5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (19)
- Beitrag zu einem Tagungsband (13)
- Vortrag (8)
- Forschungsbericht (1)
Sprache
- Englisch (27)
- Deutsch (8)
- Mehrsprachig (5)
- Französisch (1)
Schlagworte
- Corrosion (13)
- CCS (7)
- Fraktographie (7)
- Impurities (6)
- CCUS (5)
- Carbon steel (5)
- Schadensanalyse (5)
- CO2 quality (4)
- Pipeline network (4)
- Additive manufacturing (3)
- CO2 (3)
- Fractography (3)
- Machine Learning (3)
- Recommendations (3)
- Whole-chain CCS scenario (3)
- Additive Manufacturing (2)
- CCU (2)
- Carbon capture (2)
- Carbon capture storage (2)
- Carbon dioxide (2)
- Carbon steels (2)
- Cement (2)
- Datenbank (2)
- Deep Learning (2)
- Fahrrad (2)
- Lebensdauer (2)
- Martensitic steel (2)
- Pipelines (2)
- Schadensprävention (2)
- Steel (2)
- Superaustenite steel (2)
- Supercritical/dense phase CO2 (2)
- Utilization (2)
- Öffentliche Sicherheit (2)
- 3D (1)
- 3D Reconstruction (1)
- 3D metallography (1)
- 3D-Metallographie (1)
- Aluminium Alloy (1)
- Anticorrosion (1)
- Aquifer fluid (1)
- Austenitic steel 316L (1)
- Automation (1)
- Bruchflächen (1)
- CCUS, supercritical/dense phase CO2, carbon steels, martensitic steel, superaustenite steel, droplet corrosion (1)
- CO2 Corrosion (1)
- CO2 pipeline transport (1)
- CO2-Speicherung (1)
- Capture (1)
- Carbon (1)
- Carbon capture, utilization and storage technology (1)
- Casing (1)
- Cellular substructure (1)
- Characterisation (1)
- Classification (1)
- Coating (1)
- Condensate (1)
- Condensation (1)
- Contact fatigue (1)
- Corrosion and storage (CCUS) technology (1)
- Corrosion costs (1)
- Corrosion pits (1)
- Corrosion protection (1)
- Coûts de la corrosion (1)
- Crack arrest (1)
- Crevice corrosion (1)
- Defects (1)
- Dense phase (1)
- Droplet (1)
- Droplet corrosion (1)
- Electrochemical characterisation (1)
- Environment (1)
- Fatigue (1)
- Fatigue crack propagation stages (1)
- Fatigue striations (1)
- Fraktografie (1)
- Gefügeanalyse (1)
- Gefügerekonstruktion (1)
- Geothermal (1)
- Heat accumulation (1)
- Impact damage (1)
- In-situ ED-XRD (1)
- In-situ Process Monitoring (1)
- In-situ process monitoring (1)
- Inclusion cluster (1)
- Inclusion size (1)
- Injection (1)
- Inter layer time (1)
- KI (1)
- Korrosion (1)
- Kunststoffe (1)
- Laser powder bed fusion (1)
- Melt pool boundary (1)
- Metallography (1)
- Micro-shrinkages (1)
- Microstructural characterization (1)
- Microstructure (1)
- Microstructure analysis (1)
- Microstrucure reconstruction (1)
- Mis-match (1)
- Multiple cracks (1)
- Non-destructive Materials (1)
- Non-metallic inclusions (1)
- Oxyfuel (1)
- Pitting (1)
- Pitting corrosion (1)
- Polyaniline (1)
- Pores (1)
- Preventive strategies (1)
- Process development (1)
- Protection (1)
- REM (1)
- Reliability (1)
- Reproducibility (1)
- Roboter (1)
- Safety (1)
- Schwingbrüche (1)
- Schwingstreifen (1)
- Scratches (1)
- Serial sectioning (1)
- Serienschnitte (1)
- SiO2 (1)
- Standardisation (1)
- Statistics (1)
- Storage (1)
- Stratégies deprévention (1)
- Symbolik (1)
- Thermography (1)
- Topografie (1)
- Transmission electron microscopy (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (41)
- 5.1 Mikrostruktur Design und Degradation (41)
- 7 Bauwerkssicherheit (19)
- 7.6 Korrosion und Korrosionsschutz (19)
- 9 Komponentensicherheit (8)
- 9.0 Abteilungsleitung und andere (5)
- 9.4 Integrität von Schweißverbindungen (4)
- 8 Zerstörungsfreie Prüfung (2)
- 8.0 Abteilungsleitung und andere (2)
- 9.6 Additive Fertigung metallischer Komponenten (2)
Eingeladener Vortrag
- nein (8)
In this work, the focus was set on the corrosion process of condensate as drops on the surface of carbon steels (X52, X70), martensitic steel UNS S41500, and superaustenite UNS N08031 in CO2 atmosphere with impurities at 278 K (to simulate the transportation condition in a buried pipeline). Exposure tests were performed at both normal pressure and high pressure where CO2 is supercritical or in dense phase. The drop, 1 ‑ 10 μL in volume, was prepared by dropping CO2 saturated ultra-pure water onto the surface of steel coupons in a one-liter-autoclave. The CO2 gas stream, simulating the oxyfuel flue gas with varying concentration of impurities (SO2 and O2 ), was then pumped into the autoclave to observe the condensation and corrosion impacts of impurities. Comparable exposure tests were carried out with the same gas mixture and the same volume of water as vapor to observe the drop formation and the corrosion process that follows. The wettability and stability of drops on the surface of steel coupons in CO2 supercritical/dense phase environment was evaluated additionally by contact angle measurement.
Carbon Capture and Storage (CCS) is identified as an excellent technology to reach the target of CO2 reduction. However, the safety issue and cost effectiveness hinder the future of CCS. For the reliability and safety issues of injection wells the corrosion resistance of the materials used needs to be determined.
In this study, representative low cost materials including carbon steel 1.8977 and low alloyed steel 1.7225 were embedded in cement to mimic the realistic casing-cement interface. Electrochemical studies were carried out using these metal-cement specimens in comparison with those made of metal only in CO2 saturated synthetic aquifer fluid, at 333 K, to reveal the effect of cement on the steel performance. The results showed the protective effect of cement on the performance of pipeline metals during polarisation process. However, the corrosion current density was high in all cases, with and without cement, indicating that the corrosion resistance of these materials is low. This conclusion was supported by the surface analysis of the polarized specimens, which revealed both homogenous and pitting corrosions.
The research focus of this study was set on the corrosion process of condensate as droplets on the surface of carbon steels (X52, X70) martensitic steel UNS S41500, and super austenite UNS N08031 in CO2 atmosphere with impurities at 278 K (to simulate the offshore transportation condition in a buried pipeline). The possibility of dew/droplet formation on the steel surface and wetting behavior of corresponding materials were evaluated by contact angle measurement in dense CO2 at 278 K. To observe the effect of impurities (SO2 and O2) on droplet corrosion process, exposure tests were carried out in the mixed atmosphere with a drop, 1 ‑ 10 µL in volume, of CO2 saturated ultra-pure water on steel surface. Comparable exposure tests were carried out with the same gas mixture and the same volume of water, as vapor, to observe the droplet formation and the corrosion process that follows. Effects of surface roughness on the droplet formation and its corrosion process were further studied and showed no significant role upon long time exposure. The results from droplet experiments were compared to those from the bulk electrolyte for the further recommendation on the quality control of gas stream along with the use of carbon steels as transport pipelines in CCS - Carbon Capture and Storage system.
This work examined the droplet corrosion of CO2 pipeline steels caused by impurities in CO2 supercritical/dense phase at 278 K, simulating the underground transport condition. The wetting properties of carbon steels (X52 and X70) as well as martensitic steel UNS S41500, and superaustenite UNS N08031 were studied by contact angle measurement, revealing reactive wetting behavior of carbon steels. Exposure tests with CO2 saturated water droplet on steel surface showed that the impurities (220 ppmv SO2 and 6700 ppmv O2) diffused into the droplet and then reacted with metal coupons in supercritical/dense phase condition, forming the corrosion product instantly during pumping process. Due to the active wetting behavior, the carbon steels suffered from heavily attack, while negligible corrosion product was observed in cases of martensitic steel UNS S41500 and superaustenite UNS 08031 coupons. Condensation experiments that were carried out on fresh polished coupons in CO2 with 1200 ppmv H2O showed that the formation and aggregation of droplet is dependent on the presence of impurities. Without SO2 and O2, the same concentration of H2O did not cause observable corrosion process after a week of exposure. With 220 ppmv SO2 and 6700 ppmv O2 even low water concentration (5-30 ppmv) still resulted in heterogeneous nucleation and subsequent growth of droplets, leading to corrosive process on carbon steel surface albeit to a lesser extent.
Im Rahmen der Erstellung einer fraktographischen online-Datenbank an der BAM wurden systematisch Schwingversuche an einem Sinterstahl vorgenommen, dessen Sinterdichte variiert wurde. Die erzeugten Bruchflächen wurden analysiert, mit der Literatur verglichen und Datensätze in die Datenbank eingefügt.
Im Rahmen der DGM/DVM AG Fraktographie wird an der BAM eine fraktographische online-Datenbank aufgebaut. Während von metallischen Werkstoffen viele Beispiele vorliegen, die auch gut verstanden sind, sind die Brüche von Kunststoffen bislang weniger prominent vertreten. Eine teils ungeklärte Frage ist, in welcher Form sich an Kunststoffen klassische Schwingbrüche nachweisen lassen, wie sie von metallischen Werkstoffen bekannt sind. Der Vortrag zeigt einige Beispiele im Detail und stellt diese zur Diskussion.
Recent studies have shown that even at a very low concentration of impurities (less than 100 ppmv of SO2, NO2, O2 and H2O) the droplet formation and condensation of sulfuric and nitric acids in dense phase CO2 are possible and observable. To reveal the mechanism of droplet corrosion in dense phase CO2 at high pressure and low temperature, further studies on factors that affect wettability and resulting corrosion behaviors of transport pipeline steels are needed. In this study, effects of surface morphology were investigated by varying surface roughness of carbon steel coupons exposed to CO2 stream containing impurities to measure the wettability by contact angle and to observe the condensation as well as possible droplet corrosion that followed. Other considered factors were: pH of the droplet, temperature, droplet volume, and exposure time.
Carbon Capture and Storage (CCS) is identified as an excellent technology to reach the target of CO2 reduction. However, the safety issue and cost-effectiveness hinder the future of CCS. For the reliability and safety issues of injection wells, the corrosion resistance of the materials used needs to be determined.
In this study, representative low-cost materials including carbon steel 1.8977 and low alloyed steel 1.7225 were investigated in simulated pore water at 333 K and under CO2 saturation condition to represent the worst-case scenario: CO2 diffusion and aquifer fluid penetration. These simulated pore waters were made from relevant cement powder to mimic the realistic casing-cement interface. Electrochemical studies were carried out using the pore water made of cement powder dissolved in water in comparison with those dissolved in synthetic aquifer fluid, to reveal the effect of cement as well as formation water on the steel performance. Two commercially available types of cement were investigated: Dyckerhoff Variodur® and Wollastonite. Variodur® is a cement containing high performance binder with ultra-fine blast furnace slag which can be used to produce high acid resistance concrete. On the other hand, Wollastonite is an emerging natural material mainly made of CaSiO3 which can be hardened by converting to CaCO3 during CO2 injection.
The results showed the pH-reducing effect of CO2 on the simulated pore water/aquifer (from more than 10 to less than 5) leading to the active corrosion process that happened on both 1.8977 and 1.7225. Electrochemical characterization showed negative free corrosion potential and polarisation curves without passive behaviors. The tested coupons suffered from pitting corrosion, which was confirmed by surface analysis. Interestingly, basing on the pit depth measurements from the tested coupons and the hardness of cement powder, it is suggested that Variodur® performed better than Wollastonite in both aspects. The electrochemical data was compared to that resulted from exposure tests to give a recommendation on material selection for bore-hole construction.
This contribution provides current findings regarding materials susceptibility for carbon capture, utilization and storage (CCUS) applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2-stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide material recommendations for certain parts.