4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung
Filtern
Erscheinungsjahr
- 2021 (27) (entfernen)
Dokumenttyp
- Vortrag (15)
- Zeitschriftenartikel (10)
- Beitrag zu einem Tagungsband (2)
Schlagworte
- Klärschlammverordnung (6)
- Phosphor (5)
- Phosphorrückgewinnung (5)
- BOFS (4)
- Phosphorus (4)
- Hydraulic reactivity (3)
- Klärschlamm (3)
- Recycling (3)
- Abwasserbehandlung (2)
- Analytik (2)
- Calcium silicate (2)
- Carbon Fibers (2)
- Electric Arc Furnace (2)
- Fertilizer (2)
- Phosphorus recovery (2)
- Portland Cement (2)
- Pyrometallurgy (2)
- Ringversuch (2)
- Sewage sludge (2)
- Steelmaking (2)
- X-ray diffraction (2)
- Aerodynamic levitation (1)
- Ammonium (1)
- Ashdec (1)
- Bauxite Residue (1)
- Blast-furnace sludge (1)
- CFRP (1)
- Calcium alkali phosphate (1)
- Chromium (1)
- Circular economy (1)
- Clean steel (1)
- Crystalline phase identification (1)
- Diffusive gradients in thin-films (DGT) (1)
- Elektroofenstaub (1)
- Environmental evaluation (1)
- Gichtgasschlamm (1)
- Gipsabfälle (1)
- Gipsrecycling (1)
- Gypsum plasterboards (1)
- Gypsum waste (1)
- Heavy metal removal (1)
- Hydration products (1)
- In situ synchrotron x-ray diffraction (1)
- Landwirtschaftliche Klärschlammverwertung (1)
- Nachhaltigkeit (1)
- Nitrate (1)
- Oxide melts (1)
- Phase formation (1)
- Phosphorbestimmung (1)
- Phosphorus availability (1)
- Process upscaling (1)
- Raman spectroscopy (1)
- Recovery (1)
- Recycled gypsum (1)
- Recycling fertiliser (1)
- Recycling fertilizer (1)
- Red Mud (1)
- Ressourcenrückgewinnung (1)
- Rhenanite (1)
- Sc recovery (1)
- Scandium (1)
- Secondary Recources (1)
- Selective chlorination (1)
- Silicate (1)
- Steelmaking residues (1)
- Thermal analysis (1)
- X-ray absorption near-edge structure (XANES) spectroscopy (1)
- XANES (1)
- XANES spectroscopy (1)
- Zinc chloride (1)
- Zink (1)
- microspectroscopy (1)
- soil (1)
- x-ray diffraction (1)
Organisationseinheit der BAM
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (27) (entfernen)
Eingeladener Vortrag
- nein (15)
Phosphorus (P) fertilizers from secondary resources became increasingly important in the last years. However, these novel P-fertilizers can also contain toxic pollutants. Chromium in its hexavalent state (Cr(VI)) is regulated with low limit values for agricultural products due to its high toxicity, but the determination of Cr(VI) in these novel fertilizer matrices can be hampered by redox processes that lead to false results. Thus, we applied the passive sampler technique Diffusive Gradients in Thin-films (DGT) for the determination of Cr(VI) in fertilizers and compared the results with the standard wet chemical extraction method (German norm DIN EN 15192) and Cr K-edge X-ray absorption near-edge structure (XANES) spectroscopy. We determined an overall good correlation between the wet chemical extraction and the DGT method. DGT was very sensitive and in most cases selective for the analysis of Cr(VI) in P-fertilizers. However, hardly soluble Cr(VI) compounds cannot be detected with the DGT method since only mobile Cr(VI) is analyzed. Furthermore, Cr K-edge XANES spectroscopy showed that the DGT binding layer also adsorbs small amounts of mobile Cr(III) compounds which leads to overestimated Cr(VI) values. The results of certain types of P-fertilizers containing mobile Cr(III) or partly immobile Cr(VI), showed that optimization of the DGT method is required to avoid over- or underestimation of Cr(VI).
The steel industry is an important engine for sustainable growth, added value, and high-quality employment within the European Union. It is committed to reducing its CO2 emissions due to production by up to 50% by 2030 compared to 1990′s level by developing and upscaling the technologies required to contribute to European initiatives, such as the Circular Economy Action Plan (CEAP) and the European Green Deal (EGD). The Clean Steel Partnership (CSP, a public–private partnership), which is led by the European Steel Association (EUROFER) and the European Steel Technology Platform (ESTEP), defined technological CO2 mitigation pathways comprising carbon direct avoidance (CDA), smart carbon usage SCU), and a circular economy (CE). CE ap-proaches ensure competitiveness through increased resource efficiency and sustainability and consist of different issues, such as the valorization of steelmaking residues (dusts, slags, sludge) for internal recycling in the steelmaking process, enhanced steel recycling (scrap use), the use of secondary carbon carriers from non-steel sectors as a reducing agent and energy source in the steelmaking process chain, and CE business models (supply chain analyses). The current paper gives an overview of different technological CE approaches as obtained in a dedicated workshop called “Resi4Future—Residue valorization in iron and steel industry: sustainable solutions for a cleaner and more competitive future Europe” that was organized by ESTEP to focus on future challenges toward the final goal of industrial deployment.
CF Pyro: Stofflich-energetische Verwertung von carbonfaserhaltigen Abfällen in der Pyrometallurgie
(2021)
Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions.
Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented.
Recycled fertilizers produced using processes for the recovery of phosphate from residual materials such as wastewater, sewage sludge and sewage sludge ashes show very good bioavailability, but it is still a product largely unknown to the market. The aim of CLOOP is therefore to document the properties and effects of such fertilizers through chemical, mineralogical and ecological analyses as well as analytical method development and pot and field plant growth trials.
Outotec focused on 3 points in CLOOP: Experimental campaigns, process simulations as well as economic analyses with focus on the AshDec process, respectively the design of a large-scale AshDec plant for phosphorus recovery. The laboratory scale trials as well as the semi-industrial scale campaign provided valuable insights into the operating parameters of the process and the plant. As a result, for example, the temperature range could be significantly lowered, and the additive addition reduced by approx. 20 %. They have further shown that the AshDec process is not susceptible to operating fluctuations and that the product can be consistently produced at high quality. With the selection of suitable operating parameters, heavy metals (As, Pb, Cd, (Zn)) can be removed. Within the campaign, about 1.5 t of fertilizer for the plant trials in CLOOP could be produced. An AshDec plant process was digitally created in simulation software, allowing valuable process parameters to be simulated at various operating parameters. On this basis, a full-scale plant was designed. The data obtained in the project were used for a detailed economic analysis including a sensitivity analysis. It was possible to show under which conditions this plant can be operated economically.
At BAM, the AshDec fertilizer was synthesized with different additives and then applied to plant experiments at Uni Bonn. The goal hereby was to check differences in plant uptake. Because of the promising results of AshDec synthesized with sodium-carbonate and because this AshDec version does not require special off gas treatment for sulfur recovery (compared to AshDec synthesized with sodium-sulfate), all project partners agreed on continuing working with this AshDec variation. It was then used as a raw P-source for formulating it into NPK-fertilizers, by granulation with ammonium-sulfate and straw ash as potassium source. These recycling fertilizers were applied to plant- and field experiments by project partners in Brazil (University of Sao Paulo) and Australia (University of Queensland). Furthermore, in leaching experiments, the solubility of phosphorus in AshDec was compared to triple super phosphate. The experiments were carried out on soils with a varying phosphorus buffering index. Results show, that the phosphorus form in AshDec is way less soluble in water. This indicates that AshDec has the potential for a so-called next generation fertilizer – a fertilizer which’s nutrients remain in the soil and supply the plant according to its needs. At the moment, this behavior gets examined more in depth in lysimeter experiments in cooperation with University of Technology Berlin.
The focus of KWB is the Life Cycle Assessment (LCA) of different NextGen fertilizers to evaluate the entire process chain from recovery to fertilizer application. The NextGen fertilizer is credited by the amount of plant available nutrients in the product, which replace nutrients from conventional fertilizer. The LCA covers N-struvite precipitation from municipal wastewater, K-struvite precipitation from industrial wastewater and the AshDec-product from sewage sludge. The LCA task is almost complete. It could be shown that struvite precipitation has comprehensive environmental benefits, mainly since positive side effects occur in sewage sludge treatment (e.g. reduced sludge volume). In principle, the energetic and ecological profile of the AshDec process compared to direct use of sewage sludge ash cannot be assessed as being generally beneficial or negative. Regarding the global warming potential, the Ashdec process shows that the expenses (e.g. energy, chemicals) cannot be covered by the P fertilizer credit. In contrast, the impact categories “terrestrial acidification potential”, and “freshwater eutrophication potential” show positive results as the credits for conventional fertilizer are higher than the burdens for the process.
At University Bonn, the standardized pot experiments were conducted with several AshDec variations, using ryegrass, soybean, and spinach on a slightly acidic sandy soil and an organic-free standard substrate. P-uptake and biomass production of different AshDec variations were generally like those of triple super phosphate and struvite, and clearly outperformed untreated sewage sludge ash and rock phosphate. Field trials in Australia and Brazil with sugarcane on acidic soils are still ongoing and results are expected by the end of 2021.
Gypsum is widely used in the construction sector and its worldwide consumption has been increasing for several decades. Depending on the life-time of the used gypsum products, an increase of gypsum in construction and demolition waste follows. Especially against the background of a circular economy, the recycling of waste gypsum is of growing importance. However, the use of recycled gypsum makes only sense if it is environmentally friendly. Therefore, an evaluation of the environmental impacts of an industrial-scale processing for the recycling of post-consumer gypsum waste was conducted. The evaluation was performed with an established life cycle assessment software. Original data provided by industry and complementary data from a database for life cycle assessments were used for the calculations. Two scenarios for recycled gypsum with different transportation distances were calculated. These results are compared with results of the environmental evaluation of gypsum derived from coal-fired power plants (FGD gypsum) and natural gypsum. The results show that utilization of recycled gypsum can be environmentally advantageous compared to the use of natural gypsum or FGD gypsum, especially in the impact categories land transformation and resource consumption (abiotic depletion potential). For most environmental impact categories the specific transportation distances have a strong influence.
Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance.
In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts.
The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production.
Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker.
The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6).
The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions.
Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented.
Phase formation and evolution was investigated in the CaO–SiO2 system in the range of 70–80 mol% CaO. The samples were container-less processed in an aerodynamic levitation system and crystallization was followed in situ by synchrotron x-ray diffraction at the beamline P21.1 at the German electron synchrotron (DESY). Modification changes of di- and tricalcium silicate were observed and occurred at lower temperatures than under equilibrium conditions. Despite deep sample undercooling, no metastable phase formation was observed within the measurement timescale of 1 s. For the given cooling rates ranging from 300 K s−1 to about 1 K s−1, no decomposition of tricalcium silicate was observed. No differences in phase evolution were observed between reducing and oxidizing conditions imposed by the levitation gas (Ar and Ar + O2). We demonstrate that this setup has great potential to follow crystallization in refractory oxide liquids in situ. For sub-second primary phase formation faster detection and for polymorph detection adjustments in resolution have to be implemented.