4 Material und Umwelt
Filtern
Dokumenttyp
- Vortrag (95) (entfernen)
Referierte Publikation
- nein (95)
Schlagworte
- Recycling (19)
- Phosphor (11)
- Phosphorrückgewinnung (11)
- Klärschlamm (10)
- CFK (8)
- Phosphorus recovery (7)
- BOFS (5)
- Gichtgasschlamm (5)
- Hydraulic reactivity (5)
- Klärschlammverordnung (5)
Organisationseinheit der BAM
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (95) (entfernen)
Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone.
In recent decades, many researchers have investigated a thermochemical process to reduce iron oxides to metallic iron in molten BOFS. The metallic iron formed separates from the reduced slag due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced slag is adapted to that of the Portland cement clinker and the hydraulic reactive mineral alite is formed.
In this study, BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent, and the hydraulic properties of the reduced, low-iron BOFS were investigated. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, the addition of gypsum, as is also done in cement production from Portland cement clinker, has been found to accelerate the hydration rate of reduced BOFS.
Further research to improve the hydraulic properties of the reduced slag is essential. If successful, the production of a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry.
Obwohl der Leichtbau mit carbonfaserverstärkten Kunststoffen (CFK) einen wichtigen Beitrag zum Klimaschutz und zur Ressourceneffizienz liefert, stellt der wachsende Abfallstrom von aktuell 62 kt/a eine große Herausforderung dar. Weil die Produktion von Carbonfasern (CF) überwiegend auf fossilen Rohstoffen basiert und sehr energieintensiv ist, werden nachhaltige Recyclinglösungen dringend benötigt. Hier wird ein Überblick über aktuelle Recyclingprozesse gegeben und deren Limitierungen diskutiert. Darüber hinaus wird eine Möglichkeit zur sicheren chemischen Nutzung von CF-haltigen Reststoffen aufgezeigt, die nicht zur Wiederverwertung geeignet sind. Das Projekt CF Pyro untersucht deren Einsatz als Sekundärrohstoff in der Pyrometallurgie und setzt besondere Schwerpunkte bei der Reaktivität von CF, der Prozessstabilität und der Vermeidung von Emissionen gesundheitsschädlicher WHO-Fasern. Abschließend wird eine, auf den experimentellen Ergebnissen und im Dialog mit Expertinnen und Experten aus Wirtschaft, Wissenschaft und Politik entwickelten, Technologiebewertung vorgestellt.
Hydrogen plasma treatment of iron ores or iron oxide containing wastes can be an efficient option to produce green iron e.g. for steel production. This way iron oxide is reduced to metallic iron in the liquid form by the highly reactive species that are formed in a hydrogen plasma. Hydrogen plasma can be used at the same time to remove undesired gangue elements. The presentation shows the experimental setup, shows first results of iron ore reduction by hydrogen plasma and gives an outlook for industrial application of the technology.
Rotschlamm fällt in sehr großen Mengen bei der Herstellung von Aluminiumoxid an und wird fast ausschließlich deponiert. Es wird eine neue Technologie vorgestellt bei der das im Rotschlamm enthaltene Eisenoxid mittels Wasserstoffplasma reduziert wird. Es wird ein Reaktionsmechanismus über Titanomagnetit und Hercynit vorgeschlagen.
Gleichwertigkeit der nach AbfKlärV zulässigen Verfahren zur Phosphorbestimmung in Klärschlamm
(2021)
In dem Meeting wurde den Notifizierern und Ausrichtern des jährlichen länderübergreifenden Ringversuchs Klärschlamm die Ergebnisse zu Untersuchungen hinsichtlich der Gleichwertigkeit verschiedener nach AbfKlärV zulässiger Verfahren zur Phosphorbestimmung in Klärschlamm vorgestellt. Die Untersuchungen an 15 Klärschlammproben ergaben die höchsten Ergebnisse für das Messverfahren ICP-OES und das Aufschlussverfahren in der Mikrowelle. Diese Ergebnisse wurden im Ringversuch bestätigt.
The use of secondary building materials can meet the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the protection of natural ressources as well as the conservation of landfill sites. Regarding the predicted decrease of gypsum supply in Germany, particularly the recycling of gypsum (calcium sulfate) is of growing importance. Currently, the gypsum demand is fulfilled (at least 60%) by gypsum as side product from coal-fired power plants (FGD Gypsum). Germany’s natural gypsum deposits fulfil the remaining gypsum demand. Due to national climate protection goals the gypsum supply from coal power plants will decrease significantly in the future.
In addition, the content of sulfates in other secondary building materials, in particular in recycled concrete aggregates, should be minimized for quality reasons. Separated gypsum can be used in gypsum production if the high quality requirements for recycled gypsum are met. Accordingly, there have been significant advancements in the processing of gypsum residues in the last years. Since almost all processing steps in the recycling process are associated with environmental impacts, an evironmental evaluation of the use of recycled gypsum as a substitute in gypsum production has to be carefully conducted.
The presentation focusses on the techniques for generating recycled gypsum from gypsum plaster boards, the related quality requirements and a comprehensive environmental evaluation of the complete process.
Herstellung neuer Düngemittelausgangsstoffe durch thermochemische Behandlung von Klärschlammaschen
(2018)
Der Fachbereich 4.4 hat zusammen mit der Firma Outotec ein thermochemisches Verfahren im Drehrohrofen entwickelt, um die Phosphorphasen in Klärschlammasche umzuwandeln, damit die behandelten Aschen als Dünger eingesetzt werden können. In dem Vortrag wird das Verfahren erklärt, die Düngewirkung dargestellt und Pilotversuche vorgestellt.
Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment.
In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance.
In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts.
The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production.
An existing pyrometallurgical process for tantalum and niobium recovery, mainly from low grade pyrometallurgical residues, was investigated. Series of melting experiments were carried out in a pilot-scale electric arc furnace to study how the amount, the grain size and the way of feeding affect the activity of carbon as a reducing agent. During the pyrometallurgical treatment refractory metals such as tantalum and niobium are reduced to their carbide form and enriched in the molten iron-based metal phase. The cooled down slag and metal phase were analysed to investigate thermodynamic and kinetic conditions of the carbide formation. FACT Sage simulations were also used to investigate the material system in state of thermodynamic equilibrium. Results show that mass transfer and kinetics may play an important role if compared to equilibrium analyses using FACT Sage.