In 2005, a team of Polish archaeologists discovered three Coptic codices, two on papyrus and one on parchment, in the rubbish dump of a hermitage at Sheik Abd el-Gurna, Egypt. While the parchment codex and the remains of the bindings of the papyrus ones have been conserved, the text blocks of the papyrus codices were opened and disassembled and after being disinfected remained untouched for nearly 15 years, until the current project started. Currently, all three books are stored in the collection of the Coptic Museum in Cairo. Our team undertook the conservation of and archaeometric research on the papyrus codices. The first of the books contains the Canons of Pseudo-Basil, while the second is an Encomium of St. Pisenthios. Both codices have been palaeographically dated to the seventh-eighth centuries CE. In this paper, we describe our project and present the results of the work carried out on the Canons of Pseudo-Basil. Our work involved photography in transmitted light, measurements of the thickness of the papyrus leaves, and digital microscopy under three-light illumination. These measurements allowed us to determine the types of the inks and characterize the papyrus writing substrate. For conservation, we used a novel method developed in the Egyptian Museum in Berlin that comprises suspending papyrus folios on a translucent, extremely thin Japanese paper inside glass frames without the use of adhesives.In 2005, a team of Polish archaeologists discovered three Coptic codices, two on papyrus and one on parchment, in the rubbish dump of a hermitage at Sheik Abd el-Gurna, Egypt. While the parchment codex and the remains of the bindings of the papyrus ones have been conserved, the text blocks of the papyrus codices were opened and disassembled and after being disinfected remained untouched for nearly 15 years, until the current project started. Currently, all three books are stored in the collection of the Coptic Museum in Cairo. Our team undertook the conservation of and archaeometric research on the papyrus codices. The first of the books contains the Canons of Pseudo-Basil, while the second is an Encomium of St. Pisenthios. Both codices have been palaeographically dated to the seventh-eighth centuries CE. In this paper, we describe our project and present the results of the work carried out on the Canons of Pseudo-Basil. Our work involved photography in transmitted light, measurements of the thickness of the papyrus leaves, and digital microscopy under three-light illumination. These measurements allowed us to determine the types of the inks and characterize the papyrus writing substrate. For conservation, we used a novel method developed in the Egyptian Museum in Berlin that comprises suspending papyrus folios on a translucent, extremely thin Japanese paper inside glass frames without the use of adhesives.
Aluminum is an often-used building material in modern architecture. In recent years buildings from the 1950th and 1960th are increasingly subject of conservation works including the aluminum parts. Typical surface damages are signs of corrosion caused by weathering processes or scratches in the anodized layer due to extensive wear. To repair damaged aluminum surfaces, there are usually two options: smaller areas are repaired by using a touch-up pen, for larger damages it is necessary to remove the anodized layer completely. Both possibilities are disadvantageous for the objects; the touch-up pen often does not match the color together with an insufficient corrosion protection, while newly anodized layers often differ in color and gloss from the original surface.
For this reason, a research project was initiated to develop a mobile method to repair anodized aluminum parts. The first step focusses on the mobile anodization process by using the electrolyte with a gel substrate. Different cathodic materials are to be tested together with appropriate cooling material. The anodized area should be isolated to protect undamaged areas. Examinations of the produced layers are conducted by using Keyence microscope, eddy current testing and ESEM analysis. Further steps are to transform the coloring and sealing process for mobile application. Color could be applied by using a brush or by spray while the sealing process could be performed with water vapor. An heatable putty knife could be used, if heating up the area will be necessary. Once the application process is developed, the anodization will be tested on samples with artificial damages, fixed in horizontal and vertical positions. The stability of the anodized surface will be examined by accelerated ageing in a climate chamber and outdoor weathering.
The electrolyte (diluted sulfuric acid) was combined with a gel binder to enable a mobile application. Several thickening agents were tested concerning their conductivity and stability in acid systems. Anodization tests with different cathodic material and shapes were conducted. The temperature during anodization was controlled and adjusted if necessary. The anodized area was restricted by using either a lacquer, an adhesive or a removable silicon barrier. The fist results show the feasibility of the method on enclosed areas. The achieved thickness was measured by eddy current testing and the structure was controlled by ESEM analysis. The examinations show a connection between thickness and porosity of the anodized layers and the temperature during the application process.
Next steps are testing mobile coloring and sealing methods followed by mobile anodization on artificial damaged areas.