5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2018 (9) (entfernen)
Dokumenttyp
- Vortrag (4)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (2)
- Zeitschriftenartikel (1)
Sprache
- Englisch (9) (entfernen)
Referierte Publikation
- nein (9) (entfernen)
Schlagworte
- Coarsening (7)
- Degradation (6)
- Alloy 2618A (5)
- Aluminium (5)
- S-phase (5)
- Dark-field transmission electron microscopy (3)
- Dark-field transmission electron microscopy (DFTEM) (2)
- Transmission electron microscopy (2)
- Aging (1)
- Alloy 2818A (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (9) (entfernen)
Eingeladener Vortrag
- nein (4)
The influence of heat treatment and creep loading on the microstructure of an Al-Cu-Li alloy was investigated. Especially the formation of different precipitates (T1 and Theta') were characterized and the microstructural changes under different ageing conditions (with and without external strain) were investigated to determine the effect od stress on the ageing process.
The influence of heat treatment and creep loading on the microstructure of an Al-Cu-Li alloy was investigated. Especially the formation of different precipitates (T1 and Theta') were characterized and the microstructural changes under different ageing conditions (with and without external strain) were investigated to determine the effect od stress on the ageing process.
Materials subjected to high-temperature service conditions will change their microstructure with time. Associated with this aging process is a change of mechanical properties as well as a change of damage mechanisms. Within the scope of the FVV project Aging and Lifetime, Fraunhofer IWM in Freiburg and BAM in Berlin (both Germany) experimentally characterized the widespread high-temperature aluminum alloy EN AW-2618A in different overaging states. Based on the experimental findings, models for numerical lifetime assessment with the finite-element method were implemented.