The BAMline at the synchrotron X-ray source BESSY II (Berlin, Germany) is supporting researchers especially in materials science [1]. As a non-destructive characterization method, synchrotron X-ray imaging, especially tomography (SXCT) with hard X-Rays, plays an important role in structural 3D characterization. The imaging capabilities allow for in-situ and operando experiments. In this presentation the equipment, data handling pipeline as well as various examples from material science are presented.
In series-connected lithium-ion cells are susceptible to an electrical safety hazard called over-discharge. Here the behavior of copper dissolution and deposition during over-discharge is presented, which leads to irreversible loss of capacity and internal short circuits. The concentration of dissolved and deposited copper is quantified. Also, a non-uniform distribution pattern of copper deposition on the cathode is shown.
The second example deals with an Al alloy 7017 customized for a 3d-printing process by means of laser-based powder bed fusion (PBF-LB) technique. These advanced alloys have a significantly higher modulus of elasticity than conventional Al alloys, making them attractive for applications requiring high stiffness. SXCT during In-situ tensile tests confirmed that fracture initiation strongly depends on defects created during printing. However, the cracks are deflected from decohesion around inclusions/precipitates embedded in the Al matrix, increasing ductility.
Low temperature cofired ceramic (LTCC) multilayer housings offer 3D-circuits for a wide range of applications in telecommunications, microsystems and sensor technology. Such housings are produced by combining structured and metallized ceramic layers using tape-casting and multilayer technology. The characterization of the integrity, deformation, defects, and positioning of the internal metal features was carried out using in-situ SXCT at up to 950°C.
A high-precision nail penetration tool was developed to characterize the mechanically induced thermal runaway (TR) of lithium-ion battery (LIB) cells in a dynamic temperature range down to -190 °C. To investigate safety-specific low-temperature transport conditions, the damaged cells were tomographically imaged during thawing.
The chemically complex alloys (CCAs) that contain mostly refractory elements (rCCAs), may be highly resistant to heat and load, which makes them attractive candidates for use at extremely high temperatures associated with many technological applications, e.g. aeroengine turbines. However, the field of CCAs, especially their resistance in harsh (oxidative) and hot environment is still young and not much experimental evidence for the understanding mechanisms in this regime is available, which the proposed study addresses. For safe use in structural applications, in addition to their mechanical performance, the environmental resistance of this alloy is also critical. Surface degradation can significantly decrease the mechanical resistance during high temperature exposure, leading to premature failure. The AlMo0.5NbTa0.5TiZr rCCA only contains Al as a protection candidate and it is composed of a coherent B2/bcc nanoscopic cube-on-cube interweave and an hexagonal phase. The evaluation of the oxidation process in the AlMo0.5NbTa0.5TiZr rCCA in the heat-treated state has not been assessed yet. The proposed study focusses on a deeper understanding of the formation mechanism and growth kinetics of oxides at high temperature in the AlMo0.5NbTa0.5TiZr rCCA using synchrotron radiation. Due to the envisaged high temperature structural applications, the alloy is evaluated in an oxidation environment specifically between 800°C and 1000°C.