Lightweighting as a cross-cutting technology contributes significantly to achieve the European Green Deal goals. Based on, but not limited to, advanced materials and production technologies, the demand for natural resources and CO2 emmissions are reduced by lightweighting during production, as well as use phase. Therefore, lightweighting is a crucial transformation technology assisting in decoupling economic growth from resource consumption. In this manner, lightweighting contributes significantly as a key technology of relevance for many industrial sectors such as energy, mobility, and infrastructure, towards resource efficiency, climate action and economic strength, as well as a resilient Europe. To strengthen international partnerships, addressing global issues of today at the edge of science with high performance lightweight material based on carbon fibers, an overview about the BAM expertise in carbon fiber reinforced materials is given.
Advanced light weight applications like aircrafts and wind turbine blades are made of fibre reinforced plastics (FRP) with continuous fibre reinforcement and must withstand a high thermo-mechanical cyclic loading. The quality of the fibre matrix interface has a high impact on the fatigue life and was continuously improved over the years since the 50th. The fatigue life of glass fibre reinforced plastics (GFRP) used in aircraft industry is 10 to 100 times higher compared to glass fibre non crimp fabrics used for wind turbine blades.
To assure a constant and reliable high quality and strength of reinforcement fibres, synthetic fibre production is state of the art (CF, GF). There is a need for recycling GFRP and CFRP waste due to the upcoming use. Pyrolysis and solvolysis are more expensive than the mechanical route however enable a more sustainable recycling. Natural fibres and recycled synthetic fibres have a high scatter in quality and strength. Hence it is a challenge to optimize the production / recycling processes to get a reliable quality for any demanding (second life) application.
Chemical routes for using renewables resources and recycling, is going to be a good approach especially for polymer-matrix systems to get 100% quality (back) compared to the state of the art.
Finally, a proper design, life-time extension and repair is preferable to recycling to keep the carbon footprint as low as possible.
Gegenstand dieser Arbeit ist die Untersuchung eines bestehenden pyrometallurgischen Prozesses zur Rückgewinnung von Tantal und Niob aus metallurgischen Reststoffen mit vorwiegend niedriger Wertstoffkonzentration.
Zur näheren Erforschung der im vorliegenden Stoffsystem ablaufenden Reduktionsprozesse wurden in einem Elektrolichtbogenofen Schmelzversuche im Pilotmaßstab durchgeführt. Als Reduktionsmittel diente Koks, welcher mithilfe einer Argon-gespülten Eisenlanze in die flüssige mineralische Schmelze eingebracht wurde. Während der Reduktionsbehandlung werden Refraktärmetalle wie Tantal und Niob in ihre Carbide überführt und anschließend in der erschmolzenen eisenbasierten Metallphase am Boden des Reaktors angereichert. Neben Tantal und Niob gelangt auch ein Teil des im Einsatzmaterial enthaltenen Titans als unerwünschtes Begleitelement in die Metallphase.
Sein Großteil verbleibt jedoch als Oxid in der Schlacke und wird dort hauptsächlich im Mineral Perowskit (CaTiO3) gebunden. Die erstarrten Schlackeproben wurden mit verschiedenen Methoden wie Röntgenfluoreszensanalyse, Röntgenbeugung und Rasterelektronenmikroskopie mit gekoppelter energiedispersiver Röntgenanalyse untersucht, um die Bildung tantalhaltiger Mineralphasen zu verschiedenen Stadien des Reduktionsprozesses zu verfolgen.
Die hier gewonnenen Erkenntnisse zeigen, dass weniger die durch das Einblasen von Koks verursachte Reduktionsreaktion, sondern das Absinken der tantalreichen Eisentröpfchen in der flüssigen mineralischen Schmelze, gefolgt von ihrer Anreicherung in die Metallphase, für die Kinetik ausschlaggebend ist.
Da das Recycling von tantalhaltigen Post-Consumer-Abfällen praktisch nicht existiert, stellen metallurgische Reststoffe eine äußerst wichtige Rohstoffquelle für das Tantalrecycling dar. Die meisten Zinnerze enthalten von Natur aus erhebliche Mengen an Refraktärmetallen. Diese Elemente werden in den Schlacken der pyrometallurgischen Primärzinngewinnung angereichert. Aufgrund ihrer vergleichsweise hohen Wertstoffkonzentration und ihrer Funktion als zusätzlicher Schlackenbildner stellen diese Schlacken einen wertvollen Rohstoff für die Verhüttung tantalhaltiger Reststoffe dar. In der vorliegenden Arbeit wird ein existierendes Verfahren zur Tantalrückgewinnung diskutiert, dem hauptsächlich pyrometallurgische Rückstände geringer Wertstoffkonzentration als Einsatzstoff dienen. Mit Hilfe des Verfahrens sollte dasoxidisch vorliegende Tantal vollständig reduziert und in der Metallphase angereichert werden. Weiterhin sollte vermieden werden, dass unerwünschte Elemente wie Titan in die Metallphase überführt werden. Ziel der Untersuchung war es, die ablaufenden Reduktionsprozesse besser zu verstehen, um so Ansätze für die Prozessoptimierung identifizieren zu können.
Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment.
In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided.
Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases.
Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment.
In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided.
Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases.
Optimierung eines pyrometallurgischen Tantal- und Niob- Recyclingprozesses mithilfe von On-Line LIBS
(2018)
Die Entwicklung von Hochleistungselektronik zu immer kleineren Bauformen ohne Leistungseinbußen ist ohne den Einsatz von Technologiemetallen wie Niob und Tantal heute praktisch nicht mehr realisierbar. Besonders in technischen Geräten wie Smartphones und Tablets sind Tantal- und Niobkondensatoren aufgrund ihrer hohen Leistungsdichten bereits unverzichtbar geworden. Für die nachhaltige Produktion von Elektronik stellt jedoch vor allem das Tantalerz Coltan als sogenanntes „conflict mineral” ein großes Problem dar.
Um den Wirtschaftsstandort Europa unabhängiger von Primärrohstoffimporten aus Krisenregionen zu machen, ist die Entwicklung von effizienten Recyclingverfahren heute wichtiger denn je. An der Bundesanstalt für Materialforschung und -prüfung (BAM) findet daher zurzeit die Optimierung eines pyrometallurgischen Industrieprozesses zur Niob- und Tantalrückgewinnung statt, welchem hauptsächlich niedrigkonzentrierte metallurgische Rückstände aus der Tantal- und Niob- bzw. der Zinngewinnung als Einsatzstoffe dienen.
Zu diesem Zweck werden im kleintechnischen Lichtbogenofen der BAM (480 kVA, max. Materialdurchsatz ca. 150 kg/h) Versuche mit einem neuen innovativen Messgerät durchgeführt, welches eine On-Line Analyse von Hochtemperaturprozessen ermöglicht. Der eingesetzte Prototyp nutzt das Verfahren der laserinduzierten Plasmaspektroskopie (LIBS), um die chemische Zusammensetzung der Schlackephase noch im Schmelzbad und während eines Schlackeabgusses zu bestimmen. Nach einer Kalibrierung auf das vorliegende Stoffsystem ermöglicht dieser On-Line-LIBS Prototyp der BAM daher eine in-situ Bestimmung der Elementverteilung in der Schmelze. Die hier gewonnenen Daten sollen helfen, die aktuelle Prozessführung zu verbessern und die Tantal- und Niobausbeute noch weiter zu erhöhen.
Calcium sulfate hemihydrate (CaSO4ᐧ0.5H2O), also known as bassanite, has been used as a precursor to produce gypsum (dihydrate, CaSO4ᐧ2H2O) for various construction and decorative purposes since prehistoric times. The main route to obtain hemihydrate is a thermal treatment of gypsum at temperatures typically between 150 °C and 200 °C to remove some of the structural water.
In this contribution, we introduce (Fig. 1) a more efficient and sustainable method (T < 100 °C) that enables the direct, rapid, and reversibly conversion of gypsum to bassanite using reusable high salinity aqueous solutions (brines with c[NaCl] > 4 M). The optimum conditions for the efficientproduction of bassanite in a short time (< 5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the typical behaviour of the bassanite phase in low salt environments.
Traditionally, hemihydrate is obtained through a solid state thermal treatment because bassanite is considered to be metastable with respect to gypsum and anhydrite in aqueous solutions, and therefore gypsum-to-bassanite conversion should not occur in water. Its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures is inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline structure for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.
The challenge of the project ASHES is focused on the recycling of nutrients from residues of thermochemical processing of by-products of sugar cane industry (bagasse/straw) in Brazil to increase the energy efficiency of thermal conversion and to enable the recycling of process ashes as fertilisers. Dry lignocellulosic biomass (straw, bagasse) are combusted, gasified and subsequently combined with post-thermochemical treatment in the AshDec process to increase the plant availability of phosphorus. Different fertilizer formulations are granulated/pelletized and tested regarding their storage/handling characteristics.
Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions.
Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented.