardtests in das interoperable RDF-Format bis hin zur Verknüpfung von Ontologie und Daten. Letztendlich können die entsprechenden Daten in einem Triple Store abgelegt und abgefragt werden.