Half of the global material consumption is mineral material. The circularity is still low so that enhanced use of secondary building material is required to close loops. Three different secondary building materials are discussed based on exemplary research results: construction and demolition waste (C&D waste), soil-like material and incineration bottom ash (IBA). Focus was laid on the environmental compatibility of the materials examined mainly by standardized leaching tests. C&D waste was investigated after a wet treatment using a jigging machine, soil-like material and IBA were characterized with respect to their material composition. The environmental compatibility in particular was studied using standard leaching tests (batch tests and column tests). It was concluded that soil-like material can mostly be utilized even when the precautionary limit values set are exceeded by a factor of less than 2. For C&D waste the fine fraction below 2 mm and the content of brick material is problematic. IBA fulfills quality level HMVA-2 following German regulation. Higher quality levels of utilization might be achievable with better treatment technologies.
The long-term leaching behavior of incineration bottom ash (IBA) was studied with large-scale samples from two German waste incinerators with grate technology. The observation period was up to 281 days. The aging processes proceeded faster in the outdoor storage of the samples. The dominant factor in the leaching behavior is the pH, which starts at values above 12 and decreases to values below 10 (outdoors, <11 indoors). Most heavy metals exhibit minimum solubility in this pH range. The solubility of Sb depends on the prevailing Ca concentration, due to the formation of low-soluble Ca antimonate. The very low sulfate concentrations observed in the leaching tests with fresh IBA could be explained by the presence of ettringite. In the course of the aging reaction, ettringite is transformed into gypsum. The results from batch tests were compared with those from column tests, showing reasonable agreement. Leaching dynamics can be better followed with column tests. All results confirm that the use of IBA is possible under German law.
Due to its large mineral fraction, incineration bottom ash (IBA) from municipal solid waste incineration is an interesting raw material that can be used for road construction or to produce secondary building materials. However, leaching chloride, sulfate, and potentially harmful heavy metals may cause problems in using IBA in civil engineering. Investigating leaching behavior is crucial for the assessment of the environmental compatibility of IBA applications. Various test procedures are available for that purpose. In the present study, a long-term leaching test of a wet-mechanically treated IBA was performed in a lysimeter for almost six years.
While concentrations of chloride, sulfate and the majority of the heavy metals started to decrease rapidly with progressive liquid-to-solid ratio (L/S), antimony (Sb) and vanadium (V) behaved differently. At the beginning of the lysimeter test, the Sb and V concentrations were low, but after approximately one year of operation at an L/S ratio of around 0.8 L/kg, a steady increase was observed. It was shown that this increase is the result of low Ca concentrations due to the formation of CaCO3.
With the data, the solubility products from Ca-antimonate and Ca-vanadate were calculated. The unusual leaching behavior of Sb and V should be kept in mind when considering field scenarios and evaluating the impact on the environment.