4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung
Filtern
Dokumenttyp
Sprache
- Englisch (105) (entfernen)
Schlagworte
- Phosphorus (14)
- Phosphorus recovery (14)
- Sewage sludge (12)
- Recycling (10)
- Fertilizer (8)
- BOFS (6)
- Fertilzer (6)
- Hydraulic reactivity (6)
- Scandium (6)
- Portland Cement (5)
Organisationseinheit der BAM
- 4 Material und Umwelt (105)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (105)
- 4.3 Schadstofftransfer und Umwelttechnologien (14)
- 7 Bauwerkssicherheit (11)
- 7.1 Baustoffe (10)
- 7.4 Baustofftechnologie (8)
- 1 Analytische Chemie; Referenzmaterialien (4)
- 1.7 Organische Spuren- und Lebensmittelanalytik (3)
- 6 Materialchemie (3)
- 6.3 Strukturanalytik (3)
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (39)
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
Uranium and thorium species in phosphate rock and sewage sludge ash based phosphorus fertilizers
(2020)
Phosphorus (P) is an essential element for all forms of life and is thus often applied as phosphate rock-based P-fertilizers in agriculture to enable continuous farming. However, these P-fertilizers contain also hazardous uranium (U) and thorium (Th), up to 660 and 220 mg/kg, respectively. On the contrary, novel P-fertilizers made from sewage sludge (ash) contain only low mass fractions of U and Th. In addition to the total amount of U and Th in P-fertilizers, their mobility and bioavailability is important, which depends to a large extent on their chemical state, especially oxidation state and chemical bonding. Thus, we analyzed their chemical state in various P-fertilizers by U and Th L3-edge HERFD-XANES spectroscopy. Phosphate rocks and sewage sludge-based P-fertilizers contain mainly U(IV) compounds which have only a low bioavailability. In contrast, acidic treatment of phosphate rock to produce super phosphates lead to an oxidation to U(VI) compounds (including formation of uranium phosphates) with a strongly increased bioavailability. On the contrary, all analyzed P-fertilizers contain Th in form of strongly insoluble phosphates and oxides with a low bioavailability. Additionally performed water extractions and Diffusive Gradients in Thin-films (DGT) experiments support these findings.
In recent times, as the need for new high-tech materials is growing steadily to fulfil future sustainability goals, more and more looks turn towards industrial waste streams as potential sources of valuable metals. Bauxite residue (BR), accumulating during alumina production, is one of the major waste streams in the metal industry. Suitable re-use possibilities for BR are intensively investigated including approaches for the recovery of scandium (Sc). This transition metal, even though rarely recognized by the broader audience yet, has recently gained the interest of e.g. aerospace industries and SOFC-producers since its use is strongly improving the performance and durability of the respective materials.
Even though many sources classify Sc as one of the REE, there are many aspects, such as its ionic radius, which significantly differentiate Sc from the REE and cause its behaviour to be distinct as well. The large ionic potential (radius/charge) causes Sc to be incompatible in most rock forming minerals, which results in generally low concentrations in the earth’s crust and rare occurrences of natural Sc-deposits.
The general occurrence of enriched concentrations of Sc in some BRs compared to the earth’s crust is known for some time now and has especially been investigated for Greek materials. However, the (geo)chemical and mineralogical behaviour, the Sc speciation, the association and the variation of Sc occurrences in BRs of different origin is still not fully understood. This study aims to gain better knowledge on the different kinds of Sc-occurrences and their possible impact on future recovery schemes. We therefore apply a diverse set of analytical methods including novel measurement techniques such as X-ray absorption near edge structure (XANES) spectroscopy as well as standard techniques such as electron microprobe analyses, and Raman spectroscopy on BRs from Germany, Hungary and Greece. Information on the local distribution of Sc is determined by high-resolution laser ablation – inductively coupled plasma – mass spectrometry (LA-ICP-MS) mappings.
Sc in Greek BR seems to have an affinity towards Fe-Phases such as Goethite and Hematite. However, whereas some of these phases show distinct enrichment of Sc, others are particularly barren, which might be a result of the different input materials. By means of XANES measurements it was possible to show that Sc in the Greek samples occurs adsorbed on the surface of those Fe-Phases, likely in the form of amorphous Sc-hydroxide or -oxyhydroxide or can be incorporated into the crystal lattice as well. The general affinity of Sc to those kinds of phases has been reported for natural rocks such as laterites before, where similar investigations were made using the XANES method [8]. Likewise, the Fe-association has been observed for Greek BR by Vind et al. [7]. Hungarian BRs show similar results as the Greek samples and LA-ICP-MS mappings show distinct Sc enrichment rims surrounding mineral particles. In German BR, Fe as well as Ti-phases occur to be partially enriched in Sc. Depending on the original primary bauxite, the source rock of the bauxite and the bauxite processing route, it is likely that many different parameters influence the occurrence and species of Sc in the BR. Theoretically, it either can therefore remain within its original carrier or can be partially or fully redistributed within the BR. Since the processing of the bauxite involves elevated temperatures, pressure and dissolving reagents, it is however very likely that some of the Sc will be redistributed and adsorb on mineral surfaces of smaller and larger particles, making beneficiation steps rather ineffective.
The study shows that there is no general rule defining how Sc is associated mineralogically or chemically within BRs. Therefore, the effective development of a recovery method needs a case specific background knowledge on the Sc-species present in the BR of interest. This research has received funding from the European Community’s Horizon 2020 Programme SCALE (H2020/2014-2020) under grant agreement n° 730105.
New developments in legislation and technology development for P-recovery were presented with focus on the situation in Germany.
Gypsum (calcium sulfate dihydrate) has excellent building material properties and has been widely used in constructions in the last decades in many countries. Accordingly, an increase of waste gypsum in C&D waste is expected in the upcoming years. On one hand, sulfates are unwanted in other secondary building materials (particularly in recycled concrete aggregates) and should be minimized for quality reasons. On the other hand, used gypsum from CDW can also be used in gypsum production if the high quality requirements for the recycled gypsum – especially regarding the sorting accuracy - are met.
A large percentage of the gypsum from buildings was installed as gypsum plasterboards in interior fittings so far. Gypsum plasterboards are comparatively simple to remove and to separate during selective dismantling. Therefore, a high sorting purity can be achieved. In addition, techniques for the recycling of gypsum plasterboards already exist and high quality standards can be achieved. Also, the reuse in gypsum production has been improved in the last decade. Furthermore, an environmental evaluation of the whole process of gypsum plasterboard recycling and reuse showed that this approach can be environmentally advantageous. Therefore, a closed-loop recycling of gypsum plasterboards is feasible.
This poster will show the development of gypsum consumption in different countries as well as a prognosis for the upcoming of gypsum in CDW in the future decades in Germany. Furthermore, a simplified scheme of the recycling process and selected results from an environmental evaluation will be presented.
As one of the most energy and carbon consuming industries, steelmakers have an intrinsic interest in the development of technologies, reducing their carbon footprint as well as their carbon input. Besides generating new feedstocks from biomass or waste polymers, the valorization of carbon fiber reinforced polymer (CFRP) waste streams seems to be extremely promising based on the high carbon content of carbon fibers (CF), chars from CFRP and even unprocessed CFRP waste of >92%, 98% and 79%, respectively. Although, reduction of environmental impact from those high-performance materials was achieved by the development of smart recycling solutions, the continuous truncation by mechanical treatment of CF over multiple cycles, analogous to paper fibers, and the large global CFRP waste stream of 62 kt/a demand for a sustainable management of end-of-life (EOL) CFRP. Recently it was demonstrated that CF can be used safely as reductant in pyrometallurgical processes in a downhole electric furnace without significant WHO fiber emission. Therefore we anticipate a huge potential of CF based materials as sustainable reductant for steelmaking in an electric arc furnace (EAF). To facilitate the applicability of EOL CFRP in steelmaking, we investigated the interaction between CF based materials and liquid metal phases, appearing during the process, on different scales. Particularly, we examined the reactivity, wettability and dissolution behavior of CF and CFRP concerning liquid slag and steel. The presented results indicate that understanding the impact of the microstructure of CF on their behavior is crucial for their application in EAF steelmaking without risking potential hazards by WHO fiber emission. Besides the detailed elucidation of structure reactivity relationships of CF, the broader impact on circular economy will be presented.
Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost.
Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced.
This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained.
Phosphorus (P) resource availability and quality is declining and recycling P-fertilizers from waste materials are becoming increasingly important. One important secondary P resource is sewage sludge (SSL) where P is often bound as aluminum phosphate (Al-P), iron phosphate (Fe-P) and polyphosphate (poly-P), respectively. Thermal treatment in different ways is a promising way in P recycling to produce highly plant-available P-fertilizers. To investigate mechanisms behind transformation of hardly available P-species toward plant-available P forms we treated a model SSL containing different kinds of defined P sources by low-temperature conversion (LTC) at 500 °C and subsequent thermochemical treatment of the LTC product with Na additives (TCT) at 950 °C, respectively. Pot experiments with ryegrass were carried out to determine the plant availability of P of the different treatments. The poly-P (here pyrophosphates) based fertilizers had a very high plant availability after both thermal treatments. During LTC treatment the plant availability of the Fe-P and Al-P variants increased because of the Formation of Fe(II) phosphates and/or pyro-/polyphosphates. Especially the formation of Al-polyphosphate shows a high plant availability. The subsequent TCT further increased strongly the plant availability of the Fe-P variants because of the formation of highly plant-available CaNaPO4. Thus, a direct TCT without prior LTC probably also produce CaNaPO4 and is recommended for Fe-P based SSL. However, a molar Ca/P ratio of 1 in the fertilizer is favorable for CaNaPO4 formation. Thus, the knowledge on the source of primary P in SSL is essential for choosing the accurate thermal treatment method to produce highly plant-available P-fertilizers from SSL.
Phosphorus rich sewage sludge ash is a promising source to produce phosphorus recycling fertilizer. However, the low plant availability of phosphorus in these ashes makes a treatment necessary. A thermochemical treatment (800–1000 °C) with alkali additives transforms poorly plant available phosphorus phases to highly plant available calcium alkali Phosphates (Ca,Mg)(Na,K)PO4. In this study, we investigate the use of K2SO4 as additive to produce a phosphorus potassium fertilizer in laboratory-scale experiments (crucible). Pure K2SO4 is not suitable as high reaction temperatures are required due to the high melting point of K2SO4.
To overcome this barrier, we carried out series of experiments with mixtures of K2SO4 and Na2SO4 resulting in a lower economically feasible reaction temperature (900–1000 °C). In this way, the produced phosphorus potassium fertilizers (8.4 wt.% K, 7.6 wt.% P) was highly plant available for phosphorus indicated by complete extractable phosphorus in neutral ammonium citrate solution. The added potassium is, in contrast to sodium, preferably incorporated into silicates instead of phosphorus phases. Thus, the highly extractable phase (Ca,Mg)(Na,K)PO4 in the thermochemical products contain less potassium than expected. This preferred incorporation is confirmed by a pilot-scale trial (rotary kiln) and thermodynamic calculation.
The aim of this study was to investigate the passive sampler method Diffusive Gradients in Thin-films (DGT) for ammonium and nitrate in amended soils. Therefore, we used soils from a pot experiment with maize where nitrogen (N) was supplied as ammonium sulfate nitrate (ASN), without and with a nitrification inhibitor (NI). The additional use of a NI can delay the nitrification in the soil and making the ammonium available for a longer period in the soil solution after its application. Homogenized soil samples were collected directly from each pot after one week of incubation before sowing and after harvesting the maize. Nitrate and ammonium in these soil samples were extracted using DGT devices equipped with a Putolite A520E (for nitrate) and Microlite PrCH (for ammonium) binding layer. Ammonium DGT which determined the mobile and labile ammonium forms based on diffusion and the resupplies from the solid soil phase, only showed a significantly higher amount of extractable ammonium with NI compared to that without NI for some samples. However, significantly lower values were found for nitrate of treatments with NI compared to without NI after harvest. Thus, the lower nitrate amounts for treatments with NI compared to the treatments without NI after harvest indicated the delay of the nitrification process by the NI. Furthermore, we compared also the ammonium and nitrate
DGT results to chemical extraction with KCl solutions. The results demonstrated that the trends of DGT results and chemical extraction were complimentary through all the treatments.
Phosphorus (P) fertilizers from secondary resources became increasingly important in the last years. However, these novel P-fertilizers can also contain toxic pollutants. Chromium in its hexavalent state (Cr(VI)) is regulated with low limit values for agricultural products due to its high toxicity, but the determination of Cr(VI) in these novel fertilizer matrices can be hampered by redox processes that lead to false results. Thus, we applied the passive sampler technique Diffusive Gradients in Thin-films (DGT) for the determination of Cr(VI) in fertilizers and compared the results with the standard wet chemical extraction method (German norm DIN EN 15192) and Cr K-edge X-ray absorption near-edge structure (XANES) spectroscopy. We determined an overall good correlation between the wet chemical extraction and the DGT method. DGT was very sensitive and in most cases selective for the analysis of Cr(VI) in P-fertilizers. However, hardly soluble Cr(VI) compounds cannot be detected with the DGT method since only mobile Cr(VI) is analyzed. Furthermore, Cr K-edge XANES spectroscopy showed that the DGT binding layer also adsorbs small amounts of mobile Cr(III) compounds which leads to overestimated Cr(VI) values. The results of certain types of P-fertilizers containing mobile Cr(III) or partly immobile Cr(VI), showed that optimization of the DGT method is required to avoid over- or underestimation of Cr(VI).
The steel industry is an important engine for sustainable growth, added value, and high-quality employment within the European Union. It is committed to reducing its CO2 emissions due to production by up to 50% by 2030 compared to 1990′s level by developing and upscaling the technologies required to contribute to European initiatives, such as the Circular Economy Action Plan (CEAP) and the European Green Deal (EGD). The Clean Steel Partnership (CSP, a public–private partnership), which is led by the European Steel Association (EUROFER) and the European Steel Technology Platform (ESTEP), defined technological CO2 mitigation pathways comprising carbon direct avoidance (CDA), smart carbon usage SCU), and a circular economy (CE). CE ap-proaches ensure competitiveness through increased resource efficiency and sustainability and consist of different issues, such as the valorization of steelmaking residues (dusts, slags, sludge) for internal recycling in the steelmaking process, enhanced steel recycling (scrap use), the use of secondary carbon carriers from non-steel sectors as a reducing agent and energy source in the steelmaking process chain, and CE business models (supply chain analyses). The current paper gives an overview of different technological CE approaches as obtained in a dedicated workshop called “Resi4Future—Residue valorization in iron and steel industry: sustainable solutions for a cleaner and more competitive future Europe” that was organized by ESTEP to focus on future challenges toward the final goal of industrial deployment.
Recycled fertilizers produced using processes for the recovery of phosphate from residual materials such as wastewater, sewage sludge and sewage sludge ashes show very good bioavailability, but it is still a product largely unknown to the market. The aim of CLOOP is therefore to document the properties and effects of such fertilizers through chemical, mineralogical and ecological analyses as well as analytical method development and pot and field plant growth trials.
Outotec focused on 3 points in CLOOP: Experimental campaigns, process simulations as well as economic analyses with focus on the AshDec process, respectively the design of a large-scale AshDec plant for phosphorus recovery. The laboratory scale trials as well as the semi-industrial scale campaign provided valuable insights into the operating parameters of the process and the plant. As a result, for example, the temperature range could be significantly lowered, and the additive addition reduced by approx. 20 %. They have further shown that the AshDec process is not susceptible to operating fluctuations and that the product can be consistently produced at high quality. With the selection of suitable operating parameters, heavy metals (As, Pb, Cd, (Zn)) can be removed. Within the campaign, about 1.5 t of fertilizer for the plant trials in CLOOP could be produced. An AshDec plant process was digitally created in simulation software, allowing valuable process parameters to be simulated at various operating parameters. On this basis, a full-scale plant was designed. The data obtained in the project were used for a detailed economic analysis including a sensitivity analysis. It was possible to show under which conditions this plant can be operated economically.
At BAM, the AshDec fertilizer was synthesized with different additives and then applied to plant experiments at Uni Bonn. The goal hereby was to check differences in plant uptake. Because of the promising results of AshDec synthesized with sodium-carbonate and because this AshDec version does not require special off gas treatment for sulfur recovery (compared to AshDec synthesized with sodium-sulfate), all project partners agreed on continuing working with this AshDec variation. It was then used as a raw P-source for formulating it into NPK-fertilizers, by granulation with ammonium-sulfate and straw ash as potassium source. These recycling fertilizers were applied to plant- and field experiments by project partners in Brazil (University of Sao Paulo) and Australia (University of Queensland). Furthermore, in leaching experiments, the solubility of phosphorus in AshDec was compared to triple super phosphate. The experiments were carried out on soils with a varying phosphorus buffering index. Results show, that the phosphorus form in AshDec is way less soluble in water. This indicates that AshDec has the potential for a so-called next generation fertilizer – a fertilizer which’s nutrients remain in the soil and supply the plant according to its needs. At the moment, this behavior gets examined more in depth in lysimeter experiments in cooperation with University of Technology Berlin.
The focus of KWB is the Life Cycle Assessment (LCA) of different NextGen fertilizers to evaluate the entire process chain from recovery to fertilizer application. The NextGen fertilizer is credited by the amount of plant available nutrients in the product, which replace nutrients from conventional fertilizer. The LCA covers N-struvite precipitation from municipal wastewater, K-struvite precipitation from industrial wastewater and the AshDec-product from sewage sludge. The LCA task is almost complete. It could be shown that struvite precipitation has comprehensive environmental benefits, mainly since positive side effects occur in sewage sludge treatment (e.g. reduced sludge volume). In principle, the energetic and ecological profile of the AshDec process compared to direct use of sewage sludge ash cannot be assessed as being generally beneficial or negative. Regarding the global warming potential, the Ashdec process shows that the expenses (e.g. energy, chemicals) cannot be covered by the P fertilizer credit. In contrast, the impact categories “terrestrial acidification potential”, and “freshwater eutrophication potential” show positive results as the credits for conventional fertilizer are higher than the burdens for the process.
At University Bonn, the standardized pot experiments were conducted with several AshDec variations, using ryegrass, soybean, and spinach on a slightly acidic sandy soil and an organic-free standard substrate. P-uptake and biomass production of different AshDec variations were generally like those of triple super phosphate and struvite, and clearly outperformed untreated sewage sludge ash and rock phosphate. Field trials in Australia and Brazil with sugarcane on acidic soils are still ongoing and results are expected by the end of 2021.
Gypsum is widely used in the construction sector and its worldwide consumption has been increasing for several decades. Depending on the life-time of the used gypsum products, an increase of gypsum in construction and demolition waste follows. Especially against the background of a circular economy, the recycling of waste gypsum is of growing importance. However, the use of recycled gypsum makes only sense if it is environmentally friendly. Therefore, an evaluation of the environmental impacts of an industrial-scale processing for the recycling of post-consumer gypsum waste was conducted. The evaluation was performed with an established life cycle assessment software. Original data provided by industry and complementary data from a database for life cycle assessments were used for the calculations. Two scenarios for recycled gypsum with different transportation distances were calculated. These results are compared with results of the environmental evaluation of gypsum derived from coal-fired power plants (FGD gypsum) and natural gypsum. The results show that utilization of recycled gypsum can be environmentally advantageous compared to the use of natural gypsum or FGD gypsum, especially in the impact categories land transformation and resource consumption (abiotic depletion potential). For most environmental impact categories the specific transportation distances have a strong influence.
Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance.
In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts.
The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production.
Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker.
The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6).
The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions.
Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented.
Phase formation and evolution was investigated in the CaO–SiO2 system in the range of 70–80 mol% CaO. The samples were container-less processed in an aerodynamic levitation system and crystallization was followed in situ by synchrotron x-ray diffraction at the beamline P21.1 at the German electron synchrotron (DESY). Modification changes of di- and tricalcium silicate were observed and occurred at lower temperatures than under equilibrium conditions. Despite deep sample undercooling, no metastable phase formation was observed within the measurement timescale of 1 s. For the given cooling rates ranging from 300 K s−1 to about 1 K s−1, no decomposition of tricalcium silicate was observed. No differences in phase evolution were observed between reducing and oxidizing conditions imposed by the levitation gas (Ar and Ar + O2). We demonstrate that this setup has great potential to follow crystallization in refractory oxide liquids in situ. For sub-second primary phase formation faster detection and for polymorph detection adjustments in resolution have to be implemented.
During iron and steel production, several by-products such as slags, dusts and sludges are generated in addition to pig iron and steel as primary products. While established recycling routes exist for slags, there are still considerable recycling problems for other residual materials, especially for filter dusts and sludges containing zinc and lead from waste gas purification. However, the high heavy metal contents make landfilling these dusts and sludges cost-intensive and ecologically problematic. In addition, the relatively high zinc and iron loads represent a valuable material potential, which can make reprocessing of the material with recovery of the zinc and iron loads as secondary raw materials ecologically as well as economically attractive. Against this background, a process is being developed in a cooperative project between Ferro Duo GmbH and the Federal Institute for Materials Research and Testing (BAM), in which the heavy metals (zinc, lead, cadmium, etc.) contained in the filter dusts and sludges are selectively converted into chlorides in a thermochemical process after the addition of a chlorine donor and evaporated at temperatures between 650 and 1100 °C. This process can be used to recover zinc and iron as secondary raw materials.
Experiments to date in a batch reactor show that >99% of the zinc and lead can be removed from the treated material. However, a continuous process is necessary for an economical process, which is why this process is transferred to a rotary kiln and relevant process parameters are identified and optimized. The results of these investigations will be presented here.
One of the typical wastes produced in blast-furnace (BF) ironmaking is BF sludge, which mostly consists of carbon and iron oxides, but also contains toxic trace metals such as Zn, Pb, Cd, As, and Hg that render the material hazardous. Due to the lack of an established recycling process, BF sludges are landfilled, which is ecologically questionable and costly. Here, we investigate selective removal of Zn, Pb, and Cd from BF sludge by chlorination–evaporation reactions using thermodynamic modelling and laboratory-scale experiments. Specifically, BF sludge was thermochemically treated at 650–1000 °C with a spent iron(II) chloride solution from steel pickling and the effects of process temperature and retention time on removal of Zn, Pb, and Cd were investigated. Zinc and Pb were quantitatively removed from BF sludge thermochemically treated at 900–1000 °C, whereas Fe and C as well as other major elements were mostly retained. The Zn, Pb, and Cd contents in the thermochemically treated BF sludge could be lowered from ∼56 g/kg, ∼4 g/kg, and ∼0.02 g/kg to ≤0.7 g/kg, ≤0.02 g/kg, and ≤0.008 g/kg, respectively, thus rendering the processed mineral residue a non-hazardous raw material that may be re-utilized in the blast furnace or on the sinter band.
Microspectroscopy reveals dust-derived apatite grains in acidic, highly-weathered Hawaiian soils
(2021)
Dust deposition is an important source of phosphorus (P) to many ecosystems. However, there is little evidence of dust-derived P-containing minerals in soils. Here we studied P forms along a well-described climatic Gradient on Hawaii, which is also a dust deposition gradient. Soil mineralogy and soil P forms from six sites along the climatic gradient were analyzed with bulk (X-ray diffraction and P K-edge X-ray absorption near edge structure) and microscale (X-ray fluorescence, P K-edge X-ray absorption near edge structure, and Raman) analysis methods. In the wettest soils, apatite grains ranging from 5 to 30 μm in size were co-located at the micro-scale with quartz, a known continental dust indicator suggesting recent atmospheric deposition. In addition to co-location with quartz, further evidence of dust-derived P included backward trajectory modeling indicating that dust particles could be brought to Hawaii from the major global dust-loading areas in central Asia and northern Africa. Although it is not certain whether the individual observed apatite grains were derived from long-distance transport of dust, or from local dust sources such as volcanic ash or windblown fertilizer, these observations offer direct evidence that P-containing minerals have reached surface layers of highly-weathered grassland soils through atmospheric deposition.
This paper focuses on the scandium speciation in bauxite residues of different origin. Insights into mineralchemical similarities and differences of these materials will be presented and links to their natural geological background discussed. The presented research should provide fundamental knowledge for the future development of efficient and viable technologies for Sc-recovery from bauxite residues derived from different bauxites and accumulating at different localities. In total, five bauxite residues were investigated which originated from Greece, Germany, Hungary and Russia (North Ural & North Timan) using a combination of different analytical tools. Those included: laser ablation inductively coupled plasma mass spectrometry, X-ray absorption near Edge structure (XANES) spectroscopy, μ-Raman spectroscopy as well as scanning electron microscopy and electron microprobe analyses. X-ray fluorescence and inductively coupled plasma mass spectrometry were used to determine the overall chemical composition. The investigated samples were found to exhibit a relatively homogenous distribution of Sc between the larger mineral particles and the fine-grained matrix except for Al-phases like diaspore, boehmite and gibbsite. These phases were found to be particularly low in Sc. The only sample where Sc mass fractions in Al-phases exceeded 50 mg/kg was the Russian sample from North Ural. Fe-phases such as goethite, hematite and chamosite (for Russian samples) were more enriched in Sc than the Al-phases.
In fact, in Greek samples goethite showed a higher capacity to incorporate or adsorb Sc than hematite. Accessory minerals like zircon, rutile/anatase and ilmenite were found to incorporate higher mass fractions of Sc (>150 mg/kg), however, those minerals are only present in small amounts and do not represent major host phases for Sc. In Russian samples from North Ural an additional Ca–Mg rich phase was found to contain significant mass fractions of Sc (>500 mg/kg). μ-XANES spectroscopy was able to show that Sc in bauxite residue occurs adsorbed onto mineral surfaces as well as incorporated into the crystal lattice of certain Fe-phases. According to our observations the bauxite type, i.e. karstic or lateritic, the atmospheric conditions during bauxitization, i.e. oxidizing or reducing, and consequently the dominant Sc-bearing species in the primary Bauxite influence the occurrence of Sc in bauxite residues. In karstic bauxites, underlying carbonate rocks can work as a pH-barrier and stabilize Sc. This prevents the Sc from being mobilized and removed during bauxitization. Hence, karstic bauxites are more prone to show a Sc enrichment than lateritic bauxites. Reducing conditions during bauxitization support the incorporation of Sc into clay minerals such as chamosite, which can dissolve and reprecipitate during Bayer processing causing Sc to be redistributed and primarily adsorb onto mineral surfaces in the bauxite residue. Oxidizing conditions support the incorporation of Sc into the crystal lattice of Fe-oxides and hydroxides, which are not affected in the Bayer process. The genetic history of the bauxite is therefore the major influential factor for the Sc occurrence in bauxite residues.
There is an ongoing debate on European scale concerning the criticality of phosphorus. In Switzerland and Germany, phosphorus recovery from phosphorus-rich waste streams will become obligatory. Sewage sludge ash is rich in phosphorus and may become an important secondary feedstock. Thermochemical treatment of sewage sludge ash with sodium sulphate under reducing conditions was shown to remove heavy metals from the solid product and produce the fully plant available crystalline phase CaNaPO4. Pilot-scale experiments in a rotary kiln were carried out at temperatures between 750 and 1000 °C and were compared to laboratory-scale experiments with crucibles. Process upscaling was successfully demonstrated but a series of differences were noticed: In comparison to laboratory-scale, solubility of phosphorus in samples from pilot-scale experiments was lower at all chosen treatment temperatures because of shorter retention time and incomplete decomposition of sodium sulphate. X-ray diffraction analysis revealed remaining phase fractions of whitlockite (Ca3-x(Mg,Fe)x(PO4)2) and sodium sulphate from the starting materials in products and thus indicated incomplete reaction. In contrast to the results of laboratory-scale experiments, the crystalline phase CaNaPO4 was clearly absent in the products from the rotary kiln but instead a Mg-bearing phase (Ca,Mg)NaPO4 was formed. Laboratory-scale experiments confirmed (Ca,Mg)NaPO4 is an intermediate phase between whitlockite and CaNaPO4. However, both crystalline phases are characterized by high plant availability. It was shown that heavy metal removal increased at higher temperatures whereas solubility and thus plant availability of phosphorus already reached its maxima at temperatures of 950 °C in pilot-scale and 875 °C in laboratory-scale experiments.
For the European sewage sludge ash monitoring ash samples from sewage sludge incineration plants were requested from all over Europe. First results of the received samples regarding main and trace element contents were presented at ESPC4. Moreover, a list of all known European facilities for sewage sludge monoincineration was presented.
Klärschlammaschen können eine hohe Phosphatkonzentration aufweisen und stellen damit einen geeigneten Sekundärrohstoff für die Produktion von Phosphatdüngemitteln dar. Bisher wird dieses Potential der Klärschlammaschen für die Phosphor-Rückgewinnung jedoch kaum genutzt, da die in den Aschen enthaltenen Phosphate für Pflanzen kaum verfügbar und die Aschen teilweise mit toxischen Schwermetallen belastet sind.
Im AshDec®-Verfahren wird die Klärschlammaschen im Drehrohrofen im Temperaturbereich 800-1000°C unter Zugabe von Alkali-Additiven (bsp. Na2CO3) thermochemisch behandelt, um ein wirksames und schadstoffarmes Phosphatdüngemittel herzustellen. Aktuell bereitet die Firma Emter GmbH den Bau der ersten großtechnischen AshDec®-Anlage mit einer Kapazität von 30.000 Jahrestonnen Klärschlammasche am Standort ihrer Klärschlammverbrennungsanlage (Altenstadt / Oberbayern) vor. Die erste Ausbaustufe dieser Anlage wird durch das BMBF-Projekt R-Rhenania im Rahmen der Förderinitiative RePhoR begleitet.
Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone.
In recent decades, many researchers have investigated a thermochemical process to reduce iron oxides to metallic iron in molten BOFS. The metallic iron formed separates from the reduced slag due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced slag is adapted to that of the Portland cement clinker and the hydraulic reactive mineral alite is formed.
In this study, BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent, and the hydraulic properties of the reduced, low-iron BOFS were investigated. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, the addition of gypsum, as is also done in cement production from Portland cement clinker, has been found to accelerate the hydration rate of reduced BOFS.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, the production of a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry.
The diffusive gradients in thin-films (DGT) technique shows in many publications a superior correlation to the amount of plant-available phosphorus (P) in soil. However, this technique cannot give information on the plant-available P species in soil. Therefore, we combined DGT with solution 31P nuclear magnetic resonance (NMR) spectroscopy. This was achieved by using a modified DGT device in which the diffusive layer had a larger pore size, the binding layer incorporated an adsorption material with a higher capacity, and the device had a larger exposure area. The spectroscopic investigation was undertaken after elution of the deployed DGT binding layer in a NaOH solution. Adsorption tests using solutions of known organic P compounds showed that a sufficient amount of these compounds could be adsorbed on the binding layer in order for them to be analyzed by solution 31P NMR spectroscopy. Furthermore, various intermediates of the hydrolysis of trimetaphosphate in soil could be also analyzed over time.
Dust deposition is an important source of phosphorus (P) to many ecosystems. However, there is little evidence of dust-derived P-containing minerals in soils. Here we studied P forms along a well-described climatic gradient on Hawaii, which is also a dust deposition gradient. Soil mineralogy and soil P forms from six sites along the climatic gradient were analyzed with bulk (X-ray diffraction and P K-edge X-ray absorption near edge structure)
and microscale (X-ray fluorescence, P K-edge X-ray absorption near edge structure, and Raman) analysis methods. In the wettest soils, apatite grains ranging from 5 to 30 μm in size were co-located at the micro-scale with quartz, a known continental dust indicator suggesting recent atmospheric deposition. In addition to colocation with quartz, further evidence of dust-derived P included backward trajectory modeling indicating that dust particles could be brought to Hawaii from the major global dust-loading areas in central Asia and northern Africa. Although it is not certain whether the individual observed apatite grains were derived from long-distance transport of dust, or from local dust sources such as volcanic ash or windblown fertilizer, these observations offer direct evidence that P-containing minerals have reached surface layers of highly-weathered grassland soils
through atmospheric deposition.
The use of highly water-soluble phosphorus (P) fertilizers can lead to P fixation in the soil, reducing fertilization efficiency. Waste-derived, low water-solubility sources can potentially increase sugarcane’s P uptake compared to triple superphosphate by reducing adsorption to the soil.
Aims:We aimed to test struvite, hazenite, and AshDec® for their agronomic potential as recycled fertilizers for sugarcane production in a typical tropical soil.We hypothesize that these sources can reduce P fixation in the soil, increasing its availability and sugarcane’s absorption.
Methods: In a greenhouse pot experiment, two consecutive sugarcane cycles, 90 days each, were conducted in a Ferralsol. The recovered sources struvite, hazenite, AshDec®, and the conventional triple superphosphate were mixed in the soil in three P doses (30, 60, and 90 mg kg–1), aside a control (nil-P). At both harvests, sugarcane number of sprouts, plant height, stem diameter, dry mass yield, shoot phosphorus, and soil P fractionation were investigated.
Results: At 90 days, struvite and hazenite performed better for dry mass yield (70.7 and 68.3 g pot–1, respectively) than AshDec® and triple superphosphate (59.8 and 57.4 g pot–1, respectively) and for shoot P, with 98.1, 91.6, 75.6, and 66.3 mg pot–1, respectively. At 180 days, struvite outperformed all treatments for dry mass yield (95.3 g pot–1) and AshDec® (75.5 mg pot–1) for shoot P. Struvite was 38% and hazenite 21% more efficient than triple superphosphate in P uptake, while AshDec® was 6% less efficient. Soil had higher labile P under struvite, hazenite, and AshDec® than triple superphosphate by the end of the first cycle, while only the later increased nonlabile P by the end of the experiment (180 days).
Conclusions:Waste-derived P sources were more efficient in supplying P for sugarcane and delivering labile P in 180 days than triple superphosphate.
Future nutrient recovery from sewage sludge regarding three different scenarios - German case study
(2022)
Agricultural sewage sludge utilization becomes less important in Germany. In 2017, new fertilizer and waste laws caused the agricultural sewage sludge utilization to collapse by more than a quarter. From 2029, German wastewater treatment plants (WWTPs) must recover phosphorus (P) from sewage sludge if it contains more than 2 wt % P. Agricultural utilization will be prohibited for large WWTPs >100,000 population equivalents (pe) from 2029 and >50,000 pe from 2032. In Germany, each federal state must annually report amounts and quality of agriculturally utilized sewage sludge which was 16% of the total disposal in 2019. The reports of 10 states were evaluated for 2016 and 2017 representing approx. 60% of the total agriculturally used sludge volume. In 2016, 60% of the WWTPs’ sludges exceeded the recovery limit of 2 wt % P which is 70% of the amount of sludge and 85% of the phosphorus load. Other nutrients are not affected by the recovery obligation. However, many P recovery processes recover other nutrients, too. Considering three different scenarios for future German sewage sludge disposal shows that 70–77% of the P load in sewage sludge will probably be recovered in the future. At the same time, this applies for about 0–16% nitrogen, 36–52% of calcium, 31–53% of potassium, and 40–52% of magnesium. However, these recovered nutrients loads can substitute only 1% or less of the commercial fertilizer demand except from phosphorus which is up to 43% of the demand.
Conventional phosphate fertilizers are usually highly water-soluble and rapidly solubilize when moistened by the soil solution. However, if this solubilization is not in alignment with plants demand, P can react with the soil colloidal phase, becoming less available over time. This is more pronounced in acidic, oxidic tropical soils, with
high P adsorption capacity, reducing the efficiency of P fertilization. Furthermore, these fertilizers are derived from phosphate rock, a non-renewable resource, generating an environmental impact. To assess these concerns, waste-recycled P sources (struvite, hazenite and AshDec®) were studied for their potential of reducing P Fixation by the soil and improving the agronomic efficiency of the P fertilization. In our work, we compared the solubilization dynamics of struvite, hazenite, AshDec® to triple superphosphate (TSP) in a sandy clay loam Ferralsol, as well as their effect on solution pH and on soil P pools (labile, moderately-labile and non-labile) via an incubation experiment. Leaching columns containing 50 g of soil with surface application of 100 mg per column (mg col 1) of P from each selected fertilizer and one control (nil-P) were evaluated for 60 days. Daily leachate samples from the column were analyzed for P content and pH. Soil was stratified in the end and submitted to P
fractionation. All results were analyzed considering p < 0.05. Our findings showed that TSP and struvite promoted an acid P release reaction (reaching pHs of 4.3 and 5.5 respectively), while AshDec® and hazenite reaction was alkaline (reaching pHs of 8.4 and 8.5 respectively). Furthermore, TSP promoted the highest P release among all sources in 60 days (52.8 mg col 1) and showed rapid release dynamic in the beginning, while struvite and hazenite showed late release dynamics and lower total leached P (29.7 and 15.5 mg col 1 P respectively). In contrast, no P-release was detected in the leachate of the AshDec® over the whole trial period. Struvite promoted
the highest soil labile P concentration (7938 mg kg 1), followed by hazenite (5877 mg kg 1) and AshDec® (4468 mg kg 1), all higher than TSP (3821 mg kg 1), while AshDec® showed high moderately-labile P (9214 mg kg 1), reaffirming its delayed release potential.
Phosphorus recycling from sewage sludge will be obligatory in Germany from 2029. Phosphorus content determination in sewage sludge is crucial to assess the prescribed recycling rates. Currently, German law regards sample preparation using aqua regia digestion in a microwave or under reflux conditions as well as instrumental phosphorus determination by ICP-OES, ICP-MS, or photometric determination with ammonium molybdate as equivalent. However, it is questionable whether these methods are indeed equivalent regarding phosphorus quantification in sludges near the limit of 20 g/kg for mandatory recycling. To answer this question, 15 sewage sludges of 11 different wastewater treatment plants were investigated with all permitted method (digestion and measurement) combinations. Moreover, one sewage sludge was also examined in an interlaboratory comparison (ILC) with 28 participants. This study shows that the above-mentioned methods differ in some cases significantly but across all method combinations and sludges, phosphorus recovery was between 80 and 121% after normalization to the grand mean (average of 15 sludges between 85 and 111%). The ILC and the examination of 15 sludges produced largely similar results. There is a tendency to higher phosphorus recovery after microwave digestion compared to reflux digestion and ICP-OES measurements determine higher phosphorus contents than ICP-MS and photometric phosphorus determination. As a result, the authors recommend ICP-OES determination of phosphorus in sewage sludge after microwave digestion.
The leaching behavior of scandium (Sc) from bauxite residues can differ significantly when residues of different geological backgrounds are compared. The mineralogy of the source rock and the physicochemical environment during bauxitization affect the association of Sc in the bauxite i.e., how Sc is distributed amongst different mineral phases and whether it is incorporated in and/or adsorbed onto those phases. The Sc association in the bauxite is in turn crucial for the resulting Sc association in the bauxite residue. In this study systematic leaching experiments were performed on three different bauxite residues using a statistical design of experiments approach. The three bauxite residues compared originated from processing of lateritic and karstic bauxites from
Germany, Hungary, and Russia. The recovery of Sc and Fe was determined by ICP-OES measurements. Mineralogical changes were analyzed by X-ray-diffraction and subsequent Rietveld refinement. The effects of various parameters including temperature, acid type, acid concentration, liquid-to-solid ratio and residence time were studied. A response surface model was calculated for the selected case of citric acid leaching of Hungarian bauxite residue. The investigations showed that the type of bauxite residue has a strong influence. The easily leachable fraction of Sc can vary considerably between the types, reaching ~20–25% in German Bauxite residue and ~50% in Russian bauxite residue. Mineralogical investigations revealed that a major part of this fraction was released from secondary phases such as cancrinite and katoite formed during Bayer processing of the bauxite.
The effect of temperature on Sc and Fe recovery is strong especially when citric acid is used. Based on the exponential relationship between temperature and Fe-recovery it was found to be particularly important for the selectivity of Sc over Fe. Optimization of the model for a maximum Sc recovery combined with a minimum Fe
recovery yielded results of ~28% Sc recovery at <2% Fe recovery at a temperature of 60 ◦C, a citric acid normality of 1.8, and a liquid-to-solid ratio of 16 ml/g. Our study has shown that detailed knowledge about the Sc association and distribution in bauxite and bauxite residue is key to an efficient and selective leaching of Sc
from bauxite residues.
During iron and steel production, several by-products such as slags, dusts, and sludges are generated in addition to pig iron and steel as primary products. Especially for filter dusts and sludges containing zinc and lead from gas purification, there are still considerable recycling problems. However, the high heavy metal contents make landfilling of these dusts and sludges cost-intensive and ecologically problematic. In addition, the relatively high zinc and iron loads represent a valuable resource, which can make reprocessing of the material with recovery of the zinc and iron loads as secondary raw materials ecologically as well as economically attractive. Nevertheless, established recycling methods like the Waelz process fall short in regaining more than one valuable metal from the dusts and operate only under narrow ranges of material compositions, which makes it problematic to adapt these processes to new dust compositions as are to be formed in future steel work operations.
To tackle these problems, the German Federal Institute for Materials Research and Testing (BAM) and Ferro Duo GmbH investigate innovative recycling methods for steelwork dusts and sludges in a joint project. This mainly focusses on regaining valuable metals such as iron as well as zinc from blast furnace sludge (BFS) and electric arc furnace dust (EAFD) by thermochemical treatment.
Therefore, mixtures of these materials are heated under inert atmosphere employing the carbon present in BFS as internal reducing agent. During the process, metallic iron is formed in the solid reaction product while zinc and other volatile heavy metals are evaporated. This paves the way for the generation of zinc as well as sponge iron as two separate products valuable for metallurgical processes. The process basically consists of heating a mixture of BFS and EAFD to temperatures between 700 and 1100 °C under inert (e.g., nitrogen) or reducing (e.g., CO) gas flow. When a suitable mixing ratio is applied, the carbon present in the BFS can be effectively used as reducing agent for iron and zinc present in both starting materials generating a solid residue with high metallic iron and low carbon content as well as a gas stream laden with zinc and other volatile heavy metals, that can be regained by off-gas treatment.
The project aims at testing this concept as a continuous process in a pilot plant established by Ferro Duo GmbH with BAM supplying comprehensive scientific support by lab- and small scale-experiments.
Additionally, considering the necessity to mitigate CO2 emissions and the resulting shift in compositions of steel work dusts and sludges, our research also investigates replacement of carbon present in the sludges by hydrogen as potentially carbon-neutral reducing agent. Here, the use of non-explosive forming gas as reducing agent for EAFD shows potential to give a product high in metallic iron while zinc and other heavy metals are effectively evaporated from the solid material making it possible to regain them from the exhaust gas stream.
Phosphorus (P) recovery is obligatory for all sewage sludges with more than 20 g P/kg dry matter (DM) from 2029 in Germany. Nine wastewater treatment plants (WWTPs) were chosen to investigate variations of phosphorus contents and other parameters in sewage sludge over the year. Monthly sewage sludge samples from each WWTP were analyzed for phosphorus and other matrix elements (C, N, H, Ca, Fe, Al, etc.), for several trace elements (As, Cr, Mo, Ni, Pb, Sn) and loss of ignition. Among the nine WWTPs, there are four which have phosphorus contents both above and below the recovery limit of 20 g/kg DM along the year. Considering the average phosphorus content over the year, only one of them is below the limit. Compared to other matrix elements and parameters, phosphorus fuctuations are low with an average of 7% over all nine WWTPs. In total, only hydrogen and carbon are more constant in the sludge.
In several WWTPs with chemical phosphorus elimination, phosphorus fuctuations showed similar courses like iron and/or aluminum. WWTPs with chamber flter presses rather showed dilution efects of calcium dosage. As result of this study, monthly phosphorus measurement is highly recommended to determine whether a WWTP is below the
20 g/kg DM limit.
Sugarcane bagasse is commonly combusted to generate energy. Unfortunately, recycling strategies rarely consider the resulting ash as a potential fertilizer. To evaluate this recycling strategy for a sustainable circular economy, we characterized bagasse ash as a fertilizer and measured the effects of co-gasification and co-combustion of bagasse with either chicken manure or sewage sludge: on the phosphorus (P) mass fraction, P-extractability, and mineral P phases. Furthermore, we investigated the ashes as fertilizer for soybeans under greenhouse conditions. All methods in combination are reliable indicators helping to assess and predict P availability from ashes to soybeans. The fertilizer efficiency of pure bagasse ash increased with the ash amount supplied to the substrate. Nevertheless, it was not as effective as fertilization with triple-superphosphate and K<sub>2</sub>SO<sub>4</sub>, which we attributed to lower P availability. Co-gasification and co-combustion increased the P mass fraction in all bagasse-based ashes, but its extractability and availability to soybeans increased only when co-processed with chicken manure, because it enabled the formation of readily available Ca-alkali phosphates. Therefore, we recommend co-combusting biomass with alkali-rich residues to increase the availability of P from the ash to plants.
Microscopic knowledge of the structural, energetic, and electronic properties of scandium fluoride is still incomplete despite the relevance of this material as an intermediate for the manufacturing of Al−Sc alloys. In a work based on first-principles calculations and X-ray spectroscopy, we assess the stability and electronic structure of six computationally predicted ScF3 polymorphs, two of which correspond to experimentally resolved single-crystal phases. In the theoretical analysis based on density functional theory (DFT), we identify similarities among the polymorphs based on their formation energies, chargedensity distribution, and electronic properties (band gaps and density of states). We find striking analogies between the results obtained for the ow- and high-temperature phases of the material, indirectly confirming that the transition occurring between them mainly consists of a rigid rotation of the lattice. With this knowledge, we examine the X-ray absorption spectra from the Sc and F K-edge contrasting firstprinciples results obtained from the solution of the Bethe−Salpeter equation on top of all-electron DFT with high-energy-resolution fluorescence detection measurements. Analysis of the computational results sheds light on the electronic origin of the absorption maxima and provides information on the prominent excitonic effects that characterize all spectra. A comparison with measurements confirms that the sample is mainly composed of the high- and low-temperature polymorphs of ScF3. However, some fine details in the experimental results suggest that the probed powder sample may contain defects and/or residual traces of metastable polymorphs.
The amount of plant-available phosphorus (P) in soil strongly influences the yield of plants in agriculture. Therefore, various simple chemical extraction methods have been developed to estimate the plant-available P pools in soil. More recently, several experiments with the DGT technique have shown that it has a much better correlation to plant-available P in soils than standard chemical extraction methods (e.g. calcium-acetate-lactate (CAL), Colwell, Olsen, water) when soils with different characteristics are considered. However, the DGT technique cannot give information on the plant-available P species in the soil. Therefore, we combined DGT with solution 31P nuclear magnetic resonance (NMR) spectroscopy. This was achieved by using a modified DGT device in which the diffusive layer had a larger pore size, the binding layer incorporated an adsorption material with a higher capacity, and the device had a larger exposure area. The spectroscopic investigation was undertaken after elution of the deployed DGT binding layer in a NaOH solution. Adsorption tests using solutions of known organic P compounds showed that a sufficient amount of these compounds could be adsorbed on the binding layer in order for them to be analyzed by solution 31P NMR spectroscopy. Furthermore, various intermediates of the hydrolysis of trimetaphosphate in soil could be also analyzed over time.
Steelmaking slag is a by-product of steel production of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled.
With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of the Portland cement clinker.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product had a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less heat of hydration compared to OPC and its hydraulic reaction was delayed. However, adding gypsum has been shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry.
Solid wastewater-based fertilizers were screened for per- and polyfluoroalkyl substances (PFAS) by the extractable organic fluorine (EOF) sum parameter method. The EOF values for ten sewage sludges from Germany and Switzerland range from 154 to 7209 mg kg−1. For thermal treated sewage sludge and struvite the EOF were lower with values up to 121 mg kg−1. Moreover, the application of PFAS targeted
and suspect screening analysis of selected sewage sludge samples showed that only a small part of the EOF sum parameter values can be explained by the usually screened legacy PFAS. The hitherto unknown part of EOF sum parameter contains also fluorinated pesticides, pharmaceutical and aromatic compounds. Because these partly fluorinated compounds can degrade to (ultra-)short PFAS in wastewater treatment plants they should be considered as significant sources of organic fluorine in the environment. The combined results of sum parameter analysis and suspect screening reveal the need to update current regulations, such as the German fertilizer ordinance, to focus not solely on a few selected PFAS such as perfluorooctane sulfonic acid (PFOS) and perfluorooctanoic acid (PFOA) but
consider an additional sum parameter approach as a more holistic alternative. Moreover, diffusion gradient in thin-films (DGT) passive samplers were utilized as an alternative simplified extraction method for PFAS in solid wastewater-based fertilizers and subsequently quantified via combustion ion chromatography. However, the DGT method was less sensitive and only comparable to the EOF values
of the fertilizers in samples with >150 mg kg−1, because of different diffusion properties for various PFAS, but also kinetic exchange limitations.
Per- and polyfluoroalkyl substances (PFAS) are chemicals which were developed to improve humanity’s quality of life. Due to their high chemical stability and resistance to degradation by heat or acids, PFAS were used in a variety of consumer products. The continuous use of PFAS in household products and the discharge of PFAS from industrial plants into the sewer system resulted in the contamination of effluents and sewage sludge from wastewater treatment plants (WWTPs) (Roesch et al. 2022). Since sewage sludge is often used as fertilizer, its application on agricultural soils has been observed as a significant entry path for PFAS into the environment, specifically in our food chain. In Germany the sewage sludge/biosolid application on agricultural land was banned with the amendment of the German Sewage Sludge Ordinance and by 2029 sewage sludge application will be totally prohibited. However, phosphorus (P) from sewage sludge should still be recycled in WWTPs of cities with a population larger than 50,000 residents. To produce high-quality P-fertilizers for a circular economy, PFAS and other pollutants (e.g. pesticides and pharmaceuticals) must be separated from sewage sludge. Due to the strong diversity of industrial PFAS usage it is not clear if a safe application of novel recycled P-fertilizers from WWTPs can be guaranteed. Therefore, we analyzed various sewage sludges and wastewater-based fertilizers. Sewage sludge (SL) samples from various WWTPs in Germany and Switzerland, six sewage sludge ashes (SSA) from Germany, six thermally treated SL and SSA samples with different additives (temperatures: 700-1050 °C), two pyrolyzed SL samples (temperature: 400 °C) and two struvite samples from Germany and Canada were analyzed. The goal was to quantify PFAS in sewage sludges and wastewater-based P-fertilizers with the sum parameter extractable organic fluorine (EOF) by combustion ion chromatography (CIC). The results were compared with data from classical LC-MS/MS target analysis as well as selected samples by HR-MS suspect screening. The EOF values of the SLs mainly range between 154 and 538 µg/kg except for one SL which showed an elevated EOF value of 7209 µg/kg due to high organofluorine contamination. For the SSA samples the EOF values were lower and values between LOQ (approx. 60 µg/kg) and 121 µg/kg could be detected. For the pyrolyzed SLs no EOF values above the LOQ were detected. Moreover, the two wastewater-based struvite fertilizers contain 96 and 112 µg/kg EOF, respectively. In contrast to the EOF values, the sum of PFAS target values were relatively low for all SLs. Additional applied PFAS HR-MS suspect screening aimed to tentatively identify PFAS that could contribute to the hitherto unknown part of the EOF value. The majority of the detected fluorinated compounds are legacy PFAS such as short- and long-chain perfluorocarboxylic acids (PFCA), perfluorosulfonic acids (PFSA), polyfluoroalkyl phosphate esters (PAPs) and perfluorophosphonic acids (PFPA). Moreover, fluorinated pesticides, pharmaceutical as well as aromatic compounds were also identified, which are all included in the EOF parameter. Our research revealed that the current PFAS limit of 100 µg/kg for the sum of PFOS + PFOA in the German Fertilizer Ordinance is no longer up to date. Since the number of known PFAS already exceeds 10,000, the ordinance limit should be updated accordingly. Recent regulations and restrictions on using long-chain PFAS (≥C8) have resulted in a significant shift in the industry towards (ultra-)short-chain alternatives, and other, partly unknown, emerging PFAS. Ultimately, also fluorinated pesticides and pharmaceuticals, which end up as ultrashort PFAS in the WWTPs, have to be considered as possible pollutants in fertilizers from wastewater, too.
Hydrogen plasma treatment of iron ores or iron oxide containing wastes can be an efficient option to produce green iron e.g. for steel production. This way iron oxide is reduced to metallic iron in the liquid form by the highly reactive species that are formed in a hydrogen plasma. Hydrogen plasma can be used at the same time to remove undesired gangue elements. The presentation shows the experimental setup, shows first results of iron ore reduction by hydrogen plasma and gives an outlook for industrial application of the technology.
The increasing use of carbon fiber reinforced polymers (CFRP), as lightweight materials essential for the transformation, demands for a safe treatment option of carbon fiber (CF) containing waste streams. Because of their low reactivity towards oxidation processes, CF can neither be treated in a conventional nor hazardous waste incineration plant. Even the extremely high temperature in a cement rotary kiln does not lead to full conversion. To increase the sustainability of CF, other processes need to be investigated. Opening other reaction pathways, using CF waste streams as secondary resource in pyrometallurgy to replace fossil carbon, can be a solution for a safe and sustainable treatment. After first small scale experiments, CF containing waste streams were used as reductant in a semi-industrial scale electric arc furnace (EAF). First results and impressions are presented.
The increasing use of carbon fiber reinforced polymers (CFRP), as lightweight materials essential for the transformation, demands for a safe treatment option of carbon fiber (CF) containing waste streams. Because of their low reactivity towards oxidation processes, CF can neither be treated in a conventional nor hazardous waste incineration plant. Even the extremely high temperature in a cement rotary kiln does not lead to full conversion. To increase the sustainability of CF, other processes need to be investigated. Opening other reaction pathways, using CF waste streams as secondary resource in pyrometallurgy to replace fossil carbon, can be a solution for a safe and sustainable treatment. To support the industrial application, experiments on different scales were conducted. Here, results of thermochemical investigations, reactivity studies, crucible experiments and pilot plat trials are reported.
Lightweighting as a cross-cutting technology contributes significantly to achieve the European Green Deal goals. Based on, but not limited to, advanced materials and production technologies, the demand for natural resources and CO2 emmissions are reduced by lightweighting during production, as well as use phase. Therefore, lightweighting is a crucial transformation technology assisting in decoupling economic growth from resource consumption. In this manner, lightweighting contributes significantly as a key technology of relevance for many industrial sectors such as energy, mobility, and infrastructure, towards resource efficiency, climate action and economic strength, as well as a resilient Europe. To strengthen international partnerships, addressing global issues of today at the edge of science with high performance lightweight material based on carbon fibers, an overview about the BAM expertise in carbon fiber reinforced materials is given.
Steelmaking slag is a by-product of steel production, of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical cycle, used as fertiliser or landfilled.
With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of Portland cement clinker.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product has a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less hydration heat than OPC, and its hydraulic reaction was delayed. However, adding gypsum has shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS has economic and ecological benefits for both the cement and steel industries.
Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone.
In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via a thermochemical reductive treatment. The reductive treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced BOFS is adapted to that of Portland cement clinker and the hydraulic reactive mineral alite (Ca3SiO5) is formed.
In this study, German BOFS was reduced in a small-scale electric arc furnace and a low-iron mineral product rich in alite was produced. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, adding gypsum accelerated the hydration rate of the reduced BOFS.
Further research to improve the hydraulic properties of the reduced BOFS is essential. If successful, the production of a hydraulic material and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry.
AbstractRed mud is the waste of bauxite refinement into alumina, the feedstock for aluminium production1. With about 180 million tonnes produced per year1, red mud has amassed to one of the largest environmentally hazardous waste products, with the staggering amount of 4 billion tonnes accumulated on a global scale1. Here we present how this red mud can be turned into valuable and sustainable feedstock for ironmaking using fossil-free hydrogen-plasma-based reduction, thus mitigating a part of the steel-related carbon dioxide emissions by making it available for the production of several hundred million tonnes of green steel. The process proceeds through rapid liquid-state reduction, chemical partitioning, as well as density-driven and viscosity-driven separation between metal and oxides. We show the underlying chemical reactions, pH-neutralization processes and phase transformations during this surprisingly simple and fast reduction method. The approach establishes a sustainable toxic-waste treatment from aluminium production through using red mud as feedstock to mitigate greenhouse gas emissions from steelmaking.