4 Material und Umwelt
Filtern
Dokumenttyp
- Zeitschriftenartikel (2)
- Vortrag (1)
Referierte Publikation
- nein (3) (entfernen)
Schlagworte
- BAM Data Store (1)
- Cubical shape (1)
- Electron microscopy (1)
- Electronic lab notebook (ELN) (1)
- Elektronisches Laborbuch (1)
- Forschungsdatenmanagement (1)
- ISO/TC 229 Nanotechnologies (1)
- Iron oxide (1)
- Nano CRM (1)
- Nano@BAM (1)
Organisationseinheit der BAM
- 1.0 Abteilungsleitung und andere (3) (entfernen)
Eingeladener Vortrag
- nein (1)
Angesichts der zunehmenden Digitalisierung und dem Einsatz datenintensiver Methodiken in der Wissenschaft stehen Forschende vor der Herausforderung, stetig wachsende Datenmengen nachvollziehbar zu dokumentieren, langfristig zu speichern und für Dritte nachnutzbar zu machen. Um diesen Anforderungen gerecht zu werden, bietet sich die Nutzung von Software-Lösungen an, welche Forschungsdatenmanagement mit der digitalen Dokumentation von Laborinventar und Experimenten in elektronischen Laborbüchern (engl. electronic lab notebooks (ELN)) verknüpfen.
BAM is currently building up a platform of novel nanoRMs relying on iron oxide nanoparticles of different shape, size and surface chemistry. Iron oxide was chosen as a core material because of its relevance to the material and life sciences.
As a first candidate of this series, we present cubic iron oxide nanoparticles with a nominal edge length of 8 nm. These particles were synthesized by thermal decomposition of iron oleate in high boiling organic solvents adapting well-known literature procedures. After dilution to a concentration suitable for electron microscopy (TEM and SEM) as well as for small-angle X-ray scattering (SAXS) measurements, the candidate nanoRM was bottled and assessed for homogeneity and stability by both methods following the guidelines of ISO 17034 and ISO Guide 35.
The particle sizes obtained by both STEM-in-SEM and TEM are in excellent agreement with a minimum Feret of 8.3 nm ± 0.7 nm. The aspect ratio (AR) of the iron oxide cubes were extracted from the images as the ratio of minimum Feret to Feret resulting in an AR of 1.18 for TEM to 1.25 for SEM. Alternatively, a rectangular bounding box was fitted originating from the minimum Feret and the longest distance through the particle in perpendicular direction. This led to AR values of 1.05 for TEM and 1.12 for SEM, respectively. The results confirm the almost ideal cubic shape.