5 Werkstofftechnik
Filtern
Dokumenttyp
- Vortrag (362)
- Posterpräsentation (100)
- Zeitschriftenartikel (59)
- Beitrag zu einem Tagungsband (54)
- Forschungsdatensatz (27)
- Buchkapitel (6)
- Dissertation (4)
- Beitrag zu einem Sammelband (2)
- Sonstiges (2)
- Corrigendum (1)
Sprache
- Englisch (620) (entfernen)
Referierte Publikation
- nein (620) (entfernen)
Schlagworte
- Additive Manufacturing (52)
- Corrosion (44)
- Additive manufacturing (39)
- Ontology (32)
- Microstructure (28)
- Glass (27)
- Creep (22)
- Fatigue (20)
- Transmission electron microscopy (17)
- Crack growth (16)
Organisationseinheit der BAM
- 5 Werkstofftechnik (620)
- 5.1 Mikrostruktur Design und Degradation (174)
- 5.2 Metallische Hochtemperaturwerkstoffe (163)
- 5.4 Multimateriale Fertigungsprozesse (123)
- 5.6 Glas (90)
- 5.3 Polymere Verbundwerkstoffe (63)
- 5.5 Materialmodellierung (58)
- 8 Zerstörungsfreie Prüfung (54)
- 7 Bauwerkssicherheit (52)
- 9 Komponentensicherheit (47)
- 8.5 Röntgenbildgebung (42)
- 6 Materialchemie (40)
- 7.6 Korrosion und Korrosionsschutz (33)
- 5.0 Abteilungsleitung und andere (27)
- 9.4 Integrität von Schweißverbindungen (19)
- 6.3 Strukturanalytik (18)
- 6.1 Oberflächen- und Dünnschichtanalyse (16)
- 9.6 Additive Fertigung metallischer Komponenten (16)
- 1 Analytische Chemie; Referenzmaterialien (14)
- 3 Gefahrgutumschließungen; Energiespeicher (12)
- 4 Material und Umwelt (11)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (11)
- 9.0 Abteilungsleitung und andere (10)
- 8.0 Abteilungsleitung und andere (8)
- 9.3 Schweißtechnische Fertigungsverfahren (7)
- 1.2 Biophotonik (6)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (6)
- 4.2 Material-Mikrobiom Wechselwirkungen (6)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (5)
- 1.6 Anorganische Referenzmaterialien (4)
- 4.1 Biologische Materialschädigung und Referenzorganismen (4)
- 6.0 Abteilungsleitung und andere (4)
- 6.6 Physik und chemische Analytik der Polymere (4)
- 7.4 Baustofftechnologie (4)
- 8.4 Akustische und elektromagnetische Verfahren (4)
- 9.2 Versuchsanlagen und Prüftechnik (4)
- 6.4 Materialinformatik (3)
- 8.6 Faseroptische Sensorik (3)
- 1.4 Prozessanalytik (2)
- 2 Prozess- und Anlagensicherheit (2)
- 2.1 Sicherheit von Energieträgern (2)
- 3.0 Abteilungsleitung und andere (2)
- 3.4 Sicherheit von Lagerbehältern (2)
- 3.5 Sicherheit von Gasspeichern (2)
- 4.3 Schadstofftransfer und Umwelttechnologien (2)
- 6.7 Materialsynthese und Design (2)
- 7.0 Abteilungsleitung und andere (2)
- 7.7 Modellierung und Simulation (2)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (2)
- 1.0 Abteilungsleitung und andere (1)
- 1.8 Umweltanalytik (1)
- 1.9 Chemische und optische Sensorik (1)
- 3.6 Elektrochemische Energiematerialien (1)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (1)
- 6.2 Material- und Oberflächentechnologien (1)
- 9.5 Tribologie und Verschleißschutz (1)
- VP Vizepräsident (1)
- VP.1 eScience (1)
A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated.
The common fatigue life certification of aircrafts according to the certification Standards 23 and 25 follows a building block approach. Static tests at room temperature as well in humid and high temperature conditions are done on the coupon level. Additionally, a full-scale static and fatigue test must be performed on the complete airframe (minimum on the fuselage together with the wing). For each type-certificate the complete building block approach test program must be performed.
Traditionally in Germany, the certification of sailplanes (Certification Standard 22) follows rather a family concept. A shared data base was created over the last 50 years based upon a large number of material testing. In addition to static tests at room temperature and hot-humid conditions, fatigue tests are also done on the coupon level. Additional static and fatigue tests were done on complex structures such as spar-beams, fuselages and full-scale wing structures. However, for each type-certificate, only static tests should be performed in full-scale. This concept is determined by the certification memorandum CM-S-006 “Composite Lightweight Aircraft” 2017.
The presentation was given as an introduction to the discussion about the future expectations and developments of the EASA concerning the type-certification of lightweight aircrafts according to CS22 at the OSTIVE Sailplane Development Panel Meeting at the EASA in Cologne on the 11th of October 2019.
The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach, both of which are presented in “Part 2: Microstructural Evolution during Cyclic Loading and its Representation in a Physically-based Micromechanical Model“.
The current competitive situation on electricity markets forces conventional power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach.
Spherical mesoporous bioactive glasses in the silicon dioxide (SiO2)-phosphorus pentoxide (P2O5)–calcium oxide (CaO) system with a high specific surface area of up to 300m2/g and a medium pore radius of 4 nm were synthesized by using a simple one-pot surfactant-assisted sol–gel synthesis method followed by calcination at 500–700°C. The authors were able to control the particle properties by varying synthesis parameters to achieve microscale powders with spherical morphology and a particle size of around 5–10 mm by employing one structure-directing agent. Due to a high Calcium oxide content of 33·6mol% and a phosphorus pentoxide content of 4·0mol%, the powder showed very good bioactivity up to 7 d of immersion in simulated Body fluid. The resulting microspheres are promising materials for a variety of life science applications, as further processing – for example, granulation – is unnecessary. Microspheres can be applied as materials for powder-based additive manufacturing or in stable suspensions for drug release, in bone cements or fillers.
The application of implants e.g. for osteosynthesis or substitution of worn out joints is common practice since decades. Successes in surgery and orthopedics are highly dependent on the use of artificial parts for implanting into the human body. Over the years the number of surgical procedures and the number of different implants were growing rapidly. Implants, however, are exposed to complex mechanical, corrosive and tribological loads along with restriction in geometric dimension. While being essentially successful, the sheer number of cases leads to a rising number of implant failures. Such failures are painful for the affected patients and are very costly.
The failure cases presented in this paper occurred from 1981 to 2016. The predominant failure mechanism of all kinds of implants is fatigue fracture. Fatigue cracks are initiated due to a whole bunch of reasons: Material defects and fabrication defects are rare events. The main factors are cyclic overload due to improper fitting with delayed bone healing, corrosion and unauthorized modification of the implant during surgery
Statistically the mean time between damage events on rotor blades is 6 years (Deutscher Windenergie Report 2006). Due to imperfection in the production the shell structures get cracks after a few years fare before the designed life time. A shell test rig was built at BAM for efficient research on the effects of defects in production.
In-situ and ex-situ NDT give a better understanding from degradation processes in composite materials.
With advanced methods in the research on the fatigue behaviour of FRP it was found a load level of infinite life for GFRP and CFRP. This is in the range of typical strain values of airliners and rotor blades in normal operation.
Due to the fibre-composite nature NDT techniques have to be suitable to a wide length scale to image micro cracking as well as bigger defects. Therefore different techniques have to be applied and developed.
Even for the basic measurements of material data for design and engineering of composite structures there is a need to upgrade standards. With a new shear frame test rig more precise values can be obtained.
With advanced methods in the research on the fatigue behaviour of FRP it was found a load level of infinite life for GFRP and CFRP. This is in the range of typical strain values of airliners and rotor blades in normal operation.
Statistically the mean time between damage events on rotor blades is 6 years (Deutscher Windenergie Report 2006). Due to imperfection in the production the shell structures get cracks after a few years fare before the designed life time. A shell test rig was built at BAM for efficient research on the effects of defects in production.
Test blades of ~10m are an efficient way for SHM research and evaluation of NDT-methods and blade geometry.
A shell test bench was developed at BAM 5.3 which allows for static and fatigue testing of curved fiber-reinforced plastic (FRP) structures, during which in-situ the damage state can be non-destructively inspected by thermography and strain-field measurement techniques. Sandwich shell specimens with typical wind turbine blade manufacturing defects were designed and tested. The tested imperfections show a fairly significant reduction (up to 90%) of the shell test specimens‘ lifetime, depending on the type of imperfection. Using the in-situ NDT methods incorporated in the shell test bench, the location and cycle time of the initial defects and the damage evolution was investigated.
The described investigation of carbon-fibre-reinforced plastics (CFRP) documents that damage evolution can be observed by means of X-ray refractography. Comparative investigations with synchrotron technique on CFRP and grey-scale analysis on glass fibre-reinforced-plastics (GFRP) confirm these results. Moreover it was found that the fracture mechanical properties of the matrix system influence damage nucleation and propagation in the laminate during static and fatigue loads. Single-step fatigue tests were carried out on Laminates with RIM135 and LY556 matrix systems made from non-crimped fabric (NCF) or twill weave in different fibre orientations. The damage to the LY556 laminates was characterized by laminate cracks growing rapidly over the whole specimen width, whereas the damage on the RIM135 laminates was characterized by an earlier onset of micro-cracking followed by laminate cracks. The specimens were fatigued up to 108 (very high cycle fatigue (VHCF) regime) load cycles. S-N-curves of damage initiation were drawn and boundaries were identified for endurance within the VHCF regime. A phenomenology based model focusing on matrix stress was applied to reproduce the first inter-fibre failure (IFF) under static and fatigue loads.