5 Werkstofftechnik
Filtern
Dokumenttyp
- Zeitschriftenartikel (12)
- Vortrag (5)
- Beitrag zu einem Tagungsband (1)
- Sonstiges (1)
- Forschungsbericht (1)
Schlagworte
- Calcination (3)
- LTCC (3)
- Ceramic spring (2)
- Ceramics (2)
- Keramikfeder (2)
- Reaction-sintering (2)
- Sensorik (2)
- Spannungs-Dehnungs-Verhalten (2)
- Spray drying (2)
- Thermoelectric properties (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (5)
This study combines three different approaches to lower the sintering temperature of Sm-doped CaMnO3 to save energy in production and facilitate co-firing with other low-firing oxides or metallization. The surface energy of the powder was increased by fine milling, sintering kinetics were enhanced by additives, and uniaxial pressure during sintering was applied. The shrinkage, density, microstructure, and thermoelectric properties were evaluated. Compared to micro-sized powder, the use of finely ground powder allows us to lower the sintering temperature by 150 K without reduction of the power factor. By screening the effect of various common additives on linear shrinkage of CaMnO3 after sintering at 1100 ○C for 2 h, CuO is identified as the most effective additive. Densification at sintering temperatures below 1000 ○C can be significantly increased by pressure-assisted sintering. The power factor at room temperature of CaMnO3 nano-powder sintered at 1250 ○C was 445 μW/(m K2). Sintering at 1100 ○C reduced the power factor to 130 μW/(m K2) for CaMnO3 nano-powder, while addition of 4 wt.% CuO to the same powder led to ∼290 μW/(m K2). The combination of fine milling, CuO addition, and pressureassisted sintering at 950 ○C resulted in a power factor of ∼130 μW/(m K2). These results show that nano-sized powder and CuO addition are successful and recommendable strategies to produce CaMnO3 with competitive properties at significantly reduced temperatures and dwell times.
Glass-ceramic composites as insulation material for thermoelectric oxide multilayer generators
(2021)
Thermoelectric generators can be used as energy harvesters for sensor applications.
Adapting the ceramic multilayer technology, their production can be
highly automated. In such multilayer thermoelectric generators, the electrical insulation material, which separates the thermoelectric legs, is crucial for the performance of the device. The insulationmaterial should be adapted to the thermoelectric regarding its averaged coefficient of thermal expansion α and its sintering temperature while maintaining a high resistivity.
In this study, starting from theoretical calculations, a glass-ceramic Composite material adapted for multilayer generators fromcalciummanganate and Calcium cobaltite is developed. The material is optimized towards an α of 11 × 10−6 K−1 (20–500◦C), a sintering temperature of 900◦C, and a high resistivity up to 800◦C.
Calculated and measured α are in good agreement. The chosen glass-ceramic composite with 45 vol.% quartz has a resistivity of 1 × 107 Ωcm and an open porosity of <3%. Sintered multilayer samples from tape-cast thermoelectric oxides and screen-printed insulation show only small reaction layers. It can be concluded that glass-ceramic composites are a well-suited material class for insulation layers as their physical properties can be tuned by varying glass composition or dispersion phases.
Dieses Strategiepapier zielt darauf ab, Akteuren und Entscheidungsträgern den Status der Digitalisierung in der keramischen Fertigung, erfolgreiche Best-Practice-Beispiele aber auch die Herausforderungen nahezubringen, die es nun anzugehen gilt. Es ist die Vision, die Keramikfertigung durchgehend zu digitalisieren und alle Schritte des Produktkreislaufs lückenlos über die gesamte Wertschöpfungs- und Nutzungskette zu vernetzen: also eine Keramikindustrie 4.0 zu etablieren. Das Strategiepapier erfasst zunächst die Spezifität der keramischen Fertigung und nimmt eine Analyse des gegenwärtigen Standes der Digitalisierung in der keramischen Industrie vor, auch anhand einiger ausgewählter Beispiele aus der industriellen Praxis. Auf Basis der wesentlichen Bausteine für eine Fertigungsdigitalisierung werden schließlich die Chancen für Keramikproduzenten sowie der erforderliche Forschungs- und Entwicklungsbedarf aufgezeigt.
The relationship between fracture toughness and Yttria content in modern zirconia ceramics was revised. For that purpose, we evaluated here 10 modern Y2O3-stabilized zirconia (YSZ) materials currently used in biomedical applications, namely prosthetic and implant dentistry. The most relevant range between 2-5 mol% Y2O3 was addressed by selecting from conventional opaque 3 mol% YSZ up to more translucent compositions (4-5 mol% YSZs). A technical 2YSZ was used to extend the range of our evaluation. The bulk mol% Y2O3 concentration was measured by X-Ray Fluorescence Spectroscopy. Phase quantification by Rietveld refinement considered two tetragonal phases or an additional cubic phase. A first-account of the fracture toughness (KIc) of the pre-sintered blocks is given, which amounted to 0.4 – 0.7 MPa√m. In the fully-densified state, an inverse power-law behavior was obtained between KIc and bulk mol% Y2O3 content, whether using only our measurements or including literature data, challenging some established relationships. A linear relationship between KIc and the fraction of the transformable t-phase was established within the range of 30–70 vol%.
The 5G technology promises real time data transmission for industrial processes, autonomous driving, virtual and augmented reality, E-health applications and many more. The Low Temperature Co-fired Ceramics (LTCC) technology is well suited for the manufacturing of microelectronic components for such applications. Still, improvement of the technology such as further miniaturization is required. This study focuses on the characterization of inner metallization of LTCC multilayer modules, especially on the vertical interconnect access (VIA). Critical considerations for this characterization are delamination, pore clustering in and at the edge of the VIA, deformation, and stacking offset. A LTCC multilayer consisting of a glassy crystalline matrix with silver based VIAs was investigated by synchrotron x-ray tomography (CT). The aim of this study is to propose a multitude of structural characteristic values to maximize the information gained from the available dataset. Data analysis has been done with the open source software ImageJ as well as several additional plugins. The high-resolution CT data was evaluated through 2D slices for accessibility reasons. The segmentation of all 2000 slices to assess the different regions e.g. pores, silver and glass ceramic was done by a supervised machine learning algorithm. A quantitative evaluation of shape, deformation, and porosity of the VIA with respect to its dimensions is presented and the suitability of the characterization approach is assessed.
The influence of the atomization technique on the suitability of granules for dry pressing is the focus of the presented investigations. Therefore, destabilized alumina, zirconia, and zirconia toughened alumina (ZTA) slurries were spray dried and the obtained granules were used to fabricate green and finally sintered bodies for evaluation.
Granules made in a laboratory spray dryer with a two-fluid nozzle served as a reference. An ultrasonic atomizer was integrated into the same spray dryer and the influence on the granule properties was evaluated. Untapped bulk density, granule size distribution, and flowability are among the evaluated granule-related properties as well as the granule yield which is used as an indicator of the process efficiency.
Yield and flowability as most important granule properties are clearly improved when atomization is realized with ultrasound. The investigated sinter body properties include porosity, sinter body density, and biaxial strength and are as well positively affected by switching the atomization technique to ultrasound. Therefore, the Approach to improve the compressibility of granules by ultrasonic atomization, which leads to an improved microstructure, density, and strength of sintered bodies, has proven to be successful for single-component ceramics (alumina and zirconia) as well as for the multicomponent ceramic ZTA.
Transformers couple two sections of a circuit by electromagnetic induction. They are widely used to either transform alternating voltage levels or to transmit power or signals across galvanic isolation. Both of these functions are essential for the operation of sensors and controllers. Covering all aspects from idea to circuit performance and from design to manufacture, this paper presents the first comprehensive description of the making of miniaturized, rugged, up-to-100W transformers for embedding into multilayer circuit boards. For circular coils, the well-manageable Ampere-Laplace law is shown to yield reliable designs, predicting correctly the performance of manufactured hardware. This enables fast design without lengthy finite element modelling. In the low-power linear regime, basic relations describe how the device’s characteristics evolve from the material properties and device structure. While scattering Parameters are useful for the analysis of isolated transformers with their intrinsic parasitics, the interaction with the components of the final circuit and the aspects of power and efficiency are addressed by chain matrixes.
While these design rules are similar for multilayer boards of different material (like epoxy, Teflon, ceramics), the manufacturing of ceramic board transformers is considered here in detail. Low-temperature-cofired ceramic (LTCC) boards being sintered at 900 °C are particularly suited for harsh environments with chemical or thermal stress as frequently found at sensor positions. The transformer performance usually benefits from or even requires an integrated ceramic core of higher permeability, a ferrite, to shape the magnetic flux. Methods to sinter ferrites inside a dielectric ceramic multilayerandto measure their performance are therefore described in detail.Asthe sintering behaviour of dielectricandmagnetic ceramics differs considerably, their simultaneous sintering is challenging.However, the sintering temperatures of the usefulMnZnand NiZnCu ferrites can be lowered to that of the dielectric material with only moderate loss of permeability by glass additives. Furthermore, thermal mismatch between materials causes catastrophic failure or at least stress and loss of magnetic performance during cooling to room temperature after sintering. This is avoidable by either adjusting the thermal expansion coefficient of the ferrite or by enclosing the ferrite between stressreleasing separation layers.We present the state of the art in materials development according to the first approach as well as fully functional devices made with the second technique.
Other applications not directly addressed but well related to this work are characterized by low load resistance in relation to the coil resistance of the transformer. Efficient power transmission then requires that technological solutions are applied to achieve the lowest possible resistive loss inside the coils by an enlarged conductor cross-section.
As this is particularly challenging for LTCC boards, a technique is discussed to fabricate conductor traces with a thickness larger than their width.
The wireless high-frequency technology requires a robust, cost-effective, and highly integrated substrate technology offering the capability for areas of tailored permittivity. The wet-chemical porosification of low temperature co-fired ceramics (LTCC) substrates offers such an approach by locally embedding air. Porosification of LTCC in both extremely acidic and alkaline media has been investigated in previous works. However, for improving the available knowledge on the porosification of LTCC with H3PO4 as a standard and a widely used etching solution, the impact of solution concentration was systematically investigated and a substantial improvement in the etching performance was achieved. Moreover, in the present study, for the first time, the intermediate pH values, and the impact of pH as a key parameter on the etching process have been investigated. For this purpose, the applicability of phosphate buffer solution (PBS) as a prospective novel etchant mixture for the porosification of a commercially available LTCC tape (Ceramtape GC) was explored. Valuable information about surface morphology, crystalline composition, and the pore structure of the etched LTCCs was gathered employing scanning electron microscopy, transmission electron microscopy, X-ray diffraction analysis, and mercury porosimetry measurements. Based on these findings, the performance of PBS-based etchant systems towards the generation of porous LTCCs combining high depths of porosification with acceptable surface characteristics for subsequent metallization is demonstrated. Based on the obtained results, by application of a 0.2 mol L−1 solution of PBS, the effective relative permittivity of test samples with a thickness of approximately 600 µm and a porosification depth of 186 µm from each side, could be reduced up to 10% of its initial “as fired” value. Also, based on the measurement results and by measuring the depth of porosification, the permittivity of the etched layer was estimated to show a reduction of up to 22% compared to the initial “as fired” value.
Calcium cobaltite Ca3Co4O9, abbreviated Co349, is a promising thermoelectric material for high‐temperature applications in air. Its anisotropic properties can be assigned to polycrystalline parts by texturing. Tape casting and pressure‐assisted sintering (PAS) are a possible future way for a cost‐effective mass‐production of thermoelectric generators. This study examines the influence of pressure and dwell time during PAS at 900°C of tape‐cast Co349 on texture and thermoelectric properties. Tape casting aligns lentoid Co349. PAS results in a textured Co349 microstructure with the thermoelectrically favorable ab‐direction perpendicular to the pressing direction. By pressure variation during sintering, the microstructure of Co349 can be tailored either toward a maximum figure of merit as required for energy harvesting or toward a maximum power factor as required for energy harvesting. Moderate pressure of 2.5 MPa results in 25% porosity and a textured microstructure with a figure of merit of 0.13 at 700°C, two times higher than the dry‐pressed, pressureless‐sintered reference. A pressure of 7.5 MPa leads to 94% density and a high power factor of 326 µW/mK2 at 800°C, which is 11 times higher than the dry‐pressed reference (30 MPa) from the same powder.
Das Ziel des Gesamtvorhabens bestand darin, einen neuartigen kapazitiven Sensortyp zur hochauflösenden Bestimmung von Masse- und Gravitationskraftänderungen zu entwickeln. Bisherige Technologien nutzten dafür Federn oder Biegebalken aus gehärteten metallischen Werkstoffen, deren Alterungsverhalten die Präzision der Kräftemessung begrenzen. Grundprinzip des neuen Sensortyps ist es, eine auf die keramische Feder einwirkenden Änderung der Gewichts- oder Gravitationskraft durch eine Erfassung der Kapazitätsänderung am Sensor zu bestimmen. Dazu muss die durch Stauchung oder Dehnung der Feder entstehende Kapazitätsänderung mit hoher Auflösung reproduzierbar gemessen werden. Neben einem geeigneten Sensordesign waren Lösungen für Messsignalerfassung und -auswertung (Elektronik/Software) und die Systemintegration zu entwickeln.
Die wichtigsten im Rahmen des BAM-Teilvorhabens erzielten Ergebnisse sind:
- Ausgehend von kommerziellen High-end Keramikpulvern wurden durch Optimierung der keramischen Technologie nahezu porenfreie Al2O3, ZrO2 und Si3N4-Werkstoffe hergestellt und bezüglich Gefüge und Phasenbestand sowie mechanischen, thermischen und elektrischen Eigenschaften bewertet. Insbesondere die defektfreie Herstellung von nanostrukturierten Werkstoffen erforderte umfangreiche Variationen der Prozessparameter. Geeignete Werkstoffvarianten wurden für die Federherstellung ausgewählt.
- Gemeinsam mit den Projektpartnern wurden Layoutvarianten für Schraubendruckfedern mit rechteckigem Windungsquerschnitt und für die Federeinbindung in das Sensorsystem erarbeitet.
- 4 Federvarianten wurden an der BAM durch Hartbearbeitung von gesinterten Hohlzylindern umgesetzt. Fertigungstoleranzen von < ±10 µm für Windungsbreite, Windungshöhe und Windungsabstand und dünnfilm-kompatible innere Windungsflächen (Ra < 0,2 µm) wurden erreicht. Al2O3- und ZrO2-Federn können rissfrei und mit sehr guter Kantenqualität gefertigt werden, bei Si3N4-Federn konnten Kantenschädigungen nicht vollständig verhindert werden.
- Mit der entwickelten Herstellungstechnologie können sowohl „harte“ als auch sehr „weiche“ Federn produziert werden. Federkonstanten zwischen 0,02 N/mm und 10 N/mm wurden realisiert. Die Reproduzierbarkeit der Federfertigung ist gegeben, innerhalb einer Charge unterschieden sich die Federkonstanten der gefertigten Federn nur um etwa +/- 1%.
- An einem speziell entwickelten Versuchsstand wurden die Federn unter zyklischer Druckbelastung im Temperaturbereich von -20 bis +80 °C untersucht. An den Al2O3- und ZrO2-Federn wurden keine Schädigungen beobachtet, die Federkonstante wird durch die zyklische Langzeitbelastung nicht verändert.
- Die Eignung der keramischen Federn für den Applikationsfall wurde mit zahlreichen Spannungs-Dehnungs-Experimenten, teilweise an speziell aufgebauten Versuchsapparaturen, untersucht. An Al2O3- und Si3N4-Federn wurde – wie erwartet – gefunden, dass die Federkonstante unabhängig von der Belastungsgeschwindigkeit ist und unter konstanter Last auch über lange Zeiträume keine Verformung auftritt. Überraschenderweise zeigten ZrO2 (TZP)-Federn ein zeitabhängiges Verhalten unter Last. Dieses ist besonders stark bei Y-stabilisierten Werkstoffvarianten ausgebildet, wurde aber mit Hochpräzisionsmessungen auch bei Ce-stabilsierten Werkstoffen nachgewiesen. Die Deformation ist reversibel, eine vollständige Relaxation wird erst nach Tagen erreicht. Aufgrund der zeitabhängigen Verformung können ZrO2 (TZP)-Federn, trotz ihrer hervorragenden Festigkeit und Bruchzähigkeit, nicht für die konzipierten Sensorfedern eingesetzt werden.
- Das durch die Fa. Siegert TFT entwickelte Metallisierungs-Schichtsystem, bestehend aus aufgesputterten Ti-, Pt- und Au-Schichten verstärkt durch eine galvanisch aufgebrachte Au-Schicht, wurde an der BAM umfassend bewertet. Die Schichten sind untereinander und mit der Keramik weitgehend defektfrei verbunden, die lokale Schichtdicke schwankt jedoch bedingt durch Abschattungseffekte während der Beschichtungsvorgang. Es wurden Schichtwiderstände zwischen 50 und 90 Ohm und damit die Zielvorgabe des Projektes (< 100 Ohm) erreicht. In statischen und dynamischen Belastungstests wurden keine Veränderungen der Leitungswiderstände festgestellt.
- Zur Erhöhung der Kapazität des Kondensators kann der Raum zwischen den Federwindungen statt mit Luft mit einer Flüssigkeit mit hoher Dielektrizitätskonstante gefüllt werden. Als geeignete Flüssigkeit wurde Propylencarbonat mit einer Dielektrizitätskonstante von 65, einem hohen Siedepunkt und einer geringen Viskosität identifiziert. Um eine noch höhere Dielektrizitätskonstante zwischen den Federwindungen zu erreichen. wurden Suspensionen aus Silikonöl und nanokristallinem Bariumtitanat hergestellt und bezüglich ihrer Langzeitstabiltät charakterisiert.
- Gemäß den Anforderungen des Projektpartners KOMPASS wurden maßgeschneiderte Al2O3-Federn mit einer Federkonstante < 0,1 N/mm hergestellt und für den Aufbau des finalen Demonstrator eingesetzt.
Die prinzipielle Funktionsfähigkeit des neuen Sensorkonzeptes auf Basis keramischer Federn wurde mit dem im Projekt aufgebauten Demonstrator nachgewiesen. Die Umsetzung der F+E-ergebnisse in eine industrielle Nutzung zur Herstellung von Gravimetern wird vom Projektpartner KOMPASS angestrebt und ist bereits mit detaillierten Zeitplänen untersetzt.