4 Material und Umwelt
Filtern
Erscheinungsjahr
- 2022 (49) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (49)
Referierte Publikation
- ja (49) (entfernen)
Schlagworte
- Leaching (4)
- Biocides (3)
- Polyethylene (3)
- Sewage sludge (3)
- Struvite (3)
- Wastewater (3)
- Construction products (2)
- Fungi (2)
- Microbiota (2)
- Osmoadaptation (2)
Organisationseinheit der BAM
- 4 Material und Umwelt (49) (entfernen)
Paper des Monats
- ja (5)
Cellulose ethers, like methyl cellulose (MC) or hydroxypropyl cellulose (HPC), are widely used in conservation. They also occur as additives and rheology modifiers in various products like dispersions or gels. Do such products release harmful volatile organic compounds (VOC) during their accelerated aging? A mass testing series utilizing the Oddy test of 60 commercial cellulose ethers ranks the products in safe for permanent use (P, no corrosion), only for temporary use (T, slight corrosion), and unsuitable at all (F, heavy corrosion). Results show that 55% of the products passed the test whereas 33% are for temporary use as slight corrosion occurred on at least one metal coupon and only 11% failed the Oddy test. Raman measurements of the corrosion products identified oxides like massicot, litharge, cuprite, and tenorite among carbonates (hydrocerussite, plumbonacrite), and acetates like basic lead acetate, lead acetate trihydrate as well as lead formate as main phases. For example, commercial, industrial Klucel® G (HPC) scored a T rating through slight corrosion on the lead coupon. Basic lead acetate among other phases indicates the presence of acetic acid. Additional measurements of the sample with thermal desorption GC–MS utilizing the BEMMA scheme confirm the high acetic acid outgassing and reveal the presence of a small amount of formaldehyde.
The diversity of fused filament fabrication (FFF) filaments continues to grow rapidly as the popularity of FFF-3D desktop printers for the use as home fabrication devices has been greatly increased in the past decade. Potential harmful emissions and associated health risks when operating indoors have induced many emission studies. However, the lack of standardization of measurements impeded an objectifiable comparison of research findings. Therefore, we designed a chamber-based standard method, i.e., the strand printing method (SPM), which provides a standardized printing procedure and quantifies systematically the particle emission released from individual FFF-3D filaments under controlled conditions. Forty-four marketable filament products were tested. The total number of emitted particles (TP) varied by approximately four orders of magnitude (1E9 ≤ TP ≤ 1E13), indicating that origin of polymers, manufacturer-specific additives, and undeclared impurities have a strong influence. Our results suggest that TP characterizes an individual filament product and particle emissions cannot be categorized by the polymer type (e.g., PLA or ABS) alone. The user's choice of a filament product is therefore decisive for the exposure to released particles during operation. Thus, choosing a filament product awarded for low emissions seems to be an easily achievable preemptive measure to prevent health hazards.
The development of traceable new methodologies to quantify elemental air pollutants in particulate matter (PM) supports modernization of methods used in air quality monitoring networks in Europe. In the framework of the EURAMET EMPIR AEROMET II project, the combination of cascade impactor aerosol sampling and total reflection X-ray fluorescence elemental spectroscopy (TXRF) was investigated. This technique requires a traceable calibration based on reference samples. This paper describes a new, simple and effective method to produce such reference samples using flexible, reusable, and low-cost parylene C shadow masks, fabricated by photolithographic steps. These shadow masks can be used to produce reference samples that mimic the Dekati cascade impactor’s deposition patterns by applying as-prepared micro stencils to 30 mm acrylic substrates and evaporating a reference material (Ti) in arrangements of thin circular dots. The highly flexible direct patterning of acrylic discs with reference material, otherwise impossible with conventional photolithography, allows multiple reusing of the same micro stencils. The aspect ratios of the dots could be repeated with an error less than 4 %. A first set of standard reference samples for the 13 stages of the Dekati cascade impactor was produced and preliminary TXRF measurements of the deposited Ti masses were performed. The centricity of the deposition patterns turned out to be an important parameter for the quality of the TXRF results. The parylene mask technology for the production of reference samples turns out to be a promising new approach for the traceable calibration of TXRF spectrometers for the quantification of element concentrations in environmental aerosol samples but, due to its great versatility, it could be used for several other micropatterning applications on conventional and unconventional substrates.
The database gives information on the contamination of the shore of the South-Eastern Baltic with the debris of geosynthetic materials for the period 2018–2020. This new type of coastal pollution enters the natural environment due to the destruction of coastal protection structures and construction activities. The database contains sections:
(1) a list of types of geosynthetic material residues, their photographic images and photographs illustrating examples of finds in natural conditions
[1 List_geosynthetic_debris_SEB],
(2) monitoring data on the contamination of the beach strip with the debris of geotextiles, braids from gabions, geocontainers (big bags), geocells and geogrids for the beaches of the South-Eastern Baltic for the period 2018–2020
[2 Monitoring_geosynthetic_debris_SEB];
(3) statistical distributions of the found geosynthetic debris by size
[3 Scales_geosynthetic_debris_SEB] and (4) results of test surveys on the shores of Lithuania and Poland adjacent to Kaliningrad Oblast.
All data refer to the beaches of the Kaliningrad Oblast (Russia), including the Russian parts of the Vistula and Curonian Spits, but also contains information on a one-time assessment of the pollution of the beaches of the adjacent territories: the Polish shore from the Poland-Russia border on the Vistula Spit to the mouth of the Vistula River, the Lithuanian shore from the border Lithuania-Russia on the Curonian Spit to the border of Latvia-Lithuania. Materials were collected during field surveys within the ERANET-RUS_Plus joint project EI-GEO, ID 212 (RFBR 18-55-76002 ERA_a, BMBF 01DJ18005).
This Special Issue, ‘Measurement of the Environmental Impact of Materials’, is focused on the impact that materials have on the environmental compartments of soil, water and air. Leaching and emission processes, including underlying mechanisms, are a recurring topic in most published articles in the present Special Issue. Contributions have come from three continents and numerous countries (USA, Germany, France, Latvia, Poland, Russia, Japan, Korea and Thailand) indicating the global dimension of the subject.
Industrial-scale mechanical recycling of plastics has been established for years, but has technical and economic limits. Chemical recycling processes lead back to monomers or to the raw materials, so that in the end new goods can be produced for all areas of application of plastics. The variety of chemical recycling processes is large. The capacities of the plants are still low today. The profitability of the plants is strongly influenced by the price of oil; the profitability limit is currently between 50 and 60 US $ per barrel.
Phosphorus recycling from sewage sludge will be obligatory in Germany from 2029. Phosphorus content determination in sewage sludge is crucial to assess the prescribed recycling rates. Currently, German law regards sample preparation using aqua regia digestion in a microwave or under reflux conditions as well as instrumental phosphorus determination by ICP-OES, ICP-MS, or photometric determination with ammonium molybdate as equivalent. However, it is questionable whether these methods are indeed equivalent regarding phosphorus quantification in sludges near the limit of 20 g/kg for mandatory recycling. To answer this question, 15 sewage sludges of 11 different wastewater treatment plants were investigated with all permitted method (digestion and measurement) combinations. Moreover, one sewage sludge was also examined in an interlaboratory comparison (ILC) with 28 participants. This study shows that the above-mentioned methods differ in some cases significantly but across all method combinations and sludges, phosphorus recovery was between 80 and 121% after normalization to the grand mean (average of 15 sludges between 85 and 111%). The ILC and the examination of 15 sludges produced largely similar results. There is a tendency to higher phosphorus recovery after microwave digestion compared to reflux digestion and ICP-OES measurements determine higher phosphorus contents than ICP-MS and photometric phosphorus determination. As a result, the authors recommend ICP-OES determination of phosphorus in sewage sludge after microwave digestion.
Improved Durability of Wood Treated with Nano Metal Fluorides against Brown-Rot and White-Rot Fungi
(2022)
Low-water soluble metal fluorides such as magnesium fluoride (MgF2) and calcium Fluoride (CaF2) were evaluated for decay protection of wood. Initially, the biocidal efficacy of nano metal fluorides (NMFs) against wood destroying fungi was assessed with an in-vitro agar test. The results from the test showed that agar medium containing MgF2 and CaF2 was more efficient in preventing fungal decay than stand-alone MgF2 or CaF2. These metal fluorides, in their nanoscopic form synthesized using fluorolytic sol-gel synthesis, were introduced into the sapwood of Scots pine and beech wood and then subjected to accelerated ageing by leaching (EN 84). MAS 19F NMR and X-ray micro CT images showed that metal fluorides were present in treated wood, unleached and leached. Decay resistance of Scots pine and beech wood treated with NMFs was tested against Wood destroying fungi Rhodonia placenta and Trametes versicolor in accordance with EN 113. Results revealed that mass losses were reduced to below 3% in wood treated with the combination of MgF2 and CaF2.
It is concluded that NMFs provide full protection to wood even after it has been leached and can be used as wood preservatives in outdoor environments.
Numerous non-native tree species are given attention with respect to the reforestation of calamity areas in Europe. Among them, several species may form durable wood which can be used for outdoor applications, but differences in wood durability are expected between original and European growth sites. This study aimed at examining the biological durability against wooddestroying fungi and water permeability of German-grown Dawn redwood (Metasequoia glyptostroboides) and Port Orford cedar (Chamaecyparis lawsoniana). The heartwood of both wood species was assigned to durability class 4 (DC 4, less durable) in soil contact and DC 1–4 (very to less durable) against wood-destroying basidiomycetes. However, according to the Meyer-Veltrup model, their material resistance dose was notably higher compared to the reference species Norway spruce (Picea abies), and the resulting service life of above ground structures should be a multiple of the reference.