5 Werkstofftechnik
Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (13)
- Zeitschriftenartikel (9)
- Vortrag (8)
- Forschungsbericht (1)
Schlagworte
- Corrosion (18)
- CCUS (10)
- Carbon steel (9)
- Impurities (7)
- CCS (6)
- Martensitic steel (6)
- CO2 (5)
- Carbon steels (5)
- Geothermal (5)
- Superaustenite steel (5)
Organisationseinheit der BAM
- 5 Werkstofftechnik (31) (entfernen)
Eingeladener Vortrag
- nein (8)
To reveal the corrosion resistance of casing steel/mortar interface in CO2 injection condition, sandwich samples were prepared and exposed up to 20 weeks in aquifer fluid under 10 MPa and 60 °C. Cross section analysis revealed the crevice corrosion as main mechanism instead of pitting corrosion, which would be expected to happen in the extremely high Chloride concentration. Detailed analysis using EDS line scan shown the slow diffusion of Chloride, suggesting why pitting did not happen after 20 weeks. To mimic the passivated steel surface, the steel coupon was passivated in simulated pore solution having pH 13.5 for 42 days. The passivated coupon was further exposed to NGB solution for 28 days. Electrochemical characterization was performed along the exposure processes to reveal the change in impedance, indicating the corrosion resistance of steel casing/mortar interface.