4 Material und Umwelt
Filtern
Dokumenttyp
- Vortrag (75)
- Zeitschriftenartikel (42)
- Posterpräsentation (24)
- Beitrag zu einem Tagungsband (17)
- Sonstiges (5)
- Forschungsbericht (4)
- Monografie (1)
- Buchkapitel (1)
- Forschungsdatensatz (1)
Schlagworte
- Nano (29)
- OECD (20)
- Nanomaterial (14)
- VOC (13)
- Bauprodukte (12)
- Emission (9)
- Prüfrichtlinie (9)
- Volatile organic compounds (8)
- Aerosol (7)
- BEMMA (7)
Organisationseinheit der BAM
- 4.2 Material-Mikrobiom Wechselwirkungen (170) (entfernen)
Paper des Monats
- ja (3)
Eingeladener Vortrag
- nein (75)
Measurements of aerosol particles are vital for enforcing EU air quality regulations to protect human health, and for research on climate change effects. Although metrics such as PM10 and PM2.5 are currently in use, the level of uncertainty of aerosol metrics is too high and the traceability is insufficient. The project AEROMET, which has been started in June 2017 aims at implementing improvements in a) the uncertainty of particle mass, size and number concentration measurements and b) in the characterization of regulated components in airborne particles. Both are demanded by existing networks within the EU as well as by global atmospheric research.
On-site measurement campaigns
One of the objects is the application of mobile x-ray spectroscopy techniques combined with aerosol sampling techniques for quantifying particle compositions in the field for real time analysis. During two in-field measurement campaigns in Budapest, Hungary in May 2018 and Cassino, Italy in September 2018 the size dependent mass concentrations of specific elements in ambient aerosols were monitored under dynamic conditions.
Typically, airborne particles are sampled on filter substrates. During this project new sampling methods with specially designed substrate holders for an in-situ TXRF analysis were developed and applied for the first time. This approach allows a direct time and size resolved analysis without laborious digestion steps and a reduced risk of contamination.
Aerosol particles were sampled in a 13-stage DLPI impactor - size range from 0,03 µm to 10 µm - which was equipped with special adapters for acrylic discs of 30 mm diameter, serving as substrates. TXRF analysis was performed on site with the transportable spectrometer S2 PICOFOX (Bruker Nano GmbH) equipped with a Mo X-ray tube and a 30 mm² Silicon Drift Detector (SDD). Excitation conditions were 50 kV, 600 µA, measurement time 1000 s. Quantification was based on internal standardization using 50 ng of Y in solution, which was pipetted into the centre of the discs prior to sampling.
At moderate air pollution levels, i.e. PM10 ~ 20 µg/m³, sampling times of less than 2 hours were enough for the detection of elements in different particle size bins. The in-situ approach and the high sensitivity of TXRF enables the observation of rather quick changes in the quantity and distribution of elements in an ambient aerosol on the day of sampling, as the below example from the Cassino field campaign on 11 Sept. 2018 shows: The analysis of the morning and afternoon sampling shifts reveals the occurrence of the elements Fe, Ca and Si in different size bins as well as their significant temporal change in respective mass concentrations over the day while the distributions of several other elements in the aerosol remain unchanged.
The validation of these results by backup measurements is planned.
Ein Ringversuch ist eine Methode der externen Qualitätssicherung für sowohl Messverfahren als auch die Eignung von Mess- und Prüflaboratorien. Dabei werden möglichst identische Proben mit identischen Verfahren oder mit unterschiedlichen Verfahren untersucht. Die Teilnahme an Ringversuchen ist für alle akkreditierten Laboratorien ein wesentlicher Baustein der institutsinternen und -externen Qualitätssicherung. Je mehr Faktoren Einfluss auf das Endergebnis haben können, desto wichtiger ist es diese Faktoren zu kennen und deren Einflüsse durch weitestgehende Vergleichbarkeit der Messverfahren zu minimieren.
Für die Bewertung von Emissionen aus Bauprodukten haben sich Emissionsmess-kammer-Untersuchungen als Messverfahren etabliert. Um den Geruch auch für Innenraumanwendungen bewertbar zu machen sind in den letzten Jahren erste Normen entstanden (z. B. DIN ISO 16000-28 und VDI 4302-1). Um die Eignung dieser Normen und deren Anwendung zu untersuchen sind seit 2012 nunmehr 3 Ringversuche der BAM auch zum Thema Geruch durchgeführt worden.
Die bislang durchgeführten Ringversuche mit dem Ziel der Geruchsbewertung wiesen Standardabweichungen von ca. 24 bis 30 % um den jeweiligen Mittelwert auf und wiesen somit ähnliche Werte auf, die auch bei den VOC-Vergleichen ermittelt wurden. Diese Entwicklungen werden hier aufgezeigt.
Ammoniakemissionen in die Umwelt erfolgen insbesondere durch die Landwirtschaft (93,6 %), aber auch durch Verbrennungsprozesse in der die Abfallwirtschaft (2,3 %) und den Straßenverkehr (1,8 %). Dieser Stoff ist selbst in geringen Konzentrationen nicht nur eine Geruchsbelästigung, sondern auch eine Substanz mit ökologischer und klimatischer Relevanz.
Die Bestimmung von Ammoniak in relevanten Konzentrationen von kleiner 25 μg m-3 erfolgt im Allgemeinen über NH4+ als Analyten, spektralfotometrisch oder mit der Ionenchromatographie nach Überführung in die flüssige Phase. Wegen der niedrigen Konzentrationen an Ammoniak in der Außenluft wird meist eine gesammelte Probe verwendet oder die Bestimmung erfolgt nach einer aktiven, anreichernden Probenahme.
Die eigenen Arbeiten sollen dazu beitragen, die Ammoniak-Bestimmung in der Außenluft präziser, sowie schneller und kostengünstiger zu machen.
Die BAM prüfte daher kommerzielle elektrochemische und Metalloxid-basierte Sensoren, die für diesen Konzentrationsbereich aber nur bedingt geeignet sind. Deshalb wurden alternativ eigene Entwicklungen zum Nachweis von Ammoniak im Spurenbereich aufgenommen, wobei der Analyt über die Änderung der Fluoreszenz eines BODIPY-Farbstoffs bei 550 nm mittels eines portablen Fluoreszenz-Sensors direkt aus der Gasphase gemessen wird.
Zur Kalibrierung von Ammoniak-Sensoren und -Messgeräten steht ein stationäres System basierend auf der Mischung von zertifizierten Prüfgasen aus Druckflaschen mit kalibrierten Massendurchfluss-regler (MFC) zur Verfügung. Darüber hinaus erfolgt eine chemische Analyse der verwendeten Gasgemische mittels eines Massenspektrometers.
Für die Kalibrierung und Prüfung von Sensoren und Messgeräten vor Ort wurde ein mobiles Prüfsystem entwickelt. Die Generierung von Ammoniak-haltigen Gasen im Spurenbereich von 0,5 nmol/mol bis 500 nmol/mol erfolgt durch das Permeationsverfahren nach ISO 6145-10.
Für die Realisierung der Rückführbarkeit der Ammoniakbestimmung werden von den Nationalen Metrologischen Instituten sowie designierten Instituten Standards bereitgestellt und auch weiterentwickelt. Die primären metrologischen Standards beruhen auf SI-Einheiten und sind die Basis für eine Rückführbarkeit der Sensoren bzw. Analysengeräte.
Nach 1850 wurde zur weiteren Herabsetzung der Einbrenntemperatur von Glasmalfarben Borax (Na2B4O7 · 10 H2O) zugesetzt. Das Verhältnis war nun 1 Teil SiO2, 3 Teile PbO und 0,5 Teile Borax. Der analytische Nachweis von Bor in eingebrannten Malschichten war bisher jedoch nicht möglich.Daher wurden in Laborversuchen Glasmalfarben mit unterschiedlichem Gehalt an Borax auf Modellgläser aufgetragen, eingebrannt und anschließend unter simulierten Umweltbedingungen zeitraffend im Klimaschrank bewittert.
Mit Hilfe von elektronenmikroskopischen Untersuchungen können Malschichten charakterisiert werden und somit Hinweise auf mögliche Schadensursachen liefern. Erste Versuche zum Nachweis von Bor erfolgten mit Hilfe von LIBS-Messungen (Laser Induced Breakdown Spectroscopy) an im Labor hergestellten Glasmalfarben mit unterschiedlichem Boraxgehalt.
Nach 1850 wurde zur weiteren Herabsetzung der Einbrenntemperatur von Glasmalfarben Borax (Na2B4O7 · 10 H2O) zugesetzt. Das Verhältnis war nun 1 Teil SiO2, 3 Teile PbO und 0,5 Teile Borax. Der analytische Nachweis von Bor in eingebrannten Malschichten war bisher jedoch nicht möglich.
In Laborversuchen wurden Glasmalfarben mit unterschiedlichem Gehalt an Borax auf Modellgläser aufgetragen, eingebrannt und anschließend unter simulierten Umweltbedingungen zeitraffend im Klimaschrank bewittert. Mit Hilfe von elektronenmikroskopischen Untersuchungen können Malschichten charakterisiert werden und somit Hinweise auf mögliche Schadensursachen liefern. Der Nachweis von Bor erfolgte mit Hilfe von LIBS-Messungen (Laser Induced Breakdown Spectroscopy) an im Labor hergestellten Glasmalfarben mit unterschiedlichem Boraxgehalt.
Cellulose ethers, like methyl cellulose (MC) or hydroxypropyl cellulose (HPC), are widely used in conservation. They also occur as additives and rheology modifiers in various products like dispersions or gels. Do such products release harmful volatile organic compounds (VOC) during their accelerated aging? A mass testing series utilizing the Oddy test of 60 commercial cellulose ethers ranks the products in safe for permanent use (P, no corrosion), only for temporary use (T, slight corrosion), and unsuitable at all (F, heavy corrosion). Results show that 55% of the products passed the test whereas 33% are for temporary use as slight corrosion occurred on at least one metal coupon and only 11% failed the Oddy test. Raman measurements of the corrosion products identified oxides like massicot, litharge, cuprite, and tenorite among carbonates (hydrocerussite, plumbonacrite), and acetates like basic lead acetate, lead acetate trihydrate as well as lead formate as main phases. For example, commercial, industrial Klucel® G (HPC) scored a T rating through slight corrosion on the lead coupon. Basic lead acetate among other phases indicates the presence of acetic acid. Additional measurements of the sample with thermal desorption GC–MS utilizing the BEMMA scheme confirm the high acetic acid outgassing and reveal the presence of a small amount of formaldehyde.
BEMMA steht für Bewertung von Emissionen aus Materialien für Museumsausstattungen. Es ist die Kurzbezeichnung für ein Schema/Verfahren zur Untersuchung und Bewertung flüchtiger organischer Verbindungen aus Werkstoffen, die im mittelbaren Kontakt mit historischen Materialien des Kunst- und Kulturgutes stehen. Ergebnisse der Untersuchungen seit ca. 2010 bis 2017 werden präsentiert und diskutiert.
Die passive Probenahme von VOC (Volatile Organic Compounds) mit Tenax® TA und Thermodesorption GC/MS Analytik ist eine einfache, kosteneffiziente und repräsentative Methode zur Bestimmung der VOC-Konzentrationen in der Innenraumluft. In der Theorie ist die Stoffaufnahme in den Passivsammler nur abhängig vom Diffusionskoeffizienten der Substanz in Luft und der Geometrie des Sammlers (ideale Adsorption). Um sie zu charakterisieren, wird die Aufnahmerate (UR), definiert als Quotient der Massenaufnahme und dem Produkt aus Konzentration und Expositionszeit, verwendet. Viele effektive Aufnahmeraten (UR,eff) unterscheiden sich beträchtlich von idealen (theoretischen) Werten (UR,id). Literaturwerte sind in nationalen und internationalen Normen lediglich für bestimmte Expositionszeiten vorgegeben, während detaillierte Informationen über den zugehörigen Konzentrationsbereich fehlen. Außerdem ist die Anzahl der insgesamt in der Literatur beschriebenen Substanzen begrenzt. Das Ziel der vorgestellten Studie ist es diesen Fundus an Aufnahmeraten zu begutachten und zu prüfen und ihn durch die Bestimmung eigener qualitätsgesicherter Laborwerte zu ergänzen. Die bestimmten Aufnahmeraten werden als akkurat bezüglich ihrer relativen Standardabweichung und Vergleichbarkeit zu Literaturwerten betrachtet und können für Expositionszeiten von 7 Tagen bei Konzentrationen von 50 100 µg/m³ (ca. 100 300 ppm min) empfohlen werden. Die Sieben Tage Aufnahmeraten aus ISO16017 2 und ASTM D6196 sind nicht generell für diesen Zweck geeignet, wie exemplarisch für Benzol gezeigt wurde.
Gegenstand der vorzustellenden Arbeiten ist die Prüfung der Umweltbeständigkeit und -verträglichkeit von Materialien und Produkten hinsichtlich der Emission von potenziellen Schadstoffen in die Umwelt. Hierzu werden chemisch-physikalische Einflüsse (Bewitterung) und mikrobielle Beanspruchungen an Modellmaterialien evaluiert. So werden die Freisetzungsraten von Schadstoffen in Abhängigkeit der Beanspruchung beschrieben. Als Modellmaterialien kommen die Polymere Polystyrol (PS) und Polypropylen (PP) zum Einsatz, die jeweils mit polybromierten Flammschutzmitteln (PBFSM) versehen sind. Synergistische Effekte der Bewitterungsparameter und der mikrobiologischen Beanspruchung sollen dabei ebenso betrachtet werden, wie die gezielte Alterung. Auch findet eine Beschreibung des Verhaltens der ausgetragenen Schadstoffe in den Umweltkompartimenten Boden oder Wasser statt. Hier sind mit Hilfe der zu entwickelnden Screening- und non-Target-Analyseverfahren die Transformation und der Metabolismus durch Mikroorganismen zu beschreiben. Auch soll mit Hilfe der RFA und der LA-ICP-MS die Abreicherung der PBFSM in den Modellmaterialien beschrieben werden. Aus den Ergebnissen sollen Korrelationen zwischen den künstlichen Alterungsverfahren und realen Szenarien abgeleitet werden.
Gegenstand der vorzustellenden Arbeiten ist die Prüfung der Umwelt-beständigkeit und -verträglichkeit von Materialien und Produkten hinsichtlich der Emission von potenziellen Schadstoffen in die Umwelt. Hierzu werden chemisch-physikalische Einflüsse (Bewitterung) und mikrobielle Beanspruchungen an Modellmaterialien evaluiert. So werden die Freisetzungsraten von Schadstoffen in Abhängigkeit der Beanspruchung beschrieben. Als Modellmaterialien kommen die Polymere Polystyrol (PS) und Polypropylen (PP) zum Einsatz. Synergistische Effekte der Bewitterungsparameter und der mikrobiologischen Beanspruchung sollen dabei ebenso betrachtet werden, wie die gezielte Alterung. Auch findet eine Beschreibung des Verhaltens der ausgetragenen Schadstoffe in den Umweltkompartimenten Boden oder Wasser statt. Hier sind mit Hilfe der zu entwickelnden Screening- und non-Target-Analyseverfahren die Transformation und der Metabolismus durch Mikroorganismen zu beschreiben. Aus den Ergebnissen sollen Korrelationen zwischen den künstlichen Alterungsverfahren und realen Szenarien abgeleitet werden.
The objective of this study is to find out, to what extent the geochemical characteristics of lapis lazuli can be utilized in respect to its provenance. A wide range of variables is taken into consideration depending on the quantity of samples analysed from a specific geological region and the methods applied. In order to provide evidence, a multi-technique analytical approach using µXRF, ESEM, PGAA and PIXE is applied to samples from the most famous deposits of lapis lazuli. Special elements determined as fingerprints are compared in relation to the forming conditions obvious in textural features. The results and statistical output allow a differentiation that enables an optimized local classification of the blue stone. An absolute requirement for all geo-tracing performed on blue colored cultural objects of unknown provenance is awareness of the limits of analysis. The possible sources of lapis lazuli are tested by analysing the blue pigment used as paint on murals and ink on manuscripts from the Silk Road.
11 laser printers from 5 manufacturers were purchased in 2017 and tested for their UFP emissions. Size resolved sampling of the emitted particles was done with a 13 stage (30 nm to 10 µm) low pressure cascade impactor. The sampled particles were analysed for their chemical composition by thermal extraction (vaporization at 290°C) followed by GC-MS analysis. High boiling cyclic siloxanes (D10 to D16) were detected as constituents of UFP from laser printers. In comparison to measurements in 2008, aliphatic long-chain alkanes (C22 to C34) were detected additionally as chemical constituents of UFP from most of the tested printers and their amounts were higher than for cyclic siloxanes. Printers of one manufacturer showed very low UPF emissions compared to the other manufacturers.
11 laser printers from 5 manufacturers were purchased in 2017 and tested for their UFP emissions. Size resolved sampling of the emitted particles was done with a 13 stage (30 nm to 10 µm) low pressure cascade impactor. The sampled particles were analysed for their chemical composition by thermal extraction (vaporization at 290°C) followed by GC-MS analysis. High boiling cyclic siloxanes (D10 to D16) were detected as constituents of UFP from laser printers. In comparison to measurements in 2008, aliphatic long-chain alkanes (C22 to C34) were detected additionally as chemical constituents of UFP from most of the tested printers and their amounts were higher than for cyclic siloxanes. Printers of one manufacturer showed very low UPF emissions compared to the other manufacturers.
Previous studies have shown that desktop 3D printers (Fused Filament Fabrication) emit high numbers of particulate matter, mainly as ultrafine particles (UFP, particle diameter less than 100 nm). However, the chemical composition of emitted particles has been less extensively investigated. In this study, we therefore focused on the chemical composition of particles emitted from 3D printing. The measurements were conducted in a 1 m³ emission test chamber. Emitted particles were sampled by a 13-stage low-pressure cascade impactor onto aluminum foils and then analyzed by TD-GC/MS to identify their organic compounds. Nine commercial filaments made from basic polymers such as Acrylonitrile Butadiene Styrene (ABS), Acrylonitrile Styrene Acrylate (ASA), Polycarbonate (PC), Poly(methyl methacrylate) (PMMA), Nylon, High Performance Polystyrene (HIPS) and a copper-filled Polylactide (PLA) were investigated. The results show that the organic components of the particles are primarily plastic additives such as plasticizer, antioxidant agents, lubricants, UV-absorbers and UV-stabilizers from the filaments.
Previous studies have shown that desktop 3D printers (Fused Filament Fabrication) emit high numbers of particulate matter, mainly as ultrafine particles (UFP, particle diameter less than 100 nm). However, the chemical composition of emitted particles has been less extensively investigated. In this study, we therefore focused on the chemical composition of particles emitted from 3D printing. The measurements were conducted in a 1 m³ emission test chamber. Emitted particles were sampled by a 13-stage low-pressure cascade impactor onto aluminum foils and then analyzed by TD-GC/MS to identify their organic compounds. Nine commercial filaments made from basic polymers such as Acrylonitrile Butadiene Styrene (ABS), Acrylonitrile Styrene Acrylate (ASA), Polycarbonate (PC), Poly(methyl methacrylate) (PMMA), Nylon, High Performance Polystyrene (HIPS) and a copper-filled Polylactide (PLA) were investigated. The results show that the organic components of the particles are primarily plastic additives such as plasticizer, antioxidant agents, lubricants, UV-absorbers and UV-stabilizers from the filaments.
Comparison of Formaldehyde Concentrations in Emission Test Chambers Using EN 717-1 and EN 16516
(2018)
For many years EN 717-1 (Wood-based panels - Determination of formaldehyde release - Part 1: Formaldehyde emission by the chamber method) is the standard for formaldehyde emission testing of wooden boards. In 2017 EN 16516 (Construction products - Assessment of release of dangerous substances - Determination of emissions into indoor air) was published as a new harmonised standard for the emission testing of construction products. Because test chamber conditions are different, both standards give different concentrations for formaldehyde. For the determination of a conversion factor four test series were set up with different wooden boards.
Comparison of Formaldehyde Concentrations in Emission Test Chambers Using EN 717-1 and EN 16516
(2018)
For more than 25 years EN 717-1 (Wood-based panels - Determination of formaldehyde re-lease - Part 1: Formaldehyde emission by the chamber method) is the standard for formalde-hyde emission testing of wooden boards. In 2017 EN 16516 (Construction products - Assess-ment of release of dangerous substances - Determination of emissions into indoor air) was published as a new harmonised standard for the emission testing of construction products. Because test chamber conditions are different, both standards give different concentrations for formaldehyde. To determine a conversion factor four test series were set up with different wooden boards. For a loading of 1 m²/m³ the conversion factor is 1.6. This means that the formaldehyde concentration measured under the conditions of EN 16516 is a factor of 1.6 higher compared to EN 717-1.
In this work, we use a gas sensor system consisting of a commercially available gas sensor in temperature cycled operation. It is trained with an extensive gas profile for detection and quantification of hazardous volatile organic compounds (VOC) in the ppb range independent of a varying background of other, less harmful VOCs and inorganic interfering gases like humidity or hydrogen. This training was then validated using a different gas mixture generation apparatus at an independent lab providing analytical methods as reference. While the varying background impedes selective detection of benzene and naphthalene at the low concentrations supplied, both formaldehyde and total VOC can well be quantified, after calibration transfer, by models trained with data from one system and evaluated with data from the other system. The lowest achievable root mean squared errors of prediction were 49 ppb for formaldehyde (in a concentration range of 20–200 ppb) and 150 μg/m³ (in a concentration range of 25–450 μg/m³) for total VOC. The latter uncertainty improves to 13 μg/m³ with a more confined model range of 220–320 μg/m³. The data from the second lab indicate an interfering gas which cannot be detected analytically but strongly influences the sensor signal. This demonstrates the need to take into account all sensor relevant gases, like, e.g., hydrogen and carbon monoxide, in analytical reference measurements.
Aluminum is an often-used building material in modern architecture. In recent years buildings from the 1950th and 1960th are increasingly subject of conservation works including the aluminum parts. Typical surface damages are signs of corrosion caused by weathering processes or scratches in the anodized layer due to extensive wear. To repair damaged aluminum surfaces, there are usually two options: smaller areas are repaired by using a touch-up pen, for larger damages it is necessary to remove the anodized layer completely. Both possibilities are disadvantageous for the objects; the touch-up pen often does not match the color together with an insufficient corrosion protection, while newly anodized layers often differ in color and gloss from the original surface.
For this reason, a research project was initiated to develop a mobile method to repair anodized aluminum parts. The first step focusses on the mobile anodization process by using the electrolyte with a gel substrate. Different cathodic materials are to be tested together with appropriate cooling material. The anodized area should be isolated to protect undamaged areas. Examinations of the produced layers are conducted by using Keyence microscope, eddy current testing and ESEM analysis. Further steps are to transform the coloring and sealing process for mobile application. Color could be applied by using a brush or by spray while the sealing process could be performed with water vapor. An heatable putty knife could be used, if heating up the area will be necessary. Once the application process is developed, the anodization will be tested on samples with artificial damages, fixed in horizontal and vertical positions. The stability of the anodized surface will be examined by accelerated ageing in a climate chamber and outdoor weathering.
The electrolyte (diluted sulfuric acid) was combined with a gel binder to enable a mobile application. Several thickening agents were tested concerning their conductivity and stability in acid systems. Anodization tests with different cathodic material and shapes were conducted. The temperature during anodization was controlled and adjusted if necessary. The anodized area was restricted by using either a lacquer, an adhesive or a removable silicon barrier. The fist results show the feasibility of the method on enclosed areas. The achieved thickness was measured by eddy current testing and the structure was controlled by ESEM analysis. The examinations show a connection between thickness and porosity of the anodized layers and the temperature during the application process.
Next steps are testing mobile coloring and sealing methods followed by mobile anodization on artificial damaged areas.
In industrialised countries more than 80% of the time is spent indoors. Products, such as building materials and furniture, emit volatile organic compounds (VOCs), which are therefore ubiquitous in indoor air. VOC in combination may, under certain environmental and occupational conditions, result in reported sensory irritation and health complaints. Emission concentrations can become further elevated in new or refurbished buildings where the rate of air exchange with fresh ambient air may be limited due to improved energy saving aspects. A healthy indoor environment can be achieved by controlling the sources and by eliminating or limiting the release of harmful substances into the air. One way is to use (building) materials proved to be low emitting. Meanwhile, a worldwide network of professional commercial and non-commercial laboratories performing emission tests for the evaluation of products for interior use has been established. Therefore, comparability of test results must be ensured. A laboratory’s proficiency can be proven by internal and external validation measures that both include the application of suitable emission reference materials (ERM). For the emission test chamber procedure according to EN 16516, no artificial ERM is commercially available. The EU-funded EMPIR project MetrIAQ aims to fill this gap by developing new and improved ERMs. The goal is to obtain a material with a reproducible and temporally constant compound release (less than 10% variability over 14 days). Different approaches, such as the impregnation of porous materials, are being tested. The generation as well as results of the most promising materials will be presented.
Test chamber measurements are an important tool to improve indoor air quality and occupational safety. Test chamber measurements are possible for a wide range of materials, products and technologies. Determination of concerning contaminants is important to ensure good indoor air quality. The detection of concerning contaminants depends on the approriate sampling and analysis.
Nonporous corundum powder was functionalized covalently with protein binders to isolate and enrich specific proteins from complex matrices.The common crosslinker glutaraldehyde was compared with a hyperbranched polyglycerol (PG) of around 10 kDa. The latter was oxidized with periodate to generate aldehyde groups that can covalently react with the amines of the surface and the amino groups from the protein via a reductive amination process. The amount of bound protein was quantified via aromatic amino acid analysis (AAAA). As a proof of concept, IgG was extracted with protein A from crude human plasma. The advantages of corundum include the very low price, extremely high physical and chemical stability, pressure resistance, favorable binding kinetics, convenient handling, and flexible application.
Electron microscopy (EM) is the gold standard for the characterisation of the morphology (size and shape) of nanoparticles. Visual observation of objects under examination is always a necessary first step in the characterisation process. Several questions arise when undertaking to identify and count particles to measure their size and shape distribution. In addition to challenges with the dispersion and identification of the particles, more than one protocol for counting particles is in use. This paper focuses on precise rules for the counting of particles in EM micrographs, as this influences the measurement accuracy of the number of particles, thus implicitly affecting the size values of the counted particles. We review and compare four different, commonly used methods for counting, which we then apply in case studies. The impact of the selected counting rule on the obtained final particle size distribution is highlighted. One main aim of this analysis is to support the application of a specific, well-defined counting approach in accordance with regulatory
requirements to contribute to achieving more reliable and reproducible results. It is also useful for the new harmonised measurement procedures for determining the particle size and particle size distribution of nanomaterials.
EN 16516 sets the test method and requirements for the determination of emissions of Volatile Organic Compounds (VOCs) from building materials into indoor air. To address the quality control requirements for the class of semi-VOCs (SVOCs), VSL developed gaseous reference materials. A novel home-made dynamic gas mixture preparation system, operating according to ISO 6145-4 (continuous injection method), has recently been developed and validated. Thanks to the stable temperature control up to 100 oC, the system can prevent condensation of the SVOCs in air at indoor air concentration levels. The in-situ obtained SVOC gas standards can be sampled in sorbent tubes to obtain SVOC transfer standards. A study was performed to determine the optimal sorbent material and storage conditions. This study will be presented together with the results of the 2018 Round Robin test for emission test chamber measurements organised by BAM. Using the novel system, VSL prepared transfer standards with known amounts of VOCs and SVOCs for participants to evaluate their analytical performance.
Data for the publication "The role of extracellular polymeric substances of fungal biofilms in mineral attachment and weathering" (https://doi.org/10.1038/s41529-022-00253-1). It includes:
- The Summary of the EPS concentration, EPS sugar components and EPS linkages.
- The Summary of the XPS analysis of freeze-dried biofilm samples of all strains.
- The Summary of the pH, Mg, SI and Fe concentration, biomass and olivine dissolution rate for each time point of all dissolution experiments.
Angesichts der zunehmenden Digitalisierung und dem Einsatz datenintensiver Methodiken in der Wissenschaft stehen Forschende vor der Herausforderung, stetig wachsende Datenmengen nachvollziehbar zu dokumentieren, langfristig zu speichern und für Dritte nachnutzbar zu machen. Um diesen Anforderungen gerecht zu werden, bietet sich die Nutzung von Software-Lösungen an, welche Forschungsdatenmanagement mit der digitalen Dokumentation von Laborinventar und Experimenten in elektronischen Laborbüchern (engl. electronic lab notebooks (ELN)) verknüpfen.
Axial passive sampling of VOCs with Tenax® TA and thermal desorption GC-MS analysis is an accepted alternative to active sampling in occupational hygiene. In theory, the uptake into the passive sampler is only dependent on the diffusion coefficient of the analyte in air and the geometry of the sampler (ideal adsorption). For characterization, the uptake rate (UR) is used defined as the ratio of the mass adsorbed and the product of ambient concentration and exposure time. Various reported effective uptake rates (UR,eff) differ to an increasing degree from ideal values (UR,id) with increasing exposure doses (denominator of the given definition of UR), (Tolnai, 2001). In national and international standards, uptake rates are essentially sorted by the applicable exposure time, while detailed information about the corresponding concentration range is lacking. Moreover, especially for long exposure periods as applied in indoor air monitoring, the number of itemized substances is limited. Therefore it is the aim of this contribution to review and expand uptake rate data by comparison of literature and own laboratory values of assured quality. Passive samplers were exposed to nine single compound atmospheres of known concentrations for seven days. Concentrations were checked twice a day via active sampling.The determined uptake rates are considered accurate in terms of RSD and comparability to literature values and can be recommended for exposure times of seven days at 50 – 100 μg m-3 (approximately 100 – 300 ppm min). Seven-day uptake rates in ISO16017-2 and ASTM D6196 are not generally suited for this purpose, as has been exemplarily shown for benzene. Thus, it is crucial for optimization of the method to produce more reliable uptake rate data, including specific information about applicable exposure times and concentrations, which will be promoted in the course of this ongoing study.
The reliable measurement of very volatile organic compounds (VVOC) in indoor air by use of thermal desorption gas chromatography (TD-GC) in order to include them into evaluation schemes for building products even nowadays is a great challenge. For capturing these small molecules with carbon numbers ranging from C 1 –C 6 , strong adsorbents are needed. In the present study, recovery rates of nine suitable adsorbents of the groups of porous polymers, graphitised carbon blacks (GCB) and carbon molecular sieves (CMS) are tested against a complex test gas standard containing 29 VVOC. By consideration of the recovery and the relative humidity (50% RH), combinations of the GCB Carbograph 5TD, the two CMS Carboxen 1003 and Carbosieve SII as well as the porous polymer Tenax® GR were identified to be potentially suitable for sampling the majority of the VVOC out of the gas mix. The results reveal a better performance of the adsorbents in combination than being used alone, particularly under humid sampling conditions. The recovery rates of the chosen compounds on each adsorbent should be in the range of 80–120%.
Several aspects were explored towards the standardization of a suitable procedure. The use of gaseous standards is necessary and a standard gas mixture containing 60 substances was successfully generated and employed for further investigations. The suitability of different chromatography columns was addressed: The use of PLOT (Porous Layer Open Tubular) columns is well suitable for VVOC analysis. The recoveries of the 60 analytes on several adsorbents and their combinations were determined: A combination of a graphitized carbon black and a carbon molecular sieve showed great results for all analytes. Carbon molecular sieves adsorb water which can impair the analysis. Different options such as purging, the use of a drying system or splitting were investigated for water removal. This contribution will present experimental results supporting the standardization of a method for VVOC analysis.
Since 1997, the Committee for Health-related Evaluation of Building Products (AgBB) has been developing the basis for building regulations for protection against indoor health risks that may arise when building products are used. In 2009, the AgBB decided to include relevant VVOCs in the assessment procedure. The ISO 16000-6 (2021) states that the use of the thermal desorption gas chromatography technique is appropriate for VVOCs, if adaptations are considered. However, a suitable method for the trustworthy quantification of VVOC emissions from building products and in the indoor air is still missing.
This webinar will present the results of a research project on the development of a procedure for VVOC analysis:
• identification of the gaps towards standardization
• investigations on gas standards and the suitability of chromatography columns
• investigations on sorbent combinations and water management
• validation of the method and screening of VVOC emissions from building products.
In this research project, a new OECD Test Guideline (TG) for the determination of “Particle Size and Particle Size Distributions of Nanomaterials” was developed as the existing OECD TG 110 is considered to be outdated in terms of applicable size range (not covering sizes <200 nm) and methods. By its scope with an applicable size range from 1 to 1000 nm the new Test Guideline (TG PSD) covers the whole nanoscale. The TG PSD is applicable for particulate and fibrous nanomaterials. The prescribed, pairwise measurement of fibre diameter and length in the TG PSD allows for the first time to differen-tiate fibres with regard to their size-dependent hazard properties. Measurement instructions for each included method were validated within two separated interlaboratory comparisons, as a distinction between near spherical particles and fibres when applying the methods has to be made.
Besides information on content and structure of the TG PSD, this final report outlines essential steps, considerations and organisational aspects during the development of the TG. Insights into the selec-tion, preparation and prevalidation of test materials used in the interlaboratory comparison are given. Finally, main results of the interlaboratory comparisons and their impacts on the TG PSD are pre-sented.
The ISO 16000-6 standard describes a method for the determination of volatile organic compounds (VOCs) in indoor and test chamber air by sorbent-based active sampling, thermal desorption and gas chromatography coupled with mass spectrometry (GC/MS). It also gives directions to adapt this methodology to very volatile organic compounds (VVOCs). Indeed, toxicologically based guideline values are being implemented for these compounds and it becomes necessary to measure them. But a comprehensive and robust measurement method is lacking. Investigations on the use of gaseous standards, the suitability of chromatography columns, the suitable sorbent combinations and the water removal are required. The talk will highlight the points that need to be explored towards the standardisation of a suitable procedure and provide appropriate preliminary results.
Today glass is broadly used in modern architecture. For applications indoor it is possible to produce decor glass by using enamel colors and glass painting techniques without any problems. However, this is more limited for applications outdoor. Humidity and environmental pollution attack the surface of the coating and damage it strongly. There are only few colors on the market which are resistant towards acids and bases until now. Additionally, most of those colors are opaque. In order to extend the color palette, chemically resistant colored glasses are being developed which are transparent, relatively low melting and intensively toned even in thin coat thickness. To achieve such ambitious aim, many parameters have to match which act in complex manner. Metal oxides were used to color the glasses. A lead-free glass composition was developed to avoid an exposition of heavy metals to the environment. The glasses were characterized, in particular in terms of their thermal properties, their crystallization and corrosion behavior as well as their chemical and environmental durability. Different practical applications will be shown.
Fluorometric sensing is a versatile approach for trace analysis outside of the laboratory, requiring suitable sensor materials and their integration into sensing devices. The versatility of fluorophores as probes, especially in terms of the possibility to tailor their optical as well as their recognition properties by synthetic modifications in a wide range, renders them as superior active component for the preparation of optical sensing devices. Recent works at BAM in this field include, for example, the detection of nerve gas agents, illustrating impressively the aforementioned benefits of fluorophores in optical sensing applications.
In the interdisciplinary project presented here, we target hazardous gases such as ammonia, benzene, and hydrogen sulfide, next to others, which pose a major threat to human health and environmental safety and for which the availability of a sensitive and reliable detection method is highly desirable. The dyes presented follow a “turn-on” fluorescence schematic, which allows for the selective and sensitive detection of the respective gaseous analyte. The immobilization of the probe in polymeric matrices is then the next step toward the fabrication of a prototype device for molecular sensing. Further steps in the project include the assembly of instruments for test-atmosphere generation, the referencing of the sensor system, development and implementation of an optical setup, and the testing of the prototype device under laboratory conditions and in the field.
In this presentation, we give an overview over the recent developments on this topic in our groups. Highlights are hydrogen sulfide sensitive, BODIPY based transition metal complexes, which allow for a sensitive as well as selective detection of the toxic gas. In addition, we present a novel class of highly substituted BODIPY derivatives – pocket-BODIPYs – which are of a synthetically high versatility and can readily be modified to create pockets in the periphery of the molecule of defined geometries. This is illustrated on the successful encapsulation of benzene by a pocket-BODIPY derivative, confirmed by X-ray crystallographic analysis as well as by further spectroscopic and analytical methods.
Die Bestimmung der Nanopartikelgrößen- und -formverteilung nach OECD TG 125 mit einem Differentiellen Mobilitäts Analyse System (DMAS), auch bekannt als SMPS, wird vorgestellt:
- Generelles Messprinzip
- Welchen Durchmesser misst die Methode?
- Welche Partikel kann diese Methode messen?
- Welche Informationen kann diese Methode liefern?
- Wo stößt die Methode an ihre Grenzen?
- Implementierung und Datenauswertung,
- Reporting.
Anschließend wurde eine Q&A-Session für DMAS/SMPS organisiert.
Final Draft of the OECD Test Guideline for Particle Size and Particle Size Distribution of Nanomaterials.
The OECD Working Party on Manufactured Nanomaterials (WPMN) has actively worked towards understanding possible safety issues for manufactured nanomaterials and has contributed significantly to resolving these by developing Test Guidelines, Guidance Documents, Test Reports and other publications with the aim of a safe use of manufactured nanomaterials. The OECD website (www.oecd.org/science/nanosafety) and the referenced publications contain more background information.
Among others, the OECD Test Guideline “Particle Size Distribution/Fibre Length and Diameter Distributions” (TG 110, adopted in 1981) was identified to require an update to address the specific needs of manufactured nanomaterials as the TG 110 is currently only valid for particles and fibres with sizes above 250 nm. The WPMN prioritised to either update TG 110 to be applicable also to particles at the nanoscale or draft a new nanomaterial specific Test Guideline (TG). Eventually, it was decided to develop a new TG for particle size and particle size distribution measurements of nanomaterials covering the size range from 1 nm to 1000 nm for further justification. This TG overlaps with TG 110 in the size range from 250 nm to 1000 nm. When measuring particulate or fibrous materials, the appropriate TG should be selected depending on the size range of particles tested. In line with TG 110, the new TG for nanomaterials includes separate parts for particles and fibres. For the part of this TG which addresses particles, several methods applicable to nanomaterials were reviewed and included to take into account developments since 1981 when the TG110 was adopted. This TG includes the following methods: Atomic Force Microscopy (AFM), Centrifugal Liquid Sedimentation (CLS)/Analytical Ultracentrifugation (AUC), Dynamic Light Scattering (DLS), Differential Mobility Analysis System (DMAS), (Nano)Particle Tracking Analysis (PTA/NTA), Small Angle X-Ray Scattering (SAXS), Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM).
For measuring the diameter and length of fibres, analysing images captured with electron microscopy is currently the only method available. This TG includes Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM).
To test the validity of this TG, an ILC was performed. Test materials were chosen to reflect a broad 68 range of nanomaterial classes, e.g. metals, metal oxides, polymers and carbon materials. Where possible, well-characterised test materials were used. Additionally, the test materials were chosen, so that they reflect a broad range of sizes representing the size range 1 nm to 1000 nm and finally,
for fibres only, aspect ratios from length/diameter of 3 to > 50.
The church of Koszewko (Poland) is a brick building edified in the 15th century built on cobblestone foundations. There are five windows in the sanctuary. Three of them enclose heraldic panels from the Küssow’s family from the 15th century which are surrounded with Goethe glass from the 18th century to complete the windows. The colored heraldic panels are strongly damaged and corroded with massive paint layer losses, glass- and leadbreakages. Those medieval glass fragments have been shortly discovered and are of particular interest for Poland since only few medieval glazing have been conserved.
The damages as well as the glass compositions have been investigated with ESEM/EDX. Two categories of medieval glass compositions have been identified. The blue glass is particularly sensible to corrosion because of his high content in K2O. The colorless and the red glass samples belong to a stable glass type. Due to the thickness of the gel layer, it is easy to see that the degradation is strongly proceeded. The protection of those medieval stained-glass panels is absolute necessary.
The medieval panels have been restored and surrounded from a copper frame. Then they have been fixed on the wood frame in the church. The exterior glazing has been closed with a panel of Goethe glass. The gap between the Goethe- and the medieval glass is about 3 cm. The Goethe glass panel has been stabilized with a film based on polyester to protect the medieval glasses against any damages. In this way, a low cost protective glazing has been installed for a long-term conservation of each medieval stained-glass panels. The climate measurements over the period of one year on the restored windows are in process. The temperature and the relative humidity are recorded in the church interior, in the gap between the original and the Goethe glass and outdoors.
In Vorbereitung einer Restaurierung erfolgten naturwissenschaftliche Untersuchungen zu Schadensphänomenen und Glaszusammensetzungen an mittelalterlichen Gläsern aus der Dorfkirche in Koszewko (Polen)im Environmental Scanning Electron Microscope (ESEM) mit EDX. Die Ergebnisse zeigen, dass die Glasverwitterung schon sehr stark vorangeschritten ist und ein zukünftiger Schutz der mittelalterlichen Glasmalereifelder vor Umwelteinflüssen unbedingt notwendig ist. Es wurde ein Schutzverglasungsystem entwickelt, das speziell auf den langfristigen Erhalt der einzelnen mittelalterlichen Glasmalereifelder ausgelegt ist.
Quantitative chemical analysis of airborne particulate matter (PM) is vital for the understanding of health effects in indoor and outdoor environments and required by EU air quality regulations. Typically, airborne particles are sampled on filters, followed by lab-based analysis, e.g., with inductively coupled plasma mass spectrometry (ICP-MS). Within the EURAMET EMPIR AEROMET project, cascade impactor aerosol sampling was combined with on-site total reflection X-ray fluorescence (TXRF) spectroscopy. The study aimed at a proof of principles for this new mobile and on-size tool for the quantification of aerosol element compositions and element mass concentrations within short time intervals of less than 12 h. In a field campaign the method’s technical feasibility could be demonstrated. The TXRF results were traced back to a stationary, reference-free XRS setup in the laboratory of the German national metrology institute PTB at the BESSY II electron storage ring in Berlin, Germany. Simultaneous PM10-filter sampling, followed by standardized lab-based analysis, allowed for a comparison of the field campaign data of both methods. As Fig. 1 shows, the correspondence between PM10 filter sampling and ICP-MS, and on the other hand, cascade impactor sampling and TXRF is quite encouraging. However, for some of the analysed elements, e.g. V and Pb, the observed deviations are higher than expected and this highlights the fact, that spectral deconvolution strategies for TXRF on cascade impactor samples still need some improvement.
This work was supported by the EMPIR programme, co-financed by the Participating States and from the European Union’s Horizon 2020 research and innovation programme, through grant agreements 16ENV07 AEROMET and 19ENV08 AEROMET II
Reliable measurement of the size of polydisperse, complex-shaped commercial nanopowders is a difficult but necessary task, e.g., for regulatory requirements and toxicity risk assessment. Suitable methods exist for the accurate characterization of the size of non-aggregated, stabilized, spherical and monodisperse nanoparticles. In contrast, industrial nanoscale powders usually require dedicated sample preparation procedures developed for the analysis method of choice. These nano-powders tend to agglomerate and/or aggregate, a behavior which in combination with an innate broad particle size distribution and irregular shape often significantly alters the achievable accuracy of the measured size parameters. The present study systematically tests two commercially available nanoscale powders using different sample preparation methods for correlative analysis by scanning electron microscopy, dynamic light scattering, Brunauer–Emmet–Teller method and differential mobility analysis. One focus was set on the sample preparation by embedding nanoparticles in carbon-based hot-mounting resin. Literature on this topic is scarce and the accuracy of the data extracted from cross sections of these particles is unclearly stated. In this paper systematic simulations on the deviation of the size parameters of well-defined series of nanoparticles with different shapes from the nominal value were carried out and the contributing factors are discussed.
The chemical emissions from products are tested by means of emission test chambers under defined conditions (climate, loading, air change rate). The standard method for the determination of volatile organic compounds (VOC) is the sampling onto Tenax-tubes followed by thermal desorption (TDS) and gas chromatography-mass spectrometry (GC-MS) analysis. The EU-LCI list includes some very volatile organic compounds (VVOC) and some VOC for which there are limitations when using the standard method. For VVOC additional sampling is required using stronger absorbers like Carbotrap or multi-bed adsorption tubes. The analysis of VVOC also requires a different GC oven program and a different column for the separation. For the determination of formaldehyde and other low boiling aldehydes (e.g. acetaldehyde, acetone, propanal, propenal) DNPH-cartridges are used which are extracted with acetonitrile followed by liquid chromatography (HPLC-UV) analysis. The derivatisation of propenal and other unsaturated aldehydes (e.g. 2-butenal) with DNPH might lead to lower findings due to incomplete derivatization and forming of by-products. For a better quantification of acetic acid the use of ion chromatography (IC) is recommended because the analysis of acetic acid with the standard method (TDS) leads to lower findings due to break through during sampling. The use of ion chromatography for the analysis of organic acids requires a third sampling technique. The acids are adsorbed onto silica-gel and extracted with water.
3D-printing or additive manufacturing has many promising and unique advantages. Especially low cost molten polymer Deposition Printers are increasingly populär in the private and educational sector.
Their environmental friendliness can be questioned due to recently reported ultrafine particle and suspected VOC emissions, To further investigate 3D-printing as a potential indoor air pollution source we characterized fine and ultrafine particle emissions from a molten polymer deposition printer producing a 3D object with ten marketable polymer filament materials under controlled conditions in a test chamber. VOC emissions from the filaments have also been compared. Using a straightforward emission model time dependent and averaged particle emission rates were determined. The results indicate that under comparable conditions some filament materials produce mainly ultrafine particles up to an average rate of 1013 per minute. This value is in the upper ränge of typical indoor ultrafine particle sources (e.g. Smoking, frying, candle light, laser printer). The observed material-specific rates differ by five Orders of magnitude. Filament-specific gaseous emissions of organic compounds such as bisphenol A, styrene and others were also detected.
Our results suggest a detailed evaluation of related risks and considering protective measures such as housing and filtering.
The ISO 16000 standard series provide guidelines for emission measurements of volatile organic compounds (VOCs) from building materials. However, polymer-based consumer products such as toys may also release harmful substances into indoor air. In such cases, the existing standard procedures are unsuitable for official control laboratories due to high costs for large emission testing chambers. This paper aims at developing and comparing alternative and more competitive methods for the emission testing of consumer products. The influence of the emission chamber size was investigated as smaller chambers are more suited to the common size of consumer products and may help to reduce the costs of testing. Comparison of the performance of a 203 l emission test chamber with two smaller chambers with the capacity of 24 l and 44 ml, respectively, was carried out by using a polyurethane reference material spiked with 14 VOCs during the course of 28 days. The area-specific emission rates obtained in the small chambers were always similar to those of the 203 l reference chamber after a few hours. This implies that smaller chambers can provide at least useful numbers on the extent of polymer-based consumer product emissions into indoor air, thereby supporting meaningful exposure assessments.
Menschen, die in der gemäßigten Klimazone leben, verbringen bis zu 90% ihres Lebens in Innenräumen. Deshalb hat das Innenraumklima eine sehr große Bedeutung für deren Wohlergehen, Gesundheit und Leistungsfähigkeit. In Deutschland wird ca. 40% der eingesetzten Primärenergie für das Heizen, Kühlen und Klimatisieren der Innenräume verwendet.
Das Forschungsvorhaben hat eine Laufzeit vom Oktober 2013 bis März 2017. Es wird in Kooperation mit der Bundesanstalt für Materialforschung und –prüfung (BAM) und der Hochschule für Technik und Wirtschaft Berlin (HTW Berlin) durchgeführt. Die HTW Berlin koordiniert das Projekt. Die Rheinisch-Westfälische Technische Hochschule Aachen (RWTH) wird teilweise über einen Auftrag in das Projekt integriert.
Ziel des Projektes ist es Baustoffe auf ihre Geruchsemissionen zu untersuchen, um Bauprodukte mit niedrigen Emissionen und Gerüchen identifizieren zu können. Den Verbraucherinnen und Verbrauchern wird somit die Möglichkeit gegeben emissions- und geruchsarme Baustoffe zu wählen.
Die Aufgabenstellung des Projektes ist nachfolgend aufgeführt:
Arbeitspaket 1: Geruchsmessung bei Produkten mit dem Blauen Engel (siehe Kapitel 4 und 5);
Arbeitspaket 2: Untersuchung von Vergleichsmaßstäben (siehe Kapitel 6);
Arbeitspaket 3: Untersuchung der Linearität der Acetonskala (siehe Kapitel 7);
Arbeitspaket 4: Erstellung einer Produktdatenbank (siehe Kapitel 8).
Die Geruchsuntersuchung ist in den Vergabekriterien für den „Blauen Engel“ für textile Bodenbeläge (RAL UZ-128) eingebunden worden. Aus den weiteren Untersuchungen sind für die Normung wichtige Erkenntnisse erarbeitet worden.
Mit dem Fokus auf eine saubere Innenraumluft wird darauf eingegangen, welche Emissionen aus Materialien und Produkten es gibt und wie sie nach Art und Flüchtigkeit definiert sind und wie sie gemessen werden. Im weiteren wird dargestellt, was und wie viel aus Materialien und Produkten emittieren kann und wie die Emissionen zu bewerten sind. Hierbei wird auch auf besonders emissionsarme Materialien und Produkte eingegangen.
Ziel des Projektes war es, schwermetallfreie Schmelzfarben für den Einsatz auf einem Digitaldrucker zu entwickeln. Dafür sollten die Glasfarben, bei Temperaturen unter 630°C verarbeitbar und deren Eigenschaften kompatibel mit denen von Floatgläsern sein. Zudem sollte die aufgeschmolzene Farbe transparent und im Außenbereich eingesetzt beständig sein. Weiterhin mussten die Farben eine Partikelkorngröße kleiner als 20µm besitzen, um die Druckköpfe des Digitaldruckers nicht zu verstopfen. Gute Dispergierbarkeit, thixotropes Verhalten und eine schnelle Trocknung waren weitere Voraussetzungen. Die Ersetzung von PbO durch ZnO und Bi2O3 wurde getestet und zeigte positive Ergebnisse. Ein geeigneter Mahl-und Dispergierprozess wurde entwickelt. Bei der Firma „glas&räume“ wurden die Musterfarben getestet und zeigten ein gutes Druckverhalten. Bedingt durch das Tintenstrahlverfahren erreicht der Farbauftrag keine 100%ige Transparenz. Trotzdem erscheint die transparente keramische Schmelzfarbe im Vergleich zur Verwendung von opaker Schmelzfarbe tatsächlich völlig transparent. Der Unterschied ist signifikant und öffnet so ein neues Kapitel im keramischen Digitaldruck.
Environmental sustainability and –stability of Materials concerning the Migration of pollutants
(2018)
MaUS is an acronym for ”Material und Umweltsimulationen“. Plastics are in the focus of environmental politics due to their long-term behaviour and therefore to their persistence. Not only that they appear as visible contaminants in the sea and on the beach, but their unknown behaviour concerning their additives as well as the related transformation products are anxious. Therefore, we wish to establish a certified reference method to provide a method for testing plastics.
Aim of this project is the development of fast motion standard reference methods for testing plastics regarding to their environmental compatibility. To establish these testing methods, we use polystyrene (PS) and polypropylene (PP) with environmental relevant brominated flame retardants, known for their persistent bioaccumulative and toxic (PBT) properties. In case of PS the material contains 1 wt% of 1,2,5,6,9,10-hexabromocyclododecan (HBCD) and in case of PP 0.1 wt% bromodiphenylether (BDE-209), which is known as a substance of very high concern (SVHC). Furthermore, we use polycarbonate (PC), which is still used as material in baby flasks and releases Bisphenol A (BPA), an estrogenic active substance.
As an additional material PTFE is used for its importance as a source for two ubiquitous environmental substances (PFOS and PFOA), whose toxicological effects are still incompletely known.
The focus in this current work is set on the transfer of potential pollutants out of applied materials mentioned above into environmental compartments like water or soil. Here an accelerated aging concept should be developed to shortened time consuming natural processes. For these resulting simulations we use a programmable weathering chamber with dry and wet periods and with high and low temperatures. These programmes run for several weeks and according to a defined sampling schedule we take water samples, run a clean-up procedure by SPE (Molecular imprinted polymers (MiPs) resp. polymer-based cartridges (Waters Oasis HLB)) and analyse them by HPLC-UV resp. LC-MS/MS. Of most interest in case of flame retardants are photocatalytic transformation products. Therefore, we conduct a non-target-screening resp. a suspected target-screening by LC-MS/MS and HRMS.
Environmental sustainability and –stability of materials concerning the migration of pollutants
(2019)
In addition to previously reported results on the accelerated weathering of polystyrene samples (PS) containing 1 wt. % hexabromocyclododecane (HBCD), we present the first results of our investigations of polypropylene samples (PP) containing 0.1 wt. % BDE-209. All studied polymer samples were exposed to a defined weathering schedule in a climate chamber in accordance to regulation EN ISO 4892-3:2006. For the determination of BDE-209 in the collected raining water the samples were prepared in accordance to a validated protocol. Before the analyses each sample was spiked with isotopically labeled BDE-209. Subsequently the samples were extracted with isooctane. The obtained extracts were concentrated, and the resulting solutions were analyzed by GC/MS. Additionally, the total bromine content was monitored for the weathered and untreated samples using laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) and X-ray fluorescence analysis (XRF) as a non-destructive and rapid method. In general, the resulting data from the accelerated weathering will be compared to those from the natural weathering experiments. Here, the surfaces of the test pieces were analyzed by LA-ICP-MS and XRF as well. Moreover, soil bed tests were conducted in a well characterized model soil. This soil (boulder-clay, sand with 12 % loam, particle size in total 0.2-4 mm) is filled in a free-draining basin inside of an air-conditioned cellar. In this manner, TOC, water capacity and humidity are recorded parameters. To induce a leaching process from the samples by the raining water, the target water content is calculated to 8%. The actual humidity is measured by a tensiometer, assuring the duration of the raining period. A defined humidity is a fundamental parameter for a biological activity in the soil. The test polymers were placed up to the half in the soil. Microbial activity of the soil is monitored by a reference polymer (polyurethane) and should induce the release of HBCD and BDE-209 out of the test materials. These released analytes will be captured by passive samplers (silicone tubes) placed in a distinct distance to the polymer samples in the soil. The soil bed experiments are complementary to the weathering experiments due to the biological activity in the soil.
A new facility has been developed which allows for a stable and reproducible production of ambient-like model aerosols (PALMA) in the laboratory. The set-up consists of multiple aerosol generators, a custom-made flow tube homogeniser, isokinetic sampling probes, and a system to control aerosol temperature and humidity. Model aerosols containing elemental carbon, secondary organic matter from the ozonolysis of α-pinene, inorganic salts such as ammonium sulfate and ammonium nitrate, mineral dust particles,and water were generated under different environmental conditions and at different number and mass concentrations. The aerosol physical and chemical properties were characterised with an array of experimental methods, including scanning mobility particle sizing, ion chromatography, total reflection X-ray fluorescence spectroscopy and thermo-optical analysis. The facility is very versatile and can find applications in the calibration and performance characterisation of aerosol instruments monitoring ambient air. In this study, we performed, as proof of concept, an intercomparison of three different commercial PM (particulate matter) monitors (TEOM1405, DustTrak DRX 8533 and Fidas Frog) with the gravimetric reference method under three simulated environmental scenarios. The results are presented and compared to previous field studies. We believe that the laboratory-based method for simulating ambient aerosols presented here could provide in the future a useful alternative to time-consuming and expensive field campaigns, which are often required for instrument certification and calibration.
The development of traceable new methodologies to quantify elemental air pollutants in particulate matter (PM) supports modernization of methods used in air quality monitoring networks in Europe. In the framework of the EURAMET EMPIR AEROMET II project, the combination of cascade impactor aerosol sampling and total reflection X-ray fluorescence elemental spectroscopy (TXRF) was investigated. This technique requires a traceable calibration based on reference samples. This paper describes a new, simple and effective method to produce such reference samples using flexible, reusable, and low-cost parylene C shadow masks, fabricated by photolithographic steps. These shadow masks can be used to produce reference samples that mimic the Dekati cascade impactor’s deposition patterns by applying as-prepared micro stencils to 30 mm acrylic substrates and evaporating a reference material (Ti) in arrangements of thin circular dots. The highly flexible direct patterning of acrylic discs with reference material, otherwise impossible with conventional photolithography, allows multiple reusing of the same micro stencils. The aspect ratios of the dots could be repeated with an error less than 4 %. A first set of standard reference samples for the 13 stages of the Dekati cascade impactor was produced and preliminary TXRF measurements of the deposited Ti masses were performed. The centricity of the deposition patterns turned out to be an important parameter for the quality of the TXRF results. The parylene mask technology for the production of reference samples turns out to be a promising new approach for the traceable calibration of TXRF spectrometers for the quantification of element concentrations in environmental aerosol samples but, due to its great versatility, it could be used for several other micropatterning applications on conventional and unconventional substrates.
Formaldehyde is considered as carcinogenic and is emitted from particleboards and plywood used in toy manufacturing. Currently, the flask method is frequently used in Europe for market surveillance purposes to assess formaldehyde release from toys, but its concordance to Levels measured in emission test chambers is poor. Surveillance laboratories are unable to afford laborious and expensive emission chamber testing to comply with a new amendment of the European Toy Directive; they need an alternative method that can provide reliable results. Therefore, the application of miniaturised emission test chambers was tested. Comparisons between a 1 m3 emission test chamber and 44 mL microchambers with two particleboards over 28 days and between a 24 L desiccator chamber and the microchambers with three puzzle samples over 10 days resulted in a correlation coefficient r2 of 0.834 for formaldehyde at steady state. The correlation between the results obtained in microchambers vs. flask showed a high variability over 10 samples (r2: 0.145),
thereby demonstrating the error-proneness of the flask method in comparison to methods carried out under ambient parameters. An exposure assessment was also performed for three toy puzzles: indoor formaldehyde concentrations caused by puzzles were not negligible (up to 8 µg/m3), especially when more conservative exposure scenarios were considered.
Formaldehyde is considered as carcinogenic and is emitted from particleboards and plywood used in toy manufacturing. Currently, the flask method is frequently used in Europe for market surveillance purposes to assess formaldehyde release from toys, but its concordance to levels measured in emission test chambers is poor. Surveillance laboratories are unable to afford laborious and expensive emission chamber testing to comply with a new amendment of the European Toy Directive; they need an alternative method that can provide reliable results. Therefore, the application of miniaturised emission test chambers was tested. Comparisons between a 1 m3 emission test chamber and 44 mL microchambers with two particleboards over 28 days and between a 24 L desiccator chamber and the microchambers with three puzzle samples over 10 days resulted in a correlation coefficient r2 of 0.834 for formaldehyde at steady state. The correlation between the results obtained in microchambers vs. flask showed a high variability over 10 samples (r2: 0.145), thereby demonstrating the error-proneness of the flask method in comparison to methods carried out under ambient parameters. An exposure assessment was also performed for three toy puzzles: indoor formaldehyde concentrations caused by puzzles were not negligible (up to 8 μg/m3), especially when more conservative exposure scenarios were considered.
This study shows that formaldehyde Emission results in micro-scale emission chambers are comparable with results in bigger chambers both for particle boards and wooden toys. On the contrary, the WKI flask method was leading to more variable results depending on sample geometry. Thus, microchambers could be used for reliable routine market surveillance. An exposure assessment led to noticeable formaldehyde indoor air concentration values, pointing out the need for an effective Surveillance of such samples.
Formaldehyd gilt als krebserregend und wird von Spanplatten und Sperrholz emittiert, die bei der Spielzeugherstellung verwendet werden. Die Untersuchungsänter benötigen eine wirtschaftliche und zuverlässige Methode. Die Anwendung miniaturisierter Emissionsprüfkammern wurde getestet und mit größeren Emissionsprüfkammern und die Flaschenmethode verglichen. Eine Expositionsabschätzung wird auch vorgestellt.
Die von der BAM eingekauften Holzwerkstoffplatten (Verlegespanplatten, OSB, Multiplexplatten) verschiedener Hersteller zeigten teilweise hohe Formaldehyd-emissionen unter den Prüfbedingungen nach EN 16516, eine Spanplatte hielt den Grenzwert von 0,1 ppm selbst bei Prüfung nach DIN EN 717-1 nicht ein, dürfte also in Deutschland gar nicht in den Verkauf gelangen.
Holzwerkstoffe, die unter den Prüfbedingungen der DIN EN 717-1 die Formaldehydklasse E1 einhalten, können insbesondere bei großflächigem Einsatz im Innenraum zu Überschreitungen des Richtwertes für die Innenraumluft führen. Zusätzlich zur Anpassung des Luftwechsels ist auch der Parameter Beladung bei einer Überarbeitung der Norm anzupassen. In der DIN EN 16516 werden produktspezifische (am Einsatz der Produkte orientierte) Beladungsfaktoren vorgegeben. Für den Einsatz von Holzwerkstoffplatten ergäben sich Beladungen von 0,4 (Boden oder Decke), 1,0 (Wände), 1,4 (Wände plus Boden oder Decke) und 1,8 m²/m³ (Wände, Boden und Decke). Um die realen Bedingungen in modernen Gebäuden abzubilden, ist deshalb eine Beladung von 1,8 m²/m³ für die Prüfkammermessung erforderlich. Hierbei ist darauf hinzuweisen, dass für die Beladung im Referenzraum Möbel nicht berücksichtigt wurden.
Damit soll sichergestellt werden, dass die Einhaltung des Schutzniveaus bei realen Innenraumbedingungen auch unter den Randbedingungen eines niedrigen Luftwechsels sowie bei sommerlichen Bedingungen und heutigem Lüftungsverhalten der Menschen soweit wie möglich gewährleistet ist.
Indoor air quality is affected by the emission of volatile organic compounds (VOC) or the odour from building products. Odours can be measured by applying the standard ISO 16000-28:2020.
In the study presented here proposals for further technical development of the ISO method are presented. The sampling procedure and evaluation
method of the perceived intensity are investigated in particular because they have a major influence on reproducibility of measurement results.
The presentation gives general information about the European Standard EN 16516 “Construction products – Assessment of release of dangerous substances – Determination of emissions into indoor air”. This test standard was developed based on the mandate M/366 of the European commission and is a horizontal reference method for the determination of volatile organic compounds (VOC) from different classes of construction (building) products. Specific test conditions are to be selected by the product TCs (technical committees) in a way that a product is tested under its intended condition of use.
The test is based on the use of emission test chambers which are operated at constant air change rate and climate (23°C, 50 % r.h.) over 28 days. The standard defines the conditions and requirements for the measurement including loading factor, air change rate, sampling, analysis and calculation of emission rates of the substances. A 30 m³ reference room is described which is used to calculate air concentrations from the determined emission rates.
The standard EN 16516 enables the evaluation of construction products regarding their emissions into indoor air under defined and comparable conditions. The evaluation includes the determination of identified target compounds, non-identified target compounds, volatile carcinogenic compounds and the sum values TVOC, TSVOC and R.
Nonporous corundum powder, known as an abrasive material in the industry, was functionalized covalently with protein binders to isolate and enrich specific proteins from complex matrices. The materials based on corundum were characterized by TEM, ESEM, BET, DLS, and zeta potential measurements. The strong Al-O-P bonds between the corundum surface and amino phosphonic acids are used to introduce functional groups for further conjugations. The common cross-linker glutaraldehyde was compared with a hyperbranched polyglycerol (PG) of around 10 kDa. The latter is oxidized with periodate to generate aldehyde groups that can covalently react with the amines of the surface and the amino groups from the protein via a reductive amination process. The amount of bound protein was quantified via aromatic amino acid analysis (AAAA). This work shows that oxidized polyglycerol can be used as an alternative to glutaraldehyde. With polyglycerol, more of the model protein bovine serum albumin (BSA) could be attached to the surface under the same conditions, and lower nonspecific binding (NSB) was observed. As a proof of concept, IgG was extracted with protein A from crude human plasma. The purity of the product was examined by SDS-PAGE. A binding capacity of 1.8 mg IgG per g of corundum powder was achieved. The advantages of corundum are the very low price, extremely high physical and chemical stability, pressure resistance, favorable binding kinetics, and flexible application.
Nonporous corundum powder, known as an abrasive material in the industry, was functionalized covalently with protein binders to isolate and enrich specific proteins from complex matrices. The materials based on corundum were characterized by TEM, ESEM, BET, DLS, EDS, and zeta potential measurements. The strong Al-O-P bonds between the corundum surface and amino phosphonic acids were used to introduce functional groups for further conjugations. The common crosslinker glutaraldehyde was compared with a hyperbranched polyglycerol (PG) of around 10 kDa. The latter was oxidized with periodate to generate aldehyde groups that can covalently react with the amines of the surface and the amino groups from the protein via a reductive amination process. The amount of bound protein was quantified via aromatic amino acid analysis (AAAA). This work shows that oxidized polyglycerol can be used as an alternative to glutaraldehyde. With polyglycerol, more of the model protein bovine serum albumin (BSA) could be attached to the surface under the same conditions, and lower non-specific binding (NSB) was observed. As a proof of concept, IgG was extracted with protein A from crude human plasma. The purity of the product was examined by sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE). A binding capacity of 1.8 mg IgG per gram of corundum powder was achieved. The advantages of corundum include the very low price, extremely high physical and chemical stability, pressure resistance, favorable binding kinetics, convenient handling, and flexible application.
How the rock-inhabiting fungus K. petricola A95 enhances olivine dissolution through attachment
(2020)
Free-living and mycorrhizal fungi are able to enhance the weathering of rock and other solid substrates. Deciphering the exact mechanisms of these natural processes requires their experimental simulation. Moreover, by performing these simulations with genetically amenable rock-weathering fungi, one can knock-out certain fungal traits and consequently identify their weathering-relevant function. Here, the effect of the rock-inhabiting fungus, Knufia petricola A95, on the dissolution kinetics of an Fe-bearing olivine (Mg1.86Fe0.19SiO4) is investigated at 25 °C and pH 6 using reproducible batch and mixed flow experiments. The availability of a melanin-deficient mutant (ΔKppks) of K. petricola A95, which produces more extracellular polymeric substances (EPS) than the wild type (WT), enables the comparative study of the role of melanin and EPS in olivine dissolution. In abiotic dissolution experiments, the olivine dissolution rate decreased considerably over time at pH 6 but not at pH 3.5. This inhibition of abiotic olivine dissolution at pH 6 was most likely caused by the in-situ oxidation of ferrous Fe and/or the precipitation of ferric hydroxides at the olivine surface. In corresponding biotic experiments at pH 6, both the wild type K. petricola and its melanin-deficient mutant ΔKppks solubilised and bound significant amounts of Fe released by olivine dissolution. Fe oxidation and precipitation were thus prevented and olivine dissolution proceeded faster than in the abiotic experiments. By sequestering Fe directly at the olivine surface, the attached wild type K. petricola cells were particularly efficient at preventing the oxidation of Fe at the mineral surface: the slowdown of olivine dissolution almost completely disappeared. The attachment capacity of these wild type cells is most likely mediated by wild type-specific EPS. Our presented experimental systems allow the oxidation of mineral-released Fe and include a rock-inhabiting fungus, thus simulating chemical, physical and biological conditions that set dissolution rates in a way that is relevant to natural ecosystems.
Each year, an immense amount of plastic debris enters marine ecosystems, much of which ends up in the Great Pacific Garbage Patch (GPGP). The plastic fragments are home to a diverse community of microorganisms, and while researchers have gained a better understanding of these marine plastic biofilms, we lack insights into the physiology and genomic potential of the bacteria that colonize them. Examining the lifestyle of plastic colonizers from the GPGP is particularly intriguing, as the high concentration of plastics in this accumulation zone might allow for a microbial adaptation to this unique man-made habitat. A range of pigmentation was observed in 67 isolated strains obtained directly from plastic pieces sampled from the GPGP surface water. Sequence comparison between the cultivated bacterial strains and the 16S rRNA gene amplicon dataset confirmed that most of the cultivates could also be captured through DNA-only methods. Whole genome analysis of four taxonomically diverse representatives revealed multiple carotenoid pathways, including those to produce less common glycosylated carotenoids, like sarcinaxanthin glucoside. Further, we identified a potentially new Rhodobacteraceae species containing a photosynthetic gene cluster (PGC). Absorption analysis confirmed the actual production of the carotenoids and bacteriochlorophyll a. Floating plastics represent a habitat with strong UV-light exposure, making the protection with antioxidant carotenoids as well as the ability to use light as an energy source highly beneficial traits for plastic colonizers. Our findings indicate, that the production of pigments is a common adaption mechanism for plastic-associated bacteria, and that plastic biofilms present a so far overlooked source of rare carotenoids and light-harvesting mechanisms.
Der Mensch verbringt die überwiegende Zeit des Tages in Innenräumen von Gebäuden. Der Aufenthalt in Innenräumen umfasst das Wohnen, Bürotätigkeiten oder auch Nutzung öffentlicher Gebäude wie Kindertagesstätten, Schulen, Sporthallen und Bibliotheken. Um Innenräume von Gebäuden ohne Gefährdung für die menschliche Gesundheit nutzen zu können, müssen diese bei ihrer Errichtung und Verwendung dauerhaft die an sie gestellten hohen Anforderungen zu Gesundheit und Hygiene erfüllen. Die Innenraumluftqualität und ihre Wahrnehmung durch die Raumnutzer spielt für das individuelle Wohlbefinden und die Gesundheit eine entscheidende Rolle.
Dieses Buch richtet sich bevorzugt an Bauplaner, Architekten, Bauingenieure und Bauherren aber auch an Bauproduktehersteller. Ihnen allen fällt die wichtige Aufgabe zu, Aufenthaltsräume von Gebäuden durch eine gezielte Bauproduktverwendung zu gestalten und dauerhaft nutzbar zu machen. Die Frage, ob der Aufenthalt in Gebäuden den Menschen gesundheitlich beeinträchtigen oder sogar krank machen kann, hängt wesentlich von der qualitativen und quantitativen Zusammensetzung der Raumluft ab.
„Innenraumluftqualität und Bauprodukte“ enthält Angaben über wichtige Inhaltsstoffe der Raumluft und damit verbundene Einflussfaktoren, und geht im Besonderen auf Emissionen aus Bauprodukten ein. So vermögen Bauprodukte oftmals als großflächige Emissionsquellen die Innenraumluft mit verschiedenartigen Stoffen und Stoffgemischen anzureichern, mit der Folge, dass Raumnutzer diesen dauerhaft und teilweise intensiv ausgesetzt sind.
Das Buch vermittelt wichtige Erkenntnisse über flüchtige organische Verbindungen (VOC) aus Bauprodukten sowie deren Verhalten in der Raumluft etwa in Bezug auf Emissionsdauer, Hausstaubdeposition und Sekundärquellenbildung. Auf spezifische VOC-Einzelstoffemissionen – sehr flüchtige (VVOC) bis hin zu schwerflüchtigen (SVOC) – und einzelne chemische Stoffgruppen in Zusammenhang mit ihrem Vorkommen in Bauprodukten wird eingegangen.
Die wesentlichen Voraussetzungen und die Bedeutung einzelner VOC und VOC-Stoffgemische für die Expositionssituation und die Gesundheit von Raumnutzern werden in einem eigenen Kapitel beschrieben. Wichtige Kenntnisse über gesundheitliche Stoffwirkungen werden transparent erläutert. Angesprochen werden der inhalative Aufnahmepfad, Effekte durch Reizstoffe an den Atemwegen, andere toxische Wirkungen und die Auswirkungen von geruchsintensiven und -belästigenden Stoffen.Das Kapitel „Bewertung der Innenraumluftqualität“ vermittelt die allgemein anerkannte Vorgehensweise zur Beurteilung der Luftqualität und erstreckt sich auf chemische Stoffe, Geruchseinwirkungen sowie auf das Edelgas Radon. Bauplaner, Architekten, Bauingenieure und Bauherren werden in die Lage versetzt, die Bedeutung und Anwendung verschiedener Beurteilungsparameter und ihre Beurteilungswerte anschaulich nachzuvollziehen und deren Verwendung in Beurteilungen und Prüfberichten gezielt einzuordnen. Im Detail wird die notwendige Abgrenzung der Verwendung der Begrifflichkeiten „Grenzwerte“ und „toxikologisch begründete Innenraumluftrichtwerte des Ausschusses für Innenraumrichtwerte (AIR)“ mit den dazugehörigen aktuellen Richtwerten (RW II bzw. RW I) erklärt. Auch die Bedeutung und der Anwendungsbereich internationaler Beurteilungen der WHO und der europäischen Chemikalienbewertung (REACH) werden erläutert. Das Buch liefert Informationen über die Ermittlung und Verwendung statistisch abgeleiteter Beurteilungswerte, die als Referenzwerte definiert sind.
Die Ergebnisse aktueller Referenzwertstudien zum Vorkommen einzelner VOC und von VOC-Stoffgemischen als Summe aller nachgewiesenen VOC (TVOC-Wert) in Wohnräumen, Büros und auch öffentlichen Gebäuden wie Schulen – einschließlich ihrer Methodik und Analytik – werden erläutert und diskutiert. Der Verwendungszweck eines Bauproduktes in Gebäuden zwingt dazu, bereits vor dessen Einbau mittels konkretisierten Produktanforderungen eine Beurteilung des Gesundheitsschutzniveaus für die späteren Raumnutzer zu gewährleisten. Daher sind alle am Bau beteiligten Personen wie Bauplaner, Architekten, Bauingenieure und Bauproduktehersteller gefordert. Zwar treten in den Bauproduktemissionen viele VOC in eher geringeren Konzentrationen auf, jedoch zeigen einige nachweisbare Einzelstoffe sowohl Reizeffekte oder andere toxische Wirkungen als auch erhebliche Geruchsintensitäten auf.
„Innenraumluftqualität und Bauprodukte“ geht aus diesem Grund zwei bedeutsamen Fragen nach: Wie lässt sich das Gefährdungspotenzial der emittierten VOC aus Bauprodukten bevorzugt bewerten und wie lassen sich die Anforderungen an den Aufenthaltsraum zum Gesundheitsschutzniveau in Bezug auf Bauproduktemissionen prüfen, beurteilen und letztlich gewährleisten?
Hierzu gibt das Buch aktuelle Informationen zum anerkannten Prüf- und Bewertungsverfahren vom Ausschuss zur gesundheitlichen Bewertung von Bauprodukten (AgBB). Über das breit etablierte AgBB-Schema zur gesundheitlichen Beurteilung von Emissionen flüchtiger organischer Verbindungen (VVOC, VOC, SVOC) aus innenraumrelevanten Bauprodukten wird im Detail nachvollziehbar berichtet. Im Fokus steht die Anwendung des AgBB-Schemas in der Praxis. In einem umfangreichen Kapitel wird auf die Durchführung von Materialemissionsmessungen sowie Bewertungen der Geruchsemissionen und die dafür notwendigen Voraussetzungen eingegangen. Abbildungen und Messberichte geben einen weitreichenden Einblick zum Verständnis einer Prüfkammeruntersuchung auf flüchtige organische Verbindungen (VVOC, VOC, SVOC). Zur Verdeutlichung werden beispielhaft Messdaten angeführt zu unterschiedlichen Bauprodukten, wie Bodenbelägen, Bodenbelagsklebstoffen, Holz und Holzwerkstoffen, Lacken und Farben,
Kunstharzfertigputzen und Dichtstoffen. Das Buch bietet tabellarische Übersichten über das Vorkommen und die Konzentration ermittelter VOC-Emissionen aus Bauprodukten verschiedener Produktgruppen und zeigt Möglichkeiten auf, wie in der Praxis bestimmte SVOC-Emissionen, etwa Flammschutzmittel und Biozide, sowie Sekundäremissionen aus Bauprodukten analysiert und quantifiziert werden können. Darüber hinaus gibt es einen Überblick über die geltenden baurechtlichen Anforderungen in Bezug auf Hygiene und Gesundheit. Öffentlich-rechtliche Mindestforderungen zur Sicherstellung des Gesundheitsschutzniveaus für in Innenräume von Gebäuden eingebrachte Bauprodukte werden mit den zugrunde zu legenden Bestimmungen der Musterbauordnung (MBO) und ihrer neuen Muster-Verwaltungsvorschrift Technische Baubestimmungen (MVV TB) beschrieben.
Eigens wird ein Einblick in rechtliche Regelungen – in Bezug auf die gesundheitsbezogenen Anforderungen an bauliche Anlagen, die über die „Anforderungen an bauliche Anlagen bezüglich des Gesundheitsschutzes (ABG)“ konkretisiert sind – gegeben. Es wird ersichtlich, dass die Anforderungen für Emissionen flüchtiger organischer Verbindungen (VVOC, VOC, SVOC) aus Bauprodukten mindestens denen des AgBB entsprechen. Die in Europa noch lückenhafte und unvollständige Harmonisierung der Normen zum Gesundheitsschutz wird dargelegt. Das Buch leistet so Hilfestellung, um trotzdem gemäß den MBO- bzw. MVV TB-Anforderungen gesundheitsbezogene Angaben zu Produktleistungen zu ermöglichen.
There is a need for an assessment of the emission properties of volatile organic compounds (VOCs) from consumer products. A method comparison was carried out to evaluate adapted and cost-effective procedures for such items. Smaller and automated emission chambers depicted similar kinetics compared to a 203 L standard chamber. Toy samples made of PVC (Polyvinyl chloride) emitted more VOCs compared to other tested polymeric products. The emissions from 2 selected samples were studied to allow an evaluation of the resulting room concentration and external exposure of a child. Obtained concentrations were not of concern.
There is a need for an assessment of the emission properties of volatile organic compounds (VOCs) from consumer products. A method comparison was carried out to evaluate adapted and cost-effective procedures for such items. Smaller and automated emission chambers de-picted similar kinetics compared to a 203 L standard chamber. Toy samples made of PVC (Polyvinyl chloride) emitted more VOCs compared to other tested polymeric products. The emissions from 2 selected samples were studied to allow an evaluation of the resulting room concentration and external exposure of a child. Obtained concentrations were not of concern.
Moderne Vitrinen sollen gleichzeitig eine hohe Dichtigkeit und die Abwesenheit jeglicher Fremdstoffe in den Vitrinen gewährleisten. Diese Anforderungen sind zeitgleich kaum erfüllbar, da es emissionsfreie Materialien (vor allem Kleb- und Beschichtungsstoffe) nicht gibt. Um die potentiellen Emissionen zu minimieren wurde ein Messverfahren entwickelt, welches inzwischen als BEMMA-Schema (Bewertung von Emissionen aus Materialien für Museumsausstattungen) in die Museumswelt Einzug genommen hat.
Die erfolgreiche Bewertung der für den Bau verwendeten Materialien gemäß BEMMA-Schema resultiert nicht in einer emissionsfreien Vitrine, sondern soll bei der Auswahl geeigneter Materialien zur Herstellung möglichst emissionsarmer Vitrinen helfen. Konkrete handwerkliche Durchführungen beim Bau, Dichtheits-anforderungen, wie auch die Aufstellbedingungen (Umgebung der Vitrine) beeinflussen die Emissionscharakteristik der fertigen Vitrine in der Praxis. Eine saubere Vitrine hilft nichts in einer belasteten Umgebung oder auch bei emittierenden Exponaten. Inzwischen liegen Erfahrungen mit dem Schema seit 2012 vor.
Der Messablauf sieht vor, dass von den Materialien kleine Muster mit der Mikrokammer (Markes) innerhalb von 2 Tagen untersucht werden. Dabei wird mit Silikagelkartuschen auf Ameisen- und Essigsäure, mit DNPH auf Aldehyde und Ketone und mit Tenax® sowohl auf VOC als auch für die spezifische Oxim-Analytik die Abluft der Mikrokammern untersucht. Die Bewertungskriterien basieren auf den Ergebnissen einer Vorstudie mit ca. 150 verschiedenen Produkten im Zeitraum 2010 bis 2012.
Moderne Vitrinen sollen gleichzeitig eine hohe Dichtigkeit und die Abwesenheit jeglicher Fremdstoffe in den Vitrinen gewährleisten. Diese Anforderungen sind zeitgleich kaum erfüllbar, da es emissionsfreie Materialien (vor allem Kleb- und Beschichtungsstoffe) nicht gibt. Um die potentiellen Emissionen zu minimieren wurde ein Messverfahren entwickelt, welches inzwischen als BEMMA-Schema (Bewertung von Emissionen aus Materialien für Museumsausstattungen) in die Museumswelt Einzug genommen hat.
Die erfolgreiche Bewertung der für den Bau verwendeten Materialien gemäß BEMMA-Schema resultiert nicht in einer emissionsfreien Vitrine, sondern soll bei der Auswahl geeigneter Materialien zur Herstellung möglichst emissionsarmer Vitrinen helfen. Konkrete handwerkliche Durchführungen beim Bau, Dichtheits¬anforderungen, wie auch die Aufstellbedingungen (Umgebung der Vitrine) beeinflussen die Emissionscharakteristik der fertigen Vitrine in der Praxis. Eine saubere Vitrine hilft nichts in einer belasteten Umgebung oder auch bei emittierenden Exponaten. Inzwischen liegen Erfahrungen mit dem Schema seit 2012 vor.
Der Messablauf sieht vor, dass von den Materialien kleine Muster mit der Mikrokammer (Markes) innerhalb von 2 Tagen untersucht werden. Dabei wird mit Silikagelkartuschen auf Ameisen- und Essigsäure, mit DNPH auf Aldehyde und Ketone und mit Tenax® sowohl auf VOC als auch für die spezifische Oxim-Analytik die Abluft der Mikrokammern untersucht. Die Bewertungskriterien basieren auf den Ergebnissen einer Vorstudie mit ca. 150 verschiedenen Produkten im Zeitraum 2010 bis 2012.
Gegenstand der vorzustellenden Arbeiten ist die Prüfung der Umwelt-beständigkeit und -verträglichkeit von Materialien und Produkten hinsichtlich der Emission von potenziellen Schadstoffen in die Umwelt. Hierzu werden chemisch-physikalische Einflüsse (Bewitterung) und mikrobielle Beanspruchungen an Modellmaterialien evaluiert. So werden die Freisetzungsraten von Schadstoffen in Abhängigkeit der Beanspruchung beschrieben. Als Modellmaterialien kommen die Polymere Polystyrol (PS) und Polypropylen (PP) zum Einsatz. Synergistische Effekte der Bewitterungsparameter und der mikrobiologischen Beanspruchung sollen dabei ebenso betrachtet werden, wie die gezielte Alterung. Auch findet eine Beschreibung des Verhaltens der ausgetragenen Schadstoffe (polybromierte Flammschutzmittel) in den Umweltkompartimenten Boden oder Wasser statt. Hier sind mit Hilfe der zu entwickelnden Screening- und non-Target-Analyseverfahren die Transformation und der Metabolismus durch Mikroorganismen zu beschreiben. Aus den Ergebnissen sollen Korrelationen zwischen den künstlichen Alterungsverfahren und realen Szenarien abgeleitet werden.
Today glass is broadly used in modern architecture. For indoor applications it is possible to produce decorated glass by using enamel colours and glass painting techniques without any problems. However, this is more limited for applications out of doors. Humidity and environmental pollution attack the surface of the coating and can damage it. There are only a few colours on the market which are resistant towards acids and bases until now. Additionally, most of those colours are opaque. To extend the colour palette, chemically resistant low melting coloured glasses are being developed which are transparent and intensively toned even in thin coating thicknesses. To achieve such an ambitious aim, many parameters have to combine and act in a complex manner. New compositions of lead borosilicate, zinc borosilicate and lead-zinc borosilicate glasses were produced and milled as powder. The thermal properties as well as the environmental stability were analysed. The influence of PbO and ZnO on the thermal properties and the environmental stability were investigated. Evaluation of the fusing results shows that the production and mixture of transparent vitreous enamels for the exterior side of glasses is possible. The tests made it clear that the original materials for making the vitreous enamels must be excellently ground and prepared to achieve a satisfactory result. The method to produce durable vitreous enamels for exterior application also seems to allow the production of glass colours.
Equipping ZIF particles with a polyelectrolyte membrane provides functional groups at their interface, enabling further conjugations necessary for applications such as targeted drug delivery. Previous approaches to coat ZIF particles with polyelectrolytes led to surface corrosion of the template material. This work overcomes previous limitations by performing a Layer-by-Layer (LbL) polyelectrolyte coating onto ZIF-8 and ZIF-67 particles in nonaqueous environment. Using the 2-methylimidazolium salt of polystyrensulfonic acid instead of the acid itself and polyethyleneimine in methanol led to intact ZIF particles after polyelectrolyte coating. This was verified by electron microscopy. Further, zetapotential and atomic force microscopy measurements confirmed a continuous polyelectrolyte multilayer built up. The here reported adaption to the well-studied (LbL) polyelectrolyte selfassembly process provides a facile method to equip ZIF particles with a nanometer thin polyelectrolyte multilayer membrane.
Laser Powder Bed Fusion (L-PBF) is a promising additive manufacturing (AM) technology for metal part production especially for complex and lightweight structures or functional designs. In L PBF processes several by-products including welding plume and its condensates, spatter and ejected powder are generated during laser exposure. Investigations of micro- and nano-sized by-products have received little attention in literature. This study focuses on the analysis of particle emissions in L PBF of 316L stainless steel using a scattered light aerosol spectrometer and a fast mobility particle sizer spectrometer during the process which allows for in-situ analysis of particle sizes in the range of 6 nm to 100 µm. A distinct correlation of emission signals to part position can be revealed. In addition, a significant influence of laser scanning vector directions on emission signals is presented. Furthermore, differing powder layer thicknesses can be recognised by deviations in emission signals.
Laser Powder Bed Fusion (L-PBF) is a promising additive manufacturing (AM) technology for metal part production especially for complex and lightweight structures or functional designs. In L PBF processes several by-products including welding plume and its condensates, spatter and ejected powder are generated during laser exposure. Investigations of micro- and nano-sized by-products have received little attention in literature. This study focuses on the analysis of particle emissions in L PBF of 316L stainless steel using a scattered light aerosol spectrometer and a fast mobility particle sizer spectrometer during the process which allows for in-situ analysis of particle sizes in the range of 6 nm to 100 µm. A distinct correlation of emission signals to part position can be revealed. In addition, a significant influence of laser scanning vector directions on emission signals is presented. Furthermore, differing powder layer thicknesses can be recognised by deviations in emission signals.
The ISO 16000-6 standard describes a method for the determination of volatile organic compounds (VOCs) in indoor and test chamber air by sorbent-based active sampling, thermal desorption and gas chromatography coupled with mass spectrometry (GC/MS). It also gives directions to adapt this methodology to very volatile organic compounds (VVOCs). Indeed, toxicologically based guideline values are being implemented for these compounds and it becomes necessary to measure them. But a comprehensive and robust measurement method is lacking. This work highlights the points that still need to be explored towards the standardisation of a suitable procedure: investigations on sorbent combinations, the suitability of chromatography columns and the use of gaseous standards are required. The biggest challenge remains in the fact that strong sorbents adsorb water together with VVOCs. Water may impair the analysis and the optimal approach to eliminate it is still to be found and integrated into the sampling strategy.
Metagenomic datasets of air samples collected during episodes of severe smoke-haze in Malaysia
(2021)
Transboundary emissions of smoke-haze from land and forest fires have recurred annually during the dry period (June to October, over the past few decades) in South East Asia. Hazardous air quality has been recorded in Malaysia during these episodes. Agricultural practices such as slash-and-burn of biomass and peat fires particularly in Sumatera and Kalimantan, Indonesia, have been implicated as the major causes of the haze. Past findings have shown that a diversity of microbes can thrive in air including in smoke-haze polluted air. In this study, metagenomic data were generated to reveal the diversity of microorganisms in air during days with and without haze. Air samples were collected during non-haze (2013A01) and two haze (2013A04 and 2013A05) periods in the month of June 2013. DNA was extracted from the samples, subjected to Multiple Displacement Amplification and whole genome sequencing (Next Generation Sequencing) using the HiSeq 2000 Platform. Extensive bio-informatic analyses of the raw sequence data then followed. Raw reads from these six air samples were deposited in the NCBI SRA databases under Bioproject PRJNA662021 with accession numbers SRX9087478, SRX9087479 and SRX9087480.
Herein we report the synthesis of a zeolitic imidazolate framework (ZIF-8) by an easy “mix and wait” procedure. In a closed vial, without any interference, the mixture of 2-methylimidazole and basic zinc carbonate assembles into the crystalline product with approx. 90% conversion after 70 h. The reaction exhibits sigmoidal kinetics due to the self-generated water which accelerates the reaction.
Initial situation:
Aluminum is an often-used building material in modern architecture, not only for construction but as well for facades and decorative elements. In the 1950th and 1960th, after World War II, many buildings in Germany were constructed with aluminum or contain elements of colored anodized aluminum. In the last years a larger number of these buildings are increasingly in the sight of conservation works including the aluminum parts such as window frames or facade coverings.
Damaged Aluminum Surfaces:
Common damages are a change of color or gloss changes through weathering processes, drill holes or marks due to later modifications, scratches in the anodized layer due to extensive wear e.g. at handrails or door handles.
To repair damaged aluminum surfaces, there are usually two options: smaller damaged areas are repaired by using a touch-up pen. In case of larger damages, the complete re-anodization is necessary. This includes to de-anodize the surface with cleaning and grinding the whole aluminum object. Both possibilities are disadvantageous for the objects. The touch-up pen often does not match the color of the original surface together with an insufficient corrosion protection for outdoors. While the newly anodized surface differs in color and gloss from the originally applied color.
Research Approach:
The whole procedure contrasts with the principal approach in conservation which aims to intervene as less as possible, in case of the conservation of an object. To fulfill this approach in a more appropriate way the research project focuses on a mobile and partial application for colored, anodized aluminum parts.
To anodize aluminum the application of an electrolyte onto the surface together with sufficient voltage and current is necessary. Generally diluted sulfuric acid is used as electrolyte. Different possibilities are examined to enable the mobile application of the electrolyte, e. g. the application by producing a gel matrix or like in electroplating by pen or brush wrapped with a fleece fabric.
Experimental part:
First experiments are conducted to examine the structure of the anodized layer in relation with proper cleaning, anodization time with applied voltage and current and the coloring process. The aim was to reduce the preparation procedure and the anodization time as much as possible to facilitate the mobile application.
Examinations with Keyence microscope, Eddy current testing and REM are performed to characterize the layers. The results are shown in table 1. A clear connection between proper cleaning, anodization time, voltage and amperage and the achieved thickness of the anodized layer is significant. Cracks in the layer show that raising the voltage and amperage results in thicker layers but as well in a crumbled and less stable anodized surface.
Gel preparation:
In addition to the anodization process with a liquid e.g. sulfuric acid a gel application is tested to prevent the electrolyte from rinsing down during the mobile application. For this purpose, several gel-forming agents are tested together with their stability in acid systems. It was observed, that the consistency of the gels varies dependent of the time.
Conductivity:
The conductivity of sulfuric acid combined with different gel-systems was measured and compared in order to predict the possible growth of layers during anodic oxidation process.
Further steps:
Determination and optimization of application parameters like voltage, amperage and anodization-time to build up a preferably stable and sufficient thick anodized layer. Examination of gel preparation to guarantee a stable product, enforcing with textile tape for easy application.
Monodisperse iron oxide nanoparticles as reference material candidate for particle size measurements
(2020)
In order to utilize and rationally design materials at the nanoscale the reliable characterization of their physico-chemical properties is highly important, especially with respect to the assessment of their environmental or biological impact. Furthermore, the European Commission’s REACH Regulations require the registration of nanomaterials traded in quantities of at least 1 ton. Powders or dispersions where 50% (number distribution) of the constituent particles have sizes ≤ 100 nm in at least one dimension are defined as nanomaterials. This creates a need for industrial manufacturers and research or analytical service facilities to reliably characterize potential nanomaterials. Currently, BAM is developing reference nanoparticles, which shall expand the scarce list of worldwide available nano reference materials certified for particle size distribution and will also target other key parameters like shape, structure, porosity or functional properties. In this respect, materials like iron oxide or titanium dioxide are considered as candidates to complement the already available silica, Au, Ag, and polystyrene reference nanoparticles.
The thermal decomposition of iron oleate precursors in high boiling organic solvents can provide large quantities of iron oxide nanoparticles that can be varied in size and shape.[1, 2] The presence of oleic acid or other hydrophobic ligands as capping agents ensures stable dispersion in nonpolar solvents. Such monodisperse, spherical particles were synthesized at BAM and pre-characterized by electron microscopy (TEM, SEM including the transmission mode STEM-in-SEM) and dynamic light scattering comparing cumulants analysis and frequency power spectrum.
1. REACH regulations and nanosafety concerns create a strong need for nano reference materials with diverse properties.
2. Iron oxide nanoparticles are under development as new candidate reference material at BAM.
3. Narrow particle size distribution confirmed by light scattering and electron microscopy.
A brief perspective of BAM on nanocarriers is presented including examples with special emphasis on the characterization of such materials and underlying challenges. In this respect, also ongoing activities at BAM on different types of core/shell nanomaterials and related systems are briefly summarized.
In 1981 the OECD published the Test Guideline on Particle size and size distribution. This TG is still a valid document for the measurement of particles all over the world.
When nanomaterials gained importance, ISO set up a technical commitee for Nanotechnologies in 2005 and the OECD followed this step in 2006 with the Working Party on Manufactured Nanomaterials.
In the following years ISO and OECD published several documents about nanomaterials and the systematisation developed.
In 2017 it was finally clear that nanomaterials need to be adressed in another way than chemicals and in 2020 ECHA revised the REACH-Annexes accordingly and included nanomaterials.
Unfortunately there is a little problem with this: Only a few applicable test guidelines exit for the measurement of the nanomaterials. Several test guidelines date from 1981 and do not address nanomaterials.
The logical next step for the OECD would be to publish a series of test guidelines which are indeed currently prepared and will be shown in this talk.
Finally there is an additional need for the future of NM standardisation: Digitalisation.
Natural building materials for interior fitting and refurbishment - What about indoor emissions?
(2021)
Indoor air quality can be adversely affected by emissions from building materials, consequently having a negative impact on human health and well-being. In this study, more than 30 natural building materials (earth dry boards and plasters, bio-based insulation materials, and boards made of wood, flax, reed, straw, etc.) used for interior works were investigated as to their emissions of (semi-) volatile organic compounds ((S)VOC), formaldehyde, and radon. The study focused on the emissions from complete wall build-ups as they can be used for internal Partition walls and the internal insulation of external walls. Test chambers were designed, allowing the compounds to release only from the surface of the material facing indoors under testing Parameters that were chosen to simulate model room conditions. The emission test results were evaluated using the AgBB evaluation scheme, a procedure for the health-related evaluation of construction products and currently applied for the approval of specific groups of building materials in Germany.
Seventeen out of 19 sample build-ups tested in this study would have passed this scheme since they generally proved to be low-emitting and although the combined emissions of multiple materials were tested, 50% of the measurements could be terminated before half of the total testing time.
Museumsvitrinen sollen Kunst- und Kulturgut „ins rechte Licht“ setzen und vor Diebstahl oder Vandalismus schützen. Vergleicht man historische Schauvitrinen, die zumeist aus einfachen Glasscheiben in Holzrahmungen bestehen, mit heutigen Konstruktionen, lässt sich eine Entwicklung zu hochtechnisierten Gebilden ablesen, die deutlich mehr Ansprüchen genügen müssen als in der Vergangenheit.
Zahlreiche Beispiele verdeutlichen, dass Kunstwerke nicht nur außerhalb, sondern auch innerhalb von Museen oder Archiven ungünstigen Umwelteinflüssen ausgesetzt sind. So können Einbauten bzw. Dekorationen in Ausstellungsräumen, Aufbewahrungsbehältnisse in Depoträumen oder Ausstellungsvitrinen flüchtige Substanzen, sogenannte VOCs (Volatile Organic Compounds) freisetzen, die zu irreversiblen Veränderungen an den Objekten führen und diese schädigen. Hierzu zählen organische Säuren, wie Ameisen- oder Essigsäure, aber auch Verbindungen, die Sulfide enthalten. Hier wird die an der BAM entwickelte BEMMA-Bewertungsmethode vorgestellt, die von Museen verwendet werden kann Materialien mit einem geringeren Emissionspotential auszusuchen.
Healthy and energy efficient buildings must be free from disturbing odours. Odour emissions from building materials can be measured with the well-known and accepted standard ISO 16000-28 “Indoor air – Part 28: Determination of odour emissions from building products using test chambers”. For commonly used emission test chambers the sample air is collected in containers (bags) and presented to a group of panel members for the purpose of evaluating the odour. A standard sets requirements for the on-demand presentation in detail. These include the validation procedure for container materials, pre-treatment of bags, details on storage of filled bags and how to carry out the measurements. However, although these measures are proven in practice, incorrect measurements are still possible. Also errors can occur due to a very complex measurement procedure. So, there is a great need for research into how the odour samples are presented.
The proposal planned to be presented will introduce a new development in sample provision by using an adapter which enables collection and provision of sample air without storage or transport of bags. The adapter is a sample container which is permanently positioned on the emission test chamber´s outlet and continuously filled with sample air flowing through it. The flow is briefly interrupted at the time when a sample is taken by a panel member for the test.
The size of the container is sufficient to provide enough sample air for evaluation by at least one panel member via a funnel. Since sampling and presentation are technically connected, it means you can almost do away with storage or transportation and thus it can be presented almost unchanged to the panelmembers. The aim is to reduce measurement errors in the odour samples provision process and the improvement of measurement reproducibility. The paper presents the construction of the adapter as well as the results of emission and odour tests carried out so far.
For centuries, churches, secular buildings and museums have been furnished with valuable works of art. Many works of art are UV- and light-sensitive. It is well known that especially UV radiation causes damage and discoloration in paintings, textiles, plastics, wood and other materials. In particular, the wavelengths between 280 and 410 nm cause color changes, embrittlement or destruction of e.g. plastics over time. Therefore, strongly UV-absorbing glasses are advantageous for architecture and are necessary for the protection of cultural assets. As restorers in all disciplines become more and more aware, the demands placed on buildings and their furnishings in terms of climate are becoming increasingly detailed and precise. The aim in each case is to preserve the valuable artwork.
For some years now, the industry has been offering the protection of cultural objects by installing special UV-protective glasses. Currently, UV protection for church buildings is realized by laminated safety glass equipped with appropriate UV-protective plastic films. Technically, this always means a second pane of glass in front of the windows, which is installed outside the building. This creates climatic gaps that are difficult to control and deterioration due to ageing effects can be expected. At the same time, this protective glazing is not invisible and has a considerable aesthetic influence on the interior and exterior appearance of the building. Meanwhile, the preservation of historical monuments accepts such aesthetic cuts on buildings in order to protect the artwork in the interior from UV light. To this day, however, the long-term durability of UV protection provided by inserted plastic films is still controversial.
To date the only available alternative on the market is a mouth-blown UV protection glass which uses a so-called overlay to provide UV protection. This shows that UV protection can also be achieved by glasses without plastic films thus realizing an exclusive inorganic protection which normally is more stable than a polymeric one. So far there are not enough studies to prove long-term durability.
The aim of this project is to provide existing glazing or new glazing to be created with a highly transparent layer that ensures this UV-protective filter function below 400 nm. The glass coating is to be applied to the glass over a large area and fired into the surface like a classic ceramic enamel paint with the same technics. In addition, it should be long-term durable in its function. It means, that the glass has to be fused at temperatures below 630 °C during the firing process, its chemical durability has to be high, its coefficient of thermal expansion has to be as close as the one of the substrate (usually float glass) and the glass has to absorb the UV-radiation within a thin thickness (thinner as 100 µm).
In this project, the long-term durability of commercial UV-protective glasses is examined. New low melting glasses containing UV-absorbing ions are being developed. Their UV-absorption as a thin layer is analyzed as well as their chemical durability and their thermal properties.
We are grateful to BMWI for the financial support in the frame of the Central Innovation Programme for SMEs (ZIM).
Industrial and agricultural waste streams (waste water, sludges, tailings, etc.) which contain high concentrations of NH4+, PO43–, and transition metals are environmentally harmful and toxic pollutants. At the same time, phosphorous and transition metals constitute highly valuable resources. Typically, separate pathways have been considered to extract hazardous transition metals or phosphate independently from each other. Investigations on the simultaneous removal of multiple components have been carried out only to a limited extent. Here, we report the synthesis routes for Ni- and Co-struvites (NH4MPO4·6H2O, M = Ni2+ and Co2+), which allow for P, ammonia, and metal co-precipitation. By evaluating different reaction parameters, the phase and stability of transition metal struvites as well as their crystal morphologies and sizes could be optimized. Ni-struvite is stable in a wide reactant concentration range and at different metal/phosphorus (M/P) ratios, whereas Co-struvite only forms at low M/P ratios. Detailed investigations of the precipitation process using ex situ and in situ techniques provided insights into the crystallization mechanisms/crystal engineering of these materials. M-struvites crystallize via intermediate colloidal amorphous nanophases, which subsequently aggregate and condense to final crystals after extended reaction times. However, the exact reaction kinetics of the formation of a final crystalline product varies significantly depending on the involved metal cation in the precipitation process: several seconds (Mg) to minutes (Ni) to hours (Co). The achieved level of control over the morphology and size makes precipitation of transition metal struvites a promising method for direct metal recovery and binding them in the form of valuable phosphate raw materials. Under this paradigm, the crystals can be potentially up-cycled as precursor powders for electrochemical or (electro)catalytic applications, which require transition metal phosphates.
Condensation particle counters (CPCs) are widely used for the measurement of aerosol particle number concentrations in the size range from approximately 3 nm to 3 μm. For an SI-traceable calibration of the size-dependent counting efficiency, which is advisable on a regular basis and required in several applications, Faraday cup aerosol electrometers (FCAEs) are considered to be a suitable SI-traceable reference.While the volumetric aerosol inlet flowrate and the electrical current measurement in FCAEs can be related to respective SI references, inter-comparison exercises for FCAEs are still performed on a regular basis to establish reliable uncertainty budgets and to further investigate the influences of designs and operational parameters on comparability. This is strongly demanded in the international community of metrological institutes and aerosol calibration facilities around the world, which provide CPC calibrations. In the present study, the performance of FCAEs was investigated,using Ag test aerosol particles with a 30 nm particle diameter by varying the inlet flowrates from 0.5 l min−1 to 4 l min−1. From our experimental results, significant deviations were observed in FCAE currents at sample flowrates smaller than 1.5 l min−1. It is recommended that these discrepancies should be quantified before an FCAE is used for CPC calibration at low sample flowrates and small particle sizes in the sub-30 nm size range.
One criterion to evaluate the odour of a sample is perceived
intensity П which is evaluated with the aid of a comparative scale. The procedure is well accepted but also time consuming and extensive. The study should help simplify the testing procedure by asking the panel members to only indicate whether a sample is perceived as less to equally intense or of greater intensity in comparison to a given acetone concentration of 7 pi on the comparative scale. In Germany a value of 7 pi is required for products to be suitable for the indoor use. The results show that the simplified test is basically suitable.
OECD Prüfrichtlinie 125
(2023)
Diese Präsentation ist eine Einführung in die OECD TG 125 zur Bestimmung der Partikelgrößen von Nanomaterialien. Es wird auf die verchiedenen Probleme der Partikelgrößenbestimmung eingegangen wie z.B. verschiedene Oberflächenschichten, Äquivalenzdurchmesser und Verteilungsfunktionen. Gleichzeitig werden die neuen Begrifflichkeiten eingeführt, die in der TG 125 definiert neu werden.
OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien
(2021)
Abschlusspräsentation des Projektes "OECD Prüfrichtlinie zur Bestimmung der Partikelgröße und Anzahlgrößenverteilung von Nanomaterialien" - Projektteil Nanopartikel.
Es hat sich gezeigt, dass alle Methoden zur Bestimmung der Partikelgrößenverteilung Vor- und Nachteile haben. Es wird dringend empfohlen Größenverteilungen immer mit mindestens zwei unterschiedlichen Methoden zu bestimmen: Bildgebend und mit gute Anzahlstatistik.
Verschiedene Durchmesser wurden in der TG-PSD mit einem Indexsystem versehen, welches zukünftig Verwechslungen zwischen unterschiedlichen Durchmessern vermeiden soll.
Wird ein bestimmter Durchmesser benötigt (z.B. hydrodynamisch, aerodynamisch), muss die Methode passend gewählt werden. Eine Umrechnung von einem Durchmesser in einen anderen ist in der Regel fehlerbehaftet.
Es wurde ein einheitliches Reporting-System in der TG-PSD eingeführt.
The new OECD test guideline will address the following four main steps in the determination of the length and width distributions of fibers: sample preparation, image acquisition, data evaluation and uncertainty analysis. As the sample preparation has to be optimized for each material, general quality criteria will be given in the protocol. For full visibility of a fiber the appropriate resolution has to be chosen. In the data evaluation the length and diameter of each fiber will be determined concurrently to allow for application of different regulatory definitions. The quality of the results critically depends on the sample preparation as well as the data evaluation. In this step the classification rules have to be formulated and followed accurately in order to optimize reproducibility of the method. The SOP will be validated in an international round robin test, which is planned for 2018/2019.
The new OECD test guideline will address the following four main steps in the determination of the length and width distributions of fibers: sample preparation, image acquisition, data evaluation and uncertainty analysis. As the sample preparation has to be optimized for each material, general quality criteria will be given in the protocol. For full visibility of a fiber the appropriate resolution has to be chosen. In the data evaluation the length and diameter of each fiber will be determined concurrently to allow for application of different regulatory definitions. The quality of the results critically depends on the sample preparation as well as the data evaluation. In this step the classification rules have to be formulated and followed accurately in order to optimize reproducibility of the method. The SOP will be validated in an international round robin test, which is planned for 2018/2019.
The properties of nanomaterials are influenced not only by their chemical composition but also by physical properties (such as size, geometry and crystal structure). For the reliable determination and assessment of behaviour and effects of nanomaterials as well as for the determination of the exposure of humans and environment a comprehensive physical-chemical characterization of nanomaterials is essential. This is an important prerequisite to identify them as nanomaterials and to interpret and compare test results and - in future – to forecast interaction and effects of nanomaterials.
In 2006, the OECD launched a sponsorship program for the testing of nanomaterials in which 11 nanomaterials were thoroughly investigated using a variety of methods. The aim of the project was, among other things, to find out where problems occur and where there are gaps in the measurement and test procedures and where are changes required. An important outcome of the sponsorship program was the finding that the OECD Test Guidelines should in several cases be extended to the specific needs in testing of nanomaterials. The existing standardized test methods of the OECD for physical-chemical characterization have not been developed for nanomaterials in particular. A high demand for an extension of the test guidelines was identified. Germany complied with the OECD's request in 2017 and has agreed to extend the “Test Guideline on Particle Size Distribution / Fiber Length and Diameter Distributions Test Guideline” for Manufactured Nanomaterials (MN). UBA commissioned BAM and BAuA with the preparation of the Test Guideline. The aim of the project is the development of a harmonized test protocol for a valid and reproducible determination of particle size and size distribution which is one of the most relevant physical-chemical properties for MNs.
Different measuring methods provide different results for the size distribution of the particles. This is caused by the different measuring principles of the methods. Each method measures a specific parameter that ultimately determines particle size. First, the measured quantity differs for each method (Scattered light intensity, 2D image / projection, electric mobility, etc.). Second, the calculated diameters of the MN may differ (Feret Diameter, Area Projection, Mobility Diameter, Aerodynamic Diameter, Hydrodynamic Diameter). Third, a measuring method provides a size distribution which is measured either mass-based, surface-based or number-based. A conversion between the results requires additional parameters and thus possibly increases the measurement error.
In addition to the technical differences, the individual parameters are strongly influenced by the structure and material of the nanoparticles. For example, a surface functionalization can lead to very different results in the size distribution. The suitability of measurement methods differs with the material of the MN. As a result, two very different results can be measured for the particle size distribution using two different methods, which are nevertheless both correct. Several large projects in recent years therefore concluded that nanomaterials should be characterized by at least two complementary method. Imaging techniques are regarded as one of these methods for the characterization, the complementary methods are supposed to be statistical methods.
The different results for the size distribution of nanomaterials become problematic for the registration of new MN. A comparable and reproducible size distribution is a prerequisite for a standardized registration. In the future, the particle size distribution in the EU will also decide on the classification of a substance as a nanomaterial or as a non-nanomaterial. Especially in borderline cases, a standardized and comparable measurement methodology is therefore essential.
The properties of nanomaterials are influenced not only by their chemical composition but also by physical properties (such as size, geometry and crystal structure). For the reliable determination and assessment of behaviour and effects of nanomaterials as well as for the determination of the exposure of humans and environment a comprehensive physical-chemical characterization of nanomaterials is essential. This is an important prerequisite to identify them as nanomaterials and to interpret and compare test results and - in future – to forecast interaction and effects of nanomaterials.
In 2006, the OECD launched a sponsorship program for the testing of nanomaterials in which 11 nanomaterials were thoroughly investigated using a variety of methods. The aim of the project was, among other things, to find out where problems occur and where there are gaps in the measurement and test procedures and where are changes required. An important outcome of the sponsorship program was the finding that the OECD Test Guidelines should in several cases be extended to the specific needs in testing of nanomaterials. The existing standardized test methods of the OECD for physical-chemical characterization have not been developed for nanomaterials in particular. A high demand for an extension of the test guidelines was identified. Germany complied with the OECD's request in 2017 and has agreed to extend the “Test Guideline on Particle Size Distribution / Fiber Length and Diameter Distributions Test Guideline” for Manufactured Nanomaterials (MN). UBA commissioned BAM and BAuA with the preparation of the Test Guideline. The aim of the project is the development of a harmonized test protocol for a valid and reproducible determination of particle size and size distribution which is one of the most relevant physical-chemical properties for MNs.
Different measuring methods provide different results for the size distribution of the particles. This is caused by the different measuring principles of the methods. Each method measures a specific parameter that ultimately determines particle size. First, the measured quantity differs for each method (Scattered light intensity, 2D image / projection, electric mobility, etc.). Second, the calculated diameters of the MN may differ (Feret Diameter, Area Projection, Mobility Diameter, Aerodynamic Diameter, Hydrodynamic Diameter). Third, a measuring method provides a size distribution which is measured either mass-based, surface-based or number-based. A conversion between the results requires additional parameters and thus possibly increases the measurement error.
In addition to the technical differences, the individual parameters are strongly influenced by the structure and material of the nanoparticles. For example, a surface functionalization can lead to very different results in the size distribution. The suitability of measurement methods differs with the material of the MN. As a result, two very different results can be measured for the particle size distribution using two different methods, which are nevertheless both correct. Several large projects in recent years therefore concluded that nanomaterials should be characterized by at least two complementary method. Imaging techniques are regarded as one of these methods for the characterization, the complementary methods are supposed to be statistical methods.
The different results for the size distribution of nanomaterials become problematic for the registration of new MN. A comparable and reproducible size distribution is a prerequisite for a standardized registration. In the future, the particle size distribution in the EU will also decide on the classification of a substance as a nanomaterial or as a non-nanomaterial. Especially in borderline cases, a standardized and comparable measurement methodology is therefore essential.
OECD test guideline on particle size and size distribution: Comparability of measurement results
(2019)
OECD-Prüfrichtlinien werden weltweit für regulatorische Zwecke angewandt, da sie eine harmonisierte und über internationale Ringversuche validierte Vorschrift zur Analyse vorgeben. Die bestehende Prüfrichtlinie TG 110 zur Größencharakterisierung von Partikeln und Fasern ist für viele Methoden und Materialklassen nicht geeignet, weswegen es Bedarf an einer Neuentwicklung gibt. Im Fokus der neuen TG steht die reproduzierbare und vergleichbare Anwendung von Methoden zur Bestimmung von Partikelgröße sowie Größenverteilung annährend sphärischer und faserförmiger Nanomaterialien im Bereich 1-1000 nm. Berücksichtigt werden die häufig angewandten Methoden zur Größencharakterisierung mit ihren unterschiedlichen physikalisch-technischen Limitierungen und die Bestimmung unterschiedlicher Durchmesser (hydrodynamischer, Feret…). Weiterhin sind materialspezifische Einflüsse durch die Partikel sowie das Messmedium zu berücksichtigen. Jede der Methoden soll unter Berücksichtigung von ISO-Standards und den materialspezifischen Limitierungen in der neuen Prüfrichtlinie beschrieben und über einen Ringversuch validiert werden.
The OECD test guidelines (TGs) for testing chemicals have been widely used for regulatory purposes all over the world since the establishment of the Mutual Acceptance of Data (MAD) principle in 1984. This MAD principle ensures that, if a chemical is tested under the Good Laboratory Practice (GLP) conditions accordingly to an OECD TG, the data should be accepted in all OECD countries. The TGs have been developed, harmonized, internationally validated (round robin tests) and adopted by OECD countries to be used for the physical-chemical characterisation, fate estimation, and hazard identification for risk assessment of various chemicals. In addition to the TGs, OECD Guidance Documents (GDs) usually provide guidance on how to use TGs and how to interpret the results. These GDs do not have to be fully experimentally validated, and hence they are not under MAD, but they are based on relevant published scientific research.
But are the existing TGs and the related GDs applicable and adequate for the regulatory testing of nanomaterials? In general, it is accepted that most of the "endpoints" or more precisely measurement variables are applicable also for nanomaterials. However, for some endpoints new or amended TGs are needed. In addition, several GDs are needed to give more precise advice on the test performance in order to gain regulatory relevant data on nanomaterials.
The poster will present the status quo on recent TGs and GDs development for nanomaterials at OECD level with relevance for physical-chemical characterisation. Emphasis will be given to the proposed OECD TG on particle size and size distribution for manufactured nanomaterials. The development of such a TG is of special importance as particle size and size distribution is considered as major information for nanomaterial identification and characterization. A reliable and reproducible characterisation of particle size and size distribution is also needed for chemicals risk assessment of nanomaterials, for instance to interpret and compare test results and - in future – to forecast interaction and effects of nanomaterials. The presented poster will illustrate the way from the idea for a new TG and new GD to an accepted OECD TG/GD.