5 Werkstofftechnik
Filtern
Erscheinungsjahr
- 2020 (50) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (50) (entfernen)
Sprache
- Englisch (49)
- Mehrsprachig (1)
Schlagworte
- EBSD (5)
- Additive manufacturing (4)
- Additive Manufacturing (3)
- Electron backscatter diffraction (2)
- Grain boundary (2)
- High entropy alloys (2)
- LPBF (2)
- LTCC (2)
- Orientation precision (2)
- Quasicrystal (2)
- Texture (2)
- Thermodynamics (2)
- X-ray diffraction (2)
- 2PP (1)
- 3D printing (1)
- 3D-printing (1)
- AISI 304L (1)
- AISI 316L (1)
- ATZ (1)
- Aggressive environments (1)
- Alkali aluminosilicate glasses (1)
- Alpha-tricalcium phosphate (1)
- Alumina (1)
- Alumina toughened zirconia (1)
- Angle measurement (1)
- Approximant (1)
- Atom probe tomography (1)
- Automated analysis (1)
- Bacterial attachment (1)
- Binder Jetting (1)
- Bio Ceramics (1)
- Bioactive glass scaffold (1)
- Bone marrow-derived mesenchymal stem cell (1)
- CCUS (1)
- CO2 pipeline transport (1)
- Carbon Fiber Reinforced Plastics (1)
- Carbon Fibre (1)
- Carbon steel (1)
- Cement-based materials (1)
- Ceramic nano particles (1)
- Ceramics (1)
- Chrystal orientation (1)
- Clay ISRU (1)
- Compositionally complex alloys (1)
- Computed Tomography (1)
- Confined catalyst (1)
- Cooling rate (1)
- Corrosion (1)
- Corrosion resistance (1)
- CrCoNi (1)
- CrMnFeCoNi (1)
- Crack evolution (1)
- Cracks (1)
- Cryogenic (1)
- Cryogenic cycling (1)
- Crystal growth velocity (1)
- Crystal orientation (1)
- DCB geometry (1)
- Data processing (1)
- Defect detection (1)
- Degradation (1)
- Degradation signatures (1)
- Densty-based Thermodynamics (1)
- Deuterium (1)
- Differential scanning calorimetry (1)
- Diffraction Enhanced Imaging (1)
- Diffusivity (1)
- Disorientation (1)
- Double notched creep specimen (1)
- EXAFS (1)
- Endothelial progenitor cell (1)
- Epoxy Resin (1)
- Fatigue (1)
- Fatigue striations (1)
- Fibre reinforced plastic (1)
- Fuel sorption (1)
- Gas flow assisted powder deposition (1)
- Glass (1)
- Glass ceramic (1)
- Glass transition (1)
- Gnomonic projections (1)
- Grain Boundary Segregation (1)
- Grain Boundary Spinodal (1)
- Granules (1)
- High - temperature (1)
- High density polyethylene (1)
- High entropy alloy (1)
- High temperature corrosion (1)
- High temperature oxidation (1)
- High-Entropy Alloys (1)
- Hot pressing (1)
- Hot stage microscopy (1)
- Hybrid Manufacturing (1)
- Hydrogen (1)
- Hydrous glass (1)
- Impurities (1)
- In situ tensile test (1)
- In-situ ED-XRD (1)
- Inconel 686 (1)
- Inconel 718 (1)
- Indentation fracture toughness (1)
- Infrared spectroscopy (1)
- Interfacial strength (1)
- Internal friction (1)
- Ionic porosity (1)
- Iron (1)
- Kernel average misorientation (1)
- Kikuchi diffraction (1)
- Kikuchi patterns (1)
- LIBS (1)
- Laser Powder Bed Fusion (1)
- Laser cladding (1)
- Lattice rotation (1)
- Lattices (1)
- Layered manganese oxide (1)
- Layerwise Slurry Deposition (1)
- Low expansion (1)
- Low-loading (1)
- Lunar regolith (1)
- MGS-1 regolith simulant (1)
- Mars (1)
- Matrix residual stress (1)
- Mechanical properties (1)
- Medium entropy alloys (1)
- Melting (1)
- Metal and alloys (1)
- Metallic glass (1)
- Microstrucrue Design (1)
- Microstructure (1)
- Mixed conductors (1)
- Mn-oxides (1)
- Multilayer ceramic technology (1)
- NMR spectroscopy (1)
- Nano-ceramic-additive-manufacturing photoresin (1)
- NanoCAM (1)
- Nanoparticles (1)
- Nb3Sn (1)
- Neutron Diffraction (1)
- Non-serrated inhomogeneous flow (1)
- Online Process Monitoring (1)
- Oxyfuel (1)
- Oxygen evolution reaction (1)
- Packaging (1)
- Particle size (1)
- Pattern matching (1)
- Permeability (1)
- Permittivity reduction (1)
- Phase Diagram (1)
- Phase transformation (1)
- Phase transformations (1)
- Plasma imaging (1)
- Polyethylene (1)
- Polymer analysis/characterization (1)
- Polyolefins (1)
- Porosification (1)
- Powder diffraction (1)
- Projection center (1)
- Quality assurance (1)
- Reaction Sintering (1)
- Rejuvenation (1)
- Relaxation (1)
- Residual Stress (1)
- Residual stress (1)
- SEM (1)
- Scaffold (1)
- Scanning electron microscopy (1)
- SchwarzP cells (1)
- Schwingstreifen (1)
- Shadowgraphy (1)
- Single crystal Ni-Base superalloys (1)
- Sintering (1)
- Slow crack growth (1)
- Slurry (1)
- Smectite (1)
- Soda-lime silicate glass (1)
- Solubility (1)
- Split-vacancy defect complexes (1)
- Spray drying (1)
- Stable crack growth (1)
- Stress distribution (1)
- Stress intensity factor (1)
- Structural dynamics (1)
- Synchrotron micro-tomography (1)
- TEM (1)
- Thermal cycling (1)
- Thermal desorption mass spectrometry (1)
- Thermoelectric properties (1)
- Thermography (1)
- Thermoplastic prepreg (1)
- Thermoset composition (1)
- Three-dimensional Bone tissue engineering (1)
- ToF-SIMS (1)
- Transformer (1)
- Transmission electron microscopy (1)
- Transmission electron microscopy (TEM) (1)
- Two-photon polymerization (1)
- UV-irradiation (1)
- Ultrasound (1)
- Unidirectional composites (1)
- Vickers indentation (1)
- Volatiles from thermosets (1)
- Volume changes (1)
- Water content (1)
- Water speciation (1)
- Wet chemical etching (1)
- X-ray Diffraction (1)
- X-ray absorption spectroscopy (1)
- X-ray refraction (1)
- Zirconia (1)
- Zirconia-toughened alumina (1)
- hydrogen storage (1)
Organisationseinheit der BAM
- 5 Werkstofftechnik (50)
- 5.1 Mikrostruktur Design und Degradation (18)
- 5.4 Multimateriale Fertigungsprozesse (13)
- 6 Materialchemie (7)
- 5.3 Polymere Verbundwerkstoffe (6)
- 5.6 Glas (6)
- 5.0 Abteilungsleitung und andere (5)
- 7 Bauwerkssicherheit (4)
- 8 Zerstörungsfreie Prüfung (4)
- 5.2 Metallische Hochtemperaturwerkstoffe (3)
Paper des Monats
- ja (1)
Early Stage of Corrosion Formation on Pipeline Steel X70 Under Oxyfuel Atmosphere at Low Temperature
(2020)
The early stage of corrosion formation on X70 pipeline steel under oxyfuel atmosphere was investigated by applying a simulated gas mixture (CO2 containing 6700 ppmv O2, 100 ppmv NO2, 70 ppmv SO2 and 50 ppmv H2O) for 15 h at 278 K and ambient pressure. Short-term tests (6 h) revealed that the corrosion starts as local spots related to grinding marks progressing by time and moisture until a closed layer was formed. Acid droplets (pH 1.5), generated in the gas atmosphere, containing a mixture of H2SO4 and HNO3, were identified as corrosion starters. After 15 h of exposure, corrosion products were mainly X-ray amorphous and only partially crystalline. In-situ energy-dispersive X-ray diffraction (EDXRD) results showed that the crystalline fractions consist primarily of water-bearing iron sulfates. Applying Raman spectroscopy, water-bearing iron nitrates were detected as subordinated phases. Supplementary long-term tests exhibited a significant increase in the crystalline fraction and formation of additional water-bearing iron sulfates. All phases of the corrosion layer were intergrown in a nanocrystalline network. In addition, numerous globular structures have been detected above the corrosion layer, which were identified as hydrated iron sulphate and hematite. As a type of corrosion, shallow pit formation was identified, and the corrosion rate was about 0.1 mma−1. In addition to in-situ EDXRD, SEM/EDS, TEM, Raman spectroscopy and interferometry were used to chemically and microstructurally analyze the corrosion products.
Low cost, high-efficiency catalysts towards water splitting are urgently required to fulfil the increasing demand for energy. In this work, low-loading (<20 wt%) Ni-confined in layered metal oxide anode catalysts (birnessite and lepidocrocite titanate) have been synthesized by facile ion exchange methodology and subjected to systematic electrochemical studies. It was found that Ni-intercalated on K-rich birnessite (Ni-KMO) presents an onset overpotential (ηonset) as low as 100 mV and overpotential at 10 mA cm−2 (η10) of 206 mV in pH = 14 electrolyte. By combining electrochemical methods and X-ray absorption and emission spectroscopies (XAS and XES), we demonstrate Ni sites are the active sites for OER catalysis and that the Mn3+ sites facilitate Ni intercalation during the ion-exchange process, but display no observable contribution towards OER activity. The effect of the pH and the nature of the supporting electrolyte on the electrochemical performance was also evaluated.
Modern air-liners and wind turbine rotor blades are made up primarily of fiber reinforced plastics. Failure of these materials heavily impairs the serviceability and the operational safety. Consequently, knowledge of the failure behavior under static and cyclic loads is of great interest to estimate the operational strength and to compare the performance of different materials. Ideally, the damage evolution under operational load is determined with in situ non-destructive testing techniques. Here, we report in-situ synchrotron X-ray imaging of tensile stress induced cracks in carbon fiber reinforced plastics due to inter-fiber failure. An inhouse designed compact tensile testing machine with a load range up to 15 kN was integrated into the beamline. Since conventional radiographs do not reveal sufficient contrast to distinguish cracks due to inter-fiber failure and micro cracking from fiber bundles, the Diffraction Enhanced Imaging (DEI) technique is applied in order to separate primary and scattered (refracted) radiation by means of an analyzer crystal. This technique allows fast measurements over large fields-of-view and is ideal for in-situ investigations. Imaging and the tensile test are run at the highest possible frame rate (0.7 s-1 ) and the lowest possible strain rate (5.5∙10-4 s -1 ). For 0°/90° non-crimp fabrics, the first inter-fiber cracks occur at 380 MPa (strain 0.8 %). Prior to failure at about 760 MPa (strain 2.0 %), we observe the evolution of nearly equidistant (1 mm distance) cracks running across the entire sample in the fully damaged state.
Rapid cooling rates and steep temperature gradients are characteristic of additively manufactured parts and important factors for the residual stress formation. This study examined the influence of heat accumulation on the distribution of residual stress in two prisms produced by Laser Powder Bed Fusion (LPBF) of austenitic stainless steel 316L. The layers of the prisms were exposed using two different border fill scan strategies: one scanned from the centre to the perimeter and the other from the perimeter to the centre. The goal was to reveal the effect of different heat inputs on samples featuring the same solidification shrinkage. Residual stress was characterised in one plane perpendicular to the building direction at the mid height using Neutron and Lab X-ray diffraction. Thermography data obtained during the build process were analysed in order to correlate the cooling rates and apparent surface temperatures with the residual stress results. Optical microscopy and micro computed tomography were used to correlate defect populations with the residual stress distribution. The two scanning strategies led to residual stress distributions that were typical for additively manufactured components: compressive stresses in the bulk and tensile stresses at the surface. However, due to the different heat accumulation, the maximum residual stress levels differed. We concluded that solidification shrinkage plays a major role in determining the shape of the residual stress distribution, while the temperature gradient mechanism appears to determine the magnitude of peak residual stresses.
To explore the impact of ambient and structural water on static fatigue, the initiation and growth of 3279 Vickers induced median radial cracks were automatically recorded and analyzed. We find that humidity is more efficient in initiating cracks and promoting their growth than water, which is dissolved in the glass structure. In particular for slow crack growth (< 3x10-6 m s-1), tests in dry nitrogen showed a considerable decrease in the crack growth exponent with increasing water content of the glasses. On the other hand, if tests were performed in humid air, the crack growth exponent was independent of the water content of the hydrous glasses, while stress intensity decreased slightly. These observations indicate that water promotes the processes at the crack-tip regardless of its origin. However, ambient water is more efficient.
This manuscript is based on an oral contribution to the TMS 2020 annual meeting and is dedicated to Prof. Peter Liaw, who for decades has shown great interest in serrated plastic flow.
Here we will focus on the case of bulk metallic glasses, and begin with briefly summarizing some aspects of serrated and non-serrated inhomogeneous flow—a phenomenon that has perplexed materials scientists for decades. Four directions of research are identified that emerged out of the desire to fundamentally understand the intermittent inhomogeneous flow response. These research directions gear away from the phenomenological stress–strain behavior but put the underlying shear defect into focus. Unsolved problems and future research topics are discussed.
Subjecting metallic glasses repeatedly to liquid nitrogen temperature has become a popular method to homogeneously rejuvenate the material. Here we reveal the atomic-scale structural dynamics using in- situ x-ray photon correlation spectroscopy (XPCS) during and after cryogenic cycling of a Zr-based metallic glass in two structural states (plate and ribbon). Heterogeneous structural dynamics is observed at 300 K that changes to monotonic aging at 78 K. It is found that cryogenic cycling homogenizes the relaxation time distribution. This effect is much more pronounced in the ribbon, which is the only structural state that rejuvenates upon cycling. We furthermore reveal how fast atomic-scale dynamics is correlated with longtime structural relaxation times irrespective of the structural state, and that the ribbon exhibits unexpected additional fast atomic-scale relaxation in comparison to the plate material. A structural picture emerges that points towards heterogeneities in the fictive temperature as a requirement for cryogenic energy storage.
Systematic microstructure design requires reliable thermodynamic descriptions of each and all microstructure elements. While such descriptions are well established for most bulk phases, thermodynamic assessment of microstructure defects is challenging because of their individualistic nature. In this paper, a model is devised for assessing grain boundary thermodynamics based on available bulk thermodynamic data. We propose a continuous relative atomic density field and its spatial gradients to describe the grain boundary region with reference to the homogeneous bulk and derive the grain boundary Gibbs free energy functional. The grain boundary segregation isotherm and phase diagram are computed for a regular binary solid solution, and qualitatively benchmarked for the Pt–Au system. The relationships between the grain boundary's atomic density, excess free volume, and misorientation angle are discussed. Combining the current density-based model with available bulk thermodynamic databases enables constructing databases, phase diagrams, and segregation isotherms for grain boundaries, opening possibilities for studying and designing heterogeneous microstructures.
Approximant-based orientation determination of quasicrystals using electron backscatter diffraction
(2020)
Orientation mapping of quasicrystalline materials is demonstrated using crystalline approximant structures in the technique of electron backscatter diffraction (EBSD). The approximant-based orientations are symmetrised according to the rotational point group of the quasicrystal, including the visualization of orientation maps using proper colour keys for quasicrystal symmetries. Alternatively, approximant-based orientation data can also be treated using pseudosymmetry post-processing options in the EBSD system software, which enables basic grain size estimations. Approximant-based orientation analyses are demonstrated for icosahedral and decagonal quasicrystals.
This paper investigates fast and inexpensive measurement methods for defect detection in parts produced by Additive Manufacturing (AM) with special focus on lattice parts made of ceramics. By Lithography-based Ceramic Manufacturing, parts were built both without defects and with typical defects intentionally introduced. These defects were investigated and confirmed by industrial X-ray Computed Tomography. Alternative inexpensive methods were applied afterwards on the parts such as weighing, volume determination by Archimedes method and gas permeability measurement. The results showed, that defects resulting in around 20% of change in volume and mass could be separated from parts free of defects by determination of mass or volume. Minor defects were not detectable as they were in the range of process-related fluctuations. Permeability measurement did not allow to safely identify parts with defects. The measurement methods investigated can be easily integrated in AM process chains to support quality control.