The main difference between high entropy alloys and conventional alloys is the solid solution strengthening effect, which shifts from a single element to a multi-element matrix. Little is known about the effectiveness of this effect at high temperatures. Face-centered cubic, equiatomic, and single crystalline high entropy alloy CrMnFeCoNi was pre-alloyed by arc-melting and cast as a single Crystal using the Bridgman process. Mechanical characterization by creep testing were performed at temperatures of 700, 980, 1100, and 1200°C at different loads under vacuum and compared to single-crystalline pure nickel. The results allow a direct assessment of the influence of the chemical composition without any disturbance by grain boundary sliding or diffusion. The results indicate different behaviors of single crystalline pure nickel and CrMnFeCoNi. At 700°C CrMnFeCoNi is more creep-resistant than Ni, but at 980°C both alloys show a nearly similar creep strength. Above 980°C the creep behavior is identical and the solid solution strengthening effect of the CrMnFeCoNi alloy disappears.
This work presents an X-ray absorption spectroscopy study on a single-phase state of the Al8Cr17Co17Cu8Fe17Ni33 compositionally complex alloy, focused on the local crystal structure around each alloying element. The comparison of 1st shell bond lengths, obtained by the analysis of extended X-ray absorption fine structure (EXAFS) measured at the K-edges of each alloying element, indicates that Al8Cr17Co17Cu8Fe17Ni33 crystallizes in a distorted arrangement of an fcc lattice. A modest bond length dependence of the alloying elements with increasing atomic number is observed, with minima and maxima at Cr/Co, and Al/Cu, respectively. 1st shell bond lengths spread over ~0.03 Å; consequently, such variations cannot result in lattice distortions greater than ~0.04 Å. EXAFS results clearly indicate short-range order in the alloy: pairing of Al with Ni and Cu is favored, correlating well with a g’ precipitate composition (Al-Ni-Cu rich) reported in previous work, while Al-Cr bonding is unfavored and no Al-Al pairs are observed. Electronic structure information was obtained through comparison between near-edge regions of alloying Elements and corresponding pure metals. Intensity comparison of K-edge features agree with a charge variation of p states in Al8Cr17Co17Cu8Fe17Ni33, where Ni and Cu act as p states electron acceptors, suggesting an orbital hybridization with Al, responsible for a shrinkage in Al metallic radius in the alloy by 0.17 Å.
Surface degradation phenomena of two model equiatomic alloys from the CrMnFeCoNi alloy system were investigated in 2% O2 and 10% H2O (pO2 = 0.02 and 10−7 atm, respectively) at 800 °C for times up to 96 h. The crystallographic structures, morphologies, and chemical compositions of the corrosion layers developing on CrMnFeCoNi and CrCoNi were comparatively analyzed by mass gain analysis, X-ray diffraction, and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy and electron backscatter diffraction. The oxidation resistance of CrMnFeCoNi is relatively poor due to the fast growth of porous Mnoxide(s). CrCoNi forms an external chromia layer that is dense and continuous in a dry 2% O2 atmosphere. This layer buckles and spalls off after exposure to 10% H2O atmosphere. Beneath the chromia layer, a Cr-depleted zone forms in the CrCoNi alloy in both environments. As the oxide scale spalls off in the H2O-containing
atmosphere, a secondary chromia layer was observed and correspondingly enlarges the Cr-depleted zone. In contrast, as the chromia layer remains without significant spallation when CrCoNi is exposed to a dry oxidizing atmosphere, the region depleted in Cr is narrower.