5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (41)
Sprache
- Englisch (41)
Referierte Publikation
- ja (41) (entfernen)
Schlagworte
- Glass (7)
- Crystallization (6)
- EBSD (4)
- Sintering (4)
- Vickers indentation (4)
- NMR spectroscopy (3)
- Bioactive glass (2)
- Crack healing (2)
- Diopsid (2)
- Foaming (2)
- Glass ceramic (2)
- Glass transition (2)
- Infrared spectroscopy (2)
- Internal friction (2)
- SEM (2)
- Stress intensity factor (2)
- Superconducting magnet (2)
- Water content (2)
- Water speciation (2)
- 3D etching (1)
- Al2O3 (1)
- Alkali aluminosilicate glasses (1)
- Alkali and alkaline earth silicate and borate glass (1)
- Alumina coatings (1)
- Aluminosilicate glasses (1)
- Analytical scanning electron microscopy (1)
- Artificial weathering (1)
- Automated analysis (1)
- Batch reactions (1)
- Behmite (1)
- Bioactive Glass (1)
- Borate (1)
- Borosilicate glass (1)
- Brittle fracture (1)
- Bubble formation (1)
- Calculated intrinsic fracture toughness (1)
- Coating (1)
- Coefficient of thermal expansion (1)
- Corrosion (1)
- Crack growth (1)
- Crack growth in air (1)
- Crosslinking (1)
- Crystal growth (1)
- Crystal growth velocity (1)
- Crystal morphology (1)
- Crystal orientation (1)
- DCB (1)
- DCB geometry (1)
- Degradation (1)
- Differential scanning calorimetry (1)
- Efficiency (1)
- Elastic constants (1)
- Epoxy resin (1)
- Exposed metal sites (1)
- Facilitated activation (1)
- Ferrous phosphate hydrate (1)
- Fracture surface energy (1)
- Fresnoite (1)
- Geothermal (1)
- Glass Ceramic (1)
- Glass capillaries (1)
- Glass crystallization stress (1)
- Glass forming melts (1)
- Glass manufacturing (1)
- Glass powder (1)
- Glass-ceramic (1)
- Glass-ceramics definition (1)
- Growth kinetics (1)
- Growth rate (1)
- High pressure (1)
- High temperature corrosion (1)
- High-temperature corrosion (1)
- High-temperature oxidation (1)
- Hydrogen diffusivity (1)
- Hydrogen storage (1)
- Hydrous glass (1)
- Inconel 625 (1)
- Indentation fracture toughness (1)
- Ion beam erosion Sectioning (1)
- Ionic porosity (1)
- JMAK model (1)
- Long-term calculation (1)
- Low expansion (1)
- MOF-74 (1)
- Martensitic steels (1)
- Master curve (1)
- Mechanical properties (1)
- Microhardness (1)
- Microstructure (1)
- Milling (1)
- Mixed-linkers (1)
- Modeling (1)
- Moisture (1)
- Nb3Sn (1)
- Nucleation (1)
- Nydrogen melting (1)
- Orientation (1)
- Oxidation protection (1)
- Oxide coatings (1)
- Oxyfuel (1)
- Permeability (1)
- Phase transformations (1)
- Phosphate (1)
- Photovoltaic modules (1)
- Polymer (1)
- Polyurethane (1)
- Raman spectroscopy (1)
- Relaxation (1)
- Resonance testing (1)
- Roughness (1)
- Sample preparation (1)
- Sand blasting (1)
- Scaffolds (1)
- Shear thinning (1)
- Silicate glass (1)
- Silicoborate glasses (1)
- Silver metallization paste (1)
- Slow crack growth (1)
- Soda lime silicate glass (1)
- Soda-lime silicate glass (1)
- Soda-lime-silica (1)
- Soda-lime-silica glass (1)
- Sodium ion batteries (1)
- Sol-gel coating (1)
- Stable crack growth (1)
- Steel (1)
- Steel P92 (1)
- Stress intensity (1)
- Stress-corrosion (1)
- Stress-strain behavior (1)
- Stress-strain-behavior (1)
- Structural defects (1)
- Subcritical crack growth (1)
- Supersaturation (1)
- Surface crystallization (1)
- Surface energy (1)
- Surface nucleation (1)
- Synchrotron micro-tomography (1)
- TEM (1)
- Thermal expansion (1)
- Toughness (1)
- Transmittance (1)
- Viscosity (1)
- Vivianite (1)
- Volume changes (1)
- Water (1)
- Water in glass (1)
- X-ray diffraction (1)
- Young`s modulus (1)
- Young´s modulus (1)
- high pressure (1)
- infrared spectroscopy (1)
- phosphate glasses (1)
- water speciation (1)
Organisationseinheit der BAM
- 5.6 Glas (41) (entfernen)
Barium silicate glass powders 4 h milled in CO2 and Ar and sintered in air are studied with microscopy, total carbon analysis, differential thermal Analysis (DTA), vacuum hot extraction mass spectroscopy (VHE-MS), Fourier-transformed infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), and time-of-flight secondary-ion mass spectrometry (TOF-SIMS). Intensive foaming of powder compacts is evident, and VHE studies prove that foaming is predominantly caused by carbonaceous species for both milling gases. DTA Shows that the decomposition of BaCO3 particles mix-milled with glass powders occurs at similar temperatures as foaming of compacts. However, no carbonate at the glass surface could be detected by FTIR spectroscopy, XPS, and TOF-SIMS after heating to the temperature of sintering. Instead, CO2 molecules unable to rotate identified by FTIR spectroscopy after milling, probably trapped by mechanical dissolution into the glass bulk. Such a mechanism or microencapsulation in cracks and particle aggregates can explain the contribution of Ar to foaming after intense milling in Ar atmosphere. The amount of CO2 molecules and Ar, however, cannot fully explain the extent of foaming. Carbonates mechanically dissolved beneath the surface or encapsulated in cracks and micropores of particle aggregates are therefore probably the major foaming source.
Hydrogen gas diffusivity of fourteen glasses of the Na2O-Al2O3-SiO2 system are studied along the joins quartzalbite-jadeite-nepheline (Qz-Ab-Jd-Np, fully polymerized) and albite-sodium disilicate (Ab-Ds, depolymerized).
Density measurements show that ionic porosity decreases from 54.4% (Qz) to 51.5% (Np) and from 52.4% (Ab) to 50.2% (Ds). Hydrogen diffusivity D follows similar trends but at another scale. D at 523 K decreases from 4×10−12 to 3×10−14m2 s−1 (Qz-Np) and from 4×10−13 to 3×10−15m2 s−1 (Ab-Ds). Charge compensating Na+ acting as a filling agent in fully polymerized network structures leads to up to one order of Magnitude higher diffusivities as depolymerized glass structures of the same SiO2 content where Na+ takes the role of a
modifier ion. Temperature dependence of the diffusivity indicates that both the activation energy involved with the moving H2 molecule as well as the accessible volume in the structure contribute to this compositional trend.
Increasing Exposed Metal Site Accessibility in a Co-MOF-74 Material With Induced Structure-Defects
(2019)
Metal-organic frameworks (MOFs) are promising nanoporous materials with many practical applications. This owes largely to their remarkable porosity and the presence of specific chemical functionalities, such as exposed metal sites (EMS). The MOF-74 structure is known for exhibiting one of the highest EMS densities among porous materials. Moreover, the inclusion of structural defects has been proposed to enhance activity further. This was previously achieved by mixing the original linker together with a second one, having lower topology. The presence of structural defects was evidenced by the resulting crystalline properties and thermal stability. In this work, different mixtures of tetratopic 2,5-dihydroxyterephthalic acid with up to 60% of the tritopic hydroxyterephtalic acid were used to synthesize crystalline Co-MOF-74-like materials. Materials synthesized from higher proportions than 30% of hydroxyterephtalic acid in the synthesis media collapse upon partial removal of the solvent molecules. This indicates the presence of structural defects and the importance of the solvent molecules in stabilizing the crystalline structures. Electron microscope images show that crystal size reduces with inclusion of hydroxyterephtalic acid as the second linker. The presence of coordinated solvent molecules at the EMS was evaluated by Fourier-transform infrared spectra (FTIR) spectroscopy, so that a higher degree of solvent-exchange was observed during washing for defective structures. Furthermore, TG analysis suggests defective structures exhibit lower desolvation temperatures than the defect-free structures. Finally, N2 adsorption-desorption analyses at −196°C showed an enhanced accessibility of the gas to the inner porosity of the defective structures and therefore, the EMS of the material. All these finding make this pathway interesting to enhance the potential interest of these materials for an industrial application because of both a facilitated activation and a better access to the active sites.
A novel method to generalize kinetic data of viscous crack healing in glasses is proposed. The method assumes that crack healing progress is proportional to the healing time, t, and indirect proportional to viscosity, n. This way, crack length and crack width data, normalized to the initial crack length and plotted versus t/n, allow to compare crack healing progress for different cracks and healing temperatures in a master curve. Crack healing experiments conducted in this study demonstrate the applicability of this method for a commercial microscope slide glass.
Though Ni-base superalloys show a high oxidation and corrosion resistance, coatings could still improve these properties, especially if used at temperatures up to 1000 °C. Here, a coating was prepared by applying a boehmite-sol via dip-coating and a subsequent heat treatment at 600 °C for 30 minutes. To evaluate the coating, the oxidation behavior of bare and alumina coated Ni-base alloy Inconel 625 in air at 900 °C was studied for up to 2000 h. Electron microscopic studies of sample surfaces and cross-sections showed that (i) in the 3.5 µm – 6.3 mm thick scale formed on the bare alloy, Fe and Ni are located as fine precipitates at the grain boundaries of the chromia-rich scale, (ii) Ni and Ti are concentrated to a minor degree at the grain boundaries of the scale, too; and for the coated sample: (iii) the only 1.8 µm thick sol-gel alumina coating slows down the formation of chromia on the alloy surface and reduces the outward diffusion of the alloy constituents. The protective effect of the coating was evidenced by (i) diminished chromium diffusion at grain boundaries resulting in less pronounced string-like protrusions at the outer surface of the coated IN 625, (ii) formation of a Cr-enriched zone above the alloy surface which was thinner than the scale on the uncoated sample, (iii) no detectable Cr-depleted zone at the alloy surface, and (iv) a narrower zone of formation of Kirkendall pores.
The crystallization proceeds by the advance of the crystal faces into the disordered phase at the expense of the material excess, the supersaturation. Using a conservation constraint for the transformation ratio α∈[0,1] as complementing the rescaled supersaturation to 1 and a kinetic law for the normal growth velocity as function of the supersaturation raised to power g, the growth order, we derive an equation for the rate of transformation dα/dt. We integrate it for the six combinations of the three spatial dimensions D = 1, 2, 3 and the two canonical values of g = 1, 2 towards obtaining expressions for αDg. The same equation, with g = 1 and D = n (n is the so called Avrami exponent) is obtained when taking only the linear in α term from the Taylor’s expansion around α = 0 of the model equation of Johnson-Mehl-Avrami-Kolmogorov (JMAK). We verify our model by fitting datasets of α21 and α31 (from α = 0 to αupper = 0.999) with JMAK to obtain from the fit n = 1.725, 2.43, resp. We show
further how the values of n depend on the value of αupper to which the fit is performed starting always from 0. Towards building a validation protocol, we start with validating α21 with published results.
The fundamental processes of nucleation and crystallization are widely observed in systems relevant to material synthesis and biomineralization; yet most often, their mechanism remains unclear. In this study, we unravel the discrete stages of nucleation and crystallization of Fe3(PO4)2·8H2O (vivianite). We experimentally monitored the formation and transformation from ions to solid products by employing correlated, time-resolved in situ and ex situ approaches. We show that vivianite crystallization occurs in distinct stages via a transient amorphous precursor phase. The metastable amorphous ferrous phosphate (AFEP) intermediate could be isolated and stabilized. We resolved the differences in bonding environments, structure, and symmetric changes of the Fe site during the transformation of AFEP to crystalline vivianite through synchrotron X-ray absorption spectroscopy at the Fe K-edge. This intermediate AFEP phase has a lower water content and less distorted local symmetry, compared to the crystalline end product vivianite. Our combined results indicate that a nonclassical, hydration-induced nucleation and transformation driven by the incorporation and rearrangement of water molecules and ions (Fe2+ and PO4 3−) within the AFEP is the dominating mechanism of vivianite formation at moderately high to low vivianite supersaturations (saturation index ≤ 10.19). We offer fundamental insights into the aqueous, amorphous-to-crystalline transformations in the Fe2+−PO4 system and highlight the different attributes of the AFEP, compared to its crystalline counterpart.
A glass of the composition 37BaO·16CaO·47SiO2 wt% produced on an industrial scale is crystallized at 970 °C for times ranging from 15 min to 2 h. The crystallization at the immediate surface as well as the crystal growth into the bulk are analyzed using scanning electron microscopy (SEM) including energy dispersive X-ray spectroscopy (EDXS) and electron backscatter diffraction (EBSD) as well as X-ray diffraction in the Θ–2Θ setup (XRD). The immediate surface shows the oriented nucleation of walstromite as well as the formation of wollastonite and an unknown phase of the composition BaCaSi3O8. All three phases also grow into the bulk where walstromite ultimately dominates the kinetic selection and grows throughout the bulk due to a lack of bulk nucleation. Walstromite shows systematic orientation changes as well as twinning during growth. A critical analysis of the XRD-patterns acquired from various crystallized samples indicates that their evaluation is problematic and that phases detected by XRD in this system should be verified by another method such as EDXS.
Oriented surface crystallization on polished diopside glass surfaces has been studied with scanning electron microscopy, electron backscatter diffraction, transmission electron microscopy and laser scanning microscopy.
An orientation preference of [001] parallel to the glass surface was detected for separately growing diopside crystals even as small as 700 nm in size. This finding shows that crystal orientation occurs in the outermost surface layer without crystal-crystal interaction and indicates that the crystal orientation is a result of oriented nucleation. Depending on surface preparation, monomodal crystal orientation distributions with [100] perpendicular to the surface or bimodal distributions with [100] and [010] perpendicular to the glass Surface were detected. It was also shown that the degree of crystal orientation increases with decreasing Surface roughness. The observed orientation of diopside crystals could be explained in terms of the interfacial energies of different crystal faces.
The hydrogen tightness of high-pressure hydrogen storage is a Basic criterion for long-term storage. The H2 permeation coefficients of epoxy resin and a glass lacquer were determined to enable the geometric optimization of a glass capillary storage. It was found that the curing conditions have no significant influence on the H2 permeation coefficient of resin.
The H2 permeation coefficient of epoxy resin is only about three orders of Magnitude greater than that of borosilicate glass. This suggests that the initial pressure of 700 bar takes about 2.5 years to be halved in capillary array storage. Therefore, a high-pressure hydrogen storage tank based on glass capillaries is ideally suited for long-term storage in mobile applications.