4 Material und Umwelt
Filtern
Dokumenttyp
- Zeitschriftenartikel (299)
- Vortrag (280)
- Posterpräsentation (139)
- Beitrag zu einem Tagungsband (43)
- Buchkapitel (23)
- Dissertation (6)
- Sonstiges (6)
- Beitrag zu einem Sammelband (5)
- Forschungsbericht (4)
- Forschungsdatensatz (3)
Sprache
- Englisch (814) (entfernen)
Schlagworte
- Biocides (50)
- Antimicrobial resistance (34)
- Corrosion (25)
- Bacteria (24)
- Biofilms (24)
- Ink (24)
- Leaching (23)
- Biofilm (19)
- MIC (19)
- Archaeometry (17)
Organisationseinheit der BAM
- 4 Material und Umwelt (814) (entfernen)
Paper des Monats
- ja (19)
Emerging infectious diseases arise as a result of novel interactions between populations of hosts and pathogens, and can threaten the health and wellbeing of the entire spectrum of biodiversity. Bees andtheir viruses area case in point. However, detailed knowledge of the ecological factors and evolutionary forces that drive disease emergence in bees and other host–pathogen communities is surprisingly lacking. In this review, we build on the fundamental insight that viruses evolve and adapt over timescales that overlap with host ecology. At the same time, we integrate the role of host community ecology, including community structure and composition, biodiversity loss, and human driven disturbance, all of which represent significant factors in bee virus ecology. Both of these evolutionary and ecological perspectives represent major advances but, in most cases, it remains unclear how evolutionary forces actually operate across different biological scales (e.g., from cell to ecosystem). We present a molecule-to-ecology framework to help address these issues, emphasizing the role of molecular mechanisms as keybottom-up drivers of change at higher ecological scales. We consider the bee–virus system to be an ideal one in which to apply this framework. Unlike many other animal models, bees constitute a well characterized and accessible multispecies assemblage, whose populations and interspecific interactions can be experimentally manipulated and monitored in high resolution across space and time to provide robust tests of prevailing theory.
In nature, the cellular environment of DNA includes not only water and ions, but also other components and co-solutes, which can exert both stabilizing and destabilizing effects on particular oligonucleotide conformations. Among them, ectoine, known as an important osmoprotectant organic co-solute in a broad range of pharmaceutical products, turns out to be of particular relevance. In this article, we study the influence of ectoine on a short single-stranded DNA fragment and on double-stranded helical B-DNA in aqueous solution by means of atomistic molecular dynamics (MD) simulations in combination with molecular theories of solution. Our results demonstrate a conformation-dependent binding behavior of ectoine, which favors the unfolded state of DNA by a combination of electrostatic and dispersion interactions. In conjunction with the Kirkwood–Buff theory, we introduce a simple Framework to compute the influence of ectoine on the DNA melting temperature. Our findings reveal a significant linear decrease of the melting temperature with increasing ectoine concentration, which is found to be in qualitative agreement with results from denaturation experiments. The outcomes of our Computer simulations provide a detailed mechanistic rationale for the surprising destabilizing influence of ectoine on distinct DNA structures.
The particle size distribution is considered the most relevant information for nanoscale property identification and material characterization. The current OECD test guideline on particle size and size distribution (TG 110) is not applicable to ‘nano-sized’ objects. In this project we thus develop a new OECD test guideline for the measurement of the size and size distribution of particles and fibers with at least one dimension in the range of 1 - 1000 nm. A fiber is defined as an object having an aspect ratio of length/diameter l/d >3. The width and length of each fiber should be measured concurrently.
In order to measure the particle size distributions, many techniques are available. 9 methods for particles and 2 methods for fibres have been tested in a prevalidation study and appropriate methods will be compared in an interlaboratory round robin test starting in February 2019.
The particle size distribution is considered the most relevant information for nanoscale property identification and material characterization. The current OECD test guideline on particle size and size distribution (TG 110) is not applicable to ‘nano-sized’ objects. In this project we thus develop a new OECD test guideline for the measurement of the size and size distribution of particles and fibers with at least one dimension in the range of 1 - 1000 nm. A fiber is defined as an object having an aspect ratio of length/diameter l/d >3. The width and length of each fiber should be measured concurrently.
In order to measure the particle size distributions, many techniques are available. 9 methods for particles and 2 methods for fibres have been tested in a prevalidation study and appropriate methods will be compared in an interlaboratory round robin test starting in February 2019.
Transformation of carbendazim, diuron, octylisothiazolinone and terbutryn was investigated in two paints containing either white titanium dioxide or a red iron oxide pigment.
Test specimens of these coatings on glass were exposed to water contact and UVA-radiation under laboratory conditions. Panels of birch plywood were coated and exposed to natural weather conditions in a field experiment. Concentrations of biocides and transformation products were analysed in leachates from laboratory tests, runoff samples and remaining coatings. Water contact, UVA radiation as well as pigments in the paints affected the pattern and amount of transformation products.
Test methods for efficacy assessment of antimicrobial coatings are not modelled on a hospital environment, and instead use high humidity (>90%) high temperature (37 ◦C), and no airflow. Therefore, an inoculum will not dry, resulting in an antimicrobial surface exhibiting prolonged antimicrobial activity, as moisture is critical to activity. Liquids will dry quicker in a hospital ward, resulting in a reduced antimicrobial efficacy compared to the existing test, rendering the test results artificially favourable to the antimicrobial claim of the product. This study aimed to assess how hospital room environmental conditions can affect the drying time of an inoculum, and to use this data to inform test parameters for antimicrobial efficacy testing based on the hospital ward. The drying time of different droplet sizes, in a range of environmental conditions likely found in a hospital ward, were recorded (n = 630), and used to create a model to inform users of the experimental conditions required to provide a drying time similar to what can be expected in the hospital
ward. Drying time data demonstrated significant (p < 0.05) variance when humidity, temperature, and airflow were assessed. A mathematical model was created to select environmental conditions for in vitro antimicrobial efficacy testing. Drying time in different environmental conditions demonstrates that experimental set-ups affect the amount of time an inoculum stays wet, which in turn may affect the efficacy of an antimicrobial surface. This should be an important consideration for hospitals and other potential users, whilst future tests predict efficacy in the intended end-use environment.
X-ray photoelectron spectroscopy (XPS) provides elemental and chemical information from the outermost ~10 nm of the sample surface. This is in the same order of magnitude as the thickness of the outer bacterial membrane of gram-negative bacteria, as well as outer membrane molecules as exopolysaccharides and lipopolysaccharides, commonly attached to the cell surface. With the development of near-ambient pressure (NAP)-XPS, bacteria can be analysed with minimal sample preparation.
EnviroESCA is a laboratory based NAP-XPS instrument, equipped with a monochromated Al Kα radiation source and a differentially pumped energy analyser connected to an exchangeable sample environment. It allows for measurements in various gas-atmospheres, including water vapor, which makes it possible to characterise bacteria and other biological samples close to their natural, hydrated state. Artificial model-biofilms of exopolysaccharides, planktonic Pseudomonas Fluorescens and biofilms of Escherichia Coli have been characterised in hydrated and dried state.
High-resolution XPS-spectra from carbon, oxygen, nitrogen and phosphorous can be assigned to carbohydrates, lipids and proteins in general agreement with literature. Especially the carbon 1s peak is of interest. A series of measurements of an E. coli biofilm from 11 mbar in humid environment to 1 mbar air reveal changes in the C1s peak, which suggests that the bacterial surface undergo substantial Change.
Graphene and its derivatives have recently attracted much attention for sensing and deactivating pathogens. However, the mechanism of multivalent interactions at the graphene–pathogen interface is not fully understood. Since different physicochemical parameters of graphene play a role at this interface, control over graphene’s structure is necessary to study the mechanism of these interactions. In this work, different graphene derivatives and also zwitterionic graphene nanomaterials (ZGNMs) were synthesized with defined exposure, in terms of polymer coverage and functionality, and isoelectric points. Then, the switchable interactions of these nanomaterials with E. coli and Bacillus cereus were investigated to study the validity of the generally proposed “trapping” and “nano-knives” mechanisms for inactivating bacteria by graphene derivatives. It was found that the antibacterial activity of graphene derivatives strongly depends on the accessible area, i.e. edges and basal plane of sheets and tightness of their agglomerations. Our data clearly confirm the authenticity of “trapping” and “nano-knives” mechanisms for the antibacterial activity of graphene sheets.
This application note presents how EnviroESCA can be used to analyze E. coli biofilms on silicon under near ambient pressure conditions in various states of hydration. Such investigations of the outer bacterial cell surface in their hydrated state are essential for studying biological interfaces at work.
Synchrotron XPS in the soft-X-ray regime is suitable for the detection of light elements commonly found in biological samples. Various model systems of biofilms have been developed and characterised at synchrotron- and lab-based facilities. By obtaining the chemical composition at various information depths, the vertical distribution of iodine in an artificial biofilm have been determined.
Surface characterisation of Escherichia coli under various conditions by near-ambient pressure XPS
(2018)
Bacteria are inherently in a hydrated state and therefore not compatible to ultra-high vacuum techniques such as XPS without prior sample preparation involving freeze drying or fast freezing.
This has changed with the development of near-ambient pressure (NAP)-XPS, which makes it possible to characterise the bacterial surface with minimal sample preparation. This paper presents NAP-XPS measurements of Escherichia coli under various NAP conditions: at 11 mbar in a humid environment, at 2 mbar after drying in the chamber, pre-dried at 4 mbar, and at 1 mbar after overnight pumping at 10^−4 mbar. The high-resolution spectra of carbon, nitrogen, and oxygen are presented and found to be in general agreement with XPS measurements from freeze-dried and fast-frozen bacteria. However, it was found that the amount of carbon components associated with polysaccharides increases relative to aliphatic carbon during drying and increases further after overnight pumping. This implies that drying has an impact on the bacterial surface.
The XPS information depth of approximately 10 nm is in the same size range as the outer membrane of the gram-negative bacteria, which makes XPS a suitable tool for determining the elemental composition of the bacterial surface and monitor changes caused by outer stress like dehydration or exposure to antimicrobials. However, bacteria are inherently in a hydrated state, and therefore only compatible to ultra-high vacuum after extensive sample preparation, which may degrade the sample constituents. This issue is addressed by the development of near-ambient pressure (NAP)-XPS, which enables bacteria and biofilms to be characterised in their native wet state. Artificial biofilms, bacteria and biofilms of Escherichia coli have been characterised with the laboratory NAP-XPS instrument EnviroESCA from SPECS GmbH, at pressures ranging from high vacuum to 12 mbar, and in both humid and dry environment. By studying biological samples in their native wet state, new insight about composition and transport of drugs through cell membranes and the extracellular polymeric substance (EPS) of biofilms can be obtained. In this contribution, the latest progress on biofilm characterisation by NAP-XPS will be presented, and measurement capabilities and limitations will be discussed.
Near-ambient pressure XPS makes it possible to characterise samples not compatible to ultra-high vacuum, and enables the study of liquid-solid, gas-liquid and gas-solid interfaces. NAP-XPS meas-urements of biofilms, suspended nanoparticles and metal-organic frameworks were performed with EnviroESCA developed by SPECS.
An interesting application is surface characterisation of biofilms, which are bacterial communities embedded in a self-produced polysaccharide matrix. Various model systems ranging from pure polysaccharides of alginate to biofilms harvested directly from the growth medium have been char-acterised in humid conditions[1].
NAP-XPS also makes it possible to characterise nanoparticles in solution. Silver nanoparticles in aqueous solution were characterised and the Ag 3d-spectrum compared to spectra obtained of dried nanoparticles in UHV-conditions[2]. The binding energy of the Ag 3d-core level peak was shifted by 0,6 eV towards higher binding energy for suspended nanoparticles compared to the dried sample measured in UHV. This can be assigned to a change in surface potential at the water-nanoparticle interface.
Metal-organic frameworks (MOFs) are suitable materials for gas storage of small molecules due to their nanoporous, crystalline structure. However, instability in humidity remains an issue for many types of MOFs. XPS-measurements of the MOF-structure HKUST-1 were performed in various NAP-conditions to assess the stability of the sample and its interaction with the gas molecules as water, methanol and pyridine.
This application note presents how EnviroESCA can be used to analyze bacterial samples under near ambient pressure conditions in various states of hydration using different levels of humidity. Such investigations of bacterial cell wall surfaces in their hydrated state are essential for studying biological interfaces at work.
The use of innovative near-ambient pressure (NAP-)XPS instrumentation allows the detailed analysis of irregularly-surfaced biofilms. NAP-XPS enables the surface analysis of bacterial samples in their natural hydrated state without complex sample preparation techniques such as freeze-drying or fast-freezing, which are needed for XPS analysis in ultrahigh vacuum.
X-ray fluorescence analysis, due to its non-destructive nature and ist suitability to work with historic objects in situ, quickly became one of the most important methods for the evaluation of iron-gall ink. The main advantage of this qualitative and semi-quantitative method is that it makes it easy to differentiate between inks, based on the assumption that the differences result from the manufacture of the ink.
This work explores the question whether the ink ‘fingerprint’ results strictly from the elemental composition of the basic ink ingredients even if it is stored in vessels made of metals or metal alloys. In addition, we tested and compared the performance of three different XRF spectrometers.
We prepared various lab-grade inks according to historical ink recipes and measured the metal content of the ink deposited on sized cotton Linters paper with three types of XRF spectrometers: a simple hand-held device with an interaction spot of 4 mm and two devices equipped with poly-capillary Xray optics for line scanning and imaging. Since the exact elemental mass composition of the non-aged ink samples was known, we were able to evaluate the accuracy of the research procedure. Lab-grade inks were then aged in the metal jars imitating inkwells. The aging of the inks in the metal containers resulted in the significant change of the primary inks fingerprint as opposed to that of the control inks stored in glass containers. This effect was independently confirmed by the measurements conducted with every instrument we used. We will present a brief comparison of the results 43 achieved when using different spectrometers and a possible hypothesis explaining the processes that occurred.
This work presents the non-destructive spectroscopic characterisation of original Dead Sea Scrolls (DSS)parchment fragments from Ronald Reed collection. The fragments are of paramount importance becausethey have never been subjected to any treatment of preservation and restoration, this allows to investi-gate the manufacturing method of real original Jewish parchments. The manufacture of “sacred” Jewishparchments, in fact, is traditionally supposed to use a superficial tannin treatment. To study the DSS frag-ments, it was necessary both to analyse mock-up samples, especially manufactured in order to reproduceancient Oriental Jewish ritual parchments, and to compare the results with those obtained in the analysisof modern and ancient Western Jewish ritual parchments, in order to test the effectiveness of the selectedspectroscopic techniques. Traditionally, the main difference between Oriental and Western traditionalparchment preparation consisted in the dehairing method: enzymatic for Oriental and lime-based forWestern. Moreover, a finishing treatment with tannin was supposed to be applied on ritual Jewish parch-ments. The need of reference samples derives from the knowledge that each parchment preparation,treatment and degradation can induce structural modifications that affect the spectral features. FourierTransform Infrared Spectroscopy by Attenuated Total Reflection (ATR-FTIR), FT-Raman and m-Ramanwere used in this study. The experimental results allowed us to recognise, with different sensitivity, thepresence of tannin by using m-Raman and IR spectroscopies and to prove that not all the archaeologicalsamples were manufactured in the same way with vegetal extracts. Many salts (tschermigite, dolomite,calcite, gypsum and iron carbonate) were found on the surface of DSS fragments. They can derive fromthe degradation processes and storage environment before the discovery or from the manufacture. More-over, the different sensitivities and instrumental characteristics of the used techniques permitted us toestablish an analytical protocol, useful for further studies of similar materials.
Surface characterisation of biofilms by nearambient pressure X-ray photoelectron spectroscopy
(2018)
The XPS information depth of approximately 10 nm is in the same size range as the outer membrane of the gram-negative bacteria, which makes XPS a suitable tool for determining the elemental composition of the bacterial surface and monitor changes caused by outer stress like dehydration or exposure to antimicrobials. However, bacteria are inherently in a hydrated state, and therefore only compatible to ultra-high vacuum after extensive sample preparation, which may degrade the sample constituents. This issue is addressed by the development of near-ambient pressure (NAP)-XPS, which enables bacteria and biofilms to be characterised in their native wet state. Artificial biofilms, bacteria and biofilms of Escherichia coli have been characterised with the laboratory NAP-XPS instrument EnviroESCA from SPECS GmbH, at pressures ranging from high vacuum to 12 mbar, and in both humid and dry environment. By studying biological samples in their native wet state, new insight about composition and transport of drugs through cell membranes and the extracellular polymeric substance (EPS) of biofilms can be obtained.
Microbiologically influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms, either chemically (formation of hydrogen sulfide) or electrically (direct electron uptake). Methanogenetic Archaea are also known to be involved in iron corrosion, forming a multi-species biofilm on corroding metallic structures. However, mechanistic details and kinetics of the overall process in methanogen-induced MIC are poorly understood.
The present study shows the potential of high-resolution imaging and nano-Fourier-transform infrared (nano-FTIR) spectroscopy for corrosion science. The protective oxidation layers of different chlorine-gas treated silicon
carbides (SiCs) were characterized with these techniques. A nitrified SiC showed the highest resistant strength against chlorine corrosion at 1000 °C compared to the other SiCs. Nano-FTIR spectroscopy with a lateral resolution below 40 nm detected differences in the crystallinity of the bulk-SiC and in the transitional region to the protective layer. Furthermore, high-resolution imaging provides deep insight in the interfacial layer between bulk-SiC and the protective oxidation layer on sub-micrometer scale.