5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2018 (125) (entfernen)
Dokumenttyp
- Vortrag (68)
- Posterpräsentation (23)
- Beitrag zu einem Tagungsband (18)
- Zeitschriftenartikel (12)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (1)
- Sonstiges (1)
Sprache
- Englisch (125) (entfernen)
Referierte Publikation
- nein (125) (entfernen)
Schlagworte
- Additive manufacturing (8)
- Coarsening (8)
- Additive Manufacturing (7)
- Alloy 2618A (6)
- Aluminium (6)
- CCUS (6)
- Corrosion (6)
- Crack growth (6)
- Creep (6)
- Degradation (6)
- Fatigue (6)
- Carbon steels (5)
- Glass (5)
- Martensitic steel (5)
- S-phase (5)
- Superaustenite steel (5)
- Supercritical/dense phase CO2 (5)
- Vickers (5)
- Water speciation (5)
- DCB (4)
- Droplet corrosion (4)
- Soda-lime silicate glass (4)
- CCS (3)
- Concrete (3)
- Dark-field transmission electron microscopy (3)
- Ferritic-martensitic steels (3)
- High temperature corrosion (3)
- Hydrogen (3)
- Inconel 686 (3)
- Microplastics (3)
- Nanoparticles (3)
- Neutron diffraction (3)
- PE-HD (3)
- Powder (3)
- Rotor blade (3)
- Sintering (3)
- Transmission electron microscopy (3)
- Wind turbine blades (3)
- Adiabatic calorimeter (2)
- Air-coupled ultrasonic testing (2)
- Airborne ultrasonic testing (2)
- Alumina (2)
- Analysis (2)
- Anisotropy (2)
- Carbon capture (2)
- Carbon dioxide (2)
- Ceramic (2)
- Coating (2)
- Composite (2)
- Composites (2)
- Crystal plasticity (2)
- Crystallization (2)
- Damage (2)
- Dark-field transmission electron microscopy (DFTEM) (2)
- Deuterium (2)
- Diffusion (2)
- Diffusion coefficient (2)
- Fatigue of sandwich shell structures (2)
- Ferroelectret (2)
- Foaming (2)
- Glass composition (2)
- Impurities (2)
- Injection (2)
- Laser ablation in liquid (2)
- Long-term behavior (2)
- Metal seal (2)
- Microstructure (2)
- Non-destructive testing (2)
- Phase change material (2)
- Residual Stresses (2)
- Residual stress (2)
- Residual stresses (2)
- Ressidual stress (2)
- SLM (2)
- Salt eutectics (2)
- Scale-bridging (2)
- Selective Laser Melting (2)
- Selective laser melting (2)
- TED-GC-MS (2)
- Temperature (2)
- Thermal energy storage (2)
- Thermogravimetry (2)
- Thermomechanics (2)
- Titanium oxide (2)
- ToF-SIMS (2)
- UV-irradiation (2)
- VSSA (2)
- Virtual experiments (2)
- Wind turbine (2)
- X-ray laminography (2)
- XANES (2)
- 316L (1)
- 3D glass structure model (1)
- 3D printing (1)
- 3D-printing (1)
- 9-12% Cr ferritic-martensitic steels (1)
- AISI 304L (1)
- Accelerated integration scheme (1)
- Active thermography (1)
- Advanced wastewater treatment (1)
- Aggressive environement (1)
- Aggressive environment (1)
- Aggressive gases (1)
- Aging (1)
- Al-Li alloys (1)
- Alloy 2818A (1)
- Aluminum (1)
- Aluminum alloy (1)
- Amorphous silica (1)
- Annealing (1)
- Aquifer (1)
- Artefact (1)
- Atomic packing factor (1)
- Austenitic stainless steel (1)
- Austenitic steel (1)
- Bio Ceramics (1)
- Bioactive glass (1)
- Biodiesel (1)
- Bioresorbable (1)
- Brittle / ductile fracture behavior (1)
- Brown-rot fungi (1)
- Calcination (1)
- Carbon steels (1)
- Carbon fibre-reinforced-plastics (1)
- Carbon storage (1)
- Ccs (1)
- Cement (1)
- Ceramic springs (1)
- Ceramics (1)
- Chromatography (1)
- Co2-Storage (1)
- Complex loading (1)
- Composite structures (1)
- Coniophora puteana (1)
- Continnum damage model (1)
- Corrosion Fatigue (1)
- Crack Propagation (1)
- Crack propagation (1)
- Crack propagation analysis (1)
- Creep, Creep Rupture, and Stress Rupture (1)
- Creep-fatigue (1)
- Critical energy release rate (1)
- Crystal Orientation (1)
- Cycle jump (1)
- Cyclic loading (1)
- Cyclic oxidation (1)
- Cyclic softening (1)
- Damage evolution (1)
- Dentine (1)
- Destabilization (1)
- Dielectric strength (1)
- Diesel (1)
- Diffraction (1)
- Diffraction contrast (1)
- Dislocation (1)
- Dissolved water (1)
- Distributed fibre optic sensors (1)
- EBSD (1)
- EDXRD (1)
- Electron microscopy (1)
- Enamel (1)
- Environmental stress cracking (ESC) (1)
- Environmentally assisted cracking (1)
- FCH JU (1)
- Fatigue crack propagation (1)
- Fatigue damage (1)
- Fatigue fracture (1)
- Fatigue of sandwich structures (1)
- Flow Coefficient (1)
- Fluoride nanoparticles (1)
- Fluorolytic sol−gel (1)
- Fourier transform infrared spectroscopy (1)
- Fracture mechanics (1)
- Full Notch Creep Test (FNCT) (1)
- Gasabgabe (1)
- Gasgehalt (1)
- Geometrical factors (1)
- Geopolymers (1)
- Geothermal (1)
- Glas (1)
- Glass fiber reinforced polymers (1)
- Grain boundaries (1)
- Granules (1)
- Heat treatment (1)
- High - temperature corrosion (1)
- High Cycle Fatigue (1)
- High Temperature Corrosion (1)
- High temperature (1)
- High-temperature corrosion (1)
- Horizon 2020 (1)
- Hot Press (1)
- Hot isostatic pressing (HIP) (1)
- Hydrogen permeability (1)
- Hydrogen permeation (1)
- IN718 (1)
- Imaging techniques (1)
- Implant failures (1)
- In situ (1)
- In-situ (1)
- In718 (1)
- Inconel 625 (1)
- Inconel 686 coating (1)
- Indentation hardness (1)
- Initial attachment (1)
- Interface (1)
- Interfacial shear strength (1)
- Inverse ostwald ripening (1)
- Laser (1)
- Laser Cladding (1)
- Laser cladding (1)
- Laser curing (1)
- Lifetime prediction (1)
- Lightweight materials (1)
- Limestone Filler (1)
- Long-term storage (1)
- Low Cycle Fatigue (LCF) (1)
- Low cycle fatigue (1)
- Manufacturing (1)
- Martensitic steel (1)
- Mass transport (1)
- Material characterization (1)
- Material defects (1)
- Material oxidation (1)
- Mechanical and thermal testing (1)
- Metallic components (1)
- Metformin (1)
- Micro-shrinkages (1)
- Micromechanical model (1)
- Microsegregation (1)
- Microstructural evolution (1)
- Microstructure evolution (1)
- Mikroplastik (1)
- Molecular dynamics (1)
- Multilayer (1)
- Multilayer technology (1)
- Nano-powder characterization (1)
- Nanomaterial screening (1)
- Nickel based coatings (1)
- Nickel-base superalloy (1)
- Nickel-base superalloys (1)
- Optical backscatter reflectometry (1)
- Optical fibre (1)
- Oxide scale (1)
- P92 steels (1)
- Particle Size Distribution (1)
- Particle morphology (1)
- Phase field simulation (1)
- Phase-field (1)
- Photocatalysis (1)
- Phytolith (1)
- Polyaniline (1)
- Polymer (1)
- Polymer matrix composites (1)
- Porcelain (1)
- Porosity (1)
- Powdered activated carbon (1)
- Precipitation (1)
- Pressure-assisted sintering (1)
- Pull-out composite materials (1)
- Rafting (1)
- Reference Material (1)
- Relaxation (1)
- Relaxation tests (1)
- Relaxationsphänomene (1)
- Resistance stress (1)
- Rheology (1)
- Rhodonia placenta (1)
- Risswachstum (1)
- SEM wood characterization (1)
- SIMS (1)
- Safety assessment (1)
- Sandwich (1)
- Scanning transmission electron microscopy (STEM) (1)
- Sewage treatment plant (1)
- SiO2 (1)
- Silicate Glasses (1)
- Silicatglas (1)
- Silicon Carbide (1)
- Simulation of concrete (1)
- Single crystal superalloys (1)
- Single-crystals (1)
- Sinter additive (1)
- Sliding simulation (1)
- Soil sample (1)
- Spray drying (1)
- Steel (1)
- Structural health monitoring (SHM) (1)
- Structured heating (1)
- Subsurface defects (1)
- Sulfidation (1)
- Superaustenite steel (1)
- Supercritical/dense phase CO 2 (1)
- Surface Nucleation (1)
- Swept wavelength interferometry (SWI) (1)
- TAHYA (1)
- TED (1)
- Texturation (1)
- Thermal degradation (1)
- Thermo-mechanical fatigue (1)
- Thermoanalysis (1)
- Thermoanalytical Methods (1)
- Thermoelectric generator (1)
- Thermoelectric oxide (1)
- Thermoelectrics (1)
- Thermomechanical Fatigue (TMF) (1)
- Thin tribofilm (1)
- Tooth wear (1)
- Transducers (1)
- Ultrasound (1)
- Under cyclic loading (1)
- VCSEL (1)
- Vacancies (1)
- Very high cycle fatigue (1)
- Viscoplasticity (1)
- Volume Fraction (1)
- Wasser (1)
- Waste water (1)
- Withstand voltage tests (1)
- Wood protection (1)
- X-ray refractography (1)
- XRD (1)
- laser cladding (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (125) (entfernen)
Eingeladener Vortrag
- nein (68)
Powder based Additive Manufacturing (AM) processes are widely used for metallic and polymeric materials, but rarely commercially used for ceramic materials, especially for technical ceramics. This seemingly contradicting observation is explained by the fact that in powder based AM, a dry flowable powder needs to be used. Technical ceramics powders are in fact typically very fine and poorly flowable, which makes them not suitable for AM. The layerwise slurry deposition (LSD) is an innovative process for the deposition of powder layers with a high packing density for powder based AM. In the LSD process, a ceramic slurry is deposited to form thin powder layers, rather than using a dry powder This allows the use of fine powders and achieves high packing density (55-60%) in the layers after drying. When coupled with a printing head or with a laser source, the LSD enables novel AM technologies which are similar to *Denotes Presenter 42nd International Conference & Exposition on Advanced Ceramics & Composites 127 Abstracts the 3D printing or selective laser sintering, but taking advantage of having a highly dense powder bed. The LSD -3D printing, in particular, offers the potential of producing large (> 100 mm) and high quality ceramic parts, with microstructure and properties similar to traditional processing. This presentation will give an overview of the milestones in the development of this technology, with focus on the latest results applied both to silicate and to technical ceramics.
Powder bed -based technologies are amongst the most successful Additive Manufacturing (AM) techniques. "Selective laser sintering/melting" (SLS/SLM) and "binder jetting 3D printing" (3DP) especially are leading AM technologies for metals and polymers, thanks to their high productivity and scalability. In this context, the "layerwise slurry deposition" (LSD) has been developed as a layer deposition method which enables the use of SLS/SLM and 3DP technologies for advanced ceramic materials. LSD consists in the layer-by-layer deposition of a ceramic slurry by means of a doctor blade. Each layer is deposited and dried to achieve a highly packed powder layer, which can be used for SLM or for 3DP. This technique offers high flexibility in the ceramic feedstock used, especially concerning material and particle size, and is capable of producing parts with physical and mechanical properties comparable to traditionally shaped parts. In this presentation, the LSD technique will be introduced and several examples of application to porcelain, SiC and alumina products will be reported.
In powder-based Additive Manufacturing (AM) processes, an object is produced by successively depositing thin layers of a powder material and by inscribing the cross section of the object in each layer. The main methods to inscribe a layer are by binder jetting (also known as powder 3D printing) or by selective laser sintering/melting (SLS/SLM).
Powder-based AM processes have found wide application for several metallic, polymeric and also ceramic materials, due to their advantages in combining flexibility, easy upscaling and (often) good material properties of their products.
The deposition of homogeneous layers is key to the reproducibility of these processes and has a direct influence on the quality of the final parts. Accordingly, powder properties such as particle size distribution, shape, roughness and process related properties such as powder flowability and packing density need to be carefully evaluated.
Due to these requirements, these processes have been so far precluded to find commercial use for certain applications. In the following, two outstanding cases will be presented.
A first example is that powder-based AM processes are widely used for many metallic and polymeric materials, but they find no commercial application for most technical ceramics.
This seemingly contradicting observation is explained by the fact that in powder based AM, a dry flowable powder needs to be used. The processing of technical ceramics in fact typically requires very fine and poorly flowable powder, which makes them not suitable for the standard processes. There have been several approaches to adapt the raw materials to the process (e.g. by granulation), but in order to maintain the superior properties of technical ceramics it seems necessary to follow the opposite approach and adapt the process to the raw materials instead.
This was the motivation for developing the Layerwise Slurry Deposition (LSD), an innovative process for the deposition of powder layers with a high packing density. In the LSD process, a ceramic slurry is deposited to form thin powder layers, rather than using a dry powder. This allows achieving high packing density (55-60%) in the layers after drying. It is also important, that standard ceramic raw materials can be used. When coupled with a printing head or with a laser source, the LSD enables novel AM technologies which are similar to 3D printing or selective laser sintering, but taking advantage of having a highly dense powder bed.
The LSD -3D printing, in particular, offers the potential of producing large (> 100 mm) and high quality ceramic parts, with microstructure and properties similar to traditional processing. Moreover, due to the compact powder bed, no support structures are required for fixation of the part in the printing process.
Figure 1 shows the schematics of the working principle of the LSD-3D print and illustrates some examples of the resolution and features achievable.
The second outstanding case here described is the application of powder-based AM in environments with reduced or zero gravity. The vision is to be able to produce repair parts, tools and other objects during a space mission, such as on the International Space Station (ISS), without the need of delivering such parts from Earth or carrying them during the mission. AM technologies are also envisioned to play an important role even for future missions to bring mankind to colonize other planets, be it on Mars or on the Moon. In this situation, reduced gravity is also experienced (the gravitational acceleration is 0.16 g on the Moon and 0.38 g on Mars).
These environments cause the use of AM powder technologies to be very problematic: the powder layers need to be stabilized in order to avoid dispersion of the particles in the chamber. This is impossible for standard AM powder deposition systems, which rely on gravitation to spread the powder.
Also in this case, an innovative approach has been implemented to face this technological challenge. The application of a gas flow through a powder has a very strong effect on its flowability, by generating a force on each particle, which is following the gas flow field. This principle can be applied in a simple setup such as the one shown in Figure 2.
In this setup, the gas flow causes an average pressure on the powder bed in direction of the arrows, generating a stabilizing effect which acts in the same direction of the gravitational force. This effect can be used in addition to normal gravity on Earth to achieve a better stabilization of 3D printed parts in the powder bed. In this case, even a significant increase of packing density of the powder was measured, compared to the same experimental setup without gas flow. This is due to the fact that the force on each single particle follows the gas flow field, which is guiding the particles to settle between the pores of the powder bed, thus achieving an efficient packing.
The same principle can be applied in absence of gravitation, where the gas flow acts to stabilize the powder layers. It has been shown that ceramic powder could be deposited in layers and laser sintered in µ-gravity conditions during a DLR (Deutsches Zentrum für Luft- und Raumfahrt) campaign of parabolic flights, as shown in Figure 2. A follow-up campaign is dedicated to the deposition of metallic (stainless steel) powder in inert atmosphere and to study the effects of laser melting in µ-gravity.
In conclusion, the description of these two example cases shows how the development of novel technological processes can address some of the limitations of standard powder-based AM, in order to enable the use of new materials, such as technical ceramics, or to tackle the challenges of AM in space.
Effects of various geometrical and physical factors, as well as the method of data reduction (analysis of
experimental forceedisplacement curves) on the values of local interfacial strength parameters (local IFSS, td, and critical energy release rate, Gic) determined by means of a single fiber pull-out test are discussed. Experimental results of our pull-out tests on several fiberepolymer matrix systems showed that td and Gic weakly depended on geometrical factors. However, the pull-out test appeared to be sensitive to the conditions of specimen formation and testing, such as changing the nature of the contacting surfaces (fiber sizing) and the fiber pull-out rate. Of several methods of td and Gic Determination from a forceedisplacement curve, the most reliable and reproducible one is the approach based on the values of the maximum force recorded in a pull-out test and the interfacial frictional force immediately after fiber debonding.
The Topic of the presentationis a discussion on defects which can cause failure in cyclically loaded metallic components. Although also touching Features such as material defects such as pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches (which are not considered in the design process) which origin in manufacturing, and others the presentation concentrates on non-metallic inclusions. It is prefaced by an introduction to the life cycle of a fatigue crack from initiation up to fracture. Special emphasis is put on the fact that only cracks which are not arrested during one of their distinct Propagation stages can grow to a critical size.
Effective hydrogen storage capacities are prerequisite for an efficient energy provision using fuel cells. Since glass has low intrinsic hydrogen permeability, it is a promising material for hydrogen storage containers as well as hydrogen diffusion barriers. Previous studies on oxidic glasses suggest a correlation between the glass composition and hydrogen permeation that was derived mainly from silica glass. In the present study, we concentrate on the relationship between thermodynamic (i.e., configurational entropy) and topologic (i.e., free volume, network polymerization) parameters. Experimental data were gathered well below the glass transition temperature, excluding significant effects caused by structural relaxation and chemical dissolution of hydrogen. The results of seven analysed glasses on the SiO2-NaAlO2 joint showed that the hydrogen permeability in fully polymerized glasses cannot solely be derived from the total free volume of the glass structure. Hence, evidence is provided that the size distribution of free volume contributes to hydrogen solubility and diffusion. Additionally, the results indicate that the configurational heat capacity ΔCp at Tg affects the hydrogen permeability of the investigated glasses.
Efficient energy provision using fuel cells requires effective hydrogen storage capacities. Glass is a material of low intrinsic hydrogen permeability and is therefore a promising material for hydrogen storage containers or diffusion barriers. Pioneer work on oxidic glasses seems to indicate a correlation between glass composition and hydrogen permeation, which was mainly derived from the behavior of silica glass. In this study, we focus on the relationship between topologic (free volume; network polymerization) and thermodynamic (configurational entropy) glass parameters. Experiments were performed well below the glass transition temperature, which excludes significant structural relaxation and chemical dissolution of hydrogen. The compositional dependence of seven glasses on the SiO2-NaAlO2 join pointed out that in fully polymerized glasses the H2 permeability cannot be solely derived from the total free volume of the glass structure. Hence, evidence is provided that the size distribution of free volume contributes to hydrogen diffusion and solubility. Additionally, results indicate that hydrogen permeability of the glasses is affected by the configurational heat capacity ΔCp at Tg.
Premature failure of glass under load is caused by sub-critical crack growth (SCCG) originate from microscopic flaws at the surface. While SCCG is related to the humidity of the ambient atmosphere, leading to stress corrosion phenomena at the crack tip, the detailed mechanism and the effect of different network formers are still not fully understood. For more clarity, various soda silicate glasses with a second network former were investigated by double cantilever beam technique: Na2O*Al2O3*SiO2 (NAS), Na2O*B2O3*SiO2 (NBS), Na2O*PbO*SiO2 (NPbS).
Three effects on the crack growth velocity, v, versus stress intensity, KI, curves were found out. The slope in region I, which is limited by corrosion, increases in the order NAS < NBS ≲ NPbS. The velocity range of region II reflecting the transition between corrosion effected and inert crack growth (region III), varies within one order of magnitude between the glasses. The KI region of inert crack growth strongly scatters between 0.4 and 0.9 MPam1/2. For comparison, crack growth at different humidity in commercial soda lime silicate glass (NCS) was measured.