4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung
Filtern
Erscheinungsjahr
- 2021 (27) (entfernen)
Dokumenttyp
- Vortrag (15)
- Zeitschriftenartikel (10)
- Beitrag zu einem Tagungsband (2)
Schlagworte
- Klärschlammverordnung (6)
- Phosphor (5)
- Phosphorrückgewinnung (5)
- BOFS (4)
- Phosphorus (4)
- Hydraulic reactivity (3)
- Klärschlamm (3)
- Recycling (3)
- Abwasserbehandlung (2)
- Analytik (2)
Organisationseinheit der BAM
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (27) (entfernen)
Eingeladener Vortrag
- nein (15)
There is an ongoing debate on European scale concerning the criticality of phosphorus. In Switzerland and Germany, phosphorus recovery from phosphorus-rich waste streams will become obligatory. Sewage sludge ash is rich in phosphorus and may become an important secondary feedstock. Thermochemical treatment of sewage sludge ash with sodium sulphate under reducing conditions was shown to remove heavy metals from the solid product and produce the fully plant available crystalline phase CaNaPO4. Pilot-scale experiments in a rotary kiln were carried out at temperatures between 750 and 1000 °C and were compared to laboratory-scale experiments with crucibles. Process upscaling was successfully demonstrated but a series of differences were noticed: In comparison to laboratory-scale, solubility of phosphorus in samples from pilot-scale experiments was lower at all chosen treatment temperatures because of shorter retention time and incomplete decomposition of sodium sulphate. X-ray diffraction analysis revealed remaining phase fractions of whitlockite (Ca3-x(Mg,Fe)x(PO4)2) and sodium sulphate from the starting materials in products and thus indicated incomplete reaction. In contrast to the results of laboratory-scale experiments, the crystalline phase CaNaPO4 was clearly absent in the products from the rotary kiln but instead a Mg-bearing phase (Ca,Mg)NaPO4 was formed. Laboratory-scale experiments confirmed (Ca,Mg)NaPO4 is an intermediate phase between whitlockite and CaNaPO4. However, both crystalline phases are characterized by high plant availability. It was shown that heavy metal removal increased at higher temperatures whereas solubility and thus plant availability of phosphorus already reached its maxima at temperatures of 950 °C in pilot-scale and 875 °C in laboratory-scale experiments.
Phase formation and evolution was investigated in the CaO–SiO2 system in the range of 70–80 mol% CaO. The samples were container-less processed in an aerodynamic levitation system and crystallization was followed in situ by synchrotron x-ray diffraction at the beamline P21.1 at the German electron synchrotron (DESY). Modification changes of di- and tricalcium silicate were observed and occurred at lower temperatures than under equilibrium conditions. Despite deep sample undercooling, no metastable phase formation was observed within the measurement timescale of 1 s. For the given cooling rates ranging from 300 K s−1 to about 1 K s−1, no decomposition of tricalcium silicate was observed. No differences in phase evolution were observed between reducing and oxidizing conditions imposed by the levitation gas (Ar and Ar + O2). We demonstrate that this setup has great potential to follow crystallization in refractory oxide liquids in situ. For sub-second primary phase formation faster detection and for polymorph detection adjustments in resolution have to be implemented.
CF Pyro: Stofflich-energetische Verwertung von carbonfaserhaltigen Abfällen in der Pyrometallurgie
(2021)
Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions.
Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented.
Phosphorus (P) resource availability and quality is declining and recycling P-fertilizers from waste materials are becoming increasingly important. One important secondary P resource is sewage sludge (SSL) where P is often bound as aluminum phosphate (Al-P), iron phosphate (Fe-P) and polyphosphate (poly-P), respectively. Thermal treatment in different ways is a promising way in P recycling to produce highly plant-available P-fertilizers. To investigate mechanisms behind transformation of hardly available P-species toward plant-available P forms we treated a model SSL containing different kinds of defined P sources by low-temperature conversion (LTC) at 500 °C and subsequent thermochemical treatment of the LTC product with Na additives (TCT) at 950 °C, respectively. Pot experiments with ryegrass were carried out to determine the plant availability of P of the different treatments. The poly-P (here pyrophosphates) based fertilizers had a very high plant availability after both thermal treatments. During LTC treatment the plant availability of the Fe-P and Al-P variants increased because of the Formation of Fe(II) phosphates and/or pyro-/polyphosphates. Especially the formation of Al-polyphosphate shows a high plant availability. The subsequent TCT further increased strongly the plant availability of the Fe-P variants because of the formation of highly plant-available CaNaPO4. Thus, a direct TCT without prior LTC probably also produce CaNaPO4 and is recommended for Fe-P based SSL. However, a molar Ca/P ratio of 1 in the fertilizer is favorable for CaNaPO4 formation. Thus, the knowledge on the source of primary P in SSL is essential for choosing the accurate thermal treatment method to produce highly plant-available P-fertilizers from SSL.
Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance.
In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts.
The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production.
Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker.
The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6).
The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential.
The aim of this study was to investigate the passive sampler method Diffusive Gradients in Thin-films (DGT) for ammonium and nitrate in amended soils. Therefore, we used soils from a pot experiment with maize where nitrogen (N) was supplied as ammonium sulfate nitrate (ASN), without and with a nitrification inhibitor (NI). The additional use of a NI can delay the nitrification in the soil and making the ammonium available for a longer period in the soil solution after its application. Homogenized soil samples were collected directly from each pot after one week of incubation before sowing and after harvesting the maize. Nitrate and ammonium in these soil samples were extracted using DGT devices equipped with a Putolite A520E (for nitrate) and Microlite PrCH (for ammonium) binding layer. Ammonium DGT which determined the mobile and labile ammonium forms based on diffusion and the resupplies from the solid soil phase, only showed a significantly higher amount of extractable ammonium with NI compared to that without NI for some samples. However, significantly lower values were found for nitrate of treatments with NI compared to without NI after harvest. Thus, the lower nitrate amounts for treatments with NI compared to the treatments without NI after harvest indicated the delay of the nitrification process by the NI. Furthermore, we compared also the ammonium and nitrate
DGT results to chemical extraction with KCl solutions. The results demonstrated that the trends of DGT results and chemical extraction were complimentary through all the treatments.
Gypsum is widely used in the construction sector, and its worldwide consumption has been increasing now for several decades. Currently, the gypsum demand is met up to 60% by FGD gypsum (a by-product from coal-fired power plants) in Germany. The natural gypsum deposits cover the remaining gypsum demand. Due to national climate protection goals and the related shutdown of coal-fired power plants, the FGD gypsum supply will decrease significantly in the coming years and, therefore, other gypsum sources must be found.
Depending on the lifetime of the used gypsum products in the construction sector, an increase of gypsum in construction and demolition waste is to be expected. With regard to an upcoming shortage of gypsum, several approaches are being tested to recover gypsum from construction and demolition waste. Gypsum plasterboard recycling is already implemented on an industrial scale. Furthermore, new processes to recycle different types of gypsum products from construction and demolition waste are being examined. Of particular interest are different types of gypsum boards because they are well suited for selective dismantling. Therefore, they can be recovered comparatively free of impurities which is most important for the gypsum recycling.
In the research project “GipsRec 2.0”, funded by the Federal Ministry of Education and Research, recycling methods for gypsum fiberboards are being investigated. Additionally, the suitability of different types of synthetic gypsum as substitutes for FGD gypsum is being considered. Currently, the quantities of recycled gypsum are not sufficient with regard to the reduction of FGD gypsum. An increase of gypsum recycling should be achieved to narrow the future gypsum gap that will occur in the near future.
Phosphorus (P) fertilizers from secondary resources became increasingly important in the last years. However, these novel P-fertilizers can also contain toxic pollutants. Chromium in its hexavalent state (Cr(VI)) is regulated with low limit values for agricultural products due to its high toxicity, but the determination of Cr(VI) in these novel fertilizer matrices can be hampered by redox processes that lead to false results. Thus, we applied the passive sampler technique Diffusive Gradients in Thin-films (DGT) for the determination of Cr(VI) in fertilizers and compared the results with the standard wet chemical extraction method (German norm DIN EN 15192) and Cr K-edge X-ray absorption near-edge structure (XANES) spectroscopy. We determined an overall good correlation between the wet chemical extraction and the DGT method. DGT was very sensitive and in most cases selective for the analysis of Cr(VI) in P-fertilizers. However, hardly soluble Cr(VI) compounds cannot be detected with the DGT method since only mobile Cr(VI) is analyzed. Furthermore, Cr K-edge XANES spectroscopy showed that the DGT binding layer also adsorbs small amounts of mobile Cr(III) compounds which leads to overestimated Cr(VI) values. The results of certain types of P-fertilizers containing mobile Cr(III) or partly immobile Cr(VI), showed that optimization of the DGT method is required to avoid over- or underestimation of Cr(VI).
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
The steel industry is an important engine for sustainable growth, added value, and high-quality employment within the European Union. It is committed to reducing its CO2 emissions due to production by up to 50% by 2030 compared to 1990′s level by developing and upscaling the technologies required to contribute to European initiatives, such as the Circular Economy Action Plan (CEAP) and the European Green Deal (EGD). The Clean Steel Partnership (CSP, a public–private partnership), which is led by the European Steel Association (EUROFER) and the European Steel Technology Platform (ESTEP), defined technological CO2 mitigation pathways comprising carbon direct avoidance (CDA), smart carbon usage SCU), and a circular economy (CE). CE ap-proaches ensure competitiveness through increased resource efficiency and sustainability and consist of different issues, such as the valorization of steelmaking residues (dusts, slags, sludge) for internal recycling in the steelmaking process, enhanced steel recycling (scrap use), the use of secondary carbon carriers from non-steel sectors as a reducing agent and energy source in the steelmaking process chain, and CE business models (supply chain analyses). The current paper gives an overview of different technological CE approaches as obtained in a dedicated workshop called “Resi4Future—Residue valorization in iron and steel industry: sustainable solutions for a cleaner and more competitive future Europe” that was organized by ESTEP to focus on future challenges toward the final goal of industrial deployment.
Phosphorus rich sewage sludge ash is a promising source to produce phosphorus recycling fertilizer. However, the low plant availability of phosphorus in these ashes makes a treatment necessary. A thermochemical treatment (800–1000 °C) with alkali additives transforms poorly plant available phosphorus phases to highly plant available calcium alkali Phosphates (Ca,Mg)(Na,K)PO4. In this study, we investigate the use of K2SO4 as additive to produce a phosphorus potassium fertilizer in laboratory-scale experiments (crucible). Pure K2SO4 is not suitable as high reaction temperatures are required due to the high melting point of K2SO4.
To overcome this barrier, we carried out series of experiments with mixtures of K2SO4 and Na2SO4 resulting in a lower economically feasible reaction temperature (900–1000 °C). In this way, the produced phosphorus potassium fertilizers (8.4 wt.% K, 7.6 wt.% P) was highly plant available for phosphorus indicated by complete extractable phosphorus in neutral ammonium citrate solution. The added potassium is, in contrast to sodium, preferably incorporated into silicates instead of phosphorus phases. Thus, the highly extractable phase (Ca,Mg)(Na,K)PO4 in the thermochemical products contain less potassium than expected. This preferred incorporation is confirmed by a pilot-scale trial (rotary kiln) and thermodynamic calculation.
Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions.
Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented.
Ab 2029 gilt für alle Kläranlagen in Deutschland eine Pflicht zur Rückgewinnung von Phosphor (P) aus Klärschlamm. Ausgenommen sind nur Anlagen mit Schlämmen mit weniger als 20 g P/kg bezogen auf die Trockenmasse (TM). Für eine Überprüfung der Phosphorschwankungen im Klärschlamm wurden neun verschiedene Kläranlagen ausgewählt mit Phosphorgehalten nahe der "Rückgewinnungsgrenze" von 20 g/kg TM. Der entwässerte Klärschlamm dieser Anlagen wurde monatlich beprobt und auf seinen Phosphorgehalt geprüft. Die Phosphorschwankungen betrugen je nach Anlage zwischen 4 % und 13 % (relative Standardabweichung), im Mittel rund 7 %.
During iron and steel production, several by-products such as slags, dusts and sludges are generated in addition to pig iron and steel as primary products. While established recycling routes exist for slags, there are still considerable recycling problems for other residual materials, especially for filter dusts and sludges containing zinc and lead from waste gas purification. However, the high heavy metal contents make landfilling these dusts and sludges cost-intensive and ecologically problematic. In addition, the relatively high zinc and iron loads represent a valuable material potential, which can make reprocessing of the material with recovery of the zinc and iron loads as secondary raw materials ecologically as well as economically attractive. Against this background, a process is being developed in a cooperative project between Ferro Duo GmbH and the Federal Institute for Materials Research and Testing (BAM), in which the heavy metals (zinc, lead, cadmium, etc.) contained in the filter dusts and sludges are selectively converted into chlorides in a thermochemical process after the addition of a chlorine donor and evaporated at temperatures between 650 and 1100 °C. This process can be used to recover zinc and iron as secondary raw materials.
Experiments to date in a batch reactor show that >99% of the zinc and lead can be removed from the treated material. However, a continuous process is necessary for an economical process, which is why this process is transferred to a rotary kiln and relevant process parameters are identified and optimized. The results of these investigations will be presented here.
Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost.
Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced.
This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained.