4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung
Filtern
Dokumenttyp
- Vortrag (40) (entfernen)
Sprache
- Englisch (40) (entfernen)
Referierte Publikation
- nein (40)
Schlagworte
- Recycling (9)
- Phosphorus recovery (7)
- BOFS (5)
- Hydraulic reactivity (5)
- Carbon Fibers (3)
- Environmental evaluation (3)
- Fertilizer (3)
- Gypsum (3)
- Phosphorus (3)
- Portland Cement (3)
Organisationseinheit der BAM
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (40) (entfernen)
Eingeladener Vortrag
- nein (40)
Tantalum and niobium are essential for the development of electronics towards a more and more compact design, but without reducing their performance today. Especially in smart phones and tablets, tantalum and niobium capacitors with high charge densities have already become almost indispensable. However, tantalum as a critical raw material is still a problem for the sustainable production of electronics. Due to this fact, the existence of efficient recycling processes especially in Europe is becoming even more important nowadays.
The Bundesanstalt für Materialforschung und -prüfung (BAM) is currently working on the optimisation of an existing pyrometallurgical tantalum recycling process. Optimisation of this industrial process is carried out in a small-scale electric arc furnace (480 kVA, capacity approx. 150 kg/h) at BAM using a new and innovative equipment for on-line analysis of high temperature processes.
The aim of this project is to identify the best timing for an optimum slag tapping, when the slag is lower than minimum targeted tantalum concentration. Hence, LIBS (Laser induced breakdown spectroscopy) is used to identify the chemical composition of the slag layer and during slag tapping. The on-line-LIBS prototype of BAM enables an in-situ measurement of the element distribution in the melt after calibration on the slag system.
First results of this joint research project will be presented including on-line-LIBS-measurements and thermodynamic and kinetic aspects of the process.
An existing pyrometallurgical process for tantalum and niobium recovery, mainly from low grade pyrometallurgical residues, was investigated. Series of melting experiments were carried out in a pilot-scale electric arc furnace to study how the amount, the grain size and the way of feeding affect the activity of carbon as a reducing agent. During the pyrometallurgical treatment refractory metals such as tantalum and niobium are reduced to their carbide form and enriched in the molten iron-based metal phase. The cooled down slag and metal phase were analysed to investigate thermodynamic and kinetic conditions of the carbide formation. FACT Sage simulations were also used to investigate the material system in state of thermodynamic equilibrium. Results show that mass transfer and kinetics may play an important role if compared to equilibrium analyses using FACT Sage.
Calcium sulfate hemihydrate (CaSO4ᐧ0.5H2O), also known as bassanite, has been used as a precursor to produce gypsum (dihydrate, CaSO4ᐧ2H2O) for various construction and decorative purposes since prehistoric times. The main route to obtain hemihydrate is a thermal treatment of gypsum at temperatures typically between 150 °C and 200 °C to remove some of the structural water.
In this contribution, we introduce (Fig. 1) a more efficient and sustainable method (T < 100 °C) that enables the direct, rapid, and reversibly conversion of gypsum to bassanite using reusable high salinity aqueous solutions (brines with c[NaCl] > 4 M). The optimum conditions for the efficientproduction of bassanite in a short time (< 5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the typical behaviour of the bassanite phase in low salt environments.
Traditionally, hemihydrate is obtained through a solid state thermal treatment because bassanite is considered to be metastable with respect to gypsum and anhydrite in aqueous solutions, and therefore gypsum-to-bassanite conversion should not occur in water. Its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures is inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline structure for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.
The challenge of the project ASHES is focused on the recycling of nutrients from residues of thermochemical processing of by-products of sugar cane industry (bagasse/straw) in Brazil to increase the energy efficiency of thermal conversion and to enable the recycling of process ashes as fertilisers. Dry lignocellulosic biomass (straw, bagasse) are combusted, gasified and subsequently combined with post-thermochemical treatment in the AshDec process to increase the plant availability of phosphorus. Different fertilizer formulations are granulated/pelletized and tested regarding their storage/handling characteristics.
Hydrogen plasma treatment of iron ores or iron oxide containing wastes can be an efficient option to produce green iron e.g. for steel production. This way iron oxide is reduced to metallic iron in the liquid form by the highly reactive species that are formed in a hydrogen plasma. Hydrogen plasma can be used at the same time to remove undesired gangue elements. The presentation shows the experimental setup, shows first results of iron ore reduction by hydrogen plasma and gives an outlook for industrial application of the technology.
For the European sewage sludge ash monitoring ash samples from sewage sludge incineration plants were requested from all over Europe. First results of the received samples regarding main and trace element contents were presented at ESPC4. Moreover, a list of all known European facilities for sewage sludge monoincineration was presented.
New developments in legislation and technology development for P-recovery were presented with focus on the situation in Germany.
Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone.
In recent decades, many researchers have investigated a thermochemical process to reduce iron oxides to metallic iron in molten BOFS. The metallic iron formed separates from the reduced slag due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced slag is adapted to that of the Portland cement clinker and the hydraulic reactive mineral alite is formed.
In this study, BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent, and the hydraulic properties of the reduced, low-iron BOFS were investigated. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, the addition of gypsum, as is also done in cement production from Portland cement clinker, has been found to accelerate the hydration rate of reduced BOFS.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, the production of a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry.
Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost.
Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced.
This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained.
Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance.
In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts.
The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production.