Calcium sulfate hemihydrate (CaSO4ᐧ0.5H2O), also known as bassanite, has been used as a precursor to produce gypsum (dihydrate, CaSO4ᐧ2H2O) for various construction and decorative purposes since prehistoric times. The main route to obtain hemihydrate is a thermal treatment of gypsum at temperatures typically between 150 °C and 200 °C to remove some of the structural water.
In this contribution, we introduce (Fig. 1) a more efficient and sustainable method (T < 100 °C) that enables the direct, rapid, and reversibly conversion of gypsum to bassanite using reusable high salinity aqueous solutions (brines with c[NaCl] > 4 M). The optimum conditions for the efficientproduction of bassanite in a short time (< 5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the typical behaviour of the bassanite phase in low salt environments.
Traditionally, hemihydrate is obtained through a solid state thermal treatment because bassanite is considered to be metastable with respect to gypsum and anhydrite in aqueous solutions, and therefore gypsum-to-bassanite conversion should not occur in water. Its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures is inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline structure for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.
Thermochemische Aufarbeitung von Stahlwerksstäuben und -schlämmen zur Zink- und Eisenrückgewinnung
(2024)
Stahlwerksstäube und -schlämme enthalten in der Regel Schwermetalle wie Zink, Blei und Cadmium, die ein direktes Recycling verhindern und diese Stoffe potenziell umweltgefährdend machen. Um diese Schwermetalle aus den Materialien zu entfernen, werden drei thermochemische Verfahren zur Aufarbeitung von Gichtgasschlamm, Elektroofenstaub und ähnlichen Stahlwerksstäuben vorgestellt. Zum einen kann die Mischung von Elektroofenstaub mit chloridhaltigen Lösungen, wie sie z. B. in der Titandioxidproduktion anfallen, gemischt werden, um bei der thermischen Behandlung Schwermetallchloride zu effektiv verdampfen. Weiterhin kann der im Gichtgasschlamm enthaltene Kohlenstoff genutzt werden, um in Mischungen aus Gichtgasschlamm und Elektroofenstaub bei der thermischen Behandlung als Reduktionsmittel zu wirken. Dieses Verfahren führt zur Rückgewinnung von Zink und metallischem Eisen und wird im Technikums- und Pilotmaßstab erprobt. Abschließend wird die Nutzung von Wasserstoff als Reduktionsmittel für Elektroofenstaub vorgestellt. Hierbei lässt sich der Reststoff potenziell klimaneutral in Eisenschwamm umwandeln, wobei die chemischen Grundlagen anhand von DTA-Experimenten und thermodynamischen Simulationen ergründet werden.