5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (31)
- Beitrag zu einem Tagungsband (17)
- Forschungsdatensatz (17)
- Vortrag (16)
- Buchkapitel (5)
- Forschungsbericht (4)
- Monografie (1)
- Posterpräsentation (1)
Schlagworte
- Creep (11)
- Ontology (11)
- Aging (9)
- Microstructure (7)
- Aluminium (6)
- Aluminium alloy (6)
- Additive manufacturing (5)
- EN AW-2618A (5)
- FAIR data (5)
- Shear modulus (5)
Organisationseinheit der BAM
- 5 Werkstofftechnik (92)
- 5.2 Metallische Hochtemperaturwerkstoffe (91)
- 5.5 Materialmodellierung (13)
- 9 Komponentensicherheit (12)
- 5.1 Mikrostruktur Design und Degradation (10)
- 8 Zerstörungsfreie Prüfung (10)
- 9.6 Additive Fertigung metallischer Komponenten (7)
- 8.5 Röntgenbildgebung (6)
- 8.0 Abteilungsleitung und andere (4)
- 9.4 Integrität von Schweißverbindungen (4)
Eingeladener Vortrag
- nein (16)
Performing mechanical tests at high temperatures is a nontrivial issue: Compared to room temperature testing, additional phenomena like time-dependent Deformation processes and oxidation effects raise the complexity of the material’s response, while more sophisticated test setups and additional control parameters increase the number of potential sources of error. To a large extent, these complications can be overcome by carefully following all recommendations given in the respective high temperature testing standards, but more comprehensive background information helps to identify points of specific importance in particular test campaigns. In this chapter, an overview is given on general high temperature testing issues like the appropriate choice of experimental equipment and key aspects of temperature measurement. In subsequent sections, the major static and dynamic high temperature test methods are reviewed and their Special features, as compared to testing at room temperature, are highlighted based on example data sets. Influences of specimen size and environmental effects are shortly outlined in a concluding section. In the whole chapter, a focus is set on testing of “classical” metallic high temperature materials, but many considerations are equally valid for testing of intermetallics, composites, and high temperature ceramics.
A study was made on the effect of creep loading on the precipitate radii evolution of the aluminum alloy 2618A.
The overageing process of the alloy was investigated under load at a temperature of 190 °C with stresses between 79 and 181 MPa and compared to stress free isothermal ageing. The precipitates responsible for strength were characterized using dark-field transmission electron microscopy (DFTEM). This allows the experimental Determination of radii distributions of the rod-shaped Al2CuMg precipitates and the evaluation regarding their mean precipitate radius. It was found that the mean precipitate radius enables the comparison of the different microstructural conditions of crept and uncrept samples. The mean precipitate radii of the samples experiencing creep are significantly higher than those of undeformed samples. It was shown that the acquired radii distributions are viable to determine averaged particle radii for comparison of the aged samples. A ripening process including pipe diffusion along dislocations describes the data on coarsening very well for the creep samples.