4 Material und Umwelt
Filtern
Dokumenttyp
- Zeitschriftenartikel (10)
- Vortrag (7)
- Beitrag zu einem Tagungsband (2)
Schlagworte
- Leaching (19) (entfernen)
Organisationseinheit der BAM
- 4 Material und Umwelt (19)
- 4.3 Schadstofftransfer und Umwelttechnologien (19)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.8 Umweltanalytik (2)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 4.1 Biologische Materialschädigung und Referenzorganismen (1)
- 4.4 Thermochemische Reststoffbehandlung und Wertstoffrückgewinnung (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (7)
Half of global material consumption involves mineral material. The circularity is still low so that the enhanced use of secondary building material is required to close loops. Three different secondary building materials are discussed based on exemplary research results: construction and demolition waste (C&D waste), soil-like material, and incineration bottom ash (IBA). Focus was placed on the environmental compatibility of the materials examined mainly by standardized leaching tests. C&D waste was investigated after a wet treatment using a jigging machine, and soil-like material and IBA were characterized with respect to their material composition. Their environmental compatibilities in particular were studied using standard leaching tests (batch tests and column tests).
It was concluded that soil-like material can mostly be utilized even when the precautionary limit values set are exceeded by a factor of less than two. For C&D waste, the fine fraction below 2 mm and the content of brick material is problematic. IBA fulfills quality level “HMVA-2” following German regulations. Improved levels of utilization might be achievable with better treatment technologies.
The release of hazardous compounds from construction products can harm human health and the environment. To improve the sustainability of construction materials, the leaching of substances from construction products and their potential environmental impact should be assessed. Twenty-seven construction products from different product groups were examined with a combination of standardized leaching tests (dynamic surface leaching test and percolation test) and biotests (algae, daphnia, fish egg, luminescent bacteria, umu and Ames fluctuation tests). To identify the released substances, extensive qualitative and quantitative chemical analyses were performed, including gas chromatographic and liquid chromatographic screening techniques.
Results: Many of the tested eluates caused signifcant ecotoxic efects. Particularly high ecotoxicities were observed for grouts (lowest ineffective dilution (LID) up to 16384) and cork granules (LID up to 24578). The results of ecotoxicity tests allow the prioritization of the eluates that should be subjected to detailed chemical analyses. Organic screening by different methods and ranking the identifed substances based on recorded hazard classification is a suitable approach to identify the relevant toxic substances.
Conclusions: Determining the ecotoxicity of eluates from construction products records the summary effect of all leachable substances. This instrument is especially useful for construction products of complex and largely unknown composition. The ecotoxicological and the chemical–analytical approach complement each other in an ideal way to characterize the potential hazard of eluates from construction products and to identify the environmentally hazardous components in these eluates. Our results confirm that the proposed harmonized methods for testing eluate toxicity are an adequate and applicable procedure to move toward a more sustainable way of building and to reduce toxic effects of construction products in their use phase in the environment.
Release of substances from joint grouts based on various binder types and their ecotoxic effects
(2022)
Background: The leaching of substances and the ecotoxic effects of eluates were studied for joint grouts that are based on various types of binders. Eight products, two of them containing either epoxy resin, polybutadiene or polyurethane binders, or modifed cement, were investigated using harmonized leaching tests for construction products in combination with ecotoxicity tests on algae, daphnia, luminescent bacteria, fish eggs and mutagenicity in accordance with CEN/TR 17105. In addition to basic parameters, such as pH, TOC, and inorganic components, organic substances in the eluates were analysed by gas and liquid chromatography in combination with mass spectrometry. Quantitative analyses in combination with ecotoxicity data on selected substances were used to deduce which substances cause the observed ecotoxic effects.
Results: Different patterns of ecotoxic effects were observed in joint grouts with different binder types. The most ecotoxic effects were observed in epoxy resin-based products, followed by polybutadiene-based products. Fewer ecotoxic effects were observed in polyurethane-based products and modifed cements. Some of these showed no ecotoxicity. Some of the substances in the eluates were identified and related to ecotoxic effects. 4-Tert-butylphenol and amines probably contributed to the ecotoxic effects of at least one of the epoxy resin-based renders, whereas cobalt is assumed to contribute to the toxic effect on algae of one of the polybutadiene-based products. However, only some of the leached substances could be identifed, and only some of the ecotoxic effects can be explained by the available information on the composition of eluates and known ecotoxic profiles of the identified substances.
Conclusions: Ecotoxicity tests on eluates from leaching tests indicate whether environmentally hazardous substances can be leached from construction products. Combined ecotoxicity tests and chemical analysis of eluates from EU-wide harmonized leaching tests for construction products can provide information on substances that cause these effects. This supports the identifcation and development of environmentally friendly construction products.
This study confirmed that ecotoxicity tests in accordance with CEN/TR 17105 are a tool well-suited to support the implementation of the European Commission’s zero pollution vision for 2050 and to reduce pollution to levels no longer considered harmful to health and natural ecosystems.
The environmental impact assessment of materials is usually based on laboratory tests, mostly in combination with models describing the longterm fate of the substances of interest in the targeted environmental compartment. Thus, laboratory tests are the fundamental link to achieve appropriate assessment conclusions which makes it essential to generate consistent results. This just as applies to the leaching of cementitious materials. In Europe, the leaching behavior of monolithic building materials is tested in the Dynamic Surface Leaching Test following the specification CEN/TS 16637–2. An interlaboratory comparison on European level regarding this technical specification showed relatively high intra- and interlaboratory variations for the tested materials (monolithic copper slag and cement stabilized coal fly ash). Therefore the German Committee for Structural Concrete (DAfStb) framed a guideline to specify additional testing conditions for cementitious materials. To assess the possible improvement by this guidelines measures, a round robin test with 11 participants from Germany and the Netherlands was conducted. This work aims to provide insight into the factors to be considered in the testing of alkaline materials, including sample preparation, and highlights crucial procedures and their manifestation in the results. All evaluated parameters showed improved results compared to the earlier round robin test. The relative standard deviations for repeatability (RSDr) and reproducibility (RSDR) of the elements calcium, barium, antimony, chromium, molybdenum and vanadium, which are the parameters evaluated in both round robin tests, were RSDr = 4%, 4%, 2%, 5%, 5%, and 5% respectively (4% in average) for this work, in comparison to the European round robin test with an average RSDr of 29% (17%, 17%, 20%, 40%, 36%, and 42%). The RSDR improved from 41% (30%, 36%, 29%, 57%, 40%, and 56%) to 14% (12%, 8%, 6%, 28%, 15%, and 12%). CO2 ingress during testing and the inaccuracy of eluate analytics for concentrations close to the determination limits were identified as the main sources of error.
This Special Issue, ‘Measurement of the Environmental Impact of Materials’, is focused on the impact that materials have on the environmental compartments of soil, water and air. Leaching and emission processes, including underlying mechanisms, are a recurring topic in most published articles in the present Special Issue. Contributions have come from three continents and numerous countries (USA, Germany, France, Latvia, Poland, Russia, Japan, Korea and Thailand) indicating the global dimension of the subject.
Antimony in incineration bottom ash – Leaching behavior and conclusions for treatment processes
(2020)
Antimony (Sb) is used in industrial products mainly as flame retardant in plastic material. Due to such additives in plastics, about a half of Sb ends up in municipal solid waste incineration at the end-of-life and consequently in relevant amounts in the generated bottom ash. In contact with water, the initial leachability is low, as antimonates form sparingly soluble compounds with Ca2+. Following the carbonation of the incineration bottom ash (IBA) during the proceeding ageing the pH in the leachates decreases. With decreasing concentration of Ca in the eluate the solution equilibrium changes and antimonates dissolve. In Germany it is intended to regulate Sb in IBA with the planned implementation of the so called Mantelverordnung (MantelVO, containing provisions on the utilisation of mineral waste) in the near future. The limit values set in the draft might be critical for IBA and therefore pose a risk for the utilisation of the mineral fraction of IBA in the well-established recycling routes.
The potential release of hazardous substances from polymer-based products is currently in the focus of environmental policy. Environmental simulations are applied to expose such products to selected aging conditions and to investigate release processes. Commonly applied aging exposure types such as solar and UV radiation in combination with water contact, corrosive gases, and soil contact as well as expected general effects on polymers and additional ingredients of polymer-based products are described. The release of substances is based on mass-transfer processes to the material surfaces. Experimental approaches to investigate transport processes that are caused by water contact are presented. For tailoring the tests, relevant aging exposure types and release quantification methods must be combined appropriately. Several studies on the release of hazardous substances such as metals, polyaromatic hydrocarbons, flame retardants, antioxidants, and carbon nanotubes from polymers are summarized exemplarily. Differences between natural and artificial exposure tests are discussed and demonstrated for the release of flame retardants from several polymers and for biocides from paints. Requirements and limitations to apply results from short-term artificial environmental exposure tests to predict long-term environmental behavior of polymers are presented.
Potential use of incineration bottom ash in construction – Evaluation of the environmental impact
(2020)
Knowledge of the long-term leaching behavior of potentially harmful substances is crucial for the assessment of the environmental compatibility of reusing municipal solid-waste incineration bottom ash (MSWI BA) in construction, i.e., as a road base layer.
BA fractions obtained from wet-processing aiming at the improvement of environmental quality were used to investigate the mobility of relevant substances. Eluates from laboratory-scaled leaching procedures (column percolation and lysimeters) were analyzed to learn about the long-term release of substances. Unsaturated conditions and artificial rainwater (AR) were used in the lysimeter tests to simulate field conditions. In addition, batch test eluates were generated at usual liquid-to-solid ratios (L/S) for compliance testing purposes. A variety of cations and anions was measured in the eluates.
The wet treatment reduces the leaching of chloride and particularly sulfate by more than 60%. The release of typical contaminants for the treated MSWI BA such as the heavy metals Cu and Cr was well below 1% in the conducted leaching tests.
An increase in the Sb concentration observed in the lysimeter experiments starting at L/S 0.75 L/kg and in the column experiment at L/S 4 L/kg is assumed to be related to decreasing concentrations of Ca and thus to the dissolution of sparingly soluble calcium antimonate. The same leaching mechanism applies with V, but the concentration levels observed are less critical regarding relevant limit values. However, on the long term the behavior of Sb could be problematic for the application of MSWI BA in construction.
The environmental compatibility of reactive fire-retardant coatings (intumescent paints) was investigated by a combination of leaching and ecotoxicological tests. Three representative fire-retardant coating systems were tested using two leaching procedures: “Horizontal Dynamic Surface Leaching Test” (DSLT) and the “Intermittent Immersion Test” (IIT). All eluate fractions (8 for DSLT and 9 for IIT) were analyzed for pH, conductivity, concentration of total organic carbon and selected anions und cations. Additionally, a GC-MS screening of selected fractions was conducted for identification of organic compounds. Eluate fractions 1 + 2 and fraction 7 of the DSLT were analyzed in four ecotoxicological tests (algae, daphnia, fish egg, luminescent bacteria) and in one genotoxicity test (umu). Concentration of most analytes was rather low or below limit of detection for many eluates. Analytes detected in eluates of all three products are Zn, Ba, SO4(2−) and PO4(3−). Release patterns do not indicate a general trend: some compounds show maximum release in the first fractions while for others the maximum was observed in later test stages. Ecotoxic effects in eluates were found, which were higher in the eluate fraction 7 (maximum lowest ineffective dilution for luminescent bacteria (LIDL) 256) than in the eluate fraction 1 + 2 (maximum LIDL = 24). The sensitivity of the test systems was very different with highest effects for luminescent bacteria, followed by algae and daphnia and without effects in the fish egg test and umu test. A biotest battery for the comprehensive assessment is therefore advisable.