5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2020 (22) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (13)
- Vortrag (5)
- Posterpräsentation (2)
- Beitrag zu einem Sammelband (1)
- Beitrag zu einem Tagungsband (1)
Schlagworte
- LTCC (4)
- Additive manufacturing (3)
- Additive Manufacturing (2)
- Ceramics (2)
- Iron oxide nanoparticles (2)
- Machine Learning (2)
- Particle size (2)
- Reaction sintering (2)
- Sintering additives (2)
- Synchrotron Tomography (2)
- Thermoelectrics (2)
- 2PP (1)
- 3D printing (1)
- 3D-printing (1)
- ATZ (1)
- Alpha-tricalcium phosphate (1)
- Alumina (1)
- Alumina toughened zirconia (1)
- Binder Jetting (1)
- Bio Ceramics (1)
- Bioactive glass scaffold (1)
- Bone marrow-derived mesenchymal stem cell (1)
- Calcium cobaltite (1)
- Calcium manganate (1)
- Cement-based materials (1)
- Ceramic nano particles (1)
- Clay ISRU (1)
- Defect detection (1)
- Dielectric breakdown (1)
- Electron microscopy (1)
- Endothelial progenitor cell (1)
- Gas flow assisted powder deposition (1)
- Granules (1)
- Hot pressing (1)
- Hot stage microscopy (1)
- Hybrid Manufacturing (1)
- Imaging techniques (1)
- LIBS (1)
- Lattices (1)
- Layerwise Slurry Deposition (1)
- Lunar regolith (1)
- MGS-1 regolith simulant (1)
- Mars (1)
- Melting (1)
- Multilayer ceramic technology (1)
- Nano-ceramic-additive-manufacturing photoresin (1)
- Nano-powder (1)
- NanoCAM (1)
- Nanomaterials (1)
- Nanoplattform (1)
- Permittivity reduction (1)
- Plasma imaging (1)
- Porosification (1)
- Quality assurance (1)
- Reaction Sintering (1)
- Reference material (1)
- Reference nanomaterials (1)
- Reliable characterization (1)
- Scaffold (1)
- SchwarzP cells (1)
- Shadowgraphy (1)
- Sintering (1)
- Size and size distribution (1)
- Slurry (1)
- Smectite (1)
- Spray drying (1)
- Texture (1)
- Thermoelectric properties (1)
- Three-dimensional Bone tissue engineering (1)
- Transformer (1)
- Two-photon polymerization (1)
- Ultrasound (1)
- Volume specific surface area (1)
- Weibull distribution (1)
- Wet chemical etching (1)
- Zirconia (1)
- Zirconia-toughened alumina (1)
- dispersion (1)
- particle size determination (1)
- sample preparation (1)
Organisationseinheit der BAM
- 5.4 Multimateriale Fertigungsprozesse (22) (entfernen)
Eingeladener Vortrag
- nein (5)
Monodisperse iron oxide nanoparticles as reference material candidate for particle size measurements
(2020)
In order to utilize and rationally design materials at the nanoscale the reliable characterization of their physico-chemical properties is highly important, especially with respect to the assessment of their environmental or biological impact. Furthermore, the European Commission’s REACH Regulations require the registration of nanomaterials traded in quantities of at least 1 ton. Powders or dispersions where 50% (number distribution) of the constituent particles have sizes ≤ 100 nm in at least one dimension are defined as nanomaterials. This creates a need for industrial manufacturers and research or analytical service facilities to reliably characterize potential nanomaterials. Currently, BAM is developing reference nanoparticles, which shall expand the scarce list of worldwide available nano reference materials certified for particle size distribution and will also target other key parameters like shape, structure, porosity or functional properties. In this respect, materials like iron oxide or titanium dioxide are considered as candidates to complement the already available silica, Au, Ag, and polystyrene reference nanoparticles.
The thermal decomposition of iron oleate precursors in high boiling organic solvents can provide large quantities of iron oxide nanoparticles that can be varied in size and shape.[1, 2] The presence of oleic acid or other hydrophobic ligands as capping agents ensures stable dispersion in nonpolar solvents. Such monodisperse, spherical particles were synthesized at BAM and pre-characterized by electron microscopy (TEM, SEM including the transmission mode STEM-in-SEM) and dynamic light scattering comparing cumulants analysis and frequency power spectrum.
1. REACH regulations and nanosafety concerns create a strong need for nano reference materials with diverse properties.
2. Iron oxide nanoparticles are under development as new candidate reference material at BAM.
3. Narrow particle size distribution confirmed by light scattering and electron microscopy.
The 5G technology promises real time data transmission for industrial processes, autonomous driving, virtual and augmented reality, E-health applications and many more. The Low Temperature Co-fired Ceramics (LTCC) technology is well suited for the manufacturing of microelectronic components for such applications. Still, improvement of the technology such as further miniaturization is required. This study focuses on the characterization of inner metallization of LTCC multilayer modules, especially on the vertical interconnect access (VIA). Critical considerations for this characterization are delamination, pore clustering in and at the edge of the VIA, deformation, and stacking offset. A LTCC multilayer consisting of a glassy crystalline matrix with silver based VIAs was investigated by synchrotron x-ray tomography (CT). The aim of this study is to propose a multitude of structural characteristic values to maximize the information gained from the available dataset. Data analysis has been done with the open source software ImageJ as well as several additional plugins. The high-resolution CT data was evaluated through 2D slices for accessibility reasons. The segmentation of all 2000 slices to assess the different regions e.g. pores, silver and glass ceramic was done by a supervised machine learning algorithm. A quantitative evaluation of shape, deformation, and porosity of the VIA with respect to its dimensions is presented and the suitability of the characterization approach is assessed.
The 5G technology promises real time data transmission for industrial processes, autonomous driving, virtual and augmented reality, E-health applications and many more. The Low Temperature Co-fired Ceramics (LTCC) technology is well suited for the manufacturing of microelectronic components for such applications. Still, improvement of the technology such as further miniaturization is required. This study focuses on the characterization of inner metallization of LTCC multilayer modules, especially on the vertical interconnect access (VIA). Critical considerations for this characterization are delamination, pore clustering in and at the edge of the VIA, deformation, and stacking offset. A LTCC multilayer consisting of a glassy crystalline matrix with silver based VIAs was investigated by synchrotron x-ray tomography (CT). The aim of this study is to propose a multitude of structural characteristic values to maximize the information gained from the available dataset. Data analysis has been done with the open source software ImageJ as well as several additional plugins. The high-resolution CT data was evaluated through 2D slices for accessibility reasons. The segmentation of all 2000 slices to assess the different regions e.g. pores, silver and glass ceramic was done by a supervised machine learning algorithm. A quantitative evaluation of shape, deformation, and porosity of the VIA with respect to its dimensions is presented and the suitability of the characterization approach is assessed.
This paper investigates fast and inexpensive measurement methods for defect detection in parts produced by Additive Manufacturing (AM) with special focus on lattice parts made of ceramics. By Lithography-based Ceramic Manufacturing, parts were built both without defects and with typical defects intentionally introduced. These defects were investigated and confirmed by industrial X-ray Computed Tomography. Alternative inexpensive methods were applied afterwards on the parts such as weighing, volume determination by Archimedes method and gas permeability measurement. The results showed, that defects resulting in around 20% of change in volume and mass could be separated from parts free of defects by determination of mass or volume. Minor defects were not detectable as they were in the range of process-related fluctuations. Permeability measurement did not allow to safely identify parts with defects. The measurement methods investigated can be easily integrated in AM process chains to support quality control.
Practical breakdown voltage calculations using dielectric breakdown strength reference values
(2020)
Dielectric breakdown is a catastrophic failure of ceramic substrates and insulators. The use of dielectric breakdown strength (DBS) reference values for the dimensioning of such components is not straightforward, as the DBS depends on sample thickness and electrode area. This fact also hampers a valid comparison of data taken from different literature sources. Based on the empirically confirmed proportionality of DBS to the reciprocal square root of sample thickness and an approach to account for the influence of electrode area on the failure probability, a practical equation is derived to calculate the breakdown voltage for arbitrary sample thickness and electrode area from one set of DBS reference data. To validate the equation, the AC DBS of commercial alumina substrates with thicknesses ranging from 0.3 mm to 1.0 mm was performed using different printed electrodes with varying areas. The breakdown voltages comprise a range from 18 kV for thick samples to 8.5 kV for thin samples, resulting in DBS values from 17 kV/mm for 1.0 mm thick samples to 29 kV/mm for 0.3 mm thin samples, all made from the same material. The influence of electrode area is comparatively smaller. The results calculated with the proposed equation are in reasonable accordance with the measured data. Thus, the equation can be applied for a proper comparison of literature DBS data measured in different setups and for a reasonable estimation of breakdown voltages in DBS tests and applications based on reference data.
The influence of the atomization technique on the suitability of granules for dry pressing is the focus of the presented investigations. Therefore, destabilized alumina, zirconia, and zirconia toughened alumina (ZTA) slurries were spray dried and the obtained granules were used to fabricate green and finally sintered bodies for evaluation.
Granules made in a laboratory spray dryer with a two-fluid nozzle served as a reference. An ultrasonic atomizer was integrated into the same spray dryer and the influence on the granule properties was evaluated. Untapped bulk density, granule size distribution, and flowability are among the evaluated granule-related properties as well as the granule yield which is used as an indicator of the process efficiency.
Yield and flowability as most important granule properties are clearly improved when atomization is realized with ultrasound. The investigated sinter body properties include porosity, sinter body density, and biaxial strength and are as well positively affected by switching the atomization technique to ultrasound. Therefore, the Approach to improve the compressibility of granules by ultrasonic atomization, which leads to an improved microstructure, density, and strength of sintered bodies, has proven to be successful for single-component ceramics (alumina and zirconia) as well as for the multicomponent ceramic ZTA.
Reaction sintering and sintering additives for cost-effective production of thermoelectric oxides
(2020)
Thermoelectric oxides attract much interest recently. Although their thermoelectric properties are inferior to non-oxides, they exhibit distinct advantages. Thermoelectric oxides are stable in air at higher temperatures, their raw materials are less toxic, and more abundant. To enhance attractivity of these materials for industrial applications, production costs need to be reduced.
Conventionally, the legs of thermoelectric generators are sintered from green bodies of previously synthesized powder. Reaction-sintering is a fabrication method without a powder synthesis step, as the final phase is formed during the sintering from a raw material mixture. Moreover, the reduction of chemical potential during reaction-sintering is effective as an additional driving force for sintering. We show that reaction-sintering increases the densification of CaMnO3 (n-type, Sm doped). Consequently, the electrical conductivities improved by about 100 % leading to superior power factors (PF = 230 µW/mK² for CaMnO3).
Another approach to reduce the production costs is to lower the sintering temperature by adding sinter additives. The addition of 4 wt% CuO to CaMnO3 lowers the sinter temperature from 1250 °C to 1050 °C. The achieved power factor PF = 264 µW/mK is more than two times higher as reported in literature for the same dopant.
Thermoelectric materials can convert waste heat directly into electrical power by utilizing the Seebeck effect. Calcium cobaltite (Ca3Co4O9, p-type) and calcium manganate (CaMnO3, n-type) are two of the most promising oxide thermoelectric materials. The performance of these materials is evaluated by the power factor PF = S²∙σ and the figure of merit ZT = (PF ∙ T) / κ, demanding high Seebeck coefficient S, high electrical conductivity σ and low thermal conductivity κ. The latter two are increasing with increasing relative sinter density. According to theory, the relative density of ceramics can be improved by increasing the driving force for sintering. This study investigates different approaches to increase the driving force for sintering of Ca3Co4O9 and CaMnO3 to improve densities and thermoelectric properties.
The following approaches were applied: minimizing the energy input during powder synthesis by calcination, fine milling of the powder, using reaction-sintering without a powder synthesis step, and adding a transient liquid phase by sinter additives.
All different approaches led to an increased densification and thus higher electrical conductivity and higher PF. Thermal conductivity increased as well but not to the same extent. E.g. reaction-sintering increased the densification of Ca3Co4O9 (p-type) and CaMnO3 (n-type). Consequently, the electrical conductivities improved by about 100 % for both oxides leading to superior power factors (PF = 230 µW/mK² for CaMnO3). Although the thermal conductivity increased as well by 8 %, the figures of merit (ZT) were significantly higher compared to conventionally sintered bars. The addition of 4 wt% CuO as a sinter additive to CaMnO3 lowers the sinter temperature from above 1250 °C to below 1100 °C and increases the relative density. Due to the increased density, both electrical conductivity and PF increased by more than 200 % even though the sintering temperature was 150 K lower.
The possibility of creating patient-specific individual implants makes Additive Manufacturing technologies of special interest for the medical sector. For substitution of bone defects, powder based Additive Manufacturing by Binder Jetting is a suitable method to produce complex scaffold-like structures made of bioceramics with easily adapted geometries and controlled porosity. The process inherent residual porosity in the printed part, even though desired as it supports bone ingrowth, also leads to limited mechanical strength. Currently, bioceramic scaffolds made by Binder Jetting feature suitable biocompatible and biodegradable properties, while a sufficient mechanical stability is rather challenging. The purpose of this work is to apply the gas flow assisted powder deposition introduced in 2014 by Zocca et al., to the powder bed during printing of bioceramic tablets and scaffolds using α-TCP powder as feedstock. This enables exploiting the advantages of an increased powder bed density, thereby improving the mechanical properties of the printed parts.
A new approach for fabrication of ceramic components with inner channels is proposed, as a result of the combination of two additive and one subtractive manufacturing processes. In this project, porcelain parts are manufactured by the Layerwise Slurry Deposition (LSD) process, meanwhile end milling and Direct Ink Writing (DIW) are applied to create channels on the surface of the deposited ceramic. Unique to the LSD process is the Formation of a freestanding powder bed with a mechanical strength comparable to conventional slip casted ceramic green bodies. Combining these three processes allows the manufacturing of ceramic objects containing an internal path of ink, which in this case was a graphite-based ink that can be further eliminated by heat treatment to obtain a porcelain object embedded with channels. The results show the capabilities of this method and its potential to fabricate not only parts with inner channels, but also multi-material and multi-functional components (such as integrated electronic circuits).