Calcium cobaltite Ca3Co4O9, abbreviated Co349, is a promising thermoelectric material for high‐temperature applications in air. Its anisotropic properties can be assigned to polycrystalline parts by texturing. Tape casting and pressure‐assisted sintering (PAS) are a possible future way for a cost‐effective mass‐production of thermoelectric generators. This study examines the influence of pressure and dwell time during PAS at 900°C of tape‐cast Co349 on texture and thermoelectric properties. Tape casting aligns lentoid Co349. PAS results in a textured Co349 microstructure with the thermoelectrically favorable ab‐direction perpendicular to the pressing direction. By pressure variation during sintering, the microstructure of Co349 can be tailored either toward a maximum figure of merit as required for energy harvesting or toward a maximum power factor as required for energy harvesting. Moderate pressure of 2.5 MPa results in 25% porosity and a textured microstructure with a figure of merit of 0.13 at 700°C, two times higher than the dry‐pressed, pressureless‐sintered reference. A pressure of 7.5 MPa leads to 94% density and a high power factor of 326 µW/mK2 at 800°C, which is 11 times higher than the dry‐pressed reference (30 MPa) from the same powder.
Texturing of calcium cobaltite for thermoelectric applications by pressure assisted sintering
(2021)
Thermoelectric materials can convert waste heat directly into electrical power by using the Seebeck effect. Calcium cobaltite (CCO) is considered as a promising thermoelectric p-type oxide for energy harvesting applications at temperatures above 500 °C. The properties and morphology of single-crystal CCO are strongly anisotropic because of its crystal structure of alternating layers of CoO2 and Ca2CoO3. By aligning the plate-like grains, the anisotropic properties of the grains can be assigned to the poly-crystalline parts.
In this study, the combination of tape casting and pressure-assisted sintering is used to texture and densify large scale components (50 cm²). Thereby, the influence of powder preparation and applied pressure during sintering on texturing and thermoelectric properties is investigated.
The analysis of XRD pole figures revealed that tape casting already leads to highly textured CCO. By pressure variation during sintering, the microstructure of CCO can be tailored either toward maximum power factor as required for energy harvesting or toward maximum figure of merit as required for energy recovery. Low pressure lead to a porous microstructure and maximum figure of merit and higher pressure to full densification and maximum power factor. The electrical and thermal conductivity of CCO seem depending on both texture and sinter density.