Due to its large mineral fraction, incineration bottom ash (IBA) from municipal solid waste incineration is an interesting raw material that can be used for road construction or to produce secondary building materials. However, leaching chloride, sulfate, and potentially harmful heavy metals may cause problems in using IBA in civil engineering. Investigating leaching behavior is crucial for the assessment of the environmental compatibility of IBA applications. Various test procedures are available for that purpose. In the present study, a long-term leaching test of a wet-mechanically treated IBA was performed in a lysimeter for almost six years.
While concentrations of chloride, sulfate and the majority of the heavy metals started to decrease rapidly with progressive liquid-to-solid ratio (L/S), antimony (Sb) and vanadium (V) behaved differently. At the beginning of the lysimeter test, the Sb and V concentrations were low, but after approximately one year of operation at an L/S ratio of around 0.8 L/kg, a steady increase was observed. It was shown that this increase is the result of low Ca concentrations due to the formation of CaCO3.
With the data, the solubility products from Ca-antimonate and Ca-vanadate were calculated. The unusual leaching behavior of Sb and V should be kept in mind when considering field scenarios and evaluating the impact on the environment.
Small grain size fractions of municipal solid waste incineration (MSWI) bottom ash (BA) contain elemental and chemically bonded metals in appreciable amounts, especially copper. Investigations with a centrifugal concentrator were carried out using samples, which had been treated with different impact devices. Partly the impacts of single devices were visible in outlines, but mostly the surfaces of the metals were still covered with mineral residues. To generate copper rich fractions, parameters of the separation process should ensure mass yields <2%, best between 0.5 and 1%. The density of the concentrates is then generally >3.2 g/cm3. Best results were achieved with material from a special treatment train which is adapted to grain sizes <2 mm. Reliable copper contents between 20 and 40% (single runs >50%) could be realised.
However, considering the required mass yields, referred to this subset only 150–170 g copper would be recovered from 1 Mg MSWI BA. Furthermore, this copper is only in parts present in elemental form. A
dependable added value of such treatment step seems to be given only, if that enables a recycling of the mineral aggregates (tailings) in parallel to avoid landfill costs.