4 Material und Umwelt
Filtern
Dokumenttyp
- Vortrag (46)
- Posterpräsentation (21)
- Beitrag zu einem Tagungsband (12)
- Sonstiges (4)
- Zeitschriftenartikel (3)
- Buchkapitel (1)
- Forschungsbericht (1)
- Forschungsdatensatz (1)
Sprache
- Englisch (89) (entfernen)
Referierte Publikation
- nein (89) (entfernen)
Schlagworte
- Nano (16)
- OECD (13)
- Nanomaterial (6)
- Cascade impactor (5)
- Prüfrichtlinie (5)
- Test guideline (5)
- VOC (5)
- Volatile organic compounds (5)
- Aerosol (4)
- Analytical method (4)
Organisationseinheit der BAM
- 4.2 Material-Mikrobiom Wechselwirkungen (89) (entfernen)
11 laser printers from 5 manufacturers were purchased in 2017 and tested for their UFP emissions. Size resolved sampling of the emitted particles was done with a 13 stage (30 nm to 10 µm) low pressure cascade impactor. The sampled particles were analysed for their chemical composition by thermal extraction (vaporization at 290°C) followed by GC-MS analysis. High boiling cyclic siloxanes (D10 to D16) were detected as constituents of UFP from laser printers. In comparison to measurements in 2008, aliphatic long-chain alkanes (C22 to C34) were detected additionally as chemical constituents of UFP from most of the tested printers and their amounts were higher than for cyclic siloxanes. Printers of one manufacturer showed very low UPF emissions compared to the other manufacturers.
BAM is currently building up a platform of novel nanoRMs relying on iron oxide nanoparticles of different shape, size and surface chemistry. Iron oxide was chosen as a core material because of its relevance to the material and life sciences.
As a first candidate of this series, we present cubic iron oxide nanoparticles with a nominal edge length of 8 nm. These particles were synthesized by thermal decomposition of iron oleate in high boiling organic solvents adapting well-known literature procedures. After dilution to a concentration suitable for electron microscopy (TEM and SEM) as well as for small-angle X-ray scattering (SAXS) measurements, the candidate nanoRM was bottled and assessed for homogeneity and stability by both methods following the guidelines of ISO 17034 and ISO Guide 35.
The particle sizes obtained by both STEM-in-SEM and TEM are in excellent agreement with a minimum Feret of 8.3 nm ± 0.7 nm. The aspect ratio (AR) of the iron oxide cubes were extracted from the images as the ratio of minimum Feret to Feret resulting in an AR of 1.18 for TEM to 1.25 for SEM. Alternatively, a rectangular bounding box was fitted originating from the minimum Feret and the longest distance through the particle in perpendicular direction. This led to AR values of 1.05 for TEM and 1.12 for SEM, respectively. The results confirm the almost ideal cubic shape.
Data for the publication "The role of extracellular polymeric substances of fungal biofilms in mineral attachment and weathering" (https://doi.org/10.1038/s41529-022-00253-1). It includes:
- The Summary of the EPS concentration, EPS sugar components and EPS linkages.
- The Summary of the XPS analysis of freeze-dried biofilm samples of all strains.
- The Summary of the pH, Mg, SI and Fe concentration, biomass and olivine dissolution rate for each time point of all dissolution experiments.
In 1981 the OECD published the Test Guideline on Particle size and size distribution. This TG is still a valid document for the measurement of particles all over the world.
When nanomaterials gained importance, ISO set up a technical commitee for Nanotechnologies in 2005 and the OECD followed this step in 2006 with the Working Party on Manufactured Nanomaterials.
In the following years ISO and OECD published several documents about nanomaterials and the systematisation developed.
In 2017 it was finally clear that nanomaterials need to be adressed in another way than chemicals and in 2020 ECHA revised the REACH-Annexes accordingly and included nanomaterials.
Unfortunately there is a little problem with this: Only a few applicable test guidelines exit for the measurement of the nanomaterials. Several test guidelines date from 1981 and do not address nanomaterials.
The logical next step for the OECD would be to publish a series of test guidelines which are indeed currently prepared and will be shown in this talk.
Finally there is an additional need for the future of NM standardisation: Digitalisation.
In this research project, a new OECD Test Guideline (TG) for the determination of “Particle Size and Particle Size Distributions of Nanomaterials” was developed as the existing OECD TG 110 is considered to be outdated in terms of applicable size range (not covering sizes <200 nm) and methods. By its scope with an applicable size range from 1 to 1000 nm the new Test Guideline (TG PSD) covers the whole nanoscale. The TG PSD is applicable for particulate and fibrous nanomaterials. The prescribed, pairwise measurement of fibre diameter and length in the TG PSD allows for the first time to differen-tiate fibres with regard to their size-dependent hazard properties. Measurement instructions for each included method were validated within two separated interlaboratory comparisons, as a distinction between near spherical particles and fibres when applying the methods has to be made.
Besides information on content and structure of the TG PSD, this final report outlines essential steps, considerations and organisational aspects during the development of the TG. Insights into the selec-tion, preparation and prevalidation of test materials used in the interlaboratory comparison are given. Finally, main results of the interlaboratory comparisons and their impacts on the TG PSD are pre-sented.
Final Draft of the OECD Test Guideline for Particle Size and Particle Size Distribution of Nanomaterials.
The OECD Working Party on Manufactured Nanomaterials (WPMN) has actively worked towards understanding possible safety issues for manufactured nanomaterials and has contributed significantly to resolving these by developing Test Guidelines, Guidance Documents, Test Reports and other publications with the aim of a safe use of manufactured nanomaterials. The OECD website (www.oecd.org/science/nanosafety) and the referenced publications contain more background information.
Among others, the OECD Test Guideline “Particle Size Distribution/Fibre Length and Diameter Distributions” (TG 110, adopted in 1981) was identified to require an update to address the specific needs of manufactured nanomaterials as the TG 110 is currently only valid for particles and fibres with sizes above 250 nm. The WPMN prioritised to either update TG 110 to be applicable also to particles at the nanoscale or draft a new nanomaterial specific Test Guideline (TG). Eventually, it was decided to develop a new TG for particle size and particle size distribution measurements of nanomaterials covering the size range from 1 nm to 1000 nm for further justification. This TG overlaps with TG 110 in the size range from 250 nm to 1000 nm. When measuring particulate or fibrous materials, the appropriate TG should be selected depending on the size range of particles tested. In line with TG 110, the new TG for nanomaterials includes separate parts for particles and fibres. For the part of this TG which addresses particles, several methods applicable to nanomaterials were reviewed and included to take into account developments since 1981 when the TG110 was adopted. This TG includes the following methods: Atomic Force Microscopy (AFM), Centrifugal Liquid Sedimentation (CLS)/Analytical Ultracentrifugation (AUC), Dynamic Light Scattering (DLS), Differential Mobility Analysis System (DMAS), (Nano)Particle Tracking Analysis (PTA/NTA), Small Angle X-Ray Scattering (SAXS), Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM).
For measuring the diameter and length of fibres, analysing images captured with electron microscopy is currently the only method available. This TG includes Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM).
To test the validity of this TG, an ILC was performed. Test materials were chosen to reflect a broad 68 range of nanomaterial classes, e.g. metals, metal oxides, polymers and carbon materials. Where possible, well-characterised test materials were used. Additionally, the test materials were chosen, so that they reflect a broad range of sizes representing the size range 1 nm to 1000 nm and finally,
for fibres only, aspect ratios from length/diameter of 3 to > 50.
The ISO 16000-6 standard describes a method for the determination of volatile organic compounds (VOCs) in indoor and test chamber air by sorbent-based active sampling, thermal desorption and gas chromatography coupled with mass spectrometry (GC/MS). It also gives directions to adapt this methodology to very volatile organic compounds (VVOCs). Indeed, toxicologically based guideline values are being implemented for these compounds and it becomes necessary to measure them. But a comprehensive and robust measurement method is lacking. Investigations on the use of gaseous standards, the suitability of chromatography columns, the suitable sorbent combinations and the water removal are required. The talk will highlight the points that need to be explored towards the standardisation of a suitable procedure and provide appropriate preliminary results.
For centuries, churches, secular buildings and museums have been furnished with valuable works of art. Many works of art are UV- and light-sensitive. It is well known that especially UV radiation causes damage and discoloration in paintings, textiles, plastics, wood and other materials. In particular, the wavelengths between 280 and 410 nm cause color changes, embrittlement or destruction of e.g. plastics over time. Therefore, strongly UV-absorbing glasses are advantageous for architecture and are necessary for the protection of cultural assets. As restorers in all disciplines become more and more aware, the demands placed on buildings and their furnishings in terms of climate are becoming increasingly detailed and precise. The aim in each case is to preserve the valuable artwork.
For some years now, the industry has been offering the protection of cultural objects by installing special UV-protective glasses. Currently, UV protection for church buildings is realized by laminated safety glass equipped with appropriate UV-protective plastic films. Technically, this always means a second pane of glass in front of the windows, which is installed outside the building. This creates climatic gaps that are difficult to control and deterioration due to ageing effects can be expected. At the same time, this protective glazing is not invisible and has a considerable aesthetic influence on the interior and exterior appearance of the building. Meanwhile, the preservation of historical monuments accepts such aesthetic cuts on buildings in order to protect the artwork in the interior from UV light. To this day, however, the long-term durability of UV protection provided by inserted plastic films is still controversial.
To date the only available alternative on the market is a mouth-blown UV protection glass which uses a so-called overlay to provide UV protection. This shows that UV protection can also be achieved by glasses without plastic films thus realizing an exclusive inorganic protection which normally is more stable than a polymeric one. So far there are not enough studies to prove long-term durability.
The aim of this project is to provide existing glazing or new glazing to be created with a highly transparent layer that ensures this UV-protective filter function below 400 nm. The glass coating is to be applied to the glass over a large area and fired into the surface like a classic ceramic enamel paint with the same technics. In addition, it should be long-term durable in its function. It means, that the glass has to be fused at temperatures below 630 °C during the firing process, its chemical durability has to be high, its coefficient of thermal expansion has to be as close as the one of the substrate (usually float glass) and the glass has to absorb the UV-radiation within a thin thickness (thinner as 100 µm).
In this project, the long-term durability of commercial UV-protective glasses is examined. New low melting glasses containing UV-absorbing ions are being developed. Their UV-absorption as a thin layer is analyzed as well as their chemical durability and their thermal properties.
We are grateful to BMWI for the financial support in the frame of the Central Innovation Programme for SMEs (ZIM).
In many late-breaking research fields as in photovoltaics, microelectronics, nuclear waste glasses or at least mirror glasses silver diffusion in glasses is relevant to the issues of high-level functionality and recycling. The present study is focused on silver diffusion in innovative, low-melting alkali zinc borate glasses (X2O-ZnO-B2O3, X = Li, Na, K, Rb) potentially usable for silver metallization-pastes in solar cells. The glasses were coated with a thin metallic silver layer and heat treatments in air and nitrogen close to Tg at 470 °C for 2 h were performed. After heat treatment under air and nitrogen atmospheres the coating thickness, measured by a white light interferometer, was about 1.8 µm thick. Silver depth profiles determined by means of secondary neutral mass spectrometry (SNMS) indicate the fastest silver diffusion to a depth of 3.5 µm for Li2O-ZnO-B2O3 (LZB) glass. Nevertheless, the influence of the different alkali ions on the silver diffusion is small. The oxygen availability determines the silver diffusion into the glasses. The oxygen promotes the oxidation of the silver layer enabling Ag+ to diffuse into the glass and to precipitate as Ag0. Both species were detected by x-ray absorption spectroscopy (XAS). The precipitated metallic silver particles in Na2O-ZnO-B2O3 (NZB) glass have a mean size of 5.9 nm ± 1.2 nm diameter, which was determined using transmission electron microscopy (TEM). Phase separation in zinc-rich and zinc-poor phases with a mean diameter of 75 nm ± 20 nm occurred in NZB glass after heat treatment. Ion diffusion of the glasses into the silver layer was suggested by EDX-line scans.
Indoor air quality is affected by the emission of volatile organic compounds (VOC) or the odour from building products. Odours can be measured by applying the standard ISO 16000-28:2020.
In the study presented here proposals for further technical development of the ISO method are presented. The sampling procedure and evaluation
method of the perceived intensity are investigated in particular because they have a major influence on reproducibility of measurement results.
Formaldehyde is considered as carcinogenic and is emitted from particleboards and plywood used in toy manufacturing. Currently, the flask method is frequently used in Europe for market surveillance purposes to assess formaldehyde release from toys, but its concordance to levels measured in emission test chambers is poor. Surveillance laboratories are unable to afford laborious and expensive emission chamber testing to comply with a new amendment of the European Toy Directive; they need an alternative method that can provide reliable results. Therefore, the application of miniaturised emission test chambers was tested. Comparisons between a 1 m3 emission test chamber and 44 mL microchambers with two particleboards over 28 days and between a 24 L desiccator chamber and the microchambers with three puzzle samples over 10 days resulted in a correlation coefficient r2 of 0.834 for formaldehyde at steady state. The correlation between the results obtained in microchambers vs. flask showed a high variability over 10 samples (r2: 0.145), thereby demonstrating the error-proneness of the flask method in comparison to methods carried out under ambient parameters. An exposure assessment was also performed for three toy puzzles: indoor formaldehyde concentrations caused by puzzles were not negligible (up to 8 μg/m3), especially when more conservative exposure scenarios were considered.
Test chamber measurements are an important tool to improve indoor air quality and occupational safety. Test chamber measurements are possible for a wide range of materials, products and technologies. Determination of concerning contaminants is important to ensure good indoor air quality. The detection of concerning contaminants depends on the approriate sampling and analysis.
The presentation gives general information about the European Standard EN 16516 “Construction products – Assessment of release of dangerous substances – Determination of emissions into indoor air”. This test standard was developed based on the mandate M/366 of the European commission and is a horizontal reference method for the determination of volatile organic compounds (VOC) from different classes of construction (building) products. Specific test conditions are to be selected by the product TCs (technical committees) in a way that a product is tested under its intended condition of use.
The test is based on the use of emission test chambers which are operated at constant air change rate and climate (23°C, 50 % r.h.) over 28 days. The standard defines the conditions and requirements for the measurement including loading factor, air change rate, sampling, analysis and calculation of emission rates of the substances. A 30 m³ reference room is described which is used to calculate air concentrations from the determined emission rates.
The standard EN 16516 enables the evaluation of construction products regarding their emissions into indoor air under defined and comparable conditions. The evaluation includes the determination of identified target compounds, non-identified target compounds, volatile carcinogenic compounds and the sum values TVOC, TSVOC and R.
Previous studies have shown that desktop 3D printers (Fused Filament Fabrication) emit high numbers of particulate matter, mainly as ultrafine particles (UFP, particle diameter less than 100 nm). However, the chemical composition of emitted particles has been less extensively investigated. In this study, we therefore focused on the chemical composition of particles emitted from 3D printing. The measurements were conducted in a 1 m³ emission test chamber. Emitted particles were sampled by a 13-stage low-pressure cascade impactor onto aluminum foils and then analyzed by TD-GC/MS to identify their organic compounds. Nine commercial filaments made from basic polymers such as Acrylonitrile Butadiene Styrene (ABS), Acrylonitrile Styrene Acrylate (ASA), Polycarbonate (PC), Poly(methyl methacrylate) (PMMA), Nylon, High Performance Polystyrene (HIPS) and a copper-filled Polylactide (PLA) were investigated. The results show that the organic components of the particles are primarily plastic additives such as plasticizer, antioxidant agents, lubricants, UV-absorbers and UV-stabilizers from the filaments.
Many studies have already shown that viruses can spread via aerosol particles. An aerosol is a mixture of air with solid or liquid particles dispersed in it. To understand the role of aerosol particles as a transmission path of SARS-CoV-2, knowledge of the different processes in an Aerosol is therefore of particular importance. With this paper, GAeF would like to contribute to a better understanding of the term “aerosol” and the relevant aerosol processes. In the context of this paper only the essential basics will be discussed. For a deeper understanding of the partly complex processes, please refer to the literature mentioned at the end of the paper.
The paper summarises a large number of studies on the formation of virus-laden aerosol particles and their spread. Based on this, it can be concluded that exhaled aerosol particles may play a prominent role in the spread of viruses in the corona pandemic. Finally, this paper discusses possible measures to reduce the spread of aerosol particles. The measures discussed are based on the current public debate including ventilation, air purifiers, HVAC systems and masks. Advice is given on the correct and sensible use of these measures.
An aerosol is always dynamic, as particles are newly formed, transported in or with the air, removed from the air or change in the airborne state. Aerosol particles have sizes between approx. 0.001 and several 100 micrometres (and not < 5 μm as currently defined in many publications) and spread relatively quickly with air currents, even over longer distances. Larger aerosol particles sink to the ground, depending on their size and density, while small aerosol particles can remain in the air for a very long time (see Section 3). Every person emits liquid aerosol particles of various sizes through breathing and when speaking, coughing and sneezing (see Section 4). If a person is infected with a virus, such as SARS-CoV-2, these aerosol particles can contain viruses that can be released into the air and inhaled by other people. SARS-CoV-2 has a size of 0.06 to 0.14 micrometres, but the exhaled liquid aerosol particles are larger. The liquid aerosol particles can shrink by evaporation, depending on the ambient conditions (see Section 3.3). Particle size is relevant for particle transport and particle separation. The highest risk of infection exists in closed indoor spaces, as aerosol particles can accumulate there.
Here in particular, appropriate measures must be taken to reduce the concentration of aerosol particles (see Section 5).
Against the background of aerosol science, the GAeF classifies the current measures to contain the pandemic as follows:
• In principle, no measure can work on its own! According to the current state of knowledge, the interaction of the most varied measures is the best way to minimise the risk of infection.
• Keeping distance is important, because with increasing distance, directly exhaled viruses are diluted and the probability of infection decreases. The often prescribed minimum distance can be used as a guide, but it should be increased and supplemented by other measures (see below), especially for longer meetings and also indoors with reduced air movement.
• Masks help to filter some of the exhaled particles (and viruses). This reduces the concentration of exhaled particles (and viruses) in a room and thus the risk of infection. It should be noted here that the exhaled aerosol particles are relatively large due to adhering moisture and can therefore also be efficiently retained by simple masks. However, since these particles shrink with longer dwell time in the room air, simple mouth-nose masks are less efficient for self-protection. Respiratory masks are required for this purpose, which show a high degree of separation even for fine particles, e.g. of classes FFP2, N95 or KN95. These are efficient for both self-protection and protection of others unless they have an exhalation valve. Masks with an exhalation valve, on the other hand, are only for self-protection and therefore contradict the solidarity concept that fellow human beings are protected by collective mask wearing. Face shields which are used without additional masks are largely useless with regard t• aerosol particles, as the air with particles (and viruses) flows unfiltered around the shields. In everyday clinical practice, facial shields are worn in addition to masks to prevent droplet infection via the mucous membranes of the eyes. Mobile or permanently installed Plexiglas barriers are also largely ineffective against the spread of aerosols indoors. These can only prevent the smallscale spread of an aerosol in the short term, e.g. in the checkout area of a supermarket, but offer no protection in the longer term. Face shields and Plexiglas panels essentially serve as spit and splash protection against large droplets.
• Outdoors, there are practically no infections caused by aerosol transmission. However, droplet infections can still occur, especially in crowds, if minimum distances are not observed and/or masks are not worn. In closed rooms, ventilation is essential to replace the exhaled air in a room with fresh air from outside. Frequent airing and cross-ventilation is just as effective as leaving the window open all the time. From an energy point of view, however, it is more efficient to ventilate the room, especially in winter. CO2 monitors can help to monitor indoor air quality. They indicate when it is necessary to ventilate and when the air in a room has been sufficiently changed during ventilation. However, they can only be used as an indicator and even if the proposed CO2 limit concentrations are met, they do not prevent direct infection by people in the immediate vicinity.
• Air purifiers can make a useful contribution to reducing the concentration of particles and viruses in a room. When procuring air purifiers, care must be taken to ensure that they are adequately dimensioned for the room and application in question in order to significantly reduce the particle and virus load. The air throughput of the unit is more important than the pure efficiency of the filter. For energy and cost reasons, the use of highly efficient filters can even be counterproductive. Permanently installed ventilation systems can also be useful, provided they filter the air to reduce the particle and virus load in a room. To avoid infections, it is advisable to operate them with 100 % fresh air if possible.
From the point of view of the Gesellschaft für Aerosolforschung, there is a considerable need for research, especially at the interdisciplinary borders to research fields of epidemiology, infectiology, virology, ventilation technology and fluid mechanics. The implementation of targeted studies should be made possible at short notice with special funding and research programmes.
This paper was written originally in German by members of the Gesellschaft für Aerosolforschung and is supported by a large number of international aerosol experts. Both the English and German version as well as all images in the paper are available for free download at the following link: https://www.info.gaef.de/positionspapier. The “Gesellschaft für Aerosolforschung e. V.” must be named as the source, whenever an image is used.
Previous studies have shown that desktop 3D printers (Fused Filament Fabrication) emit high numbers of particulate matter, mainly as ultrafine particles (UFP, particle diameter less than 100 nm). However, the chemical composition of emitted particles has been less extensively investigated. In this study, we therefore focused on the chemical composition of particles emitted from 3D printing. The measurements were conducted in a 1 m³ emission test chamber. Emitted particles were sampled by a 13-stage low-pressure cascade impactor onto aluminum foils and then analyzed by TD-GC/MS to identify their organic compounds. Nine commercial filaments made from basic polymers such as Acrylonitrile Butadiene Styrene (ABS), Acrylonitrile Styrene Acrylate (ASA), Polycarbonate (PC), Poly(methyl methacrylate) (PMMA), Nylon, High Performance Polystyrene (HIPS) and a copper-filled Polylactide (PLA) were investigated. The results show that the organic components of the particles are primarily plastic additives such as plasticizer, antioxidant agents, lubricants, UV-absorbers and UV-stabilizers from the filaments.
Quantitative chemical analysis of airborne particulate matter (PM) is vital for the understanding of health effects in indoor and outdoor environments and required by EU air quality regulations. Typically, airborne particles are sampled on filters, followed by lab-based analysis, e.g., with inductively coupled plasma mass spectrometry (ICP-MS). Within the EURAMET EMPIR AEROMET project, cascade impactor aerosol sampling was combined with on-site total reflection X-ray fluorescence (TXRF) spectroscopy. The study aimed at a proof of principles for this new mobile and on-size tool for the quantification of aerosol element compositions and element mass concentrations within short time intervals of less than 12 h. In a field campaign the method’s technical feasibility could be demonstrated. The TXRF results were traced back to a stationary, reference-free XRS setup in the laboratory of the German national metrology institute PTB at the BESSY II electron storage ring in Berlin, Germany. Simultaneous PM10-filter sampling, followed by standardized lab-based analysis, allowed for a comparison of the field campaign data of both methods. As Fig. 1 shows, the correspondence between PM10 filter sampling and ICP-MS, and on the other hand, cascade impactor sampling and TXRF is quite encouraging. However, for some of the analysed elements, e.g. V and Pb, the observed deviations are higher than expected and this highlights the fact, that spectral deconvolution strategies for TXRF on cascade impactor samples still need some improvement.
This work was supported by the EMPIR programme, co-financed by the Participating States and from the European Union’s Horizon 2020 research and innovation programme, through grant agreements 16ENV07 AEROMET and 19ENV08 AEROMET II
A brief perspective of BAM on nanocarriers is presented including examples with special emphasis on the characterization of such materials and underlying challenges. In this respect, also ongoing activities at BAM on different types of core/shell nanomaterials and related systems are briefly summarized.
Monodisperse iron oxide nanoparticles as reference material candidate for particle size measurements
(2020)
In order to utilize and rationally design materials at the nanoscale the reliable characterization of their physico-chemical properties is highly important, especially with respect to the assessment of their environmental or biological impact. Furthermore, the European Commission’s REACH Regulations require the registration of nanomaterials traded in quantities of at least 1 ton. Powders or dispersions where 50% (number distribution) of the constituent particles have sizes ≤ 100 nm in at least one dimension are defined as nanomaterials. This creates a need for industrial manufacturers and research or analytical service facilities to reliably characterize potential nanomaterials. Currently, BAM is developing reference nanoparticles, which shall expand the scarce list of worldwide available nano reference materials certified for particle size distribution and will also target other key parameters like shape, structure, porosity or functional properties. In this respect, materials like iron oxide or titanium dioxide are considered as candidates to complement the already available silica, Au, Ag, and polystyrene reference nanoparticles.
The thermal decomposition of iron oleate precursors in high boiling organic solvents can provide large quantities of iron oxide nanoparticles that can be varied in size and shape.[1, 2] The presence of oleic acid or other hydrophobic ligands as capping agents ensures stable dispersion in nonpolar solvents. Such monodisperse, spherical particles were synthesized at BAM and pre-characterized by electron microscopy (TEM, SEM including the transmission mode STEM-in-SEM) and dynamic light scattering comparing cumulants analysis and frequency power spectrum.
1. REACH regulations and nanosafety concerns create a strong need for nano reference materials with diverse properties.
2. Iron oxide nanoparticles are under development as new candidate reference material at BAM.
3. Narrow particle size distribution confirmed by light scattering and electron microscopy.