5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (72) (entfernen)
Schlagworte
- Additive Manufacturing (13)
- Additive manufacturing (10)
- 3D printing (5)
- Ceramics (5)
- Alumina (4)
- 3D-Printing (3)
- 3D-printing (3)
- Binder Jetting (3)
- Calcination (3)
- Ceramic (3)
- Sintering (3)
- Zirconia (3)
- Binder jetting (2)
- Bioactive glass (2)
- Bioactivity (2)
- Bioceramics (2)
- Bone regeneration (2)
- Calcium cobaltite (2)
- Electron microscopy (2)
- LTCC (2)
- Layerwise Slurry Deposition (2)
- Layerwise slurry deposition (2)
- Lunar regolith (2)
- Mars (2)
- Microstructure (2)
- Nano-powder (2)
- Preceramic polymer (2)
- Pressure-assisted sintering (2)
- Reaction-sintering (2)
- Silicon carbide (2)
- Space (2)
- Spray drying (2)
- Thermoelectric properties (2)
- 2PP (1)
- 3D Druck (1)
- ATZ (1)
- Additive Fertigung (1)
- Agglomerates (1)
- Alcium alkali phosphate (1)
- Alkali-activated materials (1)
- Alpha-tricalcium phosphate (1)
- Alumina toughened zirconia (1)
- Bacteria (1)
- Biaxial strength (1)
- Binders/binding (1)
- Bio Ceramic (1)
- Bio Ceramics (1)
- Bio active ceramic (1)
- Bio-ceramic engineering (1)
- Bioactive bone grafting material (1)
- Bioactive glass scaffold (1)
- Biphasic calcium phosphate (1)
- Bone marrow-derived mesenchymal stem cell (1)
- CO2 separation membranes (1)
- Calcium Cobaltite (1)
- Calcium alkali orthophosphate materials (1)
- Cement-based materials (1)
- Ceramic multilayers (1)
- Ceramic nano particles (1)
- Ceramics 3D printing (1)
- Cerium oxide (1)
- Characterisation (1)
- Clay ISRU (1)
- Co-firings (1)
- Computed tomography (1)
- Concrete 3D-printing (1)
- Creep (1)
- Cross-sectioning (1)
- Crystallization (1)
- Cubical shape (1)
- Cuttlefish (1)
- Debinding (1)
- Defect detection (1)
- Dental (1)
- Design of experiment (1)
- Destabilization (1)
- Dielectric breakdown (1)
- Dielectric properties (1)
- Dispersion process (1)
- Drywood termite (1)
- Efficiency (1)
- Elastic properties (1)
- Electrical insulators (1)
- Electronic (1)
- Endothelial progenitor cell (1)
- Environment (1)
- FSDC (1)
- Fatigue (1)
- Filters (1)
- Firing (1)
- Flowability (1)
- Fracture toughness (1)
- Freeze casting (1)
- Frozen state photopolymerization (1)
- Fungi (1)
- Gas flow assisted powder deposition (1)
- Glass-ceramic (1)
- Glass-ceramics (1)
- Grain boundary (1)
- Granules (1)
- Hausner ratio (1)
- Hierarchical porosities (1)
- High-voltage testing (1)
- Hochleistungskeramik (1)
- Hot pressing (1)
- Hot stage microscopy (1)
- Hybrid Manufacturing (1)
- ISRU (1)
- In-situ Process Monitoring (1)
- In-vivo (1)
- Inkjet (1)
- Internal stresses (1)
- Iron oxide (1)
- LIBS (1)
- LSD print (1)
- Laser (1)
- Laser beam melting (1)
- Laser-induced slip casting (1)
- Lattices (1)
- Liquid phase sintering (1)
- Lithography-based technologies (1)
- MGS-1 regolith simulant (1)
- Melting (1)
- Meta material (1)
- Metallic Glass (1)
- Microwave technology (1)
- Mixed Ca-K-Na phosphates (1)
- Moon (1)
- Multilayer (1)
- Multilayer ceramic technology (1)
- Multilayers (1)
- Na and K rhenanites (1)
- Nano CRM (1)
- Nano-ceramic-additive-manufacturing photoresin (1)
- NanoCAM (1)
- Nanopowder (1)
- Networking (1)
- Non-destructive Materials (1)
- Optical and Magnetic Materials (1)
- Optical centrifugation (1)
- Osteogenesis (1)
- PV modules (1)
- Parabolic flight (1)
- Particle size (1)
- Particle-bed binder jetting (1)
- Passive components and circuits (1)
- Permeability (1)
- Permittivity reduction (1)
- Phase diagram (1)
- Phase transformations (1)
- Phototrophs (1)
- Photovoltaic modules (1)
- Plasma imaging (1)
- Plasma spray (1)
- Polymer-ceramic mixtures (1)
- Polymeric Materials (1)
- Porcelain (1)
- Porosification (1)
- Powder bed additive manufacturing (1)
- Powder bed density (1)
- Powder flow (1)
- Powder processing (1)
- Powder rheology (1)
- Powder-based processes (1)
- Power factor (1)
- Power law (1)
- Pressure assisted sintering (1)
- Printing (1)
- Process (1)
- Process development (1)
- Processing window (1)
- Quality assurance (1)
- Reaction Sintering (1)
- Real-time deformation (1)
- Real-time qPCR (1)
- Reference nanoparticles (1)
- Regolith (1)
- Roughness (1)
- SAXS (1)
- SDC (1)
- SEM micrography (1)
- Safety (1)
- Samarium doped ceria (1)
- Sample preparation (1)
- Sand blasting (1)
- Scaffold (1)
- Scaffold geometry (1)
- Scavenging effect of iron (1)
- Schlickerdeposition (1)
- SchwarzP cells (1)
- Self-Assembly (1)
- Self-organization (1)
- Shadowgraphy (1)
- Silicate glass-ceramics (1)
- Silicon Carbide (1)
- Silicon release (1)
- Silikatkeramik (1)
- Sintering additive (1)
- Sinus floor augmentation (1)
- Size (1)
- Slurry (1)
- Slurry optimization (1)
- Smectite (1)
- Softening temperature (1)
- Solar panels (1)
- Solid-State-Synthesis (1)
- Solid-state-synthesis (1)
- Standardisation (1)
- Technical Ceramics (1)
- Texture (1)
- Thermal expansion (1)
- Thermoelectric oxide (1)
- Thermoelectric oxides (1)
- Thermoelectrics (1)
- Thiol-ene click chemistry (1)
- Three-dimensional Bone tissue engineering (1)
- Transformer (1)
- Transmittance (1)
- Transparency (1)
- Transparent ceramic (1)
- Tricalcium Phosphate (1)
- Triply Periodical Minimal Surface (1)
- Two-photon adsorption (1)
- Two-photon polymerization (1)
- Two-photon-polymerization (1)
- Ultrasound (1)
- Viscous sintering (1)
- Wet chemical etching (1)
- Wetting (1)
- X-ray refraction (1)
- X-ray tomographic (1)
- X-ray-diffraction (1)
- Yttria stabilized zirconia (1)
- Zinc oxide (1)
- Zirconia-toughened alumina (1)
- ZnO (1)
- bioactive (1)
- biomaterials (1)
- bone (1)
- µ-gravity (1)
Organisationseinheit der BAM
- 5.4 Multimateriale Fertigungsprozesse (72) (entfernen)
Paper des Monats
- ja (3)
Instead of foreseeing and preparing for all possible scenarios of machine failures, accidents, and other challenges arising in space missions, it appears logical to take advantage of the flexibility of additive manufacturing for “in-space manufacturing” (ISM). Manned missions into space rely on complicated equipment, and their safe operation is a great challenge. Bearing in mind the absolute distance for manned missions to the Moon and Mars, the supply of spare parts for the repair and replacement of lost equipment via shipment from Earth would require too much time. With the high flexibility in design and the ability to manufacture ready-to-use components directly from a computer-aided model, additive manufacturing technologies appear to be extremely attractive in this context. Moreover, appropriate technologies are required for the manufacture of building habitats for extended stays of astronauts on the Moon and Mars, as well as material/feedstock. The capacities for sending equipment and material into space are not only very limited and costly, but also raise concerns regarding environmental issues on Earth. Accordingly, not all materials can be sent from Earth, and strategies for the use of in-situ resources, i.e., in-situ resource utilization (ISRU), are being
envisioned. For the manufacturing of both complex parts and equipment, as well as for large infrastructure, appropriate technologies for material processing in space need to be developed.
The microstructure of an apatite-wollastonite (code name AP40) glass-ceramic is analyzed in this study by combining 2D microscopy, phase analysis, X-ray absorption and synchrotron X-ray refraction computed tomography (XCT and SXRCT, respectively). It is shown that this combination provides a useful toolbox to characterize the global microstructure in a wide scale range, from sub-micrometer to millimeter. The material displays a complex microstructure comprising a glassy matrix with embedded fluorapatite and wollastonite small crystals. In this matrix, large (up to 200 μm) spike-shaped structures are distributed. Such microstructural features are oriented around a central sphere, thereby forming a structure resembling a sea urchin. A unique feature of SXRCT, in contrast to XCT, is that internal interfaces are visualized; this allows one to show the 3D distribution of these urchins with exceptionally good contrast. Furthermore, it is revealed that the spike-shaped structures are not single crystals, but rather composed of sub-micrometric crystals, which are identified as fluorapatite and diopside phases by SEM-EDX analysis.
As humanity contemplates manned missions to Mars, strategies need to be developed for the design and operation of hospitable environments to safely work in space for years. The supply of spare parts for repair and replacement of lost equipment will be one key need, but in-space manufacturing remains the only option for a timely supply. With high flexibility in design and the ability to manufacture ready-to-use components directly from a computeraided model, additive manufacturing (AM) technologies appear extremely attractive. For the manufacturing of metal parts, laser-beam melting is the most widely used AM process. However, the handling of metal powders in the absence of gravity is one prerequisite for its successful application in space. A gas flow throughout the powder bed is successfully applied to compensate for missing gravitational forces in microgravity experiments. This so-called gas-flow-assisted powder deposition is based on a porous Building platform acting as a filter for the fixation of metal particles in a gas flow driven by a pressure difference maintained by a vacuum pump.
Additive manufacturing of SiSiC by layerwise slurry deposition and binder jetting (LSD-print)
(2019)
The current work presents for the first time results on the Additive Manufacturing of SiSiC complex parts based on the Layerwise Slurry Deposition (LSD) process. This technology allows to deposit highly packed powder layers by spreading a ceramic slurry and drying. The capillary forces acting during the process are responsible for the dense powder packing and the good joining between layers. The LSD process can be combined with binder jetting to print 2D cross-sections of an object in each successive layer, thus forming a 3D part. This process is named LSD-print.
By LSD-print and silicon infiltration, SiSiC parts with complex geometries and features down to 1mm and an aspect ratio up to 4:1 could be demonstrated.
The density and morphology were investigated for a large number of samples. Furthermore, the density and the mechanical properties, measured by ball-on-three-balls method, were in all three building directions close to isostatic pressed references.
Future lunar exploration can benefit greatly from In-Situ Resource Utilization. Accordingly, the in-Situ Resource Utilization approach highlights the need for detailed analysis of lunar regolith. In this study, JSC-2A Simulant was studied regarding its sintering and melting behaviour using Differential Thermal Analysis under ambient and inert conditions. The minerals at the crystalline peaks were determined using X-Ray Diffraction analysis.
Moreover, melting droplet shape and wetting behaviour of pressed regolith samples of different particle size distributions were studied by Hot Stage Microscopy technique. Hot Stage Microscopy experiments were performed at different heating rates under ambient conditions. Bloating effects within the solidified samples were then qualitatively examined by X-ray tomography. Lastly, the optimization of processing strategies for the Additive Manufacturing of lunar regolith is discussed.
Spherical mesoporous bioactive glasses in the silicon dioxide (SiO2)-phosphorus pentoxide (P2O5)–calcium oxide (CaO) system with a high specific surface area of up to 300m2/g and a medium pore radius of 4 nm were synthesized by using a simple one-pot surfactant-assisted sol–gel synthesis method followed by calcination at 500–700°C. The authors were able to control the particle properties by varying synthesis parameters to achieve microscale powders with spherical morphology and a particle size of around 5–10 mm by employing one structure-directing agent. Due to a high Calcium oxide content of 33·6mol% and a phosphorus pentoxide content of 4·0mol%, the powder showed very good bioactivity up to 7 d of immersion in simulated Body fluid. The resulting microspheres are promising materials for a variety of life science applications, as further processing – for example, granulation – is unnecessary. Microspheres can be applied as materials for powder-based additive manufacturing or in stable suspensions for drug release, in bone cements or fillers.
Bioactive glass ceramics have excellent biocompatibility and osteoconductivity; and can form direct chemical bonds with human bones; thus, these ceramic are considered as “Smart” materials. In this study, we develop a new type of bioactive glass ceramic (AP40mod) as a scaffold containing Endothelial progenitor cells (EPCs) and Mesenchymal stem cells (BMSCs) to repair critical-sized bone defects in rabbit mandibles. For in vitro experiments:
AP40mod was prepared by Dgital light processing (DLP) system and the optimal ratio of EPCs/BMSCs was screened by analyzing cell proliferation and ALP activity, as well as the influence of genes related to osteogenesis and angiogenesis by direct inoculation into scaffolds. The scaffold showed suitable mechanical properties, with a Bending strength 52.7 MPa and a good biological activity. Additionally, when EPCs/BMSCs ratio were combined at a ratio of 2:1 with AP40mod, the ALP activity, osteogenesis and angiogenesis were significantly increased. For in vivo experiments: application of AP40mod/EPCs/BMSCs (after 7 days of in vitro spin culture) to repair and reconstruct critical-sized mandible defect in rabbit showed that all scaffolds were successfully accurately implanted into the defect area. As revealed by macroscopically and CT at the end of 9 months, defects in the AP40mod/EPCs/BMSCs group were nearly completely covered by normal bone and the degradation rate was 29.9% compared to 20.1% in the AP40mod group by the 3D reconstruction. As revealed by HE and Masson staining analyses, newly formed blood vessels, bone marrow and collagen maturity were significantly increased in the AP40mod/EPCs/BMSCs group compared to those in the AP40mod group. We directly inoculated cells on the novel material to screen for the best inoculation ratio. It is concluded that the AP40mod combination of EPCs/BMSCs is a promising approach for repairing and reconstructing large load bearing bone defect.
This paper investigates fast and inexpensive measurement methods for defect detection in parts produced by Additive Manufacturing (AM) with special focus on lattice parts made of ceramics. By Lithography-based Ceramic Manufacturing, parts were built both without defects and with typical defects intentionally introduced. These defects were investigated and confirmed by industrial X-ray Computed Tomography. Alternative inexpensive methods were applied afterwards on the parts such as weighing, volume determination by Archimedes method and gas permeability measurement. The results showed, that defects resulting in around 20% of change in volume and mass could be separated from parts free of defects by determination of mass or volume. Minor defects were not detectable as they were in the range of process-related fluctuations. Permeability measurement did not allow to safely identify parts with defects. The measurement methods investigated can be easily integrated in AM process chains to support quality control.
The freeze casting technique assisted with cryo thiol-ene photopolymerization is successfully employed for the fabrication of macroporous polymer-derived silicon oxycarbide with highly aligned porosity. It is demonstrated that the free radical initiated thiol-ene click reaction effectively cross-linked the vinyl-containing liquid polysiloxanes into infusible thermosets even at low temperatures. Furthermore, mixed solution- and suspension-based freeze casting is employed by adding silica nanopowders. SiOC/SiO2 foams with almost perfect cylindrical shapes are obtained, demonstrating that the presence of nano-SiO2 does not restrict the complete photoinduced cross-linking. The post-pyrolysis HF acid treatments of produced SiOC monoliths yields hierarchical porosities, with SiOC/SiO2 nanocomposites after etching demonstrating the highest specific surface area of 494 m2/g and pore sizes across the macro-, meso- and micropores ranges. The newly developed approach gives a versatile solution for the fabrication of bulk polymer-derived ceramics with controlled porosity.
Stereolithography processes such as lithography-based ceramic manufacturing (LCM) are technologies that can produce centimeter-sized structures in a reasonable time frame. However, for some parts specifications, they lack resolution. Two-photon-polymerization (2PP) ensures the highest geometric accuracy in additive manufacturing so far. Nevertheless, building up parts in sizes as large as a few millimeters or even centimeters is a time-consuming process, which makes the production of 2PP printed parts very costly. Regarding feedstock specification, the requirements for 2PP are different to those for LCM, and generally, feedstocks are designed to meet requirements for only one of these manufacturing technologies. In an attempt to fabricate highly precise ceramic components of a rather large size, it is necessary to develop a feedstock that suits both light-based technologies, taking advantage of LCM’s higher productivity and 2PP’s accuracy. Hybridization should bring the desired precision to the region of interest on reasonably large parts without escalating printing time and costs. In this study, specimens gained from a transparent feedstock with yttria stabilized zirconia (YSZ) particles of 5 nm at 70 wt% were presented. The resin was originally designed to suit 2PP, while being also printable with LCM. This work demonstrates how hybrid parts can be sintered into full YSZ ceramics.