Liquid-metal embrittlement (LME) of galvanized (Zn-coated) advanced high-strength steels is a long-known problem in materials science. Here we reveal the initial microstructural processes underneath the Zn-coating that lead to LME-microcrack initiation in the steel substrate. We track the microstructural evolution during the first tens of milliseconds and find pronounced signatures of Fe-Zn intermetallic precipitation in both ferrite grain boundaries and at internal ferrite-oxide phase boundaries. In concert with novel CALPHAD-integrated density-based thermodynamic modelling, we demonstrate that Zn-rich intermetallic phase-nucleation can occur at markedly low processing temperatures due to a segregation transition. We show that a small Znenrichment caused by Zn bulk-diffusion during the initial temperature rise in a joining process is sufficient to induce the segregation transition and subsequent nucleation of Fe-Zn intermetallic grain-boundary phases, which the experiments link to crack initiation sites. These findings direct focus onto LME-controlling microstructural and thermodynamic phenomena at temperatures below the ductility trough and the austenite formation temperature.
One contribution of materials science to energy efficiency is the continuous development of novel high-performance structural materials that push the strength-ductility envelope. A prominent example are modern advanced high-strength steels (AHSSs), which have enabled considerable weight reductions in the automotive sector, thereby enabling greenhouse emission reductions. To protect such advanced alloys from property degradation via corrosion, zinc (Zn) coatings are often applied through galvanization. Whilst protective, a Zn-coating comes with problems – the AHSS substrate becomes susceptible for liquid-metal embrittlement (LME) than can be the origin of significant mechanical property degradation when liquified Zn infiltrates into the steel substrate. Being for from understood, we focus here on non-cracked environments to capture the early stages of LME. This approach revealed the nucleation and growth of nano-scale intermetallic phases inside uncracked GBs (Materials Today Advances 13, 100196, 2022), highlighting the complex multi-phase microstructure developing before cracking occurs. To shed further light on the early stages of LME in AHSSs, we also consider the microstructural evolution of interrupted welds. We discuss our findings in the context of the time-resolved substructure evolution right beneath the interface between the AHSS and the Zn-based coating and track how Zn progressively infiltrates the substrate along phase and grain boundaries. The experimental results are further corroborated with thermodynamic simulations.