Phase formation and evolution was investigated in the CaO–SiO2 system in the range of 70–80 mol% CaO. The samples were container-less processed in an aerodynamic levitation system and crystallization was followed in situ by synchrotron x-ray diffraction at the beamline P21.1 at the German electron synchrotron (DESY). Modification changes of di- and tricalcium silicate were observed and occurred at lower temperatures than under equilibrium conditions. Despite deep sample undercooling, no metastable phase formation was observed within the measurement timescale of 1 s. For the given cooling rates ranging from 300 K s−1 to about 1 K s−1, no decomposition of tricalcium silicate was observed. No differences in phase evolution were observed between reducing and oxidizing conditions imposed by the levitation gas (Ar and Ar + O2). We demonstrate that this setup has great potential to follow crystallization in refractory oxide liquids in situ. For sub-second primary phase formation faster detection and for polymorph detection adjustments in resolution have to be implemented.
Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained.
Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors.