Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
LD-Schlacken weisen eine große chemische Ähnlichkeit zu Protlandzementklinker auf. Sie enthalten jedoch noch bis zu 30% Eisen, das mineralisch in oxidischer Form gebunden vorliegt. Dadurch kann sich bei der Erstarrung die wichtigste Klinkerphase "Alit" nicht ausbilden.
Durch eine reduzierende Schmelzbehandlung der Schlacke kann des mineralisch gebundene Eisen als Metall separiert werden. Dadurch wird auch die Mineralogie der Schlacke so verändert, dass auch sie nun praktisch einem Portlandzementklinker entspricht.
Entsprechende Versuche wurden am kleintechnischen Lichtbogenofen der BAM durchgeführt. Es werden Ergebnisse vorgestellt und auf Grenzen und Möglichkeiten eines derartigen Prozesses im Hinblick auf eine industrielle Umsetzung eingegangen.
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
LD-Schlacken weisen eine große chemische Ähnlichkeit zu Protlandzementklinker auf. Sie enthalten jedoch noch bis zu 30% Eisen, das mineralisch in oxidischer Form gebunden vorliegt. Dadurch kann sich bei der Erstarrung die wichtigste Klinkerphase "Alit" nicht ausbilden.
Durch eine reduzierende Schmelzbehandlung der Schlacke kann des mineralisch gebundene Eisen als Metall separiert werden. Dadurch wird auch die Mineralogie der Schlacke so verändert, dass auch sie nun praktisch einem Portlandzementklinker entspricht.
Entsprechende Versuche wurden am kleintechnischen Lichtbogenofen der BAM durchgeführt. Es werden Ergebnisse vorgestellt und auf Grenzen und Möglichkeiten eines derartigen Prozesses im Hinblick auf eine industrielle Umsetzung eingegangen.
Die Zementindustrie erzeugt etwa 6-7% der globalen CO2-Emissionen und steht damit als Industriezweig vor dem Hintergrund einer anvisierten Klimaneutralität vor gewaltigen Herausforderungen. Der Prozess der Klinkerherstellung wurde über die vergangenen Jahrzehnte bereits kontinuierlich optimiert. Seit 1990 ist es der deutschen Zementindustrie gelungen, die spezifischen CO2-Emissionen der Zementproduktion u. a. durch den Einsatz alternativer, nicht fossiler Brennstoffe und durch Absenkung des Klinkergehalts im Zement um 20 % zu senken. Weitere konventionelle Minderungsstrategien versprechen jedoch nur noch wenig zusätzliche Reduktion. Im Falle des Portlandklinkers besteht die Schwierigkeit darin, dass zwei Drittel der CO2-Emissionen rohstoffbedingt durch die Entsäuerung des Kalksteins (CaCO3) anfallen, die durch die beschriebenen Maßnahmen nicht weiter abgesenkt werden können. Vielmehr wird es erforderlich sein, noch zu entwickelnde oder zu optimierende Technologien anzuwenden und ggf. alle relevanten Ebenen wie Produktion, Weiterverarbeitung und Anwendung von Zement und Beton neu zu denken. Neben technologischen Ansätzen zur CO2-Abscheidung mit nachfolgender langfristiger Speicherung (Carbon Capture and Storage – CCS) oder Verwertung (Carbon Capture and Utilisation – CCU) werden auch alternative Rohstoffe für die Zementproduktion und alternative Bindemittel in Betracht zu ziehen sein.