4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung
Filtern
Dokumenttyp
- Vortrag (91)
- Zeitschriftenartikel (55)
- Beitrag zu einem Tagungsband (14)
- Posterpräsentation (14)
- Buchkapitel (5)
- Tagungsband (Herausgeberschaft für den kompletten Band) (1)
- Dissertation (1)
- Forschungsbericht (1)
Schlagworte
- Recycling (24)
- Phosphor (20)
- Klärschlamm (17)
- Phosphorus (15)
- Phosphorrückgewinnung (14)
- Phosphorus recovery (14)
- Sewage sludge (12)
- Fertilizer (9)
- Klärschlammverordnung (9)
- Gichtgasschlamm (7)
Organisationseinheit der BAM
- 4 Material und Umwelt (182)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (182)
- 4.3 Schadstofftransfer und Umwelttechnologien (15)
- 7 Bauwerkssicherheit (14)
- 7.1 Baustoffe (12)
- 7.4 Baustofftechnologie (9)
- 1 Analytische Chemie; Referenzmaterialien (5)
- 1.7 Organische Spuren- und Lebensmittelanalytik (3)
- 6 Materialchemie (3)
- 6.3 Strukturanalytik (3)
Paper des Monats
- ja (2)
LD-Schlacken weisen eine große chemische Ähnlichkeit zu Protlandzementklinker auf. Sie enthalten jedoch noch bis zu 30% Eisen, das mineralisch in oxidischer Form gebunden vorliegt. Dadurch kann sich bei der Erstarrung die wichtigste Klinkerphase "Alit" nicht ausbilden.
Durch eine reduzierende Schmelzbehandlung der Schlacke kann des mineralisch gebundene Eisen als Metall separiert werden. Dadurch wird auch die Mineralogie der Schlacke so verändert, dass auch sie nun praktisch einem Portlandzementklinker entspricht.
Entsprechende Versuche wurden am kleintechnischen Lichtbogenofen der BAM durchgeführt. Es werden Ergebnisse vorgestellt und auf Grenzen und Möglichkeiten eines derartigen Prozesses im Hinblick auf eine industrielle Umsetzung eingegangen.
Bei der Stahlproduktion fallen verfahrensbedingt große Mengen an Nebenprodukten und Abfällen wie Stahlwerksschlacken, Filterstäube und Gichtgasschlämme an. Hohe Anteile dieser Stoffströme werden aufgrund ihrer Zusammensetzung immer noch deponiert, obwohl sie ein hohes Wertstoffpotential aufweisen. An der Bundesanstalt für Materialforschung und -prüfung (BAM) werden Verfahren untersucht
und entwickelt, welche eine Verwertung und Kreislaufführung dieser Materialströme ermöglichen. Aus sogenannten Linz-Donawitz-(LD)-Schlacken können durch carbothermische Nachbehandlung Roheisen und ein dem Portlandzementklinker (PZK) ähnliches Bindemittel erzeugt werden. Aus Elektroofenstäuben und Gichtgasschlämmen kann Zink gewonnen und die Anteile an Eisen und Kohlenstoff in den Stahlproduktionsprozess zurückgeführt werden. Durch diese technischen Maßnahmen kann es gelingen die Deponierung von Abfällen der Stahlproduktion zukünftig deutlich zu reduzieren.
Die Zementindustrie erzeugt etwa 6-7% der globalen CO2-Emissionen und steht damit als Industriezweig vor dem Hintergrund einer anvisierten Klimaneutralität vor gewaltigen Herausforderungen. Der Prozess der Klinkerherstellung wurde über die vergangenen Jahrzehnte bereits kontinuierlich optimiert. Seit 1990 ist es der deutschen Zementindustrie gelungen, die spezifischen CO2-Emissionen der Zementproduktion u. a. durch den Einsatz alternativer, nicht fossiler Brennstoffe und durch Absenkung des Klinkergehalts im Zement um 20 % zu senken. Weitere konventionelle Minderungsstrategien versprechen jedoch nur noch wenig zusätzliche Reduktion. Im Falle des Portlandklinkers besteht die Schwierigkeit darin, dass zwei Drittel der CO2-Emissionen rohstoffbedingt durch die Entsäuerung des Kalksteins (CaCO3) anfallen, die durch die beschriebenen Maßnahmen nicht weiter abgesenkt werden können. Vielmehr wird es erforderlich sein, noch zu entwickelnde oder zu optimierende Technologien anzuwenden und ggf. alle relevanten Ebenen wie Produktion, Weiterverarbeitung und Anwendung von Zement und Beton neu zu denken. Neben technologischen Ansätzen zur CO2-Abscheidung mit nachfolgender langfristiger Speicherung (Carbon Capture and Storage – CCS) oder Verwertung (Carbon Capture and Utilisation – CCU) werden auch alternative Rohstoffe für die Zementproduktion und alternative Bindemittel in Betracht zu ziehen sein.
Die Europäische Kommission präsentierte am 11. Dezember 2019 den European Green Deal, ein Konzept mit dem Ziel, bis zum Jahr 2050 als erster Kontinent Klimaneutralität zu erreichen. Mit Inkrafttreten der Verordnung (EU) 2021/1119 des Europäischen Parlaments und des Europäischen Rates am 29. Juli 2021 zur Schaffung des Rahmens für die Verwirklichung der Klimaneutralität („Europäisches Klimagesetz“), ist dieses, sowie das Ziel der Reduzierung der Nettotreibhausgasemissionen um mindestens 55 % bis 2030 in der Gesetzgebung der Europäischen Union verankert. Die Stahlindustrie in der Europäischen Union mit ca. 57 Mio. t Nettotreibhausgasemissionen im Jahr 2020, die annähernd 2 % der Emissionen der Europäischen Union ausmachen (Inklusive Energie: 127 Mio. t; 4 %), bekennt sich zur erheblichen Reduzierung der CO2-Emissionen bis zum Jahr 2030 und zum Erreichen der Klimaneutralität bis zum Jahr 2050. Als Schlüsselwege zur Verwirklichung dieser Zielstellung hat sie zum einen Smart Carbon Usage (SCU) und zum anderen Carbon Direct Avoidance (CDA) in einer Roadmap formuliert. SCU umfasst CO2-reduzierende Maßnahmen in bestehenden Eisen- und Stahlproduktionsprozessen, Carbon Capture and Storage- (CCS) sowie Carbon Capture and Usage-Technologien (CCU). Wohingegen bei CDA CO2-Emissionen durch erneuerbare elektrische Energie sowie wasserstoffbasierte Reduktion des Eisenerzes gar nicht erst entstehen sollen. Der CDA-Weg, der voraussichtlich beschritten werden muss, um eine klimaneutrale Stahlproduktion zu erreichen [38], geht mit einer kostenintensiven Transformation der Stahlproduktion einher, die bereits von vielen Unternehmen der Stahlindustrie eingeleitet wurde und von der im Wesentlichen die beiden in Europa vorherrschenden Stahlproduktionsrouten Hochofen-Konverter-Route und Elektrolichtbogenofen-Route betroffen sind. Die CO2-Emissionen der Hochofen-Konverter-Route, von denen der überwiegende Anteil auf den Hochofen fällt, liegen laut einer für das Jahr 2015 erstellten Studie bei 1921 kg CO2/t Rohstahl inklusive der CO2-Last der Pellets als Einsatzmaterial sowie der Emissionen der nachgelagerten Stranggießanlagen und Walzwerke. Im Hochofen wird das Eisenerz durch Kohlenstoff (C) bzw. Kohlenstoffmonoxid (CO) – welche größtenteils aus dem Koks, der dem Hochofen zusammen mit dem Möller über die Gicht zugeführten wird, stammen – unter Entstehung von Roheisen und Kohlenstoffdioxid (CO2) reduziert. Das neben dem CO2 im Prozessgas enthaltene CO wird zum Beispiel zur Energiegewinnung in peripheren Prozessen ebenfalls unter Bildung von CO2 verbrannt. Zusätzlich zur Reduktion hat der Koks unter anderem physikalische Aufgaben, wie die Errichtung eines Stützgerüstes und die Gewährleistung der Permeabilität im Hochofenprozess. Somit ist eine vollkommene Substitution des Kokses zur Vermeidung der CO2-Emissionen im Hochofen nicht denkbar. Viele Strategien der Stahlunternehmen zum Erreichen der Klimaziele verfolgen daher den Wechsel von der Rohstahlproduktion aus der Hochofen-Konverter-Route hin zur Rohstahlproduktion im Elektrolichtbogenofen (EAF – Electric Arc Furnace) mit dem Einsatz von direkt reduziertem Eisen (Eisenschwamm, DRI – Direct Reduced Iron) aus vorgelagerten Direktreduktionsanlagen, die mit Wasserstoff (H2) als Reduktionsmittel betrieben werden können. Dabei ist die Elektrostahlerzeugung kein neuer Prozess und nimmt in der europäischen Union bereits jetzt einen Anteil von ca. 44 % der Rohstahlproduktion ein, jedoch überwiegend mit Schrott als Einsatzmaterial. Bei der Elektrostahlerzeugung mit Schrotteinsatz fallen laut der oben genannten Studie von Lüngen für das Jahr 20152 410 kg CO2-Emissionen pro Tonne Rohstahl an, von denen der Großteil auf die CO2-Last der fremd bezogenen elektrischen Energie zurückzuführen ist und daher nicht im Produktionsprozess selbst entsteht. Auch die Direktreduktion wird schon seit 1972 in der weltweit zweiten und bis heute in Westeuropa einzigen Direktreduktionsanlage in Hamburg betrieben. Während hier noch mit einem Reduktionsgas gearbeitet wird, das hauptsächlich aus einem aus Erdgas gewonnenen Wasserstoff-Kohlenstoffmonoxid-Gemisch besteht, liegt eine aktuelle Kernherausforderung in der Bereitstellung des in der Größenordnung der von der Transformation betroffenen Rohstahlproduktionskapazitäten notwendigen, mit erneuerbarer elektrischer Energie hergestellten Wasserstoffs. Wird zusätzlich der Strom für das Einschmelzen im Elektrolichtbogenofen aus erneuerbaren Quellen gewonnen und werden schließlich als Brennstoff verwendete Kohle und als Brennstoff verwendetes Erdgas durch CO2-neutrale Bio-Brennstoffe ersetzt, sind sowohl für den Einsatz von mit Wasserstoff reduziertem und auf Pellets ohne CO2-Last basiertem Eisenschwamm als auch für den Einsatz von Schrott CO2-Emissionen von jeweils nur 60 kg CO2/t Rohstahl erreichbar, was eine Reduktion der Emissionen, ausgehend von der Konverter-Hochofen-Route um 97 % und ausgehend von der Schrott-Elektrolichtbogenofen-Route um 85 % bedeuten würde.
Der Betrieb von Elektrolichtbogenöfen macht die an den Standorten vorhandenen Konverter sowie die Infrastruktur für Behandlung und Transport des Roheisens überflüssig. Die fortwährende Nutzung dieser bestehenden Anlagenstruktur dient daher unter anderem als Motivation für die Entwicklung einer zweiten Transformationsstrategie, die einen sogenannten Einschmelzer (SAF – Submerged Arc Furnace) als der Direktreduktionsanlage nachgelagerten Prozess vorsieht, in dem wiederum Roheisen erschmolzen wird, das anschließend im Konverter zu Rohstahl veredelt wird.
Die Transformation der Stahlindustrie beeinflusst einen weiteren CO2-intensiven Industriesektor, nämlich die Zementindustrie die verantwortlich ist für rund 4 % der CO2-Emissionen in der EU. Etwa zwei Drittel dieser Emissionen entfallen als Prozessemissionen auf die Entsäuerung des Rohstoffs Kalkstein (CaCO3), also auf die Abspaltung von CO2 unter Entstehung des für die Herstellung von Zementklinker notwendigen Branntkalks (CaO) als Zwischenstufe bei der Bildung der hydraulischen Phasen Tri- und Dicalciumsilikat. Als eines der fünf Themenfelder (5C-Ansatz: Clinker, Cement, Concrete, Construction, Carbonation), welche die europäische Zementindustrie entlang ihrer Wertschöpfungskette zum Erreichen der gesetzlichen Vorgaben der europäischen Union erarbeitet hat, umfasst das Feld "Cement" zum größten Teil die Reduzierung des Klinker-Zement-Faktors. Im Jahr 2017 betrug er 77 %, das heißt, dass 23 % des Klinkers durch alternative Materialien ersetzt wurden. Bis zum Jahr 2030 wird ein Faktor von 74 % und bis zum Jahr 2050 von 65 % angestrebt. Den größten Anteil an den Klinkersubstituten hat mit 33 % der Hüttensand aus der Stahlindustrie. Bei der Roheisenproduktion im Hochofen entsteht als Nebenprodukt Hochofenschlacke, die unter Zugabe von Schlackebildnern die Gangart des Möllers und mineralische Koksbestandteile abbindet, sowie weitere unerwünschte Begleitelemente wie Schwefel und Alkalien aufnimmt. Allein in Deutschland wurden im Jahr 2021 6,90 Mio. t – das entspricht 90 % der gesamten produzierten Hochofenschlacke – zu glasig erstarrtem Hüttensand granuliert. Dieser Hüttensand besitzt latent hydraulische Eigenschaften und wird daher seit mehr als 140 Jahren als Zementbestandteil eingesetzt, wodurch in Deutschland jährlich rund 4,5 Mio. t CO2-Emissionen eingespart werden. Alle Transformationsstrategien der Stahlindustrie beinhalten die notwendige Außerbetriebnahme der CO2-intensiven Hochöfen. Dies hat unter anderem zur Folge, dass die Hochofenschlacke als Nebenprodukt der Rohstahlerzeugung im Hochofen nicht mehr zur Verfügung stehen wird, wodurch die weitere Reduzierung des Klinker-Zement-Faktors erhebliche Zusatzmengen alternativer Materialien benötigen wird. Derzeit ist noch unklar, ob z.B. calcinierte Tone im benötigten Umfang erzeugt werden können.
Der Fachbereich Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung der Bundesanstalt für Materialforschung und -prüfung (BAM) und das Institut für Baustoffforschung FEhS forschen zusammen mit Industriepartnern und weiteren Forschungseinrichtungen im Rahmen zweier Projekte in den Kooperationssphären der Stahl- und Zementindustrie, die zur Bewältigung dieser Herausforderungen beitragen. Im Projekt SlagCEM wird die Produktion eines hydraulischen Zementbestandteils durch Reduktion von Konverter- bzw. Linz-Donawitz-Schlacke (LDS) untersucht. Die mit den zusätzlich aufgenommen Lichtbogenofenkapazitäten steigenden Mengen an Elektrolichtbogenofenschlacke (EOS, engl. electric arc furnace slag, EAFS) werden im Projekt DRI-EOS behandelt, welches die Produktion eines latent hydraulischen Hüttensandsubstituts zum Ziel hat.
Carbonfaser verstärkte Kunststoffe (CFK) sind aus dem Leichtbau nicht mehr wegzudenken. Da die Produktion der Fasern viel Energie benötigt ist deren Recycling anzustreben. Durch Bearbeitung und Handling während des Recyclings verkürzen sich die Carbonfasern (CF) analog zur Papierfaser. Zu kurze Fasern können nicht mehr in eine Flächenstruktur eingebracht werden und müssen daher aus dem Kreislauf ausgeschleust und einer Verwertung zugeführt werden. Untersuchungen des Lehr- und Forschungsgebiets Technologie der Energierohstoffe (TEER) der RWTH Aachen University haben gezeigt, dass die Bedingungen für eine energetische Nutzung von CF-Abfällen in Abfallverbrennungsanlagen nicht geeignet sind. Zudem können CF Betriebsprobleme verursachen. Des Weiteren können bei einer unzureichenden thermischen Behandlung sogenannte WHO-Fasern entstehen, die als gesundheitsschädlich einzustufen sind. Eine Alternative können Hochtemperaturverfahren mit höheren Verweilzeiten sein. Es kommt die Herstellung von Calciumcarbid in Frage, bei der CF als Kohlenstoffträger und der Kunststoff als Energieträger genutzt werden. Eine weitere Verwertungsoption stellt die Stahlproduktionsroute dar. Erste Untersuchungen der Bundesanstalt für Materialforschung und -prüfung (BAM) und TEER am kleintechnischen Lichtbogen der BAM zeigen, dass CF-Abfälle potentiell als Reduktionsmittel und Energieträger eingesetzt werden können.
Wastewater contains a diverse array of organic and inorganic compounds and its complex composition strongly depends on the location and the connected dischargers. However, municipal wastewater as a carrier of feces and urine generally contains considerable amounts of the main nutrients nitrogen and phosphorus. The latter is in the focus of the discussions about the recovery potential of wastewater due to the relatively high mass flows of phosphorus in wastewater and the finite nature and decreasing quality of phosphate rock reserves. But due to the presence of the whole periodic table of elements, wastewater might contain further valuable components of interest for recovery including those defined as critical raw materials by the European Commission. Phosphorus and most of the other critical raw materials are fixed in the sewage sludge and after incineration in the sewage sludge ash (SSA). This is accompanied by high concentration factors from wastewater via sludge to ash. However, the mass fractions of the majority of elements in sewage sludge are comparable to those of the earth crust, indicating no relative enrichment. Nevertheless, enrichment factors of 100 or higher are given for phosphorus, copper, zinc, cadmium, silver, tin, lead and the platinum group elements indicating an anthropogenic input. An economic value of sewage sludge was estimated to $460,-/t calculated on the basis of the respective market prices for high purity elements – a theoretical value. A German survey of sewage sludge ashes showed that the mass fractions and the mass flows of most of the elements present in SSA are probably too low for an economic recovery. In most cases the mass flows are rather small compared to the imports and the chemical forms are not suitable for recovery. An exception is phosphorus that is present in high mass fractions up to 13% and that bears a high substitution potential. If the application of P-recovery technologies lead to a further concentration of valuable elements e.g. as by-products in side streams of the process, it would probably make also the recovery of other elements of economic interest.
Im Verbundprojekt R-Rhenania wird eine industrielle Demonstrationsanlage am Standort der Monoverbrennungsanlage Altenstadt der Firma Emter errichtet und im Jahr 2024 den Betrieb aufnehmen. Die vorhandene Rostfeuerung-Monoverbrennung wird so umgebaut, dass ein neues thermochemisches Verfahren integriert werden kann, welches hochwirksame und schadstoffarme Dünger produziert (bis zu 17.000 t/a). Die thermochemischen Produkte werden in Gefäß- und Feldversuchen im ökologischen Landbau auf ihre Düngewirkung getestet. Die Umweltverträglichkeit der Demonstrationsanlage wird untersucht, wie auch die Übertragbarkeit des Verfahrens auf weitere Regionen.
Die Zementindustrie und weitere energieintensive Industrien wie etwa die Stahlindustrie stehen vor dem Hintergrund der Transformation unserer Gesellschaft zur Klimaneutralität vor erheblichen Herausforderungen. Ziel dieser Branchen ist perspektivisch die vollständige Vermeidung klimaschädlicher Emissionen – mit besonderem Fokus auf Kohlendioxid. Neben der Umstellung auf regenerative Energieträger, sind im Speziellen für die Zementindustrie die erheblichen Anteile an CO2-Emissionen durch die Entsäuerung von Kalkstein zukünftig zu vermeiden. Da die hervorragenden Bindemitteleigenschaften des bisher hauptsächlich in Zementen eingesetzten Portlandklinkers jedoch auf Calciumverbindungen wie Tri- und Di-calciumsilikaten basieren, stellt die Substitution des Kalks derzeit für die Zementindustrie die größte Herausforderung dar. Neben vollständig neuen Bindemittelsystemen ohne Verwendung von Kalk und CCS/CCU-Technologien zur Vermeidung der CO2-Emissionen bei Verwendung von Kalk, können Abfälle und Nebenprodukte wie etwa Betonbrechsand, verschiedene Schlacken und weitere Massenreststoffe sinnvoll zur Einsparung von Rohstoffen und zur Vermeidung von CO2-Emissionen eingesetzt werden. Es gilt diese Potentiale von Sekundärrohstoffen branchenübergreifend zu identifizieren und Synergien zwischen den Branchen nutzbar zu machen. Hierbei werden neben der chemischen Zusammensetzung der Abfälle und Nebenprodukte auch die Verfügbarkeit und der Massenstrom relevante Kriterien sein. Die potenziellen Sekundärrohstoffe und deren Gemische mit chemisch ähnlicher Zusammensetzung wie die bisher verwendeten Bindemittel, können durch verschiedene technische Ansätze wieder in reaktive Bindemittel umgewandelt und damit nutzbar gemacht werden. Eine gezielte Umwandlung der nicht reaktiven mineralischen Phasen in neue mineralische Phasen mit guten Bindemitteleigenschaften, kann u. a. durch Schmelzprozesse erzielt werden. In Schmelzen können bei hohen Temperaturen die bestehenden, nicht reaktiven mineralischen Phasen zerstört und neue mineralische Phasen mit guten Bindemitteleigenschaften erzeugt werden. Hohe Freiheitsgrade durch gezielte Einstellung der stofflichen Zusammensetzung der Schmelze, durch Stoffseparationen und durch geregelte Abkühlregimes können eine maßgeschneiderte Erzeugung neuer Bindemitteltypen ermöglichen. Aufgrund der hohen erforderlichen Temperaturen von Schmelzprozessen ist die Umsetzung dieser neuen Verfahren nach Möglichkeit in bestehenden pyrometallurgischen Produktionsrouten wie etwa der Stahlproduktion vorzunehmen. So kann etwa der Einsatz von Betonbrechsand als Schlackebildner in der Stahlproduktion zielführend sein, wenn die Schlacke wieder zu einem Bindemittel prozessiert wird und in Zementen Verwendung findet. Eine stoffliche Kreislaufführung wäre hiermit gegeben, wobei der Einsatz von Kalkstein als Schlackebildner oder Rohstoff für die Zementproduktion, und damit die entsprechenden CO2-Emissionen, vermieden werden. Die Entwicklung neuartiger Bindemittelsysteme auf Basis von Sekundärrohstoffen sollte von erforderlichen Anpassungen und neuen Entwicklungen in der Regelsetzung und Normung begleitet werden. Vor allem muss gewährleistet sein, dass die mit neuen Bindemitteln hergestellten Betone den hohen Anforderungen an Dauerhaftigkeit und Umweltverträglichkeit genügen. Des Weiteren sollte mit den etablierten Methoden, wie etwa der Lebenszyklusanalyse, untersucht werden, inwiefern und in welchem Umfang die neuen technischen Entwicklungen zu Nachhaltigkeit und Klimaschutz beitragen.
Die Zementindustrie und weitere energieintensive Industrien wie etwa die Stahlindustrie stehen vor dem Hintergrund der Transformation unserer Gesellschaft zur Klimaneutralität vor erheblichen Herausforderungen. Ziel dieser Branchen ist perspektivisch die vollständige Vermeidung klimaschädlicher Emissionen – mit besonderem Fokus auf Kohlendioxid. Neben der Umstellung auf regenerative Energieträger, sind im Speziellen für die Zementindustrie die erheblichen Anteile an CO2-Emissionen durch die Entsäuerung von Kalkstein zukünftig zu vermeiden. Da die hervorragenden Bindemitteleigenschaften des bisher hauptsächlich in Zementen eingesetzten Portlandklinkers jedoch auf Calciumverbindungen wie Tri- und Di-calciumsilikaten basieren, stellt die Substitution des Kalks derzeit für die Zementindustrie die größte Herausforderung dar. Neben vollständig neuen Bindemittelsystemen ohne Verwendung von Kalk und CCS/CCU-Technologien zur Vermeidung der CO2-Emissionen bei Verwendung von Kalk, können Abfälle und Nebenprodukte wie etwa Betonbrechsand, verschiedene Schlacken und weitere Massenreststoffe sinnvoll zur Einsparung von Rohstoffen und zur Vermeidung von CO2-Emissionen eingesetzt werden. Es gilt diese Potentiale von Sekundärrohstoffen branchenübergreifend zu identifizieren und Synergien zwischen den Branchen nutzbar zu machen. Hierbei werden neben der chemischen Zusammensetzung der Abfälle und Nebenprodukte auch die Verfügbarkeit und der Massenstrom relevante Kriterien sein. Die potenziellen Sekundärrohstoffe und deren Gemische mit chemisch ähnlicher Zusammensetzung wie die bisher verwendeten Bindemittel, können durch verschiedene technische Ansätze wieder in reaktive Bindemittel umgewandelt und damit nutzbar gemacht werden. Eine gezielte Umwandlung der nicht reaktiven mineralischen Phasen in neue mineralische Phasen mit guten Bindemitteleigenschaften, kann u. a. durch Schmelzprozesse erzielt werden. In Schmelzen können bei hohen Temperaturen die bestehenden, nicht reaktiven mineralischen Phasen zerstört und neue mineralische Phasen mit guten Bindemitteleigenschaften erzeugt werden. Hohe Freiheitsgrade durch gezielte Einstellung der stofflichen Zusammensetzung der Schmelze, durch Stoffseparationen und durch geregelte Abkühlregimes können eine maßgeschneiderte Erzeugung neuer Bindemitteltypen ermöglichen. Aufgrund der hohen erforderlichen Temperaturen von Schmelzprozessen ist die Umsetzung dieser neuen Verfahren nach Möglichkeit in bestehenden pyrometallurgischen Produktionsrouten wie etwa der Stahlproduktion vorzunehmen. So kann etwa der Einsatz von Betonbrechsand als Schlackebildner in der Stahlproduktion zielführend sein, wenn die Schlacke wieder zu einem Bindemittel prozessiert wird und in Zementen Verwendung findet. Eine stoffliche Kreislaufführung wäre hiermit gegeben, wobei der Einsatz von Kalkstein als Schlackebildner oder Rohstoff für die Zementproduktion, und damit die entsprechenden CO2-Emissionen, vermieden werden. Die Entwicklung neuartiger Bindemittelsysteme auf Basis von Sekundärrohstoffen sollte von erforderlichen Anpassungen und neuen Entwicklungen in der Regelsetzung und Normung begleitet werden. Vor allem muss gewährleistet sein, dass die mit neuen Bindemitteln hergestellten Betone den hohen Anforderungen an Dauerhaftigkeit und Umweltverträglichkeit genügen. Des Weiteren sollte mit den etablierten Methoden, wie etwa der Lebenszyklusanalyse, untersucht werden, inwiefern und in welchem Umfang die neuen technischen Entwicklungen zu Nachhaltigkeit und Klimaschutz beitragen.
Recycled fertilizers produced using processes for the recovery of phosphate from residual materials such as wastewater, sewage sludge and sewage sludge ashes show very good bioavailability, but it is still a product largely unknown to the market. The aim of CLOOP is therefore to document the properties and effects of such fertilizers through chemical, mineralogical and ecological analyses as well as analytical method development and pot and field plant growth trials.
Outotec focused on 3 points in CLOOP: Experimental campaigns, process simulations as well as economic analyses with focus on the AshDec process, respectively the design of a large-scale AshDec plant for phosphorus recovery. The laboratory scale trials as well as the semi-industrial scale campaign provided valuable insights into the operating parameters of the process and the plant. As a result, for example, the temperature range could be significantly lowered, and the additive addition reduced by approx. 20 %. They have further shown that the AshDec process is not susceptible to operating fluctuations and that the product can be consistently produced at high quality. With the selection of suitable operating parameters, heavy metals (As, Pb, Cd, (Zn)) can be removed. Within the campaign, about 1.5 t of fertilizer for the plant trials in CLOOP could be produced. An AshDec plant process was digitally created in simulation software, allowing valuable process parameters to be simulated at various operating parameters. On this basis, a full-scale plant was designed. The data obtained in the project were used for a detailed economic analysis including a sensitivity analysis. It was possible to show under which conditions this plant can be operated economically.
At BAM, the AshDec fertilizer was synthesized with different additives and then applied to plant experiments at Uni Bonn. The goal hereby was to check differences in plant uptake. Because of the promising results of AshDec synthesized with sodium-carbonate and because this AshDec version does not require special off gas treatment for sulfur recovery (compared to AshDec synthesized with sodium-sulfate), all project partners agreed on continuing working with this AshDec variation. It was then used as a raw P-source for formulating it into NPK-fertilizers, by granulation with ammonium-sulfate and straw ash as potassium source. These recycling fertilizers were applied to plant- and field experiments by project partners in Brazil (University of Sao Paulo) and Australia (University of Queensland). Furthermore, in leaching experiments, the solubility of phosphorus in AshDec was compared to triple super phosphate. The experiments were carried out on soils with a varying phosphorus buffering index. Results show, that the phosphorus form in AshDec is way less soluble in water. This indicates that AshDec has the potential for a so-called next generation fertilizer – a fertilizer which’s nutrients remain in the soil and supply the plant according to its needs. At the moment, this behavior gets examined more in depth in lysimeter experiments in cooperation with University of Technology Berlin.
The focus of KWB is the Life Cycle Assessment (LCA) of different NextGen fertilizers to evaluate the entire process chain from recovery to fertilizer application. The NextGen fertilizer is credited by the amount of plant available nutrients in the product, which replace nutrients from conventional fertilizer. The LCA covers N-struvite precipitation from municipal wastewater, K-struvite precipitation from industrial wastewater and the AshDec-product from sewage sludge. The LCA task is almost complete. It could be shown that struvite precipitation has comprehensive environmental benefits, mainly since positive side effects occur in sewage sludge treatment (e.g. reduced sludge volume). In principle, the energetic and ecological profile of the AshDec process compared to direct use of sewage sludge ash cannot be assessed as being generally beneficial or negative. Regarding the global warming potential, the Ashdec process shows that the expenses (e.g. energy, chemicals) cannot be covered by the P fertilizer credit. In contrast, the impact categories “terrestrial acidification potential”, and “freshwater eutrophication potential” show positive results as the credits for conventional fertilizer are higher than the burdens for the process.
At University Bonn, the standardized pot experiments were conducted with several AshDec variations, using ryegrass, soybean, and spinach on a slightly acidic sandy soil and an organic-free standard substrate. P-uptake and biomass production of different AshDec variations were generally like those of triple super phosphate and struvite, and clearly outperformed untreated sewage sludge ash and rock phosphate. Field trials in Australia and Brazil with sugarcane on acidic soils are still ongoing and results are expected by the end of 2021.
extraWERT Forschungsvorhaben
(2022)
Die novellierte AbfKlärV (2017) beinhaltet die Verpflichtung zum P-Recycling ab einem P-Gehalt im Klärschlamm von 20 g/kg. Im Vortrag werden Ergebnisse des Forschungsvorhabens extraWERT zu diesem Themenkomplex vorgestellt. Es werden Untersuchungen zu P-Gehalten deutscher Klärschlämme und zu den zulässigen Analysemethoden dafür vorgestellt.
Zukünftig werden vermehrt P-Recyclate auf den Düngemittelmarkt kommen. Diese müssen ausreichend charakterisiert werden, um Sicherheit und Wirksamkeit beurteilen zu können. Mit dem Vortrag wurde der wissenschaftliche Beirat für Düngungsfragen des Bundesministeriums für Ernährung und Landwirtschaft beraten.
Das Element Phosphor ist für alle Lebewesen essenziell und wird beispielsweise von Pflanzen in Form von Phosphaten aufgenommen.
In der landwirtschaftlichen Produktion werden dem Boden die Phosphate durch Wachstum und Ernte der Pflanzen entzogen und müssen ihm in Form von Phosphatdüngemitteln wieder zugeführt werden, um die Nahrungsmittelproduktion zu sichern. Rohphosphat stellt die Grundlage unserer derzeitigen Phosphatdüngemittel dar, ist aber gleichzeitig ein endlicher Rohstoff.
Des Weiteren sind insbesondere sedimentäre Rohphosphate oftmals mit erheblichen Konzentrationen toxischer Schadstoffe wie Cadmium, Uran und Thorium belastet. Eine Kreislaufführung des Phosphats sollte erfolgen, um natürliche Rohstoffvorkommen zu schonen und den Eintrag von Schadstoffen auf unsere Böden zu unterbinden.
Conventional fertilisers have their disadvantages as nutrient release is not synchronised with the demand of plants. Several approaches of "next generation fertilisers" are aiming at controlled nutrient release. Recycling fertilisers are often not soluble in water but fully plant available. They are suitable raw materials for the production of new types of controlled release fertilisers.
Carbonfasern sind äußerst stabil und werden auch in Anlagen zur Verbrennung von Sondermüll kaum zerstört. Beim Handling carbonfaserhaltiger Abfälle können Gesundheitsrisken auftreten (Abgabe von WHO-Fasern). Es werden Methoden der Verwertung carbonfaserhaltiger Reststoffe in der Pyrometallurgie diskutiert.
Bei der Stahlproduktion fallen verfahrensbedingt große Mengen an Nebenprodukten und Abfällen wie Stahlwerksschlacken, Filterstäube und Gichtgasschlämme an. Hohe Anteile dieser Stoffströme werden aufgrund ihrer Zusammensetzung immer noch deponiert, obwohl sie ein hohes Wertstoffpotential aufweisen. An der Bundesanstalt für Materialforschung und -prüfung (BAM) werden Verfahren untersucht und entwickelt, welche eine Verwertung und Kreislaufführung dieser Materialströme ermöglichen. Aus sogenannten Linz-Donawitz-(LD)-Schlacken können durch carbothermische Nachbehandlung Roheisen und ein dem Portlandzementklinker (PZK) ähnliches Bindemittel erzeugt werden. Aus Elektroofenstäuben und Gichtgasschlämmen kann Zink gewonnen und die Anteile an Eisen und Kohlenstoff in den Stahlproduktionsprozess zurückgeführt werden. Durch diese technischen Maßnahmen kann es gelingen die Deponierung von Abfällen der Stahlproduktion zukünftig deutlich zu reduzieren.
In Bayern wird Klärschlamm aus der kommunalen Abwasserreinigung weitgehend verbrannt. Monoverbrennungsanlagen - ausschließlich für kommunalen Klärschlamm - gibt es in Altenstadt, München, Gendorf, Straubing, Neu-Ulm und zukünftig auch in Augsburg. Die Anlage in Altenstadt verbrennt jährlich ca. 55.000 t Klärschlamm-Trockensubstanz und produziert dabei rund 15.000 t phosphatreiche Aschen.
Die Asche aus Altenstadt wird zurzeit überwiegend direkt landwirtschaftlich genutzt. Aufgrund der niedrigen Schadstoffgehalte ist diese Nutzung nach den düngemittelrechtlichen Regelungen gesetzlich zulässig. Um der Intention der neuen Düngeverordnung (26. Mai 2017) nach hocheffizienten, d.h. gut pflanzenverfügbaren Düngemitteln zu entsprechen, ist eine Aufbereitung der Klärschlammasche geplant. Im Rahmen des R-Rhenania Projektes errichten der Betreiber der Klärschlammverbrennungsanlage Altenstadt in Bayern Emter GmbH - und der Düngemittelhersteller sePura GmbH gemeinsam eine AshDec®-Demonstrationsanlage, die im Jahr 2023 den Betrieb aufnehmen soll. Das angewandte AshDec®-Verfahren schließt die Phosphate in der Klärschlammasche thermisch im Drehrohrofen auf und macht diese für Pflanzen vollständig verfügbar. Gleichzeitig werden Schadstoffe wie Arsen, Blei und Cadmium entfernt. Den thermischen Aufschluss kennt man bereits vom erfolgreichen, aber nicht mehr produzierten Düngemittel „Rhenania-Phosphat“, das auf der Basis von Rohphosphaten hergestellt wurde.
Die geplante Anlage wird neben den Aschen aus Altenstadt zusätzlich die Aschen aus weiteren bayerischen Verbrennungsanlagen verwerten und für eine Kapazität von 30.000 Jahrestonnen Asche ausgelegt sein. Der Projektpartner sePura plant den produzierten Dünger vollständig in Bayern zu verwerten. Dies verringert die Umweltbelastung durch lange Transportwege und fördert die Regionalität des Vorhabens.
Eine entscheidende Problematik nach Inkrafttreten der neuen
Klärschlammverordnung ist, wie Phosphor nicht nur rückgewonnen,
sondern in den Markt eingeschleust und letztlich auch
in den Kreislauf zurückgeführt werden kann. Die Wege hierzu
sind noch weitgehend ungeklärt. Die DWA-Arbeitsgruppe KEK-
1.1 hat aus diesem Grund einen Workshop durchgeführt, um
rechtliche Anforderungen an Rezyklate, Aspekte der Rezyklatqualität
und -beschaffenheit sowie den aktuellen Markt für Rezyklate
zu diskutieren. Auf Basis dieses Workshops wurde ein
Arbeitsbericht erstellt, der sich schwerpunktmäßig mit dem Einsatz
von Rezyklaten zu Düngezwecken beschäftigt. Hierzu liegen
bereits Erkenntnisse vor, und es sind bereits Praxisbeispiele in
der Umsetzung.
A new sewage sludge ordinance was set in force in Germany in 2017 that makes phosphorus recovery from sewage sludge mandatory. The technological possibilities for P-recovery from waste water, sewage sludge and sewage sludge ash were presented.
Verwertung von Klärschlamm
(2018)
Die natürlichen Nährstoffkreisläufe werden durch anthropogene Einflüsse, wie das Einbringen von Schadstoffen in nährstoffreiche Stoffströme, und die ungünstige lokale Verteilung der Nährstoffe (z.B. im Zuge der Intensivtierhaltung), erheblich gestört. Es sind lokale Unter- und Überversorgungen mit Nährstoffen zu beobachten. Gelangen die Nährstoffe in Gewässer, kommt es zum bekannten Phänomen der Eutrophierung. Hierbei ist der Nährstoff Phosphat meist der limitierende Faktor und es bestehen große Bestrebungen den anthropogenen Eintrag in Fließgewässer, Seen und Binnenmeere zu unterbinden. Der Schutz der Ostsee vor Nährstoffeinträgen ist beispielsweise ein sehr wichtiges Thema geworden und wird u.a. von der Baltic Sea Action Group verfolgt.
Weitere Auswirkungen des bestehenden Systems sind Entzüge aus dem Nährstoffkreislauf, wie etwa bei der Deponierung phosphor- aber gleichzeitig auch schadstoffhaltiger Klärschlammaschen oder bei der Mitverbrennung von Klärschlamm in Müllverbrennungsanlagen, Kraftwerken oder Zementwerken. Hier wird das Phosphat ebenfalls als Bestandteil von Aschen deponiert oder in Form von Baustoffen einer sinnvollen stofflichen Nutzung entzogen. Gegen diese Art des Verlusts von Phosphat aus dem Nährstoffkreislauf hat der Gesetzgeber mit der Novellierung der Klärschlammverordnung reagiert, die am 3. Oktober 2017 in Kraft getreten ist und u.a. Regelungen zur Rückgewinnung von Phosphat aus Klärschlamm und Klärschlammasche enthält.
Klärschlämme aus kommunalen Abwasserbehandlungsanlagen ab einer genehmigtenAusbaugröße von über 100.000 bzw. über 50.000 Einwohnerwerten (EW) dürfen nach einer Übergangsfrist ab dem 1. Januar 2029 bzw. 2032 nicht mehr in der Landwirtschaft oder im Landschaftsbau verwertet werden. Die Betreiber dieser Anlagen sind zur Rückgewinnung des im Schlamm enthaltenen Phosphors verpflichtet, wenn der Klärschlamm einen Phosphorgehalt von 20 g/kg Trockenrückstand (TR) oder mehr aufweist. Für Klärschlämme mit P-Gehalten > 40 g/kg TR reicht alternativ die Absenkung der P-Konzentration um 50 % aus. Die Rückgewinnung kann aus dem Schlamm oder aus der Verbrennungsasche des thermisch vorbehandelten Klärschlamms erfolgen.
Aus der Asche müssen mindestens 80 % des Phosphoranteils zurückgewonnen werden. Anstelle einer Phosphorrückgewinnung aus Klärschlämmen aus kleineren und mittelgroßen Abwasserbehandlungsanlagen (bis 50.000 EW) können diese Schlämme auch
weiterhin zu Düngezwecken auf Böden ausgebracht werden, sofern die Anforderungen und insbesondere die Grenzwerte der Klärschlammverordnung und des Düngerechts eingehalten werden.
In der Abwasserreinigung wird der Makronährstoff Phosphor je nach Typ und Größe der Abwasserreinigungsanlage durch verschiedene Verfahren der Phosphatelimination weitgehend in die feste Phase, den Klärschlamm, überführt. Dies geschieht durch die Zugabe von Fällmitteln auf der Basis von Eisen- oder Aluminiumsalzen, oder durch das Verfahren der vermehrten biologischen Phosphorelimination (Bio-P). Das Phosphat liegt nun abhängig vom eingesetzten Verfahren als Bestandteil der gewachsenen Biomasse, als gefälltes Salz, adsorbiert an Eisen(oxi)hydroxiden oder im Falle der Bio-P Klärschlämme auch intrazellulär in Form von Polyphosphaten vor. Weitergehende Informationen hierzu sind im Beitrag von Kratz et al. Pflanzenverfügbarkeit und agronomische Effizienz von klärschlamm-basierten Phosphor (P) – Recyclingdüngern in diesem Buch zu finden. Die Bindungsformen unterscheiden sich demnach nach Art der eingesetzten Technologie der Phosphatelimination erheblich und haben einen entscheidenden Einfluss auf die verschiedenen Möglichkeiten der P-Extraktion und Rückgewinnung.
Die P-Rückgewinnung aus Teilströmen mit erhöhten P-Gehalten kann direkt in den Kläranlagenbetrieb integriert werden und führt dort in vielen Fällen zu betrieblichen und ökonomischen Vorteilen. Sie ist in der Regel auf Bio-P-Kläranlagen beschränkt, da hier die anaerobe P-Rücklösung initiiert und genutzt werden kann. Durch die reine P-Rücklösung durch Schaffung anaerober Bedingungen ist allerdings das Potential der Rückgewinnung auf 5 bis 15 Prozent der Zulauffracht limitiert.
Die meisten Kläranlagen in Deutschland werden mit einer chemischen Phosphor-Fällung betrieben. Diese Anlagen können aus dem Klärschlamm Phosphat in ausreichend hoher Konzentration nur zurückgewinnen, indem zusätzlich anorganische Säuren wie Schwefelsäure zugeführt werden oder ein Aufschluss mit flüssigem Kohlendioxid stattfindet. Es wird angenommen, dass sich mit diesen Verfahren mehr als 50 Prozent der Zulauffracht einer Kläranlage zurückgewinnen lassen. Der Aufschluss von Klärschlamm mit Schwefelsäure geht aber mit vergleichsweise hohen Umweltwirkungen sowie mit höheren Kosten im Vergleich zu anderen Phosphor-Rückgewinnungsverfahren einher. Ein sehr hohes Potential der Rückgewinnung von Phosphor (P) ist bei allen Verfahren gegeben, die als Rohstoff die Asche aus der Monoverbrennung verwerten. Der Aufschluss mit anorganischen Säuren ermöglicht die sichere Phosphor-Rückgewinnung von mehr als 80% Prozent des Kläranlagenzulaufs. Die Verfahren sind zum Teil großtechnisch umgesetzt oder es befinden sich großtechnische Anlagen im Bau. Auch thermochemische Verfahren wurden entwickelt und deren Einsatzbereitschaft im großtechnischen Maßstab erfolgreich demonstriert. In dem nachfolgenden Beitrag werden unterschiedliche praxiserprobte Verfahren zur Phosphor-Rückgewinnung unter technischen und wirtschaftlichen Aspekten vorgestellt.
Vortrag über die Regelungen der AbfKlärV bezüglich P-Rückgewinnung. Diskussion der Auswirkung einer konzentrationsbezogenen Grenze auf die Pflicht zur P-Rückgewinnung. Diskussion der nach AbfKlärV zulässigen analytischen Verfahren zur Bestimmung von P in Klärschlamm und Ableitung von Empfehlungen. Vorstellung der Ergebnisse eines Ringversuchs mit 28 Laboren.
Die Europäische Kommission präsentierte am 11. Dezember 2019 den European Green Deal, ein Konzept mit dem Ziel, bis zum Jahr 2050 als erster Kontinent Klimaneutralität zu erreichen. Mit Inkrafttreten der Verordnung (EU) 2021/1119 des Europäischen Parlaments und des Europäischen Rates am 29. Juli 2021 zur Schaffung des Rahmens für die Verwirklichung der Klimaneutralität („Europäisches Klimagesetz“), ist dieses, sowie das Ziel der Reduzierung der Nettotreibhausgasemissionen um mindestens 55 % bis 2030 in der Gesetzgebung der Europäischen Union verankert. Die Stahlindustrie in der Europäischen Union mit ca. 57 Mio. t Nettotreibhausgasemissionen im Jahr 2020, die annähernd 2 % der Emissionen der Europäischen Union ausmachen (Inklusive Energie: 127 Mio. t; 4 %), bekennt sich zur erheblichen Reduzierung der CO2-Emissionen bis zum Jahr 2030 und zum Erreichen der Klimaneutralität bis zum Jahr 2050. Als Schlüsselwege zur Verwirklichung dieser Zielstellung hat sie zum einen Smart Carbon Usage (SCU) und zum anderen Carbon Direct Avoidance (CDA) in einer Roadmap formuliert. SCU umfasst CO2-reduzierende Maßnahmen in bestehenden Eisen- und Stahlproduktionsprozessen, Carbon Capture and Storage- (CCS) sowie Carbon Capture and Usage-Technologien (CCU). Wohingegen bei CDA CO2-Emissionen durch erneuerbare elektrische Energie sowie wasserstoffbasierte Reduktion des Eisenerzes gar nicht erst entstehen sollen. Der CDA-Weg, der voraussichtlich beschritten werden muss, um eine klimaneutrale Stahlproduktion zu erreichen [38], geht mit einer kostenintensiven Transformation der Stahlproduktion einher, die bereits von vielen Unternehmen der Stahlindustrie eingeleitet wurde und von der im Wesentlichen die beiden in Europa vorherrschenden Stahlproduktionsrouten Hochofen-Konverter-Route und Elektrolichtbogenofen-Route betroffen sind. Die CO2-Emissionen der Hochofen-Konverter-Route, von denen der überwiegende Anteil auf den Hochofen fällt, liegen laut einer für das Jahr 2015 erstellten Studie bei 1921 kg CO2/t Rohstahl inklusive der CO2-Last der Pellets als Einsatzmaterial sowie der Emissionen der nachgelagerten Stranggießanlagen und Walzwerke. Im Hochofen wird das Eisenerz durch Kohlenstoff (C) bzw. Kohlenstoffmonoxid (CO) – welche größtenteils aus dem Koks, der dem Hochofen zusammen mit dem Möller über die Gicht zugeführten wird, stammen – unter Entstehung von Roheisen und Kohlenstoffdioxid (CO2) reduziert. Das neben dem CO2 im Prozessgas enthaltene CO wird zum Beispiel zur Energiegewinnung in peripheren Prozessen ebenfalls unter Bildung von CO2 verbrannt. Zusätzlich zur Reduktion hat der Koks unter anderem physikalische Aufgaben, wie die Errichtung eines Stützgerüstes und die Gewährleistung der Permeabilität im Hochofenprozess. Somit ist eine vollkommene Substitution des Kokses zur Vermeidung der CO2-Emissionen im Hochofen nicht denkbar. Viele Strategien der Stahlunternehmen zum Erreichen der Klimaziele verfolgen daher den Wechsel von der Rohstahlproduktion aus der Hochofen-Konverter-Route hin zur Rohstahlproduktion im Elektrolichtbogenofen (EAF – Electric Arc Furnace) mit dem Einsatz von direkt reduziertem Eisen (Eisenschwamm, DRI – Direct Reduced Iron) aus vorgelagerten Direktreduktionsanlagen, die mit Wasserstoff (H2) als Reduktionsmittel betrieben werden können. Dabei ist die Elektrostahlerzeugung kein neuer Prozess und nimmt in der europäischen Union bereits jetzt einen Anteil von ca. 44 % der Rohstahlproduktion ein, jedoch überwiegend mit Schrott als Einsatzmaterial. Bei der Elektrostahlerzeugung mit Schrotteinsatz fallen laut der oben genannten Studie von Lüngen für das Jahr 20152 410 kg CO2-Emissionen pro Tonne Rohstahl an, von denen der Großteil auf die CO2-Last der fremd bezogenen elektrischen Energie zurückzuführen ist und daher nicht im Produktionsprozess selbst entsteht. Auch die Direktreduktion wird schon seit 1972 in der weltweit zweiten und bis heute in Westeuropa einzigen Direktreduktionsanlage in Hamburg betrieben. Während hier noch mit einem Reduktionsgas gearbeitet wird, das hauptsächlich aus einem aus Erdgas gewonnenen Wasserstoff-Kohlenstoffmonoxid-Gemisch besteht, liegt eine aktuelle Kernherausforderung in der Bereitstellung des in der Größenordnung der von der Transformation betroffenen Rohstahlproduktionskapazitäten notwendigen, mit erneuerbarer elektrischer Energie hergestellten Wasserstoffs. Wird zusätzlich der Strom für das Einschmelzen im Elektrolichtbogenofen aus erneuerbaren Quellen gewonnen und werden schließlich als Brennstoff verwendete Kohle und als Brennstoff verwendetes Erdgas durch CO2-neutrale Bio-Brennstoffe ersetzt, sind sowohl für den Einsatz von mit Wasserstoff reduziertem und auf Pellets ohne CO2-Last basiertem Eisenschwamm als auch für den Einsatz von Schrott CO2-Emissionen von jeweils nur 60 kg CO2/t Rohstahl erreichbar, was eine Reduktion der Emissionen, ausgehend von der Konverter-Hochofen-Route um 97 % und ausgehend von der Schrott-Elektrolichtbogenofen-Route um 85 % bedeuten würde.
Der Betrieb von Elektrolichtbogenöfen macht die an den Standorten vorhandenen Konverter sowie die Infrastruktur für Behandlung und Transport des Roheisens überflüssig. Die fortwährende Nutzung dieser bestehenden Anlagenstruktur dient daher unter anderem als Motivation für die Entwicklung einer zweiten Transformationsstrategie, die einen sogenannten Einschmelzer (SAF – Submerged Arc Furnace) als der Direktreduktionsanlage nachgelagerten Prozess vorsieht, in dem wiederum Roheisen erschmolzen wird, das anschließend im Konverter zu Rohstahl veredelt wird.
Die Transformation der Stahlindustrie beeinflusst einen weiteren CO2-intensiven Industriesektor, nämlich die Zementindustrie die verantwortlich ist für rund 4 % der CO2-Emissionen in der EU. Etwa zwei Drittel dieser Emissionen entfallen als Prozessemissionen auf die Entsäuerung des Rohstoffs Kalkstein (CaCO3), also auf die Abspaltung von CO2 unter Entstehung des für die Herstellung von Zementklinker notwendigen Branntkalks (CaO) als Zwischenstufe bei der Bildung der hydraulischen Phasen Tri- und Dicalciumsilikat. Als eines der fünf Themenfelder (5C-Ansatz: Clinker, Cement, Concrete, Construction, Carbonation), welche die europäische Zementindustrie entlang ihrer Wertschöpfungskette zum Erreichen der gesetzlichen Vorgaben der europäischen Union erarbeitet hat, umfasst das Feld "Cement" zum größten Teil die Reduzierung des Klinker-Zement-Faktors. Im Jahr 2017 betrug er 77 %, das heißt, dass 23 % des Klinkers durch alternative Materialien ersetzt wurden. Bis zum Jahr 2030 wird ein Faktor von 74 % und bis zum Jahr 2050 von 65 % angestrebt. Den größten Anteil an den Klinkersubstituten hat mit 33 % der Hüttensand aus der Stahlindustrie. Bei der Roheisenproduktion im Hochofen entsteht als Nebenprodukt Hochofenschlacke, die unter Zugabe von Schlackebildnern die Gangart des Möllers und mineralische Koksbestandteile abbindet, sowie weitere unerwünschte Begleitelemente wie Schwefel und Alkalien aufnimmt. Allein in Deutschland wurden im Jahr 2021 6,90 Mio. t – das entspricht 90 % der gesamten produzierten Hochofenschlacke – zu glasig erstarrtem Hüttensand granuliert. Dieser Hüttensand besitzt latent hydraulische Eigenschaften und wird daher seit mehr als 140 Jahren als Zementbestandteil eingesetzt, wodurch in Deutschland jährlich rund 4,5 Mio. t CO2-Emissionen eingespart werden. Alle Transformationsstrategien der Stahlindustrie beinhalten die notwendige Außerbetriebnahme der CO2-intensiven Hochöfen. Dies hat unter anderem zur Folge, dass die Hochofenschlacke als Nebenprodukt der Rohstahlerzeugung im Hochofen nicht mehr zur Verfügung stehen wird, wodurch die weitere Reduzierung des Klinker-Zement-Faktors erhebliche Zusatzmengen alternativer Materialien benötigen wird. Derzeit ist noch unklar, ob z.B. calcinierte Tone im benötigten Umfang erzeugt werden können.
Der Fachbereich Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung der Bundesanstalt für Materialforschung und -prüfung (BAM) und das Institut für Baustoffforschung FEhS forschen zusammen mit Industriepartnern und weiteren Forschungseinrichtungen im Rahmen zweier Projekte in den Kooperationssphären der Stahl- und Zementindustrie, die zur Bewältigung dieser Herausforderungen beitragen. Im Projekt SlagCEM wird die Produktion eines hydraulischen Zementbestandteils durch Reduktion von Konverter- bzw. Linz-Donawitz-Schlacke (LDS) untersucht. Die mit den zusätzlich aufgenommen Lichtbogenofenkapazitäten steigenden Mengen an Elektrolichtbogenofenschlacke (EOS, engl. electric arc furnace slag, EAFS) werden im Projekt DRI-EOS behandelt, welches die Produktion eines latent hydraulischen Hüttensandsubstituts zum Ziel hat.
Rotschlamm fällt in sehr großen Mengen bei der Herstellung von Aluminiumoxid an und wird fast ausschließlich deponiert. Es wird eine neue Technologie vorgestellt bei der das im Rotschlamm enthaltene Eisenoxid mittels Wasserstoffplasma reduziert wird. Es wird ein Reaktionsmechanismus über Titanomagnetit und Hercynit vorgeschlagen.
Steelmaking slag is a by-product of steel production, of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical cycle, used as fertiliser or landfilled.
With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of Portland cement clinker.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product has a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less hydration heat than OPC, and its hydraulic reaction was delayed. However, adding gypsum has shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS has economic and ecological benefits for both the cement and steel industries.