5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (2)
- Vortrag (1)
Sprache
- Englisch (2)
- Mehrsprachig (1)
Schlagworte
- 12%Cr steel (1)
- 3D Reconstruction (1)
- 3D metallography (1)
- 3D-Metallographie (1)
- Automation (1)
- Cyclic steam oxidation (1)
- Gefügeanalyse (1)
- Gefügerekonstruktion (1)
- Metallography (1)
- Microstructure (1)
- Microstructure analysis (1)
- Microstrucure reconstruction (1)
- Roboter (1)
- Serial sectioning (1)
- Serienschnitte (1)
- Specimen geometry (1)
- Surface treatments (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
Die klassische Metallographie basiert auf Abbildungen einzelner Schliffebenen und kann auf räumliche Formen und Anordnungen des Gefüges nur bedingt schließen. Die Idee, aus metallographischen Serienschliffen dreidimensionale Gefügestrukturen zu rekonstruieren, ist daher naheliegend und nicht neu. Allerdings ist der Aufwand, in Handarbeit viele Einzel-Schliffe zu präparieren und zu Bildstapeln zusammenzusetzen, sehr hoch und steht einer häufigen Anwendung entgegen.
Deshalb wird an der BAM ein Roboter-gestütztes 3D-Metallographie-System entwickelt, das an einer Schliffprobe die Schritte Präparation und Bildeinzug vollautomatisch mit vielen Wiederholungen ausführt. Die Präparation umfasst Schleifen, Polieren und optional Ätzen der Schlifffläche, der Bildeinzug autofokussierte lichtmikroskopische Aufnahmen bei mehreren Vergrößerungsstufen. Der erhaltene Bildstapel wird anschließend vorverarbeitet, segmentiert und in ein 3D-Modell umgesetzt, das einer mikrotomographischen Aufnahme ähnelt, allerdings mit besserer lateraler Auflösung bei großem Volumen. Im Gegensatz zu tomographischen Verfahren besteht die Möglichkeit der Kontrastierung durch klassische chemische Ätzung. Die Integration eines REMs ist geplant. Bislang durchgeführte Arbeiten verdeutlichen die Möglichkeiten der Darstellung von Heißgas-Korrosionsschichten, Grauguss-Werkstoffen und Keramik-basierten mikroelektronischen Strukturen (Vias).
Many microstructural features exhibit non-trivial geometries, which can only be derived to a limited extent from two-dimensional images. E.g., graphite arrangements in lamellar gray cast iron have complex geometries, and the same is true for additively manufactured materials and three-dimensional conductive path structures. Some can be visualized using tomographic methods, but some cannot be due to weak contrast and/or lack of resolution when analyzing macroscopic objects. Classic metallography can help but must be expanded to the third dimension. The method of reconstructing three-dimensional structures from serial metallographic sections surely is not new. However, the effort required to manually assemble many individual sections into image stacks is very high and stands in the way of frequent application. For this reason, an automated, robot-supported 3D metallography system is being developed at BAM, which carries out the steps of repeated preparation and image acquisition on polished specimen.
Preparation includes grinding, polishing and optionally etching of the polished surface. Image acquisition comprises autofocused light microscopic imaging at several magnification levels. The image stacks obtained are then pre-processed, segmented, and converted into 3D models, which in the result appear like microtomographic models, but with high resolution at large volume. Contrasting by classical chemical etching reveals structures that cannot be resolved using tomographic methods. The integration of further imaging and measuring methods into this system is underway. Some examples will be discussed in the presentation.
The steam side oxidation of ferritic–martensitic VM12-SHC steel was investigated under thermo-cyclic conditions in water steam at 620/320 °C and 30 bar with a focus on assessing the influence of pre-oxidation time, specimen geometry and surface finish. The specimens were pre-oxidized under isothermal conditions in water steam at 620 °C and 30 bar for 500 h or 1500 h. After pre-oxidation treatment, all specimens were subjected up to 258 thermal cycles. Three different geometries—rectangular coupons, U-shaped ring segments and ring samples—were investigated to evaluate the influence of open/closed shape, and flat/curved surface on corrosion rate. At the same time, two types of surface finish were considered: “as received” and “ground.” The formation of a protective scale by pre-oxidation was investigated. EBSD and ESMA analyses revealed that the Cr-content of the alloy appeared to be insufficient for obtaining a protective oxide scale under studied conditions, at the same time the anayses confirmed that initial oxidation depends on presence of minor alloying elements as Si and Mn, strong oxide formers which can alter the kinetics and morphology of the corrosion reaction. Moreover, rectangular coupons with small wall thickness and flat surface exhibited the highest corrosion rate, while “ground” curved samples showed only local oxidation. This indicates that for same pre-oxidation time, oxidation kinetics is controlled by curvature.